CN105347757B - 一种无机保温砂浆 - Google Patents
一种无机保温砂浆 Download PDFInfo
- Publication number
- CN105347757B CN105347757B CN201510811516.9A CN201510811516A CN105347757B CN 105347757 B CN105347757 B CN 105347757B CN 201510811516 A CN201510811516 A CN 201510811516A CN 105347757 B CN105347757 B CN 105347757B
- Authority
- CN
- China
- Prior art keywords
- parts
- heat insulation
- insulation mortar
- mortar
- sebs
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种无机保温砂浆配方，其重量组成如下：水泥70‑90份、粉煤灰18‑22份、重钙0‑10份、淀粉醚0.05份、纤维素醚0.75份、木质纤维0.04份、PP纤维0.02份、5044N胶粉1.5份、玻化微珠100‑120份、SEBS FG 1901X 0.5‑1份。在本发明配方中加入SEBS FG 1901X热塑性弹性，提高了砂浆高低温的抗开裂性能，砂浆对多种保温材料均具有良好的粘结力；具有良好的柔性、耐水性、耐候性。
Description
技术领域
本发明属建筑材料技术领域，具体地说是一种无机保温砂浆配方及其制备方法，特别涉及耐高低温开裂性的无机保温砂浆配方及其制备方法。
背景技术
保温砂浆是以各种轻质材料为骨料，以水泥为胶凝料，掺和一些改性添加剂，经生产企业搅拌混合而制成的一种预拌干粉砂浆。主要用于建筑外墙保温，具有施工方便、耐久性好等优点。
市面上的保温砂浆主要为两种：1、无机保温砂浆(玻化微珠防火保温砂浆，复合硅酸铝保温砂浆，珍珠岩保温砂浆)；2、有机保温砂浆(胶粉聚苯颗粒保温砂浆)。
无机保温砂浆是一种用于建筑物内外墙粉刷的新型保温节能砂浆材料，根据胶凝材料的不同分为水泥基无机保温砂浆和石膏基无机保温砂浆。具有节能利废、保温隔热、防火防冻、耐老化的优异性能以及低廉的价格等特点，有着广泛的市场需求。
保温砂浆由于在室外使用，外部气候变化大，温差变化大，高温时达到50℃；低温时会到-40℃以下。保温砂浆在使用时会出现开裂现象，影响使用效果与美观。
发明内容
本发明目的在于提供一种耐高低温开裂性的无机保温砂浆配方及砂浆的制备方法。
实现上述发明目的技术方案：
一种无机保温砂浆配方，其重量组成如下：水泥70-90份、粉煤灰18-22份、重钙 0-10份、淀粉醚0.05份、纤维素醚0.75份、木质纤维0.04份、PP纤维0.02份、5044N 胶粉1.5份、玻化微珠100-120份、SEBS FG 1901X 0.5-1份。
发明中的水泥为425#普硅水泥；
发明中的PP纤维长度为8-12mm；
发明中的纤维素醚为羟丙基甲基纤维素、甲基纤维素、乙基纤维素，分子量为10万-20万；
SEBS FG 1901X为科腾公司生产；为接枝马来酸酐的SEBS产品。
5044N胶粉为德国瓦克公司产品5044N，一种具有抗皂化性能的遇水可再分散的醋酸乙烯酯/乙烯共聚胶粉。
本发明优选配方为：水泥80份、粉煤灰20份、淀粉醚0.05份、纤维素醚0.75 份、木质纤维0.04份、PP纤维0.02份、5044N胶粉1.5份、玻化微珠110份、SEBS FG 1901X 1份。
无机保温砂浆配方的制备方法：按照配方的比例称量各组分，先将水泥、粉煤灰、淀粉醚、纤维素醚、木质纤维、PP纤维、5044N胶粉、玻化微珠、SEBS FG 1901X倒入搅拌机中混合均匀，即得到均匀灰色粉体砂浆。
