CN105332127A - Textile material used for baby quilt and manufacturing method thereof - Google Patents
Textile material used for baby quilt and manufacturing method thereof Download PDFInfo
- Publication number
- CN105332127A CN105332127A CN201510594463.XA CN201510594463A CN105332127A CN 105332127 A CN105332127 A CN 105332127A CN 201510594463 A CN201510594463 A CN 201510594463A CN 105332127 A CN105332127 A CN 105332127A
- Authority
- CN
- China
- Prior art keywords
- textile material
- fibre
- fiber
- yarn
- dawn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a textile material used for a baby quilt and a manufacturing method thereof. The textile material mainly comprises yarns. The yarns comprise the components in the following parts by weight: 58-65 parts of chitosan fibers, 25-28 parts of cotton fibers, 10-20 parts of bamboo charcoal fibers, 10-15 parts of wool fibers, and 5-10 parts of chinlon. The textile material used for a baby quilt, manufactured by the method, has warm-keeping, moisture absorption, and ventilating functions, and the quilt is good in stiffness. In addition, bacteriostasis rate of the quilt reaches up to more than 99.9%, antibiosis washability reaches more than 80 times, and the color of the quilt is not easy to change after being washed.
Description
Technical field
The invention belongs to textile material field, be specifically related to a kind of baby by with textile material and preparation method thereof.
Background technology
Along with the continuous progress of technology, present weaving face fabric highly embodies the feature of the novelty of product, complexity, variation and functionalization, great demand is produced to the clothes of high-performance, high added value, specific function, dress ornament and family's textile fabric, especially weaving face fabric for baby, because infant skin is tender, so need soft fabric to prepare corresponding material etc., antibiosis is also needed to have certain requirement in addition again, but general antibacterial textile effect is bad, and antibacterial washability is poor.
Therefore, in the art, a kind of baby with good antibacterial effect and antibacterial washability is expected to develop by with textile material.
Summary of the invention
For the deficiencies in the prior art, the object of the present invention is to provide a kind of baby by with textile material.
For reaching this object, the present invention by the following technical solutions:
The invention provides a kind of baby by with textile material, described textile material mainly comprises yarn, and described yarn is made up of the component comprising following weight portion:
Baby of the present invention by with in textile material, in the component of described yarn, the consumption of chitosan fiber can be 58 weight portions, 59 weight portions, 60 weight portions, 61 weight portions, 62 weight portions, 63 weight portions, 64 weight portions or 65 weight portions.
Baby of the present invention by with in textile material, in the component of described yarn, the consumption of cotton fiber can be 25 weight portions, 25.3 weight portions, 25.5 weight portions, 25.8 weight portions, 26 weight portions, 26.3 weight portions, 26.5 weight portions, 26.8 weight portions, 27 weight portions, 27.3 weight portions, 27.5 weight portions, 27.8 weight portions or 28 weight portions.
Baby of the present invention by with in textile material, in the component of described yarn, the consumption of bamboo-carbon fibre can be 10 weight portions, 11 weight portions, 12 weight portions, 13 weight portions, 14 weight portions, 15 weight portions, 16 weight portions, 17 weight portions, 18 weight portions, 19 weight portions or 20 weight portions.
Baby of the present invention by with in textile material, in the component of described yarn, the consumption of wool fibre can be 10 weight portions, 10.5 weight portions, 11 weight portions, 11.5 weight portions, 12 weight portions, 12.5 weight portions, 13 weight portions, 13.5 weight portions, 14 weight portions, 14.5 weight portions or 15 weight portions.
Baby of the present invention by with in textile material, in the component of described yarn, the consumption of polyamide fibre can be 5 weight portions, 5.5 weight portions, 6 weight portions, 6.5 weight portions, 7 weight portions, 7.5 weight portions, 8 weight portions, 8.5 weight portions, 9 weight portions, 9.5 weight portions, 10 weight portions, 10.5 weight portions, 11 weight portions, 11.5 weight portions, 12 weight portions, 12.5 weight portions, 13 weight portions, 13.5 weight portions, 14 weight portions, 14.5 weight portions or 15 weight portions.
