CN105239457A - Mildew-proofing, drying and anti-bacterial treatment agent for printing paper - Google Patents
Mildew-proofing, drying and anti-bacterial treatment agent for printing paper Download PDFInfo
- Publication number
- CN105239457A CN105239457A CN201510560469.5A CN201510560469A CN105239457A CN 105239457 A CN105239457 A CN 105239457A CN 201510560469 A CN201510560469 A CN 201510560469A CN 105239457 A CN105239457 A CN 105239457A
- Authority
- CN
- China
- Prior art keywords
- parts
- sodium
- mildew
- dry
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a mildew-proofing, drying and anti-bacterial treatment agent for printing paper, which is composed of following components, by mass, 32-36 parts of bentonite, 34-38 parts of light-calcined magnesium oxide, 30-34 parts of polyacrylamide starch, 34-38 parts of basalt powder, 30-34 parts of shell powder, 34-38 parts of polysaccharides, 30-34 parts of hard gypsum ore, 36-40 parts of polyoxyethylene trimethyl ammonium chloride, 30-34 parts of sodium diacetate, 34-38 parts of polyhexamethylene guanidine, 30-34 parts of sodium pyrosulfite, 34-38 parts of 3-iodo-2-propinylbutyl carbamate, 30-34 parts of methyl isothiazolinone, 34-38 parts of tinidazole, 30-34 parts of sodium ethyl p-hydroxybenzoate, 34-38 parts of alkyl glycoside, 30-34 parts of extract liquid of Eupatorium adenophora, 34-38 parts of diafenthiuron, 30-34 parts of tripterygium wilfordii, 34-38 parts of teflubenzuron, 30-34 parts of green muscardine fungus, 34-38 parts of biological prallethrin and 30-34 parts of hexaflumuron. The product has excellent mildew-proofing, drying and anti-bacterial performances and is suitable for printing paper.
Description
Technical field
The present invention relates to the dry antibiosis additive of a kind of printing sheets mildew-resistant, belong to printing technology.
Background technology
For the general designation of the paper of various printed article.Such as letterpress paper, offset printing paper, senior gloss paperboard, newsprint, writing paper etc.Its characteristic is that printing adaptability is better, opacity is higher.Different according to printing process, paper has specific performance.Such as, the printing newsprint of newpapers and periodicals and the letterpress paper of book printing, absorbency is good with not print through; For overlapping the newsprint of colour printing, then there is high water suction distortion expansion and contraction; For the loan of intaglio printing, its paper is fine and smooth, and the svelteness printed off is true to nature.Specialize in the paper of printing.Can be divided into by purposes: newsprint, pamphlet paper, cover paper, loan etc.Letterpress paper, gravure paper, offset printing paper etc. can be divided into by the difference of printing process.Paper is the thin slice made with string, as writing picture, printing books and newspapers, packaging etc.These printings, due to its particularity, once storage, should be noted that protection against the tide, need anti-mildew desinsection yet, avoid being affected, general dry finishing agent, does not possess mildew-resistant and antibacterial functions, cannot meet paper storage request.
Summary of the invention
The object of the present invention is to provide the dry antibiosis additive of a kind of printing sheets mildew-resistant, so that the dry antibacterial treatment of the mildew-resistant realizing printing sheets better.
To achieve these goals, technical scheme of the present invention is as follows.
The dry antibiosis additive of a kind of printing sheets mildew-resistant, be made up of the component of following mass fraction: bentonite 32 ~ 36 parts, light calcined magnesia 34 ~ 38 parts, polyacrylamide starch 30 ~ 34 parts, basalt powder 34 ~ 38 parts, oyster shell whiting 30 ~ 34 parts, polysaccharides 34 ~ 38 parts, Anhydrite Ore 30 ~ 34 parts, polyethylene glycol oxide trimethyl ammonium chloride 36 ~ 40 parts, sodium Diacetate 30 ~ 34 parts, polyhexamethylene guanide 34 ~ 38 parts, sodium pyrosulfite 30 ~ 34 parts, IPBC 34 ~ 38 parts, methylisothiazolinone 30 ~ 34 parts, Tinidazole 34 ~ 38 parts, nipagin A sodium 30 ~ 34 parts, alkyl glycoside 34 ~ 38 parts, eupatorium adenophorum extracting solution 30 ~ 34 parts, diafenthiuron 34 ~ 38 parts, thunder godvine 30 ~ 34 parts, Teflubenzuron 34 ~ 38 parts, green muscardine fungus 30 ~ 34 parts, biological prallethrin 34 ~ 38 parts, HEXAFLUMURON 30 ~ 34 parts.
