CN107956119A - A kind of preparation method embroidered with anti-acarus and bacteria finishing agent - Google Patents
A kind of preparation method embroidered with anti-acarus and bacteria finishing agent Download PDFInfo
- Publication number
- CN107956119A CN107956119A CN201711238677.9A CN201711238677A CN107956119A CN 107956119 A CN107956119 A CN 107956119A CN 201711238677 A CN201711238677 A CN 201711238677A CN 107956119 A CN107956119 A CN 107956119A
- Authority
- CN
- China
- Prior art keywords
- parts
- acarus
- good
- finishing agent
- embroidery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
This application discloses a kind of preparation method embroidered with anti-acarus and bacteria finishing agent, deionized water, castor oil, accelerating agent, sodium dichromate, vinyl acetate resin, fibroin, aluminium oxide, fatty alcohol polyoxyethylene ether, aluminum acetate, glacial acetic acid and ethylene glycol are weighed；Anti-mold effect is good, 3.2 3.8MPa of tensile strength, and resistance to moisture is excellent；It is of low cost, increase gloss, adhesion 1 grade, good corrosion resistance, wash durability is good, water-fastness 450 550 times；Anti-mite sterilizing ability is strong, and resistance to 80 120 acarids of soaping property walk quickly and keep away rate 92 96%, pliability 1mm, and glossiness is good；Fabric is with a good drape effect, extends embroidery service life, fast drying, fire resistance is good, and anti-microbial property is good, to Escherichia coli bacteriostasis rate 99.7 99.9%, to staphylococcus aureus bacteriostasis rate 99.95 99.99%, to Candida albicans bacteriostasis rate 98.5 99.5%.
Description
Technical field
The application belongs to embroidery material field, more particularly to a kind of preparation method embroidered with anti-acarus and bacteria finishing agent.
Background technology
Embroidery preservation difficulty is larger, and just because of this, the value of ancient times embroidery is far more than other collectibles.Qing Dynasty's embroidery preserves
So far most of colors come off, discoloration, or have begun to rot, and existing preservation preferably embroidery is Gansu collection among the people
《Happiness,position and longevity》, the most of discoloration of common Qing Dynasty embroidery on the market, embroidery art is thicker, and composition is simple, still《Happiness,position and longevity》Long 260cm
Wide 110cm is intact so far, bright-colored, and embroidery art is fine, and personage is life-like, and generic name man embroidery, this collection was once used for
The Republic of China's presidential palace is celebrated a festival or central scroll during birthday.Such embroidery is extremely rare, in the market only this, it is worth far more than thousand
Ten thousand, it is precious non-material cultural heritage except having higher reserve value, also very deep cultural deposits.
Cross embroidery is also referred to as cross peach blossom, is a kind of traditional embroidering method in widespread among the people.Its skill of handling needles very simple,
Oriented according to the longitude and latitude of cloth, the Saint Andrew's cross shape stitching of equal size is arranged in the pattern of design requirement.Due to its skill of handling needles
Feature, the general moulding of grain pattern of cross embroidery is terse, of a tightly knit structure, often in the pictorial style of symmetrical layout.Also there is realistic style
Grain pattern, subject matter is mostly nature flowers and plants.Cross embroidery has strong decorated style among the people.
Pyridine quaternary ammonium salt（Tie up orchid PF, water-proofing agent PF etc.）, it is the waterproofing agent of durability suitable for cotton and polyester-cotton blend yarn fabric.
The combination of acid amides, alcohol is mainly used for the water-proofing treatment of natural fiber and synthetic fibers.Organo-silicon compound：Generally by containing hydrogen silicone oil
Formed with methyl-silicone oil or hydroxy silicon oil.Cellulose fibre, wool, silk and various synthetic fabrics are widely used in, is being closed
It is first-class in cotton into the waterproof effect on fiber and durability ratio.
Nano silver is acted on cell membrane protein, can directly destroy bacterial cell membrane and oxygen metabolism enzyme（-SH）With reference to resistance
Hinder absorption of the microorganisms such as bacterium to nutriment necessary to the growth such as amino acid, uracil, so that suppress its growth, and this is only
The special mechanism of action, can kill the microorganisms such as most bacteriums, fungi.
With fixed hydrophilic lipophilic group, aligned in the surface energy of solution, and surface tension can be remarkably decreased
Material, Gu potent permeability can be kept.
