CN105295762A - 一种抗静电超薄双面胶 - Google Patents

一种抗静电超薄双面胶 Download PDF

Info

Publication number
CN105295762A
CN105295762A CN201510702129.1A CN201510702129A CN105295762A CN 105295762 A CN105295762 A CN 105295762A CN 201510702129 A CN201510702129 A CN 201510702129A CN 105295762 A CN105295762 A CN 105295762A
Authority
CN
China
Prior art keywords
antistatic
glue
layer
ultrathin double
double
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510702129.1A
Other languages
English (en)
Other versions
CN105295762B (zh
Inventor
江叔福
杨晓明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang fry new material Limited by Share Ltd
Original Assignee
Zhejiang Ouren New Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Ouren New Material Co Ltd filed Critical Zhejiang Ouren New Material Co Ltd
Priority to CN201510702129.1A priority Critical patent/CN105295762B/zh
Publication of CN105295762A publication Critical patent/CN105295762A/zh
Application granted granted Critical
Publication of CN105295762B publication Critical patent/CN105295762B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于材料技术领域，特别涉及一种抗静电超薄双面胶，该双面胶由上而下依次为上离型膜、胶水层、PET膜层、胶水层及下离型膜层组成。所述胶水层为抗静电聚丙烯酸胶水层，该胶水层的厚度为1-3μm，所述PET膜层的厚度为1-12μm。所述抗静电聚丙烯酸胶水层包含以下重量百分数计的组分：聚丙烯酸酯胶水20-65％、溶剂30-80％、固化剂2-10％、抗静电剂0.1-0.5％。膜层上涂刷有抗静电液，该抗静电液渗透到胶水层中，与胶水层中的抗静电剂发生协同效应，使制备得到的双面胶的抗静电性能显著提高，厚度为2-10μm，可用于电子产品中。

Description

一种抗静电超薄双面胶
技术领域
本发明属于材料技术领域，特别涉及一种抗静电超薄双面胶。
背景技术
随着电子消费产品的迅猛发展，智能手机、IPAD等电子消费产品逐渐向薄型化、便携式方向发展。由于在电子产品行业规定用于粘结电子部件的胶带的粘着力应大于5N/25mm，为了满足这个要求，传统的聚酯双面胶带的聚酯层双面涂覆的胶水的厚度都较厚，从而导致胶带的总体厚度也较厚，不能满足电子产品薄型化发展的要求。
现在市面上所售的普通的双面胶带厚度较厚，存在着剥离力不均匀，上、下PET离型膜的离型力未差异化设计，容易造成离型膜分离失败，影响粘贴作业、加工性和作业性。而且普通的双面胶带的颜色单一、抗静电能力较差，无法满足电子产品的装配需求。
所以制备一种可应用于电子行业的带有颜色的、抗静电能力强的超薄双面胶是非常有必要的。
发明内容
本发明的目的是提供一种抗静电超薄双面胶，该双面胶的抗静电能力显著，而且双面胶的厚度为2-10μm，可应用在电子数码等技术领域。
本发明的目的可以通过以下技术方案来实现：
一种抗静电超薄双面胶，其特征在于：该双面胶由上而下依次为上离型膜、胶水层、PET膜层、胶水层及下离型膜层组成。
所述胶水层为抗静电聚丙烯酸酯胶水层，该胶水层的厚度为1-3μm。所述PET膜层的厚度为1-12μm。优选的，所述PET膜层的厚度为1.9-4.5μm。
所述抗静电聚丙烯酸酯胶水层包含以下重量百分数计的组分：
所述聚丙烯酸酯类胶水为含有可以与异氰酸酯反应的羟基和羧基的聚丙烯酸酯类单体的混合单体共聚物。
所述溶剂为乙酸乙酯、甲苯、丁酮中的一种或几种；所述抗静电剂为聚乙炔、聚噻吩、聚吡咯、聚苯胺、聚苯撑、聚苯撑乙烯、聚苯咪唑和聚双炔中的一种或几种的组合；所述固化剂为异氰酸酯。
所述PET膜层上涂刷有高分子抗静电液。该抗静电液为聚苯胺、聚噻吩、聚苯咪唑中的一种或几种的组合。所述高分子抗静电液的涂刷量为0.003-0.006g/cm2。优选的，所述高分子抗静电液的涂刷量为0.005g/cm2。
膜层上涂刷有抗静电液，该抗静电液渗透到胶水层中，与胶水层中的抗静电剂发生协同效应，使制备得到的双面胶的抗静电性能显著提高。
本发明的有益效果是：
1、本发明制备的抗静电超薄双面胶的导电性能非常优异,其表面电阻可达到1.6×104-2.5×105Ω，厚度为2-10μm，可用于电子产品中。
2、本发明制备的抗静电超薄双面胶的，剥离力非常高，与PET膜的粘结力非常强，而且初粘性好，对被贴物有瞬间的高黏着效果。
具体实施方式
下面结合实施例，对本发明作进一步说明：
原料：
实施例1
(1)聚丙烯酸酯胶水的制备：
称量以下原料，
将上述原料在搅拌转速为400rpm下搅拌混合30分钟、50-100目孔径过滤，静置60分钟，检测其固含量为22wt％，备用。
(2)抗静电超薄双面胶的制备：
将PET膜放卷，放卷张力为50N，随后在PET膜的两个面上涂刷聚苯胺抗静电液，涂刷量为0.005g/cm2，烘干。在上离型膜上涂布胶水层，胶水层的厚度为2μm，在胶水层表面覆盖PET膜，然后在PET膜上继续涂布聚丙烯酸胶水层，胶水层的厚度为2μm，烘干；最后在上述的PET膜的胶水层上覆盖下离型膜，收卷，收卷速度为30米/min。
实施例2
(1)聚丙烯酸胶水的制备：
称量以下原料，
将上述原料在搅拌转速为400rpm下搅拌混合30分钟、50-100目孔径过滤，静置60分钟，检测其固含量为20wt％，备用。
(2)抗静电超薄双面胶的制备：
将PET膜放卷，放卷张力为50N，随后在PET膜的两个面上涂刷聚噻吩抗静电液，涂刷量为0.005g/cm2，烘干。在上离型膜上涂布胶水层，胶水层的厚度为2μm，在胶水层表面覆盖PET膜，然后在PET膜上继续涂布聚丙烯酸胶水层，胶水层的厚度为2μm，烘干；最后在上述的PET膜的胶水层上覆盖下离型膜，收卷，收卷速度为30米/min。
实施例3
(1)聚丙烯酸酯胶水的制备：
称量以下原料，
将上述原料在搅拌转速为400rpm下搅拌混合30分钟、50-100目孔径过滤，静置60分钟，检测其固含量为15wt％，备用。
(2)抗静电超薄双面胶的制备：
将PET膜放卷，放卷张力为50N，随后在PET膜的两个面上涂刷聚苯咪唑抗静电液，涂刷量为0.005g/cm2，烘干。在上离型膜上涂布胶水层，胶水层的厚度为2μm，在胶水层表面覆盖PET膜，然后在PET膜上继续涂布聚丙烯酸胶水层，胶水层的厚度为2μm，烘干；最后在上述的PET膜的胶水层上覆盖下离型膜，收卷，收卷速度为30米/min。
对比例1
(1)聚丙烯酸胶水的制备：
称量以下原料，
将上述原料在搅拌转速为400rpm下搅拌混合30分钟、50-100目孔径过滤，静置60分钟，检测其固含量为15wt％，备用。
(2)抗静电超薄双面胶的制备：
在上离型膜上涂布胶水层，胶水层的厚度为2μm，在胶水层表面覆盖PET膜，然后在PET膜上继续涂布聚丙烯酸胶水层，胶水层的厚度为2μm，烘干；最后在上述的PET膜的胶水层上覆盖下离型膜，收卷，收卷速度为30米/min。
对比例2
(1)聚丙烯酸胶水的制备：
称量以下原料，
聚丙烯酸酯30wt％
丁酮65.7wt％
异氰酸酯4.3wt％
将上述原料在搅拌转速为400rpm下搅拌混合30分钟、50-100目孔径过滤，静置60分钟，检测其固含量为15wt％，备用。
(2)抗静电超薄双面胶的制备：
将PET膜放卷，放卷张力为50N，随后在PET膜的两个面上涂刷聚乙炔抗静电液，涂刷量为5g/cm2，烘干。在上离型膜上涂布胶水层，胶水层的厚度为2μm，在胶水层表面覆盖PET膜，然后在PET膜上继续涂布聚丙烯酸胶水层，胶水层的厚度为2μm，烘干；最后在上述的PET膜的胶水层上覆盖下离型膜，收卷，收卷速度为30米/min。
对实施例1-3及对比例1、2中制备的双面胶的性能进行测试，测试结果如下表所示。
实施例1-3中制备的抗静电双面胶的抗静电性能非常优异，其表面电阻为1.6×104-2.5×105Ω，可用于电子行业。而且制备的双面胶的剥离强度、初粘力及保持力也非常好，大大提高了其安全性能。所述实施例1-3中的抗静电双面胶中的抗静电液和抗静电剂产生了协同的效应，所以其抗静电性能大大提高。相对而言，对比例1和对比例2的表面电阻值就高了。