Further, the dry antibiosis additive of above-mentioned printing sheets mildew-resistant, be made up of the component of following mass fraction: bentonite 32 parts, light calcined magnesia 34 parts, polyacrylamide starch 30 parts, basalt powder 34 parts, oyster shell whiting 30 parts, polysaccharides 34 parts, Anhydrite Ore 30 parts, polyethylene glycol oxide trimethyl ammonium chloride 36 parts, sodium Diacetate 30 parts, polyhexamethylene guanide 34 parts, sodium pyrosulfite 30 parts, IPBC 34 parts, methylisothiazolinone 30 parts, Tinidazole 34 parts, nipagin A sodium 30 parts, alkyl glycoside 34 parts, eupatorium adenophorum extracting solution 30 parts, diafenthiuron 34 parts, thunder godvine 30 parts, Teflubenzuron 34 parts, green muscardine fungus 30 parts, biological prallethrin 34 parts, HEXAFLUMURON 30 parts.
Further, the dry antibiosis additive of above-mentioned printing sheets mildew-resistant, be made up of the component of following mass fraction: bentonite 34 parts, light calcined magnesia 36 parts, polyacrylamide starch 32 parts, basalt powder 36 parts, oyster shell whiting 32 parts, polysaccharides 36 parts, Anhydrite Ore 32 parts, polyethylene glycol oxide trimethyl ammonium chloride 38 parts, sodium Diacetate 32 parts, polyhexamethylene guanide 36 parts, sodium pyrosulfite 32 parts, IPBC 36 parts, methylisothiazolinone 32 parts, Tinidazole 36 parts, nipagin A sodium 32 parts, alkyl glycoside 36 parts, eupatorium adenophorum extracting solution 32 parts, diafenthiuron 36 parts, thunder godvine 32 parts, Teflubenzuron 36 parts, green muscardine fungus 32 parts, biological prallethrin 36 parts, HEXAFLUMURON 32 parts.
Further, the dry antibiosis additive of above-mentioned printing sheets mildew-resistant, be made up of the component of following mass fraction: bentonite 36 parts, light calcined magnesia 38 parts, polyacrylamide starch 34 parts, basalt powder 38 parts, oyster shell whiting 34 parts, polysaccharides 38 parts, Anhydrite Ore 34 parts, polyethylene glycol oxide trimethyl ammonium chloride 40 parts, sodium Diacetate 34 parts, polyhexamethylene guanide 38 parts, sodium pyrosulfite 34 parts, IPBC 38 parts, methylisothiazolinone 34 parts, Tinidazole 38 parts, nipagin A sodium 34 parts, alkyl glycoside 38 parts, eupatorium adenophorum extracting solution 34 parts, diafenthiuron 38 parts, thunder godvine 34 parts, Teflubenzuron 38 parts, green muscardine fungus 34 parts, biological prallethrin 38 parts, HEXAFLUMURON 34 parts.
Further, above-mentioned printing sheets mildew-resistant dry antibiosis additive preparation method step is as follows:
(1) by the bentonite of described mass fraction, light calcined magnesia, polyacrylamide starch, basalt powder, oyster shell whiting, polysaccharides, Anhydrite Ore, sodium Diacetate, polyhexamethylene guanide, sodium pyrosulfite, IPBC, methylisothiazolinone, Tinidazole, alkyl glycoside, eupatorium adenophorum extracting solution, diafenthiuron, thunder godvine, Teflubenzuron, green muscardine fungus, biological prallethrin, HEXAFLUMURON is mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 40KHz, rate of dispersion about 5000 ~ 5400r/min, jitter time is 30 ~ 60min,
(2) add the nipagin A sodium of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 35KHz, rate of dispersion about 4800 ~ 5200r/min, and jitter time is 30 ~ 50min;
(3) add the polyethylene glycol oxide trimethyl ammonium chloride of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 30KHz, rate of dispersion about 4600 ~ 4800r/min, and jitter time is 20 ~ 40min; Mix this product that rear obtained solid content is about 20 ~ 70%.
