CN105368020A - 防滴灌带灼伤用可降解地膜 - Google Patents
防滴灌带灼伤用可降解地膜 Download PDFInfo
- Publication number
- CN105368020A CN105368020A CN201510538153.6A CN201510538153A CN105368020A CN 105368020 A CN105368020 A CN 105368020A CN 201510538153 A CN201510538153 A CN 201510538153A CN 105368020 A CN105368020 A CN 105368020A
- Authority
- CN
- China
- Prior art keywords
- film
- drip irrigation
- degradable
- irrigation zone
- burnt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种防滴灌带灼伤用可降解地膜,各原料按重量百分比为:聚乳酸25%-50%、聚己内酯25-50%、聚乙二醇15%-25%、滑石粉5%-10%、增塑剂0.1%-2%。选用聚乳酸作为主要原料,聚乳酸作为一种生物可降解材料具有生物可降解性,能够最终降解为水和二氧化碳,杜绝了不可降解聚乙烯膜对环境的破坏。通过聚乙二醇的引入有效降低聚乳酸的玻璃化温度,改善其加工性能,克服脆性断裂,提高其韧性,加快降解速率;同时有效的改善了材料的疏水性,使得地膜表面具有亲水性,膜上水滴及膜下的水蒸气形成的水滴可以可平铺在膜上,顺着膜表面滑下,杜绝了膜上膜下水滴凸镜的形成,进而起到防止滴灌带灼伤的效果。
Description
技术领域
本发明涉及土壤灌溉的技术领域,具体说是一种防滴灌带灼伤用可降解地膜。
背景技术
膜下滴灌技术作为地膜栽培技术的深化是集覆膜技术与滴灌技术两者优点相结合的一种新型灌溉技术。据目前农户使用情况来看,现今常用的地膜材料大多为疏水性材料,它使得在地膜上下表面的小水珠,无法自由滑落,在阳光照射下形成凸透镜,阳光聚交后,当聚交中心点恰巧落在膜下的滴灌带上时,形成局部高温,将滴灌带面灼伤熔化,影响其正常使用。另一方面,今使用的普通农用地膜多采用不可降解的聚乙烯薄膜或聚丙烯薄膜,它的不可降解性给我们带来了诸多环境问题,一方面是它作为一种白色污染对环境影响较为恶劣,另一方面土地中它的存在也对耕地的可持续利用带来了极大的威胁。
为了解决滴灌带防灼伤这一技术问题,国内外的研究学者也做了一些贡献。一般采用内添及外涂两种改性方法对塑料膜进行改性达到防水滴聚焦的效果,内添加法是将防雾滴剂与树脂相混炼制膜,这样膜的内部和表面都含有许多防雾滴剂分子,使膜面具有防雾滴性;外涂法即在塑料膜的表面涂上含有防雾滴剂的涂层。然内添加法用的防雾滴剂需与树脂的具有相容性及耐高温性等限制了它的使用;而外涂法过程繁琐,也可能产生表面固定不牢等缺点。
为了解决地膜不可降解性,国内外的研究学者也做了一些贡献。现有可降解地膜主要包括:聚乙烯膜改性型地膜、淀粉添加型降解地膜、植物纤维地膜等。其中,聚乙烯膜改性型地膜主要通过在聚乙烯膜主料中添加生物可降解母料来实现的,其主原料仍为不可降解的聚乙烯材料未能从根本上达到完全可降解;淀粉添加型降解地膜的强度、拉伸性、透光性均较差,且降解时间难以控制,存在未到破膜期就降解破碎的问题和不完全降解的问题;纸地膜或麻地膜存在强度低、抗风雨能力差、易破碎、不适宜机械铺膜的问题。因此,现有的降解地膜产品普遍存在缺陷,难以被农民广泛接受。
发明内容
本发明要解决的技术问题是提供一种防滴灌带灼伤用可降解地膜。
本发明为解决公知技术中存在的技术问题所采取的技术方案是:
本发明的防滴灌带灼伤用可降解地膜,各原料按重量百分比为:聚乳酸25%-50%、聚己内酯25-50%、聚乙二醇15%-25%、滑石粉5%-10%、增塑剂0.1%-2%。
本发明还可以采用以下技术措施:
所述的聚乳酸为吹塑级聚乳酸。
所述的聚已内酯为分子量为500-2000。
所述的聚乙二醇的分子量为800-4000。
所述的滑石粉已由聚氨酯树脂乳液进行过表面处理。
所述的增塑剂为亚磷酸三苯酯。
本发明具有的优点和积极效果是:
本发明的防滴灌带灼伤用可降解地膜中,选用聚乳酸作为主要原料,聚乳酸作为一种生物可降解材料具有生物可降解性,能够最终降解为水和二氧化碳,杜绝了不可降解聚乙烯膜对环境的破坏。经过聚氨酯树脂乳液进行表面处理的滑石粉与基体聚乳酸树脂良好结合,既提高材料的热变形温度,又提高冲击强度。通过聚乙二醇的引入有效降低聚乳酸的玻璃化温度,改善其加工性能,克服脆性断裂,提高其韧性,加快降解速率;同时有效的改善了材料的疏水性,使得地膜表面具有亲水性,膜上水滴及膜下的水蒸气形成的水滴可以可平铺在膜上,顺着膜表面滑下,杜绝了膜上膜下水滴凸镜的形成,进而起到防止滴灌带灼伤的效果。
具体实施方式
以下结合实施例对技术方案进行具体说明。
本发明的防滴灌带灼伤用可降解地膜,各原料按重量百分比为:聚乳酸25%-50%、聚己内酯25-50%、聚乙二醇15%-25%、滑石粉5%-10%、增塑剂0.1%-2%。
聚乳酸为吹塑级聚乳酸。
聚已内酯为分子量为500-2000。
聚乙二醇的分子量为800-4000。
滑石粉已由聚氨酯树脂乳液进行过表面处理。
增塑剂为亚磷酸三苯酯。
实施例1:
将原料组成重量比为聚乳酸34%、聚己内酯35%、聚乙二醇25%、滑石粉5%、亚磷酸三苯酯1%的混合物加入高速混合机中,混合均匀后通过双螺杆挤出机挤出造粒,吹塑成膜即得到防滴灌带灼伤用可降解农用地膜。
表1为膜下滴灌带的对比灼烧情况。
表2为本发明的防滴灌带灼伤用可降解地膜的降解情况。
对比采用本发明实施例1制备的地膜与普通农用地膜与滴灌带进行膜下滴灌,滴灌带的灼伤情况如表1可以发现,采用本发明的地膜的滴灌带无灼伤情况发生,而采用普通的农用地膜在3个月就发现了出现部分被灼伤情况。本发明的地膜使用于蔬菜的种植过程中,11月份开始即在蔬菜地上铺膜,其降解情况如表2可见,3个月后膜开始有小部分降解产生破洞,以利于植物根部的呼吸,4个月进入大裂期,地膜大部分降解,6个月后基本没看到明显的地膜残留。
实施例2:
将原料组成重量比为聚乳酸50%、聚己内酯25%、聚乙二醇15%、滑石粉8%、亚磷酸三苯酯2%的混合物加入高速混合机中,混合均匀后通过双螺杆挤出机挤出造粒,吹塑成膜即得到防滴灌带灼伤用可降解农用地膜。
实施例3:
将原料组成重量比为聚乳酸25%、聚己内酯50%、聚乙二醇15%、滑石粉9.9%、亚磷酸三苯酯0.1%的混合物加入高速混合机中,混合均匀后通过双螺杆挤出机挤出造粒,吹塑成膜即得到防滴灌带灼伤用可降解农用地膜。
实施例4:
将原料组成重量比为聚乳酸34%、聚己内酯35%、聚乙二醇20%、滑石粉10%、亚磷酸三苯酯1%的混合物加入高速混合机中,混合均匀后通过双螺杆挤出机挤出造粒,吹塑成膜即得到防滴灌带灼伤用可降解农用地膜。
实施例5:
将原料组成重量比为聚乳酸30%、聚己内酯40%、聚乙二醇20%、滑石粉9.9%、亚磷酸三苯酯0.1%的混合物4加入高速混合机中,混合均匀后通过双螺杆挤出机挤出造粒,吹塑成膜即得到防滴灌带灼伤用可降解农用地膜。
以上所述,仅是本发明的较佳实施例而已,并非对本发明作任何形式上的限制,虽然本发明已以较佳实施例公开如上,然而,并非用以限定本发明,任何熟悉本专业的技术人员,在不脱离本发明技术方案范围内,当然会利用揭示的技术内容作出些许更动或修饰,成为等同变化的等效实施例,但凡是未脱离本发明技术方案的内容,依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰,均属于本发明技术方案的范围内。
Claims (6)
1.一种防滴灌带灼伤用可降解地膜,其特征在于,各原料按重量百分比为:聚乳酸25%-50%、聚己内酯25-50%、聚乙二醇15%-25%、滑石粉5%-10%、增塑剂0.1%-2%。
2.根据权利要求1所述的防滴灌带灼伤用可降解地膜,其特征在于:聚乳酸为吹塑级聚乳酸。
3.根据权利要求1或2所述的防滴灌带灼伤用可降解地膜,其特征在于:聚已内酯为分子量为500-2000。
4.根据权利要求1或2所述的防滴灌带灼伤用可降解地膜,其特征在于:聚乙二醇的分子量为800-4000。
5.根据权利要求1所述的防滴灌带灼伤用可降解地膜,其特征在于:滑石粉已由聚氨酯树脂乳液进行过表面处理。
6.根据权利要求1所述的防滴灌带灼伤用可降解地膜,其特征在于:增塑剂为亚磷酸三苯酯。