在本发明中采用可再生分散胶粉、无机胶凝材料、优质骨科及具有保水、增加、畜变、抗裂等功能的助剂预混干拌而成。在本发明配方中加入SEBS FG 1901X物质，该物质为SEBS产品经过极性化改性的产品，是一种热塑性弹性体，其中不饱和双键经过加氢饱和，具有两个玻璃化转变温度，高温玻璃化转变温度达到140℃，低温玻璃化转变温度低到-60℃，同时由于进行了极性化改性，可以与玻化微珠、PP纤维、纤维素醚等有极好的相容性。由于SEBS FG 1901X的加入改变了砂浆的抗裂性能，不仅改变低温抗裂性能，也改变了高温抗裂性能。经过120℃高温处理80小时与-50℃低温处理80小时，加入SEBS FG 1901X没有出现开裂现象；不加入SEBS FG 1901X相比，出现多处开裂现象，每平米出现5-8处开裂。
发明的砂浆对多种保温材料均具有良好的粘结力；具有良好的柔性、耐水性、耐候性。
本发明的砂浆可现场直接加水调和使用，方便操作；安全环保，符合产业政策。
具体实施方式
下面结合实施例进一步描述本发明，但并不限制本发明的保护范围。
实施例1
将425#水泥80g、粉煤灰20g、淀粉醚0.05g、20w的羟丙基甲基纤维素0.75g、木质纤维0.04g、9mmt张的PP纤维0.02g、5044N胶粉1.5g、玻化微珠110g、SEBS FG 1901X 1g 倒入搅拌机中混合均匀，即得到均匀灰色粉体砂浆；再加入130g水，通过搅拌得到保温砂浆。经过干燥后进行性能检测。性能见表1：
表1制备的无机保温砂浆各项技术指标
高低温抗裂性能：经过120℃高温处理80小时与-50℃低温处理80小时，没有出现开裂现象。
对比例1
将425#水泥80g、粉煤灰20g、淀粉醚0.05g、20w的纤维素醚0.75g、木质纤维0.04g、9mmt张的PP纤维0.02g、5044N胶粉1.5g、玻化微珠110g倒入搅拌机中混合均匀，即得到均匀灰色粉体砂浆；再加入130g水，通过搅拌得到保温砂浆。经过干燥后进行性能检测。性能见表2：
表2制备的无机保温砂浆各项技术指标
高低温抗裂性能：经过120℃高温处理80小时与-50℃低温处理80小时，出现多处开裂现象，每平米出现8处开裂。
实施例2
将425#水泥100g、粉煤灰20g、淀粉醚0.05g、20w的羟丙基甲基纤维素0.75g、木质纤维0.04g、12mm张的PP纤维0.02g、5044N胶粉1.5g、玻化微珠90g、SEBS FG 1901X 1g 倒入搅拌机中混合均匀，即得到均匀灰色粉体砂浆；再加入130g水，通过搅拌得到保温砂浆。经过干燥后进行性能检测。性能见表3：
表3制备的无机保温砂浆各项技术指标
高低温抗裂性能：经过120℃高温处理80小时与-50℃低温处理80小时，没有出现开裂现象。
Claims (4)
1.一种无机保温砂浆，其重量组成如下：水泥70-90份、粉煤灰18-22份、重钙0-10份、淀粉醚0.05份、纤维素醚 0.75份、木质纤维0.04份、PP纤维0.02份、5044N胶粉1.5份、玻化微珠100-120份、SEBS FG 1901X 0.5-1份；按前面所述的重量比例称量各组分，将水泥、粉煤灰、淀粉醚、纤维素醚、木质纤维、PP纤维、5044N胶粉、玻化微珠、SEBS FG 1901X倒入搅拌机中混合均匀，即得到均匀灰色粉体砂浆。
2.根据权利要求1的无机保温砂浆，其特征在于所述的PP纤维长度为8-12mm。
3.根据权利要求1的无机保温砂浆，其特征在于所述的纤维素醚为羟丙基甲基纤维素、甲基纤维素、乙基纤维素，分子量为10万-20万。
4.权利要求1的无机保温砂浆，其特征在于：水泥80份、粉煤灰20份、淀粉醚0.05份、纤维素醚 0.75份、木质纤维0.04份、PP纤维0.02份、5044N胶粉1.5份、玻化微珠110份、SEBSFG 1901X 1份。