CN105360163A - Bamboo wood mould inhibitor and preparation method thereof - Google Patents
Bamboo wood mould inhibitor and preparation method thereof Download PDFInfo
- Publication number
- CN105360163A CN105360163A CN201510800134.6A CN201510800134A CN105360163A CN 105360163 A CN105360163 A CN 105360163A CN 201510800134 A CN201510800134 A CN 201510800134A CN 105360163 A CN105360163 A CN 105360163A
- Authority
- CN
- China
- Prior art keywords
- sodium
- bamboo wood
- mould inhibitor
- wood mould
- nitrophenol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a bamboo wood mould inhibitor and a preparation method thereof, and the bamboo wood mould inhibitor comprises the following raw material components by weight: 7-9% of ammonium sulfate, 6-8% of sodium pentachlorophenol, 7-9% of sodium benzoate, 11-16% of uric acid, dimethyl dithiocarbamate 3-4% of copper dimethyldithiocarbamate, 11-13% of Tert-Butylhydroquinone, 11-15% of dilauryl thiodipropionate, 6-9% of dodecyl trimethyl ammonium chloride, 4-6% of nitrophenol, 11-14% of tung oil, 6-8% of sodium dichromate and 4-5% of chlorothalonil. By a preparation method provided by the invention, bamboo wood product bacteria elimination can be further improved, bacteria can be prevented from greatly breeding, and the preparation process is simple and easy to further expand and use.
Description
Technical field
The present invention relates to bamboo processing technical field, be specifically related to a kind of bamboo wood mould inhibitor and preparation method thereof.
Background technology
Bamboo country is the earliest studied, cultivates and utilized in China in the world, and mao bamboon is that Chinese cultivated is long, area the widest, economic worth also most important bamboo kind.Its pole type is thick, should supply for building, and as beam column, frame, scaffold etc., the thin bamboo strip is excellent, for apparatus and the handicraft of the various thickness of braiding.
But bamboo is in the process of processing; usually can produce some common mildew phenomenas; when businessman stores or be placed on for a long time inside family and do not use; or the place stored is comparatively moist; bamboo product surface can be caused to occur that one is gone mouldy; not only have impact on the aesthetic property of bamboo product; surface is distributed, and the smell is awful; timber is as important house ornamentation apparatus; in use because coarse the causing of manufacture craft goes mouldy; also make the quality of bamboo wood products after going mouldy reduce, resistance to compression, resistance to tension declines simultaneously.
Summary of the invention
For the deficiencies in the prior art, the invention provides a kind of bamboo wood mould inhibitor and preparation method thereof, bamboo wood surface when depositing use is not easily produced and goes mouldy.
For realizing above object, the present invention is achieved by the following technical programs:
A kind of bamboo wood mould inhibitor, the components by weight percent of raw material is: ammonium sulfate 7-9%, penta sodium pentachlorophenate 6-8%, Sodium Benzoate 7-9%, uric acid 11-16%, cupric dimethyldithio carbamate 3-4%, ditert-butylhydro quinone 11-13%, dilauryl thiodipropionate 11-15%, Dodecyl trimethyl ammonium chloride 6-9%, nitrophenol 4-6%, tung oil 11-14%, sodium dichromate 6-8%, tpn 4-5%.
Preferably, the components by weight percent of raw material is: ammonium sulfate 7-8%, penta sodium pentachlorophenate 7-8%, Sodium Benzoate 7-9%, uric acid 12-14%, cupric dimethyldithio carbamate 3-4%, ditert-butylhydro quinone 12-13%, dilauryl thiodipropionate 11-14%, Dodecyl trimethyl ammonium chloride 7-8%, nitrophenol 4-6%, tung oil 12-14%, sodium dichromate 6-8%, tpn 4-5%.
Preferably, the components by weight percent of raw material is: ammonium sulfate 7%, penta sodium pentachlorophenate 7%, Sodium Benzoate 7%, uric acid 13%, cupric dimethyldithio carbamate 3%, ditert-butylhydro quinone 13%, dilauryl thiodipropionate 12%, Dodecyl trimethyl ammonium chloride 7%, nitrophenol 5%, tung oil 14%, sodium dichromate 7%, tpn 5%.
The preparation method of described bamboo wood mould inhibitor, step is as follows:
1) by pulp furnish, add suitable quantity of water, raw material sulphuric acid ammonium, penta sodium pentachlorophenate, Sodium Benzoate, uric acid, cupric dimethyldithio carbamate, ditert-butylhydro quinone, dilauryl thiodipropionate, Dodecyl trimethyl ammonium chloride, nitrophenol are put into container heating water bath and stirred, control temperature 60-70 DEG C, pressure 0.6-0.7MPa, the reaction time is 40-50 minute;
2) pressure is adjusted to normal pressure, control temperature is 40-50 DEG C, continues to add tung oil, sodium dichromate, tpn, continue stirring reaction 20-30 minute, naturally cool in reactant.