Claims (9)

1.一种抗静电超薄双面胶，其特征在于：该双面胶由上而下依次为上离型膜、胶水层、PET膜层、胶水层及下离型膜组成。
2.根据权利要求1所述的抗静电超薄双面胶，其特征在于：所述胶水层为抗静电聚丙烯酸胶水层，该胶水层的厚度为1-3μm，所述PET膜层的厚度为1-12μm。
3.根据权利要求1所述的抗静电超薄双面胶，其特征在于：所述抗静电聚丙烯酸胶水层包含以下重量百分数计的组分：
4.根据权利要求3所述的抗静电超薄双面胶，其特征在于：所述聚丙烯酸酯类胶水为含有1-2个双键的聚丙烯酸酯类。
5.根据权利要求3所述的抗静电超薄双面胶，其特征在于：所述溶剂为乙酸乙酯、甲苯、丁酮中的一种或几种；所述固化剂为异氰酸酯。
6.根据权利要求3所述的抗静电超薄双面胶，其特征在于：所述抗静电剂为聚乙炔、聚噻吩、聚吡咯、聚苯胺、聚苯撑、聚苯撑乙烯聚苯咪唑和聚双炔的一种或几种的组合。
7.根据权利要求1所述的抗静电超薄双面胶，其特征在于：所述PET膜层的表面涂刷有高分子抗静电液。
8.根据权利要求7所述的抗静电超薄双面胶，其特征在于：所述高分子抗静电液为聚苯胺、聚噻吩、聚苯咪唑中的一种或几种的组合。
9.根据权利要求7或8所述的抗静电超薄双面胶，其特征在于：所述高分子抗静电液的涂刷量为0.003-0.006g/cm2。
CN201510702129.1A 2015-10-23 2015-10-23 一种抗静电超薄双面胶 Active CN105295762B (zh)