CN104909627A - 一种轻质多孔吸音的保温砂浆及其制备方法 - Google Patents

一种轻质多孔吸音的保温砂浆及其制备方法 Download PDF

Info

Publication number
CN104909627A
CN104909627A CN201510283120.1A CN201510283120A CN104909627A CN 104909627 A CN104909627 A CN 104909627A CN 201510283120 A CN201510283120 A CN 201510283120A CN 104909627 A CN104909627 A CN 104909627A
Authority
CN
China
Prior art keywords
parts
insulation mortar
silicon carbide
absorbing
porous sound
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510283120.1A
Other languages
English (en)
Inventor
黄二华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Rui He Decorative Engineering Co Ltd
Original Assignee
Hefei Rui He Decorative Engineering Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Rui He Decorative Engineering Co Ltd filed Critical Hefei Rui He Decorative Engineering Co Ltd
Priority to CN201510283120.1A priority Critical patent/CN104909627A/zh
Publication of CN104909627A publication Critical patent/CN104909627A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种轻质多孔吸音的保温砂浆，其特征在于，由下列重量份的原料制备制成：普通水泥40-45、玻化微珠27-30、蜂窝煤渣7-9、短切玻璃纤维3-5、活性氧化铝微粉3-4、火山渣5-7、碳化硅2-3、绒毛浆4.5-6.5、预胶化淀粉2.5-3.5、聚磷酸铵0.2-0.3、增效剂8-10；本发明采用玻化微珠、火山渣、蜂窝煤渣、碳化硅等材料，保温隔热性能好，具有丰富的气孔，与水泥混合，使得产品在大量气孔的前提下具有较理想的防水效果，同时吸音效果好；添加聚磷酸酯等阻燃成分，配合增效剂的添加，进一步增强了产品的阻燃性，同时增强产品的抗裂性以及耐高温性能；本发明轻质多孔，节约资源，值得推广。