Gorgeous band, which is embroidered, is also referred to as bandlet embroidery, is directly embroidered on the fabric using silk ribbon as embroider line.Gorgeous band embroidery gloss is soft and graceful, color
Coloured silk is abundant, decorative pattern is eye-catching and has three-dimensional sense, is a kind of new and original kimonos decorative form.Drawn work is embroidered, and is to have very much spy in embroidery
One classification of color, its embroidery method are, according to the position of layout, first to pump a certain number of warp thread and weft yarn on the fabric,
Then using the cloth silk left on cloth cover, regular volume is carried out around ligation with embroider line, the yarn eye of open-work is compiled out, is combined into various
Pattern line kind.Embroidering embroidery face with drawn work has unique mesh effect, and beautiful dainty, tinkling of pieces of jade class is exquisitely carved, decorative very strong.Due to making thoroughly
Acquire a certain degree of difficulty, it is mostly simple geometry lines and block face that pattern is embroidered in drawn work, makees exquisite exquisite intersperse in a width embroidery.
The content of the invention
The technical problem of solution：
The application is directed to above-mentioned technical problem, there is provided a kind of preparation method embroidered with anti-acarus and bacteria finishing agent, solves existing thorn
Embroider with technical problems such as poor, the low and anti-mite sterilizing ability differences of glossiness of anti-acarus and bacteria finishing agent anti-mold effect.
Technical solution：
A kind of preparation method embroidered with anti-acarus and bacteria finishing agent, includes the following steps：
The first step：According to parts by weight proportioning weigh 100 parts of deionized water, 1.5-5.5 parts of castor oil, 1.5-5.5 parts of accelerating agent,
8-12 parts of sodium dichromate, 3-7 parts of vinyl acetate resin, 10-30 parts of fibroin, 4-12 parts of aluminium oxide, fatty alcohol polyoxyethylene ether
2-6 parts of 0.1-0.5 parts, 4-8 parts of aluminum acetate, 0.5-4.5 parts of glacial acetic acid and ethylene glycol；
Second step：Sodium dichromate, aluminium oxide and aluminum acetate are put into grinder and grind 10-20min, then input carries temperature
In the reaction kettle of meter, mixer and heating unit, open mixer and start to mix, be gradually heating to 40-80 DEG C, mixing velocity is
200-400r/min, mixes 120-160min；
3rd step：Sequentially add vinyl acetate resin, deionized water and castor oil, adjust mixing velocity to 400-600 r/min,
6-10h is mixed, is warming up to 100-140 DEG C, adds surplus stock, stirs 50-90min, is put into sand mill, 20- is sanded
40min, after filtering to obtain the final product.
As a preferred technical solution of the present invention：Embroidery is pressed with the raw material of anti-acarus and bacteria finishing agent in the first step
Parts by weight proportioning is as follows：100 parts of deionized water, 1.5 parts of castor oil, 1.5 parts of accelerating agent, 8 parts of sodium dichromate, vinyl acetate tree
3 parts of fat, 10 parts of fibroin, 4 parts of aluminium oxide, 0.1 part of fatty alcohol polyoxyethylene ether, 4 parts of aluminum acetate, 0.5 part of glacial acetic acid and ethylene glycol 2
Part.
As a preferred technical solution of the present invention：Embroidery is pressed with the raw material of anti-acarus and bacteria finishing agent in the first step
Parts by weight proportioning is as follows：100 parts of deionized water, 5.5 parts of castor oil, 5.5 parts of accelerating agent, 12 parts of sodium dichromate, vinyl acetate
7 parts of resin, 30 parts of fibroin, 12 parts of aluminium oxide, 0.5 part of fatty alcohol polyoxyethylene ether, 8 parts of aluminum acetate, 4.5 parts of glacial acetic acid and second two
6 parts of alcohol.
As a preferred technical solution of the present invention：Embroidery is pressed with the raw material of anti-acarus and bacteria finishing agent in the first step
Parts by weight proportioning is as follows：100 parts of deionized water, 3.5 parts of castor oil, 3.5 parts of accelerating agent, 10 parts of sodium dichromate, vinyl acetate
5 parts of resin, 20 parts of fibroin, 8 parts of aluminium oxide, 0.3 part of fatty alcohol polyoxyethylene ether, 6 parts of aluminum acetate, 2.5 parts of glacial acetic acid and second two
4 parts of alcohol.
As a preferred technical solution of the present invention：The accelerating agent uses zinc-ethylphenyl dithiocarbamate.
Beneficial effect：
A kind of embroidery of the present invention uses above technical scheme and prior art phase with the preparation method of anti-acarus and bacteria finishing agent
Than having following technique effect：1st, preparation method is simple, and anti-mold effect is good, tensile strength 3.2-3.8MPa, and resistance to moisture is excellent
It is good；2nd, it is of low cost, increase gloss, adhesion 1 grade, good corrosion resistance, wash durability is good, 450-550 times water-fastness；3rd, prevent
Acarus and bacteria ability is strong, and resistance to 80-120 acarid of soaping property walks quickly and keeps away rate 92-96%, pliability 1mm, and glossiness is good；4th, fabric hangs down sense
It is good, extend embroidery service life, fast drying, fire resistance is good, and anti-microbial property is good, to Escherichia coli bacteriostasis rate 99.7-99.9%,
To staphylococcus aureus bacteriostasis rate 99.95-99.99%, to Candida albicans bacteriostasis rate 98.5-99.5%, can produce extensively
And constantly replace current material.
