CN106279787A - 改性淀粉复合地膜 - Google Patents
改性淀粉复合地膜 Download PDFInfo
- Publication number
- CN106279787A CN106279787A CN201610651483.0A CN201610651483A CN106279787A CN 106279787 A CN106279787 A CN 106279787A CN 201610651483 A CN201610651483 A CN 201610651483A CN 106279787 A CN106279787 A CN 106279787A
- Authority
- CN
- China
- Prior art keywords
- parts
- modified starch
- mulching film
- starch composite
- composite mulching
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种改性淀粉复合地膜,由以下重量份原料组成:聚丙烯20~30份、醋酸酯淀粉50~60份、聚乙烯醇5~10份、增塑剂5~10份、分散剂1~5份、纳米二氧化钛0.5~1.5份。本发明提供的改性淀粉复合地膜具有制备简单、成本较低、可降解、改性淀粉复合安全。
Description
技术领域
本发明属于高分子材料领域,尤其涉及一种改性淀粉复合地膜及其制备方法。
背景技术
地膜为地面复盖薄膜,用于地面复盖,以提高土壤温度,保持土壤水分,维持土壤结构,防止害虫侵袭作物和某些微生物引起的病害等,促进植物生长的功能。地膜复盖技术的推广,也有力地促进了化工、轻工、农机制造、农资供销、交通运输等相关产业的发展。
现有地膜多采用高分子难降解的塑料薄膜,作物收获后残留在土壤中,难以降解,破坏了土壤的原有结构,使土壤失去了保水保肥特性,严重时会引起地下水难于下渗和土壤次生盐碱化严重等后果。
发明内容
本发明目的是针对上述问题,提供一种改性淀粉复合地膜。
本发明通过以下技术方案实现的:
改性淀粉复合地膜,由以下重量份原料组成:
聚丙烯20~30份、醋酸酯淀粉40~60份、聚乙烯醇5~10份、增塑剂5~10份、分散剂1~5份、纳米二氧化钛0.5~1.5份;
本发明通过以下方法制备:
1)将醋酸酯淀粉在80℃条件下烘干备用;
2)将聚丙烯、醋酸酯淀粉、聚乙烯醇、增塑剂、分散剂,纳米二氧化钛、置于高速搅拌机中转速为3000~4000转/min,搅拌5~10min,出料;
3)将步骤2中混合物,在150℃~170℃下热熔挤出吹塑,制成筒状地膜,切割、包装即得。
本发明具有以下优点:
所述醋酸酯淀粉原料选自:郑州百利化工产品有限公司。该醋酸酯淀粉特点是糊的凝沉性低,对酸、碱、热的稳定性高,用作薄膜原料,成膜性能好,且易分解,环保安全。淀粉与聚乙烯醇结合用作成膜剂具有良好的拉伸强度和延伸率,制备薄膜具有和聚乙烯相同的优点。
所述增塑剂为合成植物酯,原料选自:苏州伊格特化工有限公司,是一种新型改性淀粉增塑剂,植物油增塑剂在特定的条件下能被微生物分解,可生物降解。分散剂为乙撑双硬脂酰胺,原料选自深圳市龙华新区大浪中盛塑胶化工厂,牌号EBS-SF,是一类优良分散剂能促进塑料及颗粒助剂分散,还可增加薄膜润滑防粘连;纳米二氧化钛具有光催化性能,可以促进地膜在自然条件下的降解速度更快。
本发明制备过程简单,易于操作和控制,制备成本低廉,产品性能优异和稳定,本发明原料能够相互作用,使得本发明淀粉/聚丙烯可降解复合材料在淀粉含量比较高的前提下,体现出优异的力学性能和一定的耐高温性。实现塑料制品的完全可降解,且降解产物对环境无污染,因而是一种新型环境友好产品。
具体实施方式
实施例1:
原料按以下比例选取:
聚丙烯25份、醋酸酯淀粉55份、聚乙烯醇9份、增塑剂7份、分散剂2份、纳米二氧化钛0.8份;
制备步骤:
1)将醋酸酯淀粉在80℃条件下烘干;
2)将聚丙烯、醋酸酯淀粉、增塑剂、分散剂、纳米二氧化钛、置于高速搅拌机中转速为3000转/min,搅拌6min,出料;
3)将步骤2中混合物,在155℃下热熔挤出吹塑,制成筒状地膜,切割、包装即得。
实施例2:
原料按以下比例选取:
聚丙烯22、醋酸酯淀粉58、聚乙烯醇7、增塑剂8份、分散剂3份、纳米二氧化钛1份;
制备步骤:
1)将醋酸酯淀粉在80℃条件下烘干;
2)将聚丙烯、醋酸酯淀粉、聚乙烯醇、增塑剂、分散剂、纳米二氧化钛、置于高速搅拌机中转速为3500转/min,搅拌5min,出料;
3)将步骤2中混合物,在160℃下热熔挤出吹塑,制成筒状地膜,切割、包装即得。
实施例3:
原料按以下比例选取:
聚丙烯30、醋酸酯淀粉52、聚乙烯醇5、增塑剂6份、分散剂2份、纳米二氧化钛0.8份;
制备步骤:
1)将醋酸酯淀粉在80℃条件下烘干;
2)将聚丙烯、醋酸酯淀粉、聚乙烯醇、增塑剂、分散剂、纳米二氧化钛、置于高速搅拌机中转速为3800转/min,搅拌6min,出料;
3)将步骤2中混合物,在170℃下热熔挤出吹塑,制成筒状地膜,切割、包装即得。
以上所提供的内容,仅为本发明改性淀粉复合地膜及其制造方法的较佳实施例而已,当然不能以此来限定本发明之权利范围,因此依本发明申请专利范围所作的等同变化,仍属本发明所涵盖的范围。
性能测试:
根据实施例1~3所得地膜,力学性能及透光性能按照GB/T1040.3和GB/T2410-2008进行测试,结果如下表:
Claims (5)
1.改性淀粉复合地膜,其特征在于,所述改性淀粉复合地膜包括以下重量原料份组成:
聚丙烯20~30份、醋酸酯淀粉40~60份、聚乙烯醇5~10份、增塑剂5~10份、分散剂1~5份、纳米二氧化钛0.5~1.5份。
2.根据权利要求1所述的改性淀粉复合地膜,其特征在于,所述增塑剂为合成植物酯。
3.根据权利要求1所述改性淀粉复合地膜,其特征在于,所述分散剂为乙撑双硬脂酰胺。
4.根据权利要求1所述改性淀粉复合地膜,其特征在于,所述纳米二氧化钛为锐钛型纳米二氧化钛。
5.根据权利要求1所述改性淀粉复合地膜的制备方法,包括以下步骤:
1)将醋酸酯淀粉在80℃条件下烘干备用;
2)将聚丙烯、醋酸酯淀粉、聚乙烯醇、增塑剂、分散剂,纳米二氧化钛、置于高速搅拌机中转速为3000~4000转/min,搅拌5~10min,出料;
3)将步骤2中混合物,在150℃~170℃下熔融挤出吹塑,制成筒状地膜,切割、包装即得。