Baby of the present invention by with in textile material, the fiber number of described chitosan fiber is the 1.0-2.8 dawn, such as 1.0 dawn, 1.2 dawn, 1.4 dawn, 1.6 dawn, 1.8 dawn, 2.0 dawn, 2.2 dawn, 2.4 dawn, 2.5 dawn, 2.6 dawn, 2.7 dawn or 2.8 dawn, brute force is the 1.0-2.8g/ dawn, such as 1.0 dawn, 1.2 dawn, 1.4 dawn, 1.6 dawn, 1.8 dawn, 2.0 dawn, 2.2 dawn, 2.4 dawn, 2.5 dawn, 2.6 dawn, 2.7 dawn or 2.8 dawn.
Preferably, baby of the present invention by with in textile material, described yarn is made up of the component comprising following weight portion: chitosan fiber 60 parts, 27 parts, described cotton fiber, described bamboo-carbon fibre 18 parts, described wool fibre 13 parts, 8 parts, described polyamide fibre.
Baby of the present invention by with in textile material, described yarn also comprises core, and described leisurely mood is outside equipped with by described chitosan fiber, described cotton fiber, described bamboo-carbon fibre, described wool fibre, the yarn that described polyamide fibre is made.
On the other hand, the invention provides baby described in first aspect by the preparation method with textile material, described preparation method comprises the following steps:
1) chitosan fiber is made fiber-spinnable;
2) staple fibre of certain length is made, equably by described chitosan fiber, described cotton fiber, described bamboo-carbon fibre, described wool fibre, described polyamide fibre mixes and full and uniform twisted;
3) utilize carding machine to be combed into and can spin compound strip;
4) by compound strip with required described chitosan fiber, described cotton fiber, described bamboo-carbon fibre, described wool fibre, described polyamide fibre drafting according to a certain percentage;
5) after being carded to combed sliver, then become yarn through rove-spun yarn-winder, then be combined on described core by spiral turn.
Baby of the present invention by with in the preparation method of textile material, described in step (1), the fiber number of chitosan fiber is the 1.0-2.8 dawn, and brute force is the 1.0-2.8g/ dawn.
Baby of the present invention by with in the preparation method of textile material, described in step (2), the length of staple fibre is 3.0-4.0cm, such as 3.0cm, 3.2cm, 3.4cm, 3.5cm, 3.6cm, 3.8cm or 4.0cm.
Relative to prior art, the present invention has following beneficial effect:
Baby of the present invention is by with textile material, and have warming, moisture absorption and airing function, stiffness is good, and in addition, its bacteriostasis rate can reach more than 99.9%, and antibacterial washability can reach more than 80 times, not easy to change after washing.
Detailed description of the invention
Technical scheme of the present invention is further illustrated below by detailed description of the invention.Those skilled in the art should understand, described embodiment is only help to understand the present invention, should not be considered as concrete restriction of the present invention.
Embodiment 1
In the present embodiment, the yarn of textile material is made up of the component comprising following weight portion:
Preparation method comprises the following steps:
1) chitosan fiber is made fiber-spinnable, fiber number is the 1.0-2.8 dawn, and brute force is the 1.0-2.8g/ dawn;
2) staple fibre of certain length is made, equably by described chitosan fiber, described cotton fiber, described bamboo-carbon fibre, described wool fibre, described polyamide fibre mixes and full and uniform twisted;
3) utilize carding machine to be combed into and can spin compound strip;
4) by compound strip with required described chitosan fiber, described cotton fiber, described bamboo-carbon fibre, described wool fibre, described polyamide fibre drafting according to a certain percentage;
5) after being carded to combed sliver, then become yarn through rove-spun yarn-winder, then be combined on described core by spiral turn.
