CN105238309A - 一种耐油纳米阻尼胶黏剂 - Google Patents
一种耐油纳米阻尼胶黏剂 Download PDFInfo
- Publication number
- CN105238309A CN105238309A CN201510634190.7A CN201510634190A CN105238309A CN 105238309 A CN105238309 A CN 105238309A CN 201510634190 A CN201510634190 A CN 201510634190A CN 105238309 A CN105238309 A CN 105238309A
- Authority
- CN
- China
- Prior art keywords
- parts
- oil
- raw material
- adhesive
- composite fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐油纳米阻尼胶黏剂,由下述重量份的原料制得:辛基酚聚氧乙烯醚1-3、氢化松香树脂3-5、聚醋酸乙烯酯1-3、聚丙烯酸酯乳液6-13、氢氧化钙0.6-0.9、纳米氧化铝粉末0.1-0.2、微米氧化铈粉末0.2-0.4、松油1-2、环氧大豆油1-2、乳液型丙烯酸酯压敏胶粘剂10-20、改性复合纤维1-2。本发明利用纳米填料增加本发明的耐油特性,油不渗透,适用于油污多的工作环境,加入氢化松香树脂,增加粘度的同时增强隔音效果;聚丙烯酸酯乳液是一种抗渗能力突出的胶粘浆料,与其余原料复配合理,增加本发明的耐油性。
Description
技术领域
本发明涉及胶黏剂技术领域,尤其涉及一种耐油纳米阻尼胶黏剂。
背景技术
建筑隔声,是指随着现代城市的发展,噪声源的增加,建筑物的密集,高强度轻质材料的使用,对建筑物进行有效的隔声防护措施。建筑隔声除了要考虑建筑物内人们活动所引起的声音干扰外,还要考虑建筑物外交通运输、工商业活动等噪声传入所造成的干扰。
建筑墙体、石膏板、混凝土等的缝隙,如果不用隔声密封剂填堵,都会成为噪音传播的有效通道,大幅度降低工程原本可以取得的隔音效果,利用特制的隔音胶对缝隙进行处理,可以成百倍地降低噪音通过缝隙的传播,该隔音胶可以直接使用在几乎任何清洁的物体上,包括石膏板、水泥板、硅酸钙板、混凝土、砖和金属等。聚丙烯酸酯乳液(NBS共聚体)水泥砂浆又称:丙乳砂浆,是丙烯酸酯共聚乳液改性的聚合物水泥砂浆(简称:NBS丙乳水泥砂浆),NBS丙乳是一种水泥基高分子聚合物的水分散体,加入水泥砂浆后也称为聚合物水泥砂浆。该砂浆具有优异的粘结、抗裂、抗冻、防渗、防腐、抗氯离子渗透、耐老化和耐蚀性能,适用于海洋、水闸、瀑布、港口工程、公路、桥梁、冶金、化工、工业地坪与民用建筑等钢结构和钢筋混凝土结构的防渗、防腐护面和修补工程。
天然纤维材料具有吸潮、隔音、减震、降噪、耐冲击性高、手感好等特点,在室内装饰等领域具有和其他材料(如玻璃钢)无可比拟的优点,其是一种新型的优良环保型材料。天然纤维制品废弃后可以自然降解,因此天然纤维废料对环境的影响较小。
氢化松香是一种重要的松香改性产品,具有抗氧性能好、脆性小、热稳定性高、颜色浅等特点,广泛应用于胶粘剂、合成橡胶、涂料、油墨、造纸、电子、食品等领域。氢化松香的传统生产方法是以松香为原料、Pd/C为催化剂、采用熔融法,在210~270℃、10.0~25.0MPa的高温高压下加氢制得,近些年来,不断有新的生产或者改进工艺以降低生产成本。。
发明内容
本发明目的就是为了弥补已有技术的缺陷,提供一种耐油纳米阻尼胶黏剂。
本发明是通过以下技术方案实现的:
一种耐油纳米阻尼胶黏剂,由下述重量份的原料制得:
辛基酚聚氧乙烯醚1-3、氢化松香树脂3-5、聚醋酸乙烯酯1-3、聚丙烯酸酯乳液6-13、氢氧化钙0.6-0.9、纳米氧化铝粉末0.1-0.2、微米氧化铈粉末0.2-0.4、松油1-2、环氧大豆油1-2、乳液型丙烯酸酯压敏胶粘剂10-20、改性复合纤维1-2;
所述的改性复合纤维由下述重量份的原料制得:
苎麻纤维3-5、秸秆1-3、柚子皮4-6、椰子壳纤维3-5、棉花1-2;
所述的改性复合纤维的制备方法为:
(1)将柚子皮、秸秆、椰子壳纤维切碎,在浓度为3-5%的盐酸溶液中浸泡1-3小时,取出,去离子水洗涤,烘干得酸洗原料;
(2)将其余原料在浓度为4-5%的氢氧化钠溶液中浸泡3-5小时,取出,去离子水洗涤,烘干得碱洗原料;