The invention provides a kind of bamboo wood mould inhibitor and preparation method thereof, raw material adopted in the product is all raw materials that market at prices is comparatively cheap, the processing cost of production can be reduced, the composition of penta sodium pentachlorophenate effectively can not only play the effect of desinsection to the moth of bamboo wood surface, and effectively can also play the effect suppressing the growth of sick worm, in the scope of pulp furnish, the ditert-butylhydro quinone composition added has non-oxidizability, effectively can suppress bacillus subtilis, staphylococcus aureus, Escherichia coli; Dodecyl trimethyl ammonium chloride, tpn also have effect of certain disinfection, sodium dichromate is as the application of strong oxidizing property, further bacterium colony residual in bamboo wood can be killed, and the tung oil composition added in the feed can make bamboo and wood products smear bamboo provided by the invention wood mould inhibitor, with the air exclusion in the external world, the oxygen gas component in air and its bamboo and wood products is avoided to be oxidized, cause certain corrosion, avoid providing oxygen to make it grow further to bacterium colony, go mouldy and affect the use of bamboo wood.
Preparation technology of the present invention is also comparatively simple, is convenient to further genralrlization application.
Embodiment
For making the object of the embodiment of the present invention, technical scheme and advantage clearly, below in conjunction with embodiments of the invention, the technical scheme in the embodiment of the present invention is clearly and completely described.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
Embodiment 1:
The present embodiment provides a kind of bamboo wood mould inhibitor, and the components by weight percent of raw material is: ammonium sulfate 7%, penta sodium pentachlorophenate 7%, Sodium Benzoate 7%, uric acid 13%, cupric dimethyldithio carbamate 3%, ditert-butylhydro quinone 13%, dilauryl thiodipropionate 12%, Dodecyl trimethyl ammonium chloride 7%, nitrophenol 5%, tung oil 14%, sodium dichromate 7%, tpn 5%.
The preparation method of bamboo wood mould inhibitor, step is as follows:
1) by pulp furnish, add suitable quantity of water, raw material sulphuric acid ammonium, penta sodium pentachlorophenate, Sodium Benzoate, uric acid, cupric dimethyldithio carbamate, ditert-butylhydro quinone, dilauryl thiodipropionate, Dodecyl trimethyl ammonium chloride, nitrophenol are put into container heating water bath and stirred, control temperature 60-70 DEG C, pressure 0.6-0.7MPa, the reaction time is 40-50 minute;
2) pressure is adjusted to normal pressure, control temperature is 40-50 DEG C, continues to add tung oil, sodium dichromate, tpn, continue stirring reaction 20-30 minute, naturally cool in reactant.
Embodiment 2:
The present embodiment provides a kind of bamboo wood mould inhibitor, and the components by weight percent of raw material is: ammonium sulfate 8%, penta sodium pentachlorophenate 8%, Sodium Benzoate 8%, uric acid 12%, cupric dimethyldithio carbamate 4%, ditert-butylhydro quinone 12%, dilauryl thiodipropionate 13%, Dodecyl trimethyl ammonium chloride 7%, nitrophenol 4%, tung oil 12%, sodium dichromate 8%, tpn 4%.
The preparation method of bamboo wood mould inhibitor, step is as follows:
1) by pulp furnish, add suitable quantity of water, raw material sulphuric acid ammonium, penta sodium pentachlorophenate, Sodium Benzoate, uric acid, cupric dimethyldithio carbamate, ditert-butylhydro quinone, dilauryl thiodipropionate, Dodecyl trimethyl ammonium chloride, nitrophenol are put into container heating water bath and stirred, control temperature 60-70 DEG C, pressure 0.6-0.7MPa, the reaction time is 40-50 minute;
2) pressure is adjusted to normal pressure, control temperature is 40-50 DEG C, continues to add tung oil, sodium dichromate, tpn, continue stirring reaction 20-30 minute, naturally cool in reactant.
Embodiment 3:
The present embodiment provides the present embodiment to provide a kind of bamboo wood mould inhibitor, and the components by weight percent of raw material is: ammonium sulfate 9%, penta sodium pentachlorophenate 6%, Sodium Benzoate 9%, uric acid 16%, cupric dimethyldithio carbamate 3%, ditert-butylhydro quinone 11%, dilauryl thiodipropionate 11%, Dodecyl trimethyl ammonium chloride 6%, nitrophenol 4%, tung oil 14%, sodium dichromate 6%, tpn 5%.
