CN105219264A - 大豆蛋白胶-高质量血胶共聚木塑胶黏剂及其制备工艺 - Google Patents
大豆蛋白胶-高质量血胶共聚木塑胶黏剂及其制备工艺 Download PDFInfo
- Publication number
- CN105219264A CN105219264A CN201510598693.3A CN201510598693A CN105219264A CN 105219264 A CN105219264 A CN 105219264A CN 201510598693 A CN201510598693 A CN 201510598693A CN 105219264 A CN105219264 A CN 105219264A
- Authority
- CN
- China
- Prior art keywords
- glue
- high quality
- soybean
- quality blood
- hour
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
大豆蛋白胶-高质量血胶共聚木塑胶黏剂及其制备工艺,涉及一种胶黏剂,其成分主要包括大豆蛋白胶与高质量血胶,制备完成后,将大豆蛋白胶和高质量血胶混合,比重为100:30,加入8份聚乙烯醇,升温至90℃,加热时长1小时即可得到大豆蛋白胶-高质量血胶共聚胶黏剂。本发明的特点:无毒无害,工艺简单,性优价廉,用途广泛,稳定性好,抗水性强,粘结强度高,实用性强。
Description
技术领域:
本发明涉及一种胶黏剂,具体涉及大豆蛋白胶-高质量血胶共聚木塑胶黏剂配方及其制备工艺。
背景技术:
化学工业是近现代发展十分迅速的国民经济的支柱产业,而精细化工尾气重要组成部分,在20世纪得到了突飞猛进的发展,未解决人类的衣食住行以及能源、资源与环境问题作出重要贡献。
胶黏剂是现代工业发展和人类生活水平提高必不可少的重要材料,胶黏剂及粘结技术以其他连接方式无法比拟的特种工艺,在现代经济、现代国防、现代科技中发挥着重大的作用。
发明内容:
本发明所要解决的技术问题在于克服现有技术的缺陷,提供一种大豆蛋白胶-高质量血胶共聚木塑胶黏剂配方及其制备工艺。
本发明所要解决的技术问题采用以下技术方案来实现。
大豆蛋白胶-高质量血胶共聚木塑胶黏剂,其特征在于:其成分主要包括大豆蛋白胶与高质量血胶,具体为
大豆蛋白胶包括:
E-44环氧树脂:20-30份,E-51环氧树脂:10-15份,改性胺与聚酰胺混合体10-15份,滑石粉:20-25份,促进剂:1-2份,偶联剂:1-2份;大豆150-200份,水20-30份,香精5-6份;
高质量血胶包括:
血粉:100-120份,蒸馏水:450-500份,二甲基硅橡胶:45-50份,二酰氧庚烷二丁基锡:0.1-0.2份,气相法白炭黑:10-15份,20%碳酸钠水溶液:15-20份、氢氧化钙:10-20份。
大豆蛋白胶-高质量血胶共聚木塑胶黏剂制备工艺,其特征在于:包括大豆蛋白胶与高质量血胶制备,具体为:
大豆蛋白胶的制备包括:
将E-44环氧树脂、E-51环氧树脂均匀混合得到A组分;改性胺与聚酰胺混合体、滑石粉、促进剂、偶联剂混合得到B组分,A组分与B组分混合得到混合物;
从大豆中分离蛋白8%-20%、尿素15%-17%、多聚磷酸钠1%-10%,将尿素分散在水中,混合制成尿素溶液,加入蛋白和混合物,在常温下搅拌1-2小时,再加入多聚磷酸钠,继续搅拌2-3小时,最后将香精加入,高温搅拌20分钟,温度控制在90-95℃;
高质量血胶的制备包括:
1)取血粉浸泡在蒸馏水中,保持蒸馏水温度控制在28-30℃,浸泡时长4-5小时,蒸馏水量为血粉的四倍;
2)将20%碳酸钠水溶液加入到蒸馏水中,搅拌2-3小时;
3)同时调配氢氧化钙与余下的蒸馏水,搅拌均匀,搅拌速度20-30r/min,每3-5分钟搅拌一次,一次时长3分钟,随时去除表面泡沫,待搅拌木浆提出胶面,向下流的胶液立即丝断成胶胨状,停止搅拌,冷却1小时;
4)将调配的氢氧化钙与余下的蒸馏水加入2)步骤中,继续搅拌,随时去除表面泡沫,搅拌1小时,得到B混合物;
5)取二甲基硅橡胶,与二酰氧庚烷二丁基锡和5气相法白炭黑混合得到B胶剂;
6)取B混合物与B胶剂搅拌搅拌,冷却,即可;
制备完成后,将大豆蛋白胶和高质量血胶混合,比重为100:20-50,加入5-10份聚乙烯醇,升温至90℃,加热时长1小时即可得到大豆蛋白胶-高质量血胶共聚木塑胶黏剂。
本发明的特点:无毒无害,工艺简单,性优价廉,用途广泛,稳定性好,抗水性强,粘结强度高,实用性强。
具体实施方式:
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
具体实施例1:大豆蛋白胶-高质量血胶共聚木塑胶黏剂,其成分主要包括大豆蛋白胶与高质量血胶,具体为