Embodiment 2
In the present embodiment, the yarn of textile material is made up of the component comprising following weight portion:
Preparation method comprises the following steps:
1) chitosan fiber is made fiber-spinnable, fiber number is the 1.0-2.8 dawn, and brute force is the 1.0-2.8g/ dawn;
2) staple fibre of certain length is made, equably by described chitosan fiber, described cotton fiber, described bamboo-carbon fibre, described wool fibre, described polyamide fibre mixes and full and uniform twisted;
3) utilize carding machine to be combed into and can spin compound strip;
4) by compound strip with required described chitosan fiber, described cotton fiber, described bamboo-carbon fibre, described wool fibre, described polyamide fibre drafting according to a certain percentage;
5) after being carded to combed sliver, then become yarn through rove-spun yarn-winder, then be combined on described core by spiral turn.
Embodiment 3
In the present embodiment, the yarn of textile material is made up of the component comprising following weight portion:
Preparation method comprises the following steps:
1) chitosan fiber is made fiber-spinnable, fiber number is the 1.0-2.8 dawn, and brute force is the 1.0-2.8g/ dawn;
2) staple fibre of certain length is made, equably by described chitosan fiber, described cotton fiber, described bamboo-carbon fibre, described wool fibre, described polyamide fibre mixes and full and uniform twisted;
3) utilize carding machine to be combed into and can spin compound strip;
4) by compound strip with required described chitosan fiber, described cotton fiber, described bamboo-carbon fibre, described wool fibre, described polyamide fibre drafting according to a certain percentage;
5) after being carded to combed sliver, then become yarn through rove-spun yarn-winder, then be combined on described core by spiral turn.
Embodiment 4
In the present embodiment, the yarn of textile material is made up of the component comprising following weight portion:
Preparation method comprises the following steps:
1) chitosan fiber is made fiber-spinnable, fiber number is the 1.0-2.8 dawn, and brute force is the 1.0-2.8g/ dawn;
2) staple fibre of certain length is made, equably by described chitosan fiber, described cotton fiber, described bamboo-carbon fibre, described wool fibre, described polyamide fibre mixes and full and uniform twisted;
3) utilize carding machine to be combed into and can spin compound strip;
4) by compound strip with required described chitosan fiber, described cotton fiber, described bamboo-carbon fibre, described wool fibre, described polyamide fibre drafting according to a certain percentage;
5) after being carded to combed sliver, then become yarn through rove-spun yarn-winder, then be combined on described core by spiral turn.
Embodiment 5
In the present embodiment, the yarn of textile material is made up of the component comprising following weight portion:
Preparation method comprises the following steps:
1) chitosan fiber is made fiber-spinnable, fiber number is the 1.0-2.8 dawn, and brute force is the 1.0-2.8g/ dawn;
2) staple fibre of certain length is made, equably by described chitosan fiber, described cotton fiber, described bamboo-carbon fibre, described wool fibre, described polyamide fibre mixes and full and uniform twisted;
3) utilize carding machine to be combed into and can spin compound strip;
4) by compound strip with required described chitosan fiber, described cotton fiber, described bamboo-carbon fibre, described wool fibre, described polyamide fibre drafting according to a certain percentage;
5) after being carded to combed sliver, then become yarn through rove-spun yarn-winder, then be combined on described core by spiral turn.
Comparative example 1
In this comparative example, the yarn of textile material is made up of the component comprising following weight portion:
Preparation method is identical with embodiment 1.
Comparative example 2
In this comparative example, the yarn of textile material is made up of the component comprising following weight portion:
Preparation method is identical with embodiment 2.
Comparative example 3
In this comparative example, the yarn of textile material is made up of the component comprising following weight portion:
Preparation method is identical with embodiment 3.
Comparative example 4
In this comparative example, the yarn of textile material is made up of the component comprising following weight portion:
Preparation method is identical with embodiment 4.
Comparative example 5
In this comparative example, the yarn of textile material is made up of the component comprising following weight portion:
Preparation method is identical with embodiment 4.
Comparative example 6
In this comparative example, the yarn of textile material is made up of the component comprising following weight portion:
Preparation method is identical with embodiment 5.
Comparative example 7
In this comparative example, the yarn of textile material is made up of the component comprising following weight portion:
According to national standard FZ/T73023-2006, the fungistatic effect of textile material is tested; Textile material is washed 100 times in warm water (40-50 DEG C), observe changing color of textile situation and the biocidal property according to above-mentioned standard testing fabric, and then recording its antibacterial washability (after namely washing how many times, antibiotic rate is still more than 99%), result is as shown in table 1.