Embodiment
Embodiment 1:
100 parts of deionized water, 1.5 parts of castor oil, zinc-ethylphenyl dithiocarbamate 1.5 are weighed according to parts by weight proportioning
Part, 8 parts of sodium dichromate, 3 parts of vinyl acetate resin, 10 parts of fibroin, 4 parts of aluminium oxide, 0.1 part of fatty alcohol polyoxyethylene ether, acetic acid
2 parts of 4 parts of aluminium, 0.5 part of glacial acetic acid and ethylene glycol.
Sodium dichromate, aluminium oxide and aluminum acetate are put into grinder and grind 10min, then input carries thermometer, stirs
In the reaction kettle for mixing machine and heating unit, open mixer and start to mix, be gradually heating to 40 DEG C, mixing velocity 200r/
Min, mixes 120min.
Vinyl acetate resin, deionized water and castor oil are sequentially added, adjusting mixing velocity to 400 r/min, mixes 6h,
Be warming up to 100 DEG C, add surplus stock, stir 50min, put into sand mill, 20min is sanded, after filtering to obtain the final product.
Preparation method is simple, and anti-mold effect is good, tensile strength 3.2MPa, and resistance to moisture is excellent；It is of low cost, increase light
Pool, adhesion 1 grade, good corrosion resistance, wash durability is good, water-fastness 450 times；Anti-mite sterilizing ability is strong, resistance to soaping property 80 times
Acarid walks quickly and keeps away rate 92%, pliability 1mm, and glossiness is good；Fabric is with a good drape effect, extends embroidery service life, fast drying, fire resistance
Good, anti-microbial property is good, to Escherichia coli bacteriostasis rate 99.7%, to staphylococcus aureus bacteriostasis rate 99.95%, to Candida albicans
Bacteriostasis rate 98.5%, can extensively produce and constantly replace current material.
Embodiment 2:
100 parts of deionized water, 5.5 parts of castor oil, zinc-ethylphenyl dithiocarbamate 5.5 are weighed according to parts by weight proportioning
Part, 12 parts of sodium dichromate, 7 parts of vinyl acetate resin, 30 parts of fibroin, 12 parts of aluminium oxide, 0.5 part of fatty alcohol polyoxyethylene ether, vinegar
6 parts of sour 8 parts of aluminium, 4.5 parts of glacial acetic acid and ethylene glycol.
Sodium dichromate, aluminium oxide and aluminum acetate are put into grinder and grind 20min, then input carries thermometer, stirs
In the reaction kettle for mixing machine and heating unit, open mixer and start to mix, be gradually heating to 80 DEG C, mixing velocity 400r/
Min, mixes 160min.
Vinyl acetate resin, deionized water and castor oil are sequentially added, adjusts mixing velocity to 600 r/min, mixing
10h, is warming up to 140 DEG C, adds surplus stock, stirs 90min, puts into sand mill, 40min is sanded, after filtering to obtain the final product.
Preparation method is simple, and anti-mold effect is good, tensile strength 3.5MPa, and resistance to moisture is excellent；It is of low cost, increase light
Pool, adhesion 1 grade, good corrosion resistance, wash durability is good, water-fastness 500 times；Anti-mite sterilizing ability is strong, resistance to soaping property 100 times
Acarid walks quickly and keeps away rate 94%, pliability 1mm, and glossiness is good；Fabric is with a good drape effect, extends embroidery service life, fast drying, fire resistance
Good, anti-microbial property is good, to Escherichia coli bacteriostasis rate 99.8%, to staphylococcus aureus bacteriostasis rate 99.97%, to Candida albicans
Bacteriostasis rate 99%, can extensively produce and constantly replace current material.
Embodiment 3:
100 parts of deionized water, 3.5 parts of castor oil, zinc-ethylphenyl dithiocarbamate 3.5 are weighed according to parts by weight proportioning
Part, 10 parts of sodium dichromate, 5 parts of vinyl acetate resin, 20 parts of fibroin, 8 parts of aluminium oxide, 0.3 part of fatty alcohol polyoxyethylene ether, acetic acid
4 parts of 6 parts of aluminium, 2.5 parts of glacial acetic acid and ethylene glycol.
Sodium dichromate, aluminium oxide and aluminum acetate are put into grinder and grind 15min, then input carries thermometer, stirs
In the reaction kettle for mixing machine and heating unit, open mixer and start to mix, be gradually heating to 60 DEG C, mixing velocity 300r/
Min, mixes 140min.