Above-mentioned each component function is as follows:
(1) bentonite: a kind of clay rock mass containing a large amount of montmorillonite, a small amount of beidellite and saponite.Greasy texture, has very large thixotropy, and therefore nano-bentonite can make coating levelability good for the auxiliary agent of coating, is convenient to brushing.Can be used for colour-wash, part mill base can be saved and make color and luster keep permanent.It is a kind of clay mineral of cheapness.For the grade of coating not only can be improved in building coating, for the production of high-grade paint, and the cost of raw material of coating can be reduced.
(2) light calcined magnesia: faint yellow or white powder.Be dissolved in acid and ammonium salt, be insoluble in water and ethanol.Be widely used in multiple fields such as building materials, chemical industry, metallurgy, medicine, be production PLASTIC LAMINATED, ideal material that slag etc. is spattered in light cellular partition board, magnesium sulfate, papermaking, desulfurization process, steel mill's furnace retaining.
(3) polyacrylamide starch: this product is white fibrous bulky powder, nontoxic, is insoluble to most organic solvent, soluble in water.In the industries such as water treatment, oil exploitation, papermaking, ore dressing, be able to extensive use.
(4) basalt powder: this product is good grinding-material, can be used to grind metal, grinding stone material; Industrially also can do filter, drier, catalyst etc.It supported by the arm in concrete, weight concrete can be made to alleviate, not only sturdy and durable, have sound insulation, the feature such as heat insulation, be the good aggregate of skyscraper lightweight concrete simultaneously.
(5) oyster shell whiting: this product is oyster shell whiting pulverized powder, its main component of 95% is calcium carbonate, also has a small amount of amino acid and polysaccharide material.Can do the high-grade material of food, cosmetics and interior decoration, it is extensively adapted to animal and fowl fodder and food calcium source additive, ornaments processing, drier etc.Because itself does not burn, can be used to fire protection flame retarding.
(6) polysaccharides: this product can activating immune cell, the growth of Tumor suppression.Can Promote immunity systemic-function, allow immune system constantly can produce natural killer cell, interferon, interleukin 8 and usually destroy the cancer cell existed, and then safeguard whole immune in a healthy and balanced way.
(7) Anhydrite Ore: main as outside construction material and cement raw material, also can be used to manufacture sulfuric acid.Be widely used in the departments such as rubber, plastics, fertilizer, agricultural chemicals, paint, weaving, food, medicine, daily-use chemical industry, industrial art, culture and education.
(8) polyethylene glycol oxide trimethyl ammonium chloride: as the disinfectant of swimming pool.Biocidal algae-killing agent is used as in industry water and other water systems.
(9) sodium Diacetate: white crystals, with acetic acid smell, easy moisture absorption, very easily water-soluble.Stable in properties, cheap novel foodstuff Midew preventive for feed, acid and a modifying agent, have high-effect anti-mould, anticorrosion, fresh-keeping, and improve palatability, have additional nutrients value, helps the effects such as growth, be now widely used in animal and fowl fodder.
(10) polyhexamethylene guanide: there is broad-spectrum; Valid density is low; Speed of action is fast; Stable in properties; Premium properties soluble in water; Can use at normal temperatures; For a long time antibacterial, have no side effect; Non-corrosiveness; Colourless, odorless; Nontoxic; Do not fire, not quick-fried, use safety; Moderate; Convenient transportation.Absorption in electronegative each bacterioid, virus, enters cell membrane usually, suppresses the synthesis of film lactones plastid, causes thalline apoptosis, reach best bactericidal effect.