(3)将酸洗原料、碱洗原料混匀,在70-80℃条件下水煮4-8分钟,再进行蒸气爆破处理,所述蒸汽爆破处理的压力为0.9-1.5MPa,蒸汽爆破处理时间为5-10分钟,即得。
所述的一种耐油纳米阻尼胶黏剂,
制备方法步骤如下:
(1)在反应釜中加入辛基酚聚氧乙烯醚、氢化松香树脂、聚醋酸乙烯酯以及适量水搅拌均匀;
(2)加热至50-60℃加入微米氧化铈粉末、松油、环氧大豆油、乳液型丙烯酸酯压敏胶粘剂加完后保温1-3小时;
(3)反应完成后,降温至室温,加入其余原料以及适量水混匀,搅拌均匀,即得。
本发明的优点是:(1)本发明利用纳米填料增加本发明的耐油特性,油不渗透,适用于油污多的工作环境,加入氢化松香树脂,增加粘度的同时增强隔音效果;聚丙烯酸酯乳液是一种抗渗能力突出的胶粘浆料,与其余原料复配合理,增加本发明的耐油性;
(2)利用蒸汽爆破处理复配天然纤维,蒸汽爆破作为一项新技术,被认为是生物再生利用过程中取得的重大进展之一,该法不需要添加任何化学物质,也不需要使用任何催化剂,因此生产过程十分洁净、环保,在爆破前用酸碱处理,增加孔隙度,能够更好的达到改性纤维的效果,所得纤维与其余原料复配良好,相容性高的同时还能增加粘胶的粘度。
(3)本发明具有显著的密封隔音效果,永远保持粘弹性,隔音永不失效果,适用于几乎任何缝隙的隔音密封,使用非常简单;无有机物挥发、无气味;环境友好、不含任何有毒物质;非常经济的噪音治理方案。。
具体实施方式
一种耐油纳米阻尼胶黏剂,由下述重量份的原料制得:
辛基酚聚氧乙烯醚1、氢化松香树脂3、聚醋酸乙烯酯1、聚丙烯酸酯乳液6、氢氧化钙0.6、纳米氧化铝粉末0.1、微米氧化铈粉末0.2、松油1、环氧大豆油1、乳液型丙烯酸酯压敏胶粘剂10、改性复合纤维1;
所述的改性复合纤维由下述重量份的原料制得:
苎麻纤维3、秸秆1、柚子皮4、椰子壳纤维3、棉花1;
所述的改性复合纤维的制备方法为:
(1)将柚子皮、秸秆、椰子壳纤维切碎,在浓度为3%的盐酸溶液中浸泡1小时,取出,去离子水洗涤,烘干得酸洗原料;
(2)将其余原料在浓度为4%的氢氧化钠溶液中浸泡3小时,取出,去离子水洗涤,烘干得碱洗原料;
(3)将酸洗原料、碱洗原料混匀,在70℃条件下水煮4分钟,再进行蒸气爆破处理,所述蒸汽爆破处理的压力为0.9MPa,蒸汽爆破处理时间为5分钟,即得。
所述的一种耐油纳米阻尼胶黏剂,
制备方法步骤如下:
(1)在反应釜中加入辛基酚聚氧乙烯醚、氢化松香树脂、聚醋酸乙烯酯以及适量水搅拌均匀;
(2)加热至50℃加入微米氧化铈粉末、松油、环氧大豆油、乳液型丙烯酸酯压敏胶粘剂加完后保温1小时;
(3)反应完成后,降温至室温,加入其余原料以及适量水混匀,搅拌均匀,即得。
本实施例可以形成一个阻尼值在0.7以上的温域达100℃以上的阻尼平台,T-剥离强度>30N/cm,能起到隔音、粘结双重作用。
将没有进行填缝隔音处理的石膏板A与用本实施例作为填缝剂的石膏板B进行隔音对比,石膏板B比石膏板A更能够隔音,噪音减少4-6分贝。
Claims (2)
1.一种耐油纳米阻尼胶黏剂,其特征在于,由下述重量份的原料制得:
辛基酚聚氧乙烯醚1-3、氢化松香树脂3-5、聚醋酸乙烯酯1-3、聚丙烯酸酯乳液6-13、氢氧化钙0.6-0.9、纳米氧化铝粉末0.1-0.2、微米氧化铈粉末0.2-0.4、松油1-2、环氧大豆油1-2、乳液型丙烯酸酯压敏胶粘剂10-20、改性复合纤维1-2;
所述的改性复合纤维由下述重量份的原料制得:
苎麻纤维3-5、秸秆1-3、柚子皮4-6、椰子壳纤维3-5、棉花1-2;
所述的改性复合纤维的制备方法为:
(1)将柚子皮、秸秆、椰子壳纤维切碎,在浓度为3-5%的盐酸溶液中浸泡1-3小时,取出,去离子水洗涤,烘干得酸洗原料;
(2)将其余原料在浓度为4-5%的氢氧化钠溶液中浸泡3-5小时,取出,去离子水洗涤,烘干得碱洗原料;
(3)将酸洗原料、碱洗原料混匀,在70-80℃条件下水煮4-8分钟,再进行蒸气爆破处理,所述蒸汽爆破处理的压力为0.9-1.5MPa,蒸汽爆破处理时间为5-10分钟,即得。
2.根据权利要求1所述的一种耐油纳米阻尼胶黏剂,其特征在于,
制备方法步骤如下:
(1)在反应釜中加入辛基酚聚氧乙烯醚、氢化松香树脂、聚醋酸乙烯酯以及适量水搅拌均匀;
(2)加热至50-60℃加入微米氧化铈粉末、松油、环氧大豆油、乳液型丙烯酸酯压敏胶粘剂加完后保温1-3小时;
(3)反应完成后,降温至室温,加入其余原料以及适量水混匀,搅拌均匀,即得。