Vinyl acetate resin, deionized water and castor oil are sequentially added, adjusting mixing velocity to 500 r/min, mixes 8h,
Be warming up to 120 DEG C, add surplus stock, stir 70min, put into sand mill, 30min is sanded, after filtering to obtain the final product.
Preparation method is simple, and anti-mold effect is good, tensile strength 3.8MPa, and resistance to moisture is excellent；It is of low cost, increase light
Pool, adhesion 1 grade, good corrosion resistance, wash durability is good, water-fastness 550 times；Anti-mite sterilizing ability is strong, resistance to soaping property 120 times
Acarid walks quickly and keeps away rate 96%, pliability 1mm, and glossiness is good；Fabric is with a good drape effect, extends embroidery service life, fast drying, fire resistance
Good, anti-microbial property is good, to Escherichia coli bacteriostasis rate 99.9%, to staphylococcus aureus bacteriostasis rate 99.99%, to Candida albicans
Bacteriostasis rate 99.5%, can extensively produce and constantly replace current material.
Composition all components in above example can be commercially available.
The above embodiments are merely intended to illustrate the present invention rather than to limit it, therefore with the present invention's
Any change in claims suitable implication and scope, should be construed as being included in the scope of the claims.
Claims (5)
1. a kind of preparation method embroidered with anti-acarus and bacteria finishing agent, it is characterised in that include the following steps：
The first step：According to parts by weight proportioning weigh 100 parts of deionized water, 1.5-5.5 parts of castor oil, 1.5-5.5 parts of accelerating agent,
8-12 parts of sodium dichromate, 3-7 parts of vinyl acetate resin, 10-30 parts of fibroin, 4-12 parts of aluminium oxide, fatty alcohol polyoxyethylene ether
2-6 parts of 0.1-0.5 parts, 4-8 parts of aluminum acetate, 0.5-4.5 parts of glacial acetic acid and ethylene glycol；
Second step：Sodium dichromate, aluminium oxide and aluminum acetate are put into grinder and grind 10-20min, then input carries temperature
In the reaction kettle of meter, mixer and heating unit, open mixer and start to mix, be gradually heating to 40-80 DEG C, mixing velocity is
200-400r/min, mixes 120-160min；
3rd step：Sequentially add vinyl acetate resin, deionized water and castor oil, adjust mixing velocity to 400-600 r/min,
6-10h is mixed, is warming up to 100-140 DEG C, adds surplus stock, stirs 50-90min, is put into sand mill, 20- is sanded
40min, after filtering to obtain the final product.
2. the preparation method of the anti-acarus and bacteria finishing agent of embroidery according to claim 1, it is characterised in that：The first step
Middle embroidery is as follows with the raw materials by weight portion proportioning of anti-acarus and bacteria finishing agent：100 parts of deionized water, 1.5 parts of castor oil, promote
1.5 parts of agent, 8 parts of sodium dichromate, 3 parts of vinyl acetate resin, 10 parts of fibroin, 4 parts of aluminium oxide, 0.1 part of fatty alcohol polyoxyethylene ether,
2 parts of 4 parts of aluminum acetate, 0.5 part of glacial acetic acid and ethylene glycol.
3. the preparation method of the anti-acarus and bacteria finishing agent of embroidery according to claim 1, it is characterised in that：The first step
Middle embroidery is as follows with the raw materials by weight portion proportioning of anti-acarus and bacteria finishing agent：100 parts of deionized water, 5.5 parts of castor oil, promote
5.5 parts of agent, 12 parts of sodium dichromate, 7 parts of vinyl acetate resin, 30 parts of fibroin, 12 parts of aluminium oxide, fatty alcohol polyoxyethylene ether 0.5
Part, 8 parts of aluminum acetate, 4.5 parts of glacial acetic acid and 6 parts of ethylene glycol.
4. the preparation method of the anti-acarus and bacteria finishing agent of embroidery according to claim 1, it is characterised in that：The first step
Middle embroidery is as follows with the raw materials by weight portion proportioning of anti-acarus and bacteria finishing agent：100 parts of deionized water, 3.5 parts of castor oil, promote
3.5 parts of agent, 10 parts of sodium dichromate, 5 parts of vinyl acetate resin, 20 parts of fibroin, 8 parts of aluminium oxide, fatty alcohol polyoxyethylene ether 0.3
Part, 6 parts of aluminum acetate, 2.5 parts of glacial acetic acid and 4 parts of ethylene glycol.
5. the preparation method of the anti-acarus and bacteria finishing agent of embroidery according to claim 1, it is characterised in that：The accelerating agent
Using zinc-ethylphenyl dithiocarbamate.