(11) sodium pyrosulfite: white or yellow crystalline powder or little crystallization.Water-soluble, the aqueous solution is in acid.Be dissolved in glycerine, be slightly soluble in ethanol.For departments such as printing and dyeing, organic synthesis, printing, process hides, pharmacy; Preservative agent, bleaching agent, raising agent is made in food processing.
(12) IPBC: white crystalline powder, water insoluble, be soluble in lower alcohols organic solvent.Broad-spectrum sterilization, can effectively kill mould, saccharomycete, algea and bacteria, have special efficacy to fungi.
(13) methylisothiazolinone: a kind of efficient germicide, heat-resisting waterborne preservative, good effect is had for suppression microbial growth, can anti-bacteria, fungi, mould and mould growth, there is broad-spectrum antibacterial ability, for sterilization and anticorrosions such as papermaking paint, oil-field flooding, daily-use chemical industries.
(14) Tinidazole: white or pale yellow crystals or crystalline powder; Mildly bitter flavor.Dissolve in acetone or chloroform, slightly soluble in water or ethanol.These product have greater activity to protozoon and anaerobic bacteria.To tool antibacterial activities such as the Bacteroides such as bacteroides fragilis, Fusobacterium, fusobacterium, peptococcus, peptostreptococcus, Wei Rong Coccus and Jia get Na bacterium, the concentration of 2 ~ 4mg/L can suppress most of anaerobic bacteria.The nitro of these product is reduced into a kind of cell toxicant, thus acts on the DNA metabolic process of bacterium, impels bacterial death.
(15) nipagin A sodium: this medicine is white, crystalline, almost odorless powder.Mildly bitter flavor, fiber crops of burning.Be dissolved in cold water hardly, be soluble in ethanol, ether, acetone or propylene glycol etc.As food preservative, also for the industry such as pharmacy, leather.The Antifungal activity of this product to mould is stronger.
(16) alkyl glycoside: synthesized by renewable resource natural fat alcohol and glucose, it is the more comprehensive new non-ionic surfactants of a kind of performance, have the characteristic of conventional nonionic and anion surfactant concurrently, there is high surface, good ecological security and intermiscibility.There is stronger broad spectrum antibiotic activity, product thickening effect significantly, be easy to dilution, gel-free phenomenon, easy to use.And resistance to highly basic, resistance to strong acid, resistance to hard water, salt-resistance are strong.For washing agent, cosmetics, agricultural chemicals, weaving and printing and dyeing etc.
(17) eupatorium adenophorum extracting solution: Eupatorium adenophorum is perennial herb or becomes suffruticose plant.The sturdy prosperity of rhizome, uprightly, plant height 30-200 centimetre, branch to life, tiltedly on, stem purple, by white or rust pubescence.Extract can be used as a kind of biological insecticides, fumigant, acaricide and bactericide and uses.
(18) diafenthiuron: a kind of new sulfur ureas efficient insecticide, acaricide, have tag, stomach toxicity, interior suction and fumigation action, and there is certain ovicidal effect.
(19) thunder godvine: bitter, pungent, cool in nature, greatly poison.Return liver, kidney channel.Removing toxic substances desinsection.
(20) Teflubenzuron: as pesticide, has preventive effect to the larva of Aleyrodidae, Diptera, Coleoptera, Hymenoptera, Lepidoptera and Psyllidae.It can suppress the growth of juvenile stage insect, hinders decortication.
(21) green muscardine fungus: this agent belongs to Ascomycota, Hypocreales, Clavicipitaceae, Metarhizium is a kind of insect pathogenic bacteria of wide spectrum.A class disinsection fungal of various pests can be parasitized, enter in pest body by body surface invasion effect, in pest body, constantly increase breeding by consuming nutrition, mechanical penetration, generation toxin, and constantly propagate in pest population, make insect lethal.
(22) biological prallethrin: limpid yellowish to amber thick liquid, is soluble in most of organic solvent; Be insoluble in water.There is strong action of contace poison, and have cockroach and outstanding drive effect.Be mainly used in the house pests such as the control of processing mosquito-repellent incense, electric mosquito repellent, vaporizer mosquito liquid and spray housefly, mosquito, lice, cockroach.