大豆蛋白胶包括:
E-44环氧树脂:20份,E-51环氧树脂:10份,改性胺与聚酰胺混合体10份,滑石粉:20份,促进剂:1份,偶联剂:1份;大豆150份,水20份,香精5份;
高质量血胶包括:
血粉:100份,蒸馏水:450份,二甲基硅橡胶:45份,二酰氧庚烷二丁基锡:0.1份,气相法白炭黑:10份,20%碳酸钠水溶液:15份、氢氧化钙:10份。
具体实施例2:大豆蛋白胶-高质量血胶共聚木塑胶黏剂,其成分主要包括大豆蛋白胶与高质量血胶,具体为
大豆蛋白胶包括:
E-44环氧树脂:30份,E-51环氧树脂:15份,改性胺与聚酰胺混合体15份,滑石粉:25份,促进剂:2份,偶联剂:2份;大豆200份,水30份,香精6份;
高质量血胶包括:
血粉:120份,蒸馏水:500份,二甲基硅橡胶:50份,二酰氧庚烷二丁基锡:0.2份,气相法白炭黑:15份,20%碳酸钠水溶液:20份、氢氧化钙:20份。
大豆蛋白胶-高质量血胶共聚木塑胶黏剂制备工艺,包括大豆蛋白胶与聚氨酯改性淀粉制备,具体为:
大豆蛋白胶的制备包括:
将E-44环氧树脂、E-51环氧树脂均匀混合得到A组分;改性胺与聚酰胺混合体、滑石粉、促进剂、偶联剂混合得到B组分,A组分与B组分混合得到混合物;
从大豆中分离蛋白8%-20%、尿素15%-17%、多聚磷酸钠1%-10%,将尿素分散在水中,混合制成尿素溶液,加入蛋白和混合物,在常温下搅拌1-2小时,再加入多聚磷酸钠,继续搅拌2-3小时,最后将香精加入,高温搅拌20分钟,温度控制在90-95℃;
高质量血胶的制备包括:
6)取血粉浸泡在蒸馏水中,保持蒸馏水温度控制在28-30℃,浸泡时长4-5小时,蒸馏水量为血粉的四倍;
7)将20%碳酸钠水溶液加入到蒸馏水中,搅拌2-3小时;
8)同时调配氢氧化钙与余下的蒸馏水,搅拌均匀,搅拌速度20-30r/min,每3-5分钟搅拌一次,一次时长3分钟,随时去除表面泡沫,待搅拌木浆提出胶面,向下流的胶液立即丝断成胶胨状,停止搅拌,冷却1小时;
9)将调配的氢氧化钙与余下的蒸馏水加入2)步骤中,继续搅拌,随时去除表面泡沫,搅拌1小时,得到B混合物;
10)取二甲基硅橡胶,与二酰氧庚烷二丁基锡和5气相法白炭黑混合得到B胶剂;
6)取B混合物与B胶剂搅拌搅拌,冷却,即可;
制备完成后,将大豆蛋白胶和高质量血胶混合,比重为100:20-50,加入5-10份聚乙烯醇,升温至90℃,加热时长1小时即可得到大豆蛋白胶-高质量血胶共聚木塑胶黏剂。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (2)
1.大豆蛋白胶-高质量血胶共聚木塑胶黏剂,其特征在于:其成分主要包括大豆蛋白胶与高质量血胶,具体为
大豆蛋白胶包括:
E-44环氧树脂:20-30份,E-51环氧树脂:10-15份,改性胺与聚酰胺混合体10-15份,滑石粉:20-25份,促进剂:1-2份,偶联剂:1-2份;大豆150-200份,水20-30份,香精5-6份;
高质量血胶包括:
血粉:100-120份,蒸馏水:450-500份,二甲基硅橡胶:45-50份,二酰氧庚烷二丁基锡:0.1-0.2份,气相法白炭黑:10-15份,20%碳酸钠水溶液:15-20份、氢氧化钙:10-20份。
2.大豆蛋白胶-高质量血胶共聚木塑胶黏剂制备工艺,其特征在于:包括大豆蛋白胶与高质量血胶制备,具体为:
大豆蛋白胶的制备包括:
将E-44环氧树脂、E-51环氧树脂均匀混合得到A组分;改性胺与聚酰胺混合体、滑石粉、促进剂、偶联剂混合得到B组分,A组分与B组分混合得到混合物;
从大豆中分离蛋白8%-20%、尿素15%-17%、多聚磷酸钠1%-10%,将尿素分散在水中,混合制成尿素溶液,加入蛋白和混合物,在常温下搅拌1-2小时,再加入多聚磷酸钠,继续搅拌2-3小时,最后将香精加入,高温搅拌20分钟,温度控制在90-95℃;
高质量血胶的制备包括:
1)取血粉浸泡在蒸馏水中,保持蒸馏水温度控制在28-30℃,浸泡时长4-5小时,蒸馏水量为血粉的四倍;
2)将20%碳酸钠水溶液加入到蒸馏水中,搅拌2-3小时;
3)同时调配氢氧化钙与余下的蒸馏水,搅拌均匀,搅拌速度20-30r/min,每3-5分钟搅拌一次,一次时长3分钟,随时去除表面泡沫,待搅拌木浆提出胶面,向下流的胶液立即丝断成胶胨状,停止搅拌,冷却1小时;
4)将调配的氢氧化钙与余下的蒸馏水加入2)步骤中,继续搅拌,随时去除表面泡沫,搅拌1小时,得到B混合物;
5)取二甲基硅橡胶,与二酰氧庚烷二丁基锡和5气相法白炭黑混合得到B胶剂;
6)取B混合物与B胶剂搅拌搅拌,冷却,即可;
制备完成后,将大豆蛋白胶和高质量血胶混合,比重为100:20-50,加入5-10份聚乙烯醇,升温至90℃,加热时长1小时即可得到大豆蛋白胶-高质量血胶共聚木塑胶黏剂。