Description

一种轻质多孔吸音的保温砂浆及其制备方法
技术领域
本发明涉及建筑保温材料领域，特别是一种轻质多孔吸音的保温砂浆及其制备方法。
背景技术
一直以来砂浆都是大量的建筑用料，特别是近年来，各种新型化合物的出现，在传统的砂浆加入这些各种新型的外加剂，配制出各种新型的复合砂浆，对传统砂浆进行了很大的改善，使其发挥了很大的经济效益。无机保温砂浆是一种较新的保温材料，但是由于填料重量大，无空腔结构，强度高，有一定吸水性。本发明采用玻化微珠、火山渣、蜂窝煤渣、碳化硅等材料，保温隔热性能好，与基层材料粘结紧密，具有丰富的气孔，与水泥混合，使得保温砂浆存在大量气孔的前提下具有较理想的防水效果，同时具有一定的吸音效果。本发明材料添加多种轻质填料，不但可以减轻建筑物的自身重量，而且还可以提高建筑物的保温隔热性能，降低取暖制冷能耗，节约资源；添加聚磷酸酯等阻燃成分，配合增效剂的添加，进一步增强了产品的阻燃性，同时增强产品的抗裂性以及耐高温性能，采用农作物秸秆为基料，节能环保；本发明吸音效果好，轻质多孔，节约资源，值得推广。
发明内容
本发明的目的是提供一种轻质多孔吸音的保温砂浆及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种轻质多孔吸音的保温砂浆，由下列重量份的原料制备制成：普通水泥40-45、玻化微珠27-30、蜂窝煤渣7-9、短切玻璃纤维3-5、活性氧化铝微粉3-4、火山渣5-7、碳化硅2-3、绒毛浆4.5-6.5、预胶化淀粉2.5-3.5、聚磷酸铵0.2-0.3、增效剂8-10；
所述增效剂由以下重量份的原料制备而成：农作物秸秆45-50、水性聚氨酯20-24、碳化硅3-5、聚丙烯纤维2-3、丙烯酸甲酯7-9、油酸丁酯4-6、氢氧化铝4-5、200目莫来粉7-9、聚乙二醇3-5、环氧大豆油2-3、羟丙基甲基纤维素醚 1-2、水20-25；制备方法如下：首先将农作物秸秆干燥后粉碎成100-200目粉末，与氢氧化铝、200目莫来粉、碳化硅、聚丙烯纤维混合均匀形成混合粉料，然后将聚乙二醇溶于水中，加入丙烯酸乙酯、油酸丁酯，加热至50℃-60℃，反应1-1.5小时，冷却至室温，加入其余剩余成分，以300-400转/分的速度搅拌8-10分钟后加入混合粉料，以500-600转/分的速度搅拌20-30分钟得到混合浆料，最后将混合浆料泵入喷雾干燥设备中，控制进风温度 120-150℃、出风温度 80-100℃，即可制成增效剂。
本发明所述一种轻质多孔吸音的保温砂浆，由以下具体步骤制成：首先将蜂窝煤渣、火山渣、碳化硅混合后研磨40-50分钟，形成200-300目粉末，然后与其他剩余成分混合，加入到双轴卧式搅拌釜中，以300-400转/分钟匀速搅拌15-20分钟，包装即得到保温砂浆预拌料。
本发明的有益效果是：本发明采用玻化微珠、火山渣、蜂窝煤渣、碳化硅等材料，保温隔热性能好，具有丰富的气孔，与水泥混合，使得产品在大量气孔的前提下具有较理想的防水效果，同时吸音效果好；添加聚磷酸酯等阻燃成分，配合增效剂的添加，进一步增强了产品的阻燃性，同时增强产品的抗裂性以及耐高温性能；本发明轻质多孔，节约资源，值得推广。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种轻质多孔吸音的保温砂浆，由下列重量份（公斤）的原料制备制成：普通水泥40、玻化微珠27、蜂窝煤渣7、短切玻璃纤维3、活性氧化铝微粉3、火山渣5、碳化硅2、绒毛浆4.5、预胶化淀粉2.5、聚磷酸铵0.2、增效剂8；
所述增效剂由以下重量份（公斤）的原料制备而成：农作物秸秆45、水性聚氨酯20、碳化硅3、聚丙烯纤维2、丙烯酸甲酯7、油酸丁酯4、氢氧化铝4、200目莫来粉7、聚乙二醇3、环氧大豆油2、羟丙基甲基纤维素醚 1、水20；制备方法如下：首先将农作物秸秆干燥后粉碎成100-200目粉末，与氢氧化铝、200目莫来粉、碳化硅、聚丙烯纤维混合均匀形成混合粉料，然后将聚乙二醇溶于水中，加入丙烯酸乙酯、油酸丁酯，加热至50℃-60℃，反应1-1.5小时，冷却至室温，加入其余剩余成分，以300-400转/分的速度搅拌8-10分钟后加入混合粉料，以500-600转/分的速度搅拌20-30分钟得到混合浆料，最后将混合浆料泵入喷雾干燥设备中，控制进风温度 120-150℃、出风温度 80-100℃，即可制成增效剂。
本发明所述一种轻质多孔吸音的保温砂浆，由以下具体步骤制成：首先将蜂窝煤渣、火山渣、碳化硅混合后研磨40-50分钟，形成200-300目粉末，然后与其他剩余成分混合，加入到双轴卧式搅拌釜中，以300-400转/分钟匀速搅拌15-20分钟，包装即得到保温砂浆预拌料。
本发明保温砂浆采用现配现用的方式，使用时将保温砂浆加入0.8倍量的水搅拌均匀形成膏状物质即可使用。
经各种试验测定，本发明保温砂浆各项性能为 ：堆积密度为279 kg/m3，导热系数为0.055W/m.K，抗压强度为0.36Mpa，线性收缩率为0.30%。

Claims (2)

1.一种轻质多孔吸音的保温砂浆，其特征在于，由下列重量份的原料制备制成：普通水泥40-45、玻化微珠27-30、蜂窝煤渣7-9、短切玻璃纤维3-5、活性氧化铝微粉3-4、火山渣5-7、碳化硅2-3、绒毛浆4.5-6.5、预胶化淀粉2.5-3.5、聚磷酸铵0.2-0.3、增效剂8-10；
所述增效剂由以下重量份的原料制备而成：农作物秸秆45-50、水性聚氨酯20-24、碳化硅3-5、聚丙烯纤维2-3、丙烯酸甲酯7-9、油酸丁酯4-6、氢氧化铝4-5、200目莫来粉7-9、聚乙二醇3-5、环氧大豆油2-3、羟丙基甲基纤维素醚 1-2、水20-25；制备方法如下：首先将农作物秸秆干燥后粉碎成100-200目粉末，与氢氧化铝、200目莫来粉、碳化硅、聚丙烯纤维混合均匀形成混合粉料，然后将聚乙二醇溶于水中，加入丙烯酸乙酯、油酸丁酯，加热至50℃-60℃，反应1-1.5小时，冷却至室温，加入其余剩余成分，以300