Table 1
| Bacteriostasis rate | Discolouration | Antibacterial washability | |
| Embodiment 1 | 99.9％ | Nondiscolouring | 85 times |
| Embodiment 2 | 99.93％ | Nondiscolouring | 80 times |
| Embodiment 3 | 99.94％ | Nondiscolouring | 82 times |
| Embodiment 4 | 99.9％ | Nondiscolouring | 84 times |
| Embodiment 5 | 99.97％ | Nondiscolouring | 80 times |
| Comparative example 1 | 80.5％ | Slightly variable color | 25 times |
| Comparative example 2 | 78.6％ | Variable color | 30 times |
| Comparative example 3 | 77.9％ | Variable color | 28 times |
| Comparative example 4 | 76.5％ | Variable color | 25 times |
| Comparative example 5 | 73.45％ | Variable color | 24 times |
| Comparative example 6 | 75.26％ | Variable color | 28 times |
| Comparative example 7 | 72.28％ | Variable color | 26 times |
As can be seen from Table 1, baby prepared by embodiment of the present invention 1-5 can be reached more than 99.9% by with the bacteriostasis rate of textile material, and antibacterial washability can reach more than 80 times, not easy to change after washing.Such as, and when the consumption of some component in yarn component used is when the scope of the invention is outer, the bacteriostasis rate of textile material prepared by comparative example 1-4 is only about 80%, and antibacterial washability is poor, and variable color can be produced after washing.
Applicant states, by above-described embodiment, the present invention illustrates that baby of the present invention is by with textile material and preparation method thereof, but the present invention is not limited to above-described embodiment, does not namely mean that the present invention must rely on above-described embodiment and could implement.Person of ordinary skill in the field should understand, any improvement in the present invention, to equivalence replacement and the interpolation of auxiliary element, the concrete way choice etc. of each raw material of product of the present invention, all drops within protection scope of the present invention and open scope.
Claims (7)
1. baby is by with a textile material, and described textile material mainly comprises yarn, it is characterized in that, described yarn is made up of the component comprising following weight portion:
2. baby according to claim 1 is by with textile material, and it is characterized in that, the fiber number of described chitosan fiber is the 1.0-2.8 dawn, and brute force is the 1.0-2.8g/ dawn.
3. baby according to claim 1 and 2 is by with textile material, and it is characterized in that, described yarn is made up of the component comprising following weight portion: chitosan fiber 60 parts, 27 parts, described cotton fiber, described bamboo-carbon fibre 18 parts, described wool fibre 13 parts, 8 parts, described polyamide fibre.
4. the baby according to any one of claim 1-3 is by with textile material, and it is characterized in that, described yarn also comprises core, described leisurely mood is outside equipped with by described chitosan fiber, described cotton fiber, described bamboo-carbon fibre, described wool fibre, the yarn that described polyamide fibre is made.
5. the baby according to any one of claim 1-4, by the preparation method with textile material, is characterized in that, described preparation method comprises the following steps:
1) chitosan fiber is made fiber-spinnable;
2) staple fibre of certain length is made, equably by described chitosan fiber, described cotton fiber, described bamboo-carbon fibre, described wool fibre, described polyamide fibre mixes and full and uniform twisted;
3) utilize carding machine to be combed into and can spin compound strip;
4) by compound strip with required described chitosan fiber, described cotton fiber, described bamboo-carbon fibre, described wool fibre, described polyamide fibre drafting according to a certain percentage;
5) after being carded to combed sliver, then become yarn through rove-spun yarn-winder, then be combined on described core by spiral turn.
6. baby according to claim 5 is by the preparation method with textile material, it is characterized in that, described in step (1), the fiber number of chitosan fiber is the 1.0-2.8 dawn, and brute force is the 1.0-2.8g/ dawn.
7. the baby according to claim 5 or 6, by the preparation method with textile material, is characterized in that, described in step (2), the length of staple fibre is 3.0-4.0cm.