The preparation method of bamboo wood mould inhibitor, step is as follows:
1) by pulp furnish, add suitable quantity of water, raw material sulphuric acid ammonium, penta sodium pentachlorophenate, Sodium Benzoate, uric acid, cupric dimethyldithio carbamate, ditert-butylhydro quinone, dilauryl thiodipropionate, Dodecyl trimethyl ammonium chloride, nitrophenol are put into container heating water bath and stirred, control temperature 60-70 DEG C, pressure 0.6-0.7MPa, the reaction time is 40-50 minute;
2) pressure is adjusted to normal pressure, control temperature is 40-50 DEG C, continues to add tung oil, sodium dichromate, tpn, continue stirring reaction 20-30 minute, naturally cool in reactant.
Embodiment 4:
The present embodiment provides the present embodiment to provide a kind of bamboo wood mould inhibitor, and the components by weight percent of raw material is: ammonium sulfate 7%, penta sodium pentachlorophenate 6%, Sodium Benzoate 7%, uric acid 11%, cupric dimethyldithio carbamate 4%, ditert-butylhydro quinone 11%, dilauryl thiodipropionate 15%, Dodecyl trimethyl ammonium chloride 9%, nitrophenol 6%, tung oil 11%, sodium dichromate 8%, tpn 5%.
The preparation method of bamboo wood mould inhibitor, step is as follows:
1) by pulp furnish, add suitable quantity of water, raw material sulphuric acid ammonium, penta sodium pentachlorophenate, Sodium Benzoate, uric acid, cupric dimethyldithio carbamate, ditert-butylhydro quinone, dilauryl thiodipropionate, Dodecyl trimethyl ammonium chloride, nitrophenol are put into container heating water bath and stirred, control temperature 60-70 DEG C, pressure 0.6-0.7MPa, the reaction time is 40-50 minute;
2) pressure is adjusted to normal pressure, control temperature is 40-50 DEG C, continues to add tung oil, sodium dichromate, tpn, continue stirring reaction 20-30 minute, naturally cool in reactant.
Above embodiment only in order to technical scheme of the present invention to be described, is not intended to limit; Although with reference to previous embodiment to invention has been detailed description, those of ordinary skill in the art is to be understood that: it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature; And these amendments or replacement, do not make the essence of appropriate technical solution depart from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (4)
1. a bamboo wood mould inhibitor, it is characterized in that, the components by weight percent of raw material is: ammonium sulfate 7-9%, penta sodium pentachlorophenate 6-8%, Sodium Benzoate 7-9%, uric acid 11-16%, cupric dimethyldithio carbamate 3-4%, ditert-butylhydro quinone 11-13%, dilauryl thiodipropionate 11-15%, Dodecyl trimethyl ammonium chloride 6-9%, nitrophenol 4-6%, tung oil 11-14%, sodium dichromate 6-8%, tpn 4-5%.
2. bamboo wood mould inhibitor as claimed in claim 1, it is characterized in that, the components by weight percent of raw material is: ammonium sulfate 7-8%, penta sodium pentachlorophenate 7-8%, Sodium Benzoate 7-9%, uric acid 12-14%, cupric dimethyldithio carbamate 3-4%, ditert-butylhydro quinone 12-13%, dilauryl thiodipropionate 11-14%, Dodecyl trimethyl ammonium chloride 7-8%, nitrophenol 4-6%, tung oil 12-14%, sodium dichromate 6-8%, tpn 4-5%.
3. bamboo wood mould inhibitor as claimed in claim 2, it is characterized in that, the components by weight percent of raw material is: ammonium sulfate 7%, penta sodium pentachlorophenate 7%, Sodium Benzoate 7%, uric acid 13%, cupric dimethyldithio carbamate 3%, ditert-butylhydro quinone 13%, dilauryl thiodipropionate 12%, Dodecyl trimethyl ammonium chloride 7%, nitrophenol 5%, tung oil 14%, sodium dichromate 7%, tpn 5%.
4. the preparation method of the bamboo wood mould inhibitor as described in any one of claim 1-3, it is characterized in that, step is as follows:
1) by pulp furnish, add suitable quantity of water, raw material sulphuric acid ammonium, penta sodium pentachlorophenate, Sodium Benzoate, uric acid, cupric dimethyldithio carbamate, ditert-butylhydro quinone, dilauryl thiodipropionate, Dodecyl trimethyl ammonium chloride, nitrophenol are put into container heating water bath and stirred, control temperature 60-70 DEG C, pressure 0.6-0.7MPa, the reaction time is 40-50 minute;
2) pressure is adjusted to normal pressure, control temperature is 40-50 DEG C, continues to add tung oil, sodium dichromate, tpn, continue stirring reaction 20-30 minute, naturally cool in reactant.