(23) HEXAFLUMURON: this product is novel acylureas insecticides, except having other acyl group ureas desinsection features, insecticidal spectrum is wider.
This beneficial effect of the invention is: the dry antibiosis additive process of preparing of this printing sheets mildew-resistant is simple, prepared product has the dry anti-microbial property of comparatively superior mildew-resistant, be adapted at printing sheets field to use, improve properties of product, process easy to use.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is described, better to understand the present invention.
embodiment 1
The dry antibiosis additive of printing sheets mildew-resistant in the present embodiment, be made up of the component of following mass fraction: bentonite 32 parts, light calcined magnesia 34 parts, polyacrylamide starch 30 parts, basalt powder 34 parts, oyster shell whiting 30 parts, polysaccharides 34 parts, Anhydrite Ore 30 parts, polyethylene glycol oxide trimethyl ammonium chloride 36 parts, sodium Diacetate 30 parts, polyhexamethylene guanide 34 parts, sodium pyrosulfite 30 parts, IPBC 34 parts, methylisothiazolinone 30 parts, Tinidazole 34 parts, nipagin A sodium 30 parts, alkyl glycoside 34 parts, eupatorium adenophorum extracting solution 30 parts, diafenthiuron 34 parts, thunder godvine 30 parts, Teflubenzuron 34 parts, green muscardine fungus 30 parts, biological prallethrin 34 parts, HEXAFLUMURON 30 parts.
Above-mentioned printing sheets mildew-resistant dry antibiosis additive preparation method step is as follows:
(1) bentonite of described mass fraction, light calcined magnesia, polyacrylamide starch, basalt powder, oyster shell whiting, polysaccharides, Anhydrite Ore, sodium Diacetate, polyhexamethylene guanide, sodium pyrosulfite, IPBC, methylisothiazolinone, Tinidazole, alkyl glycoside, eupatorium adenophorum extracting solution, diafenthiuron, thunder godvine, Teflubenzuron, green muscardine fungus, biological prallethrin, HEXAFLUMURON are mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5400r/min, jitter time is 60min;
(2) add the nipagin A sodium of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5200r/min, and jitter time is 50min;
(3) add the polyethylene glycol oxide trimethyl ammonium chloride of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 4800r/min, and jitter time is 40min; Mix this product that rear obtained solid content is about 20%.
embodiment 2
The dry antibiosis additive of printing sheets mildew-resistant in the present embodiment, be made up of the component of following mass fraction: bentonite 34 parts, light calcined magnesia 36 parts, polyacrylamide starch 32 parts, basalt powder 36 parts, oyster shell whiting 32 parts, polysaccharides 36 parts, Anhydrite Ore 32 parts, polyethylene glycol oxide trimethyl ammonium chloride 38 parts, sodium Diacetate 32 parts, polyhexamethylene guanide 36 parts, sodium pyrosulfite 32 parts, IPBC 36 parts, methylisothiazolinone 32 parts, Tinidazole 36 parts, nipagin A sodium 32 parts, alkyl glycoside 36 parts, eupatorium adenophorum extracting solution 32 parts, diafenthiuron 36 parts, thunder godvine 32 parts, Teflubenzuron 36 parts, green muscardine fungus 32 parts, biological prallethrin 36 parts, HEXAFLUMURON 32 parts.
Above-mentioned printing sheets mildew-resistant dry antibiosis additive preparation method step is as follows:
(1) bentonite of described mass fraction, light calcined magnesia, polyacrylamide starch, basalt powder, oyster shell whiting, polysaccharides, Anhydrite Ore, sodium Diacetate, polyhexamethylene guanide, sodium pyrosulfite, IPBC, methylisothiazolinone, Tinidazole, alkyl glycoside, eupatorium adenophorum extracting solution, diafenthiuron, thunder godvine, Teflubenzuron, green muscardine fungus, biological prallethrin, HEXAFLUMURON are mixed, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 5200r/min, jitter time is 45min;
(2) add the nipagin A sodium of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 27kHz, rate of dispersion about 5000r/min, and jitter time is 40min;
(3) add the polyethylene glycol oxide trimethyl ammonium chloride of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 25kHz, rate of dispersion about 4700r/min, and jitter time is 30min; Mix this product that rear obtained solid content is about 35%.
embodiment 3
The dry antibiosis additive of printing sheets mildew-resistant in the present embodiment, be made up of the component of following mass fraction: bentonite 36 parts, light calcined magnesia 38 parts, polyacrylamide starch 34 parts, basalt powder 38 parts, oyster shell whiting 34 parts, polysaccharides 38 parts, Anhydrite Ore 34 parts, polyethylene glycol oxide trimethyl ammonium chloride 40 parts, sodium Diacetate 34 parts, polyhexamethylene guanide 38 parts, sodium pyrosulfite 34 parts, IPBC 38 parts, methylisothiazolinone 34 parts, Tinidazole 38 parts, nipagin A sodium 34 parts, alkyl glycoside 38 parts, eupatorium adenophorum extracting solution 34 parts, diafenthiuron 38 parts, thunder godvine 34 parts, Teflubenzuron 38 parts, green muscardine fungus 34 parts, biological prallethrin 38 parts, HEXAFLUMURON 34 parts.
Above-mentioned printing sheets mildew-resistant dry antibiosis additive preparation method step is as follows:
(1) bentonite of described mass fraction, light calcined magnesia, polyacrylamide starch, basalt powder, oyster shell whiting, polysaccharides, Anhydrite Ore, sodium Diacetate, polyhexamethylene guanide, sodium pyrosulfite, IPBC, methylisothiazolinone, Tinidazole, alkyl glycoside, eupatorium adenophorum extracting solution, diafenthiuron, thunder godvine, Teflubenzuron, green muscardine fungus, biological prallethrin, HEXAFLUMURON are mixed, ultrasonic high speed dispersion, ultrasonic frequency is 40kHz, rate of dispersion 5000r/min, jitter time is 30min;
(2) add the nipagin A sodium of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 35kHz, rate of dispersion 4800r/min, and jitter time is 30min;
(3) add the polyethylene glycol oxide trimethyl ammonium chloride of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 4600r/min, and jitter time is 20min; Mix this product that rear obtained solid content is about 70%.
Carry out performance measurement for the coating in embodiment 1, embodiment 2 and embodiment 3 and certain commercial coating, measured data are as shown in table 1.
Table 1 the performance test results
Visible, material of the present invention has good drying, antibacterial and mouldproof sex change energy.
The above is the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention; can also make some improvements and modifications, these improvements and modifications are also considered as protection scope of the present invention.
Claims (5)
1. the dry antibiosis additive of printing sheets mildew-resistant, it is characterized in that: be made up of the component of following mass fraction: bentonite 32 ~ 36 parts, light calcined magnesia 34 ~ 38 parts, polyacrylamide starch 30 ~ 34 parts, basalt powder 34 ~ 38 parts, oyster shell whiting 30 ~ 34 parts, polysaccharides 34 ~ 38 parts, Anhydrite Ore 30 ~ 34 parts, polyethylene glycol oxide trimethyl ammonium chloride 36 ~ 40 parts, sodium Diacetate 30 ~ 34 parts, polyhexamethylene guanide 34 ~ 38 parts, sodium pyrosulfite 30 ~ 34 parts, IPBC 34 ~ 38 parts, methylisothiazolinone 30 ~ 34 parts, Tinidazole 34 ~ 38 parts, nipagin A sodium 30 ~ 34 parts, alkyl glycoside 34 ~ 38 parts, eupatorium adenophorum extracting solution 30 ~ 34 parts, diafenthiuron 34 ~ 38 parts, thunder godvine 30 ~ 34 parts, Teflubenzuron 34 ~ 38 parts, green muscardine fungus 30 ~ 34 parts, biological prallethrin 34 ~ 38 parts, HEXAFLUMURON 30 ~ 34 parts.
2. the dry antibiosis additive of printing sheets mildew-resistant according to claim 1, it is characterized in that: the dry antibiosis additive of described printing sheets mildew-resistant is made up of the component of following mass fraction: bentonite 32 parts, light calcined magnesia 34 parts, polyacrylamide starch 30 parts, basalt powder 34 parts, oyster shell whiting 30 parts, polysaccharides 34 parts, Anhydrite Ore 30 parts, polyethylene glycol oxide trimethyl ammonium chloride 36 parts, sodium Diacetate 30 parts, polyhexamethylene guanide 34 parts, sodium pyrosulfite 30 parts, IPBC 34 parts, methylisothiazolinone 30 parts, Tinidazole 34 parts, nipagin A sodium 30 parts, alkyl glycoside 34 parts, eupatorium adenophorum extracting solution 30 parts, diafenthiuron 34 parts, thunder godvine 30 parts, Teflubenzuron 34 parts, green muscardine fungus 30 parts, biological prallethrin 34 parts, HEXAFLUMURON 30 parts.
3. according to the dry antibiosis additive of the printing sheets mildew-resistant described in claim 1 to 2, it is characterized in that: the dry antibiosis additive of described printing sheets mildew-resistant is made up of the component of following mass fraction: bentonite 34 parts, light calcined magnesia 36 parts, polyacrylamide starch 32 parts, basalt powder 36 parts, oyster shell whiting 32 parts, polysaccharides 36 parts, Anhydrite Ore 32 parts, polyethylene glycol oxide trimethyl ammonium chloride 38 parts, sodium Diacetate 32 parts, polyhexamethylene guanide 36 parts, sodium pyrosulfite 32 parts, IPBC 36 parts, methylisothiazolinone 32 parts, Tinidazole 36 parts, nipagin A sodium 32 parts, alkyl glycoside 36 parts, eupatorium adenophorum extracting solution 32 parts, diafenthiuron 36 parts, thunder godvine 32 parts, Teflubenzuron 36 parts, green muscardine fungus 32 parts, biological prallethrin 36 parts, HEXAFLUMURON 32 parts.
4. the dry antibiosis additive of the printing sheets mildew-resistant according to claims 1 to 3, it is characterized in that: the dry antibiosis additive of described printing sheets mildew-resistant is made up of the component of following mass fraction: bentonite 36 parts, light calcined magnesia 38 parts, polyacrylamide starch 34 parts, basalt powder 38 parts, oyster shell whiting 34 parts, polysaccharides 38 parts, Anhydrite Ore 34 parts, polyethylene glycol oxide trimethyl ammonium chloride 40 parts, sodium Diacetate 34 parts, polyhexamethylene guanide 38 parts, sodium pyrosulfite 34 parts, IPBC 38 parts, methylisothiazolinone 34 parts, Tinidazole 38 parts, nipagin A sodium 34 parts, alkyl glycoside 38 parts, eupatorium adenophorum extracting solution 34 parts, diafenthiuron 38 parts, thunder godvine 34 parts, Teflubenzuron 38 parts, green muscardine fungus 34 parts, biological prallethrin 38 parts, HEXAFLUMURON 34 parts.
5. the dry antibiosis additive of the printing sheets mildew-resistant according to claim 1 or 4, is characterized in that: described printing sheets mildew-resistant dry antibiosis additive preparation method step is as follows:
(1) by the bentonite of described mass fraction, light calcined magnesia, polyacrylamide starch, basalt powder, oyster shell whiting, polysaccharides, Anhydrite Ore, sodium Diacetate, polyhexamethylene guanide, sodium pyrosulfite, IPBC, methylisothiazolinone, Tinidazole, alkyl glycoside, eupatorium adenophorum extracting solution, diafenthiuron, thunder godvine, Teflubenzuron, green muscardine fungus, biological prallethrin, HEXAFLUMURON is mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 40KHz, rate of dispersion about 5000 ~ 5400r/min, jitter time is 30 ~ 60min,
(2) add the nipagin A sodium of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 35KHz, rate of dispersion about 4800 ~ 5200r/min, and jitter time is 30 ~ 50min;
(3) add the polyethylene glycol oxide trimethyl ammonium chloride of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 30KHz, rate of dispersion about 4600 ~ 4800r/min, and jitter time is 20 ~ 40min; Mix this product that rear obtained solid content is about 20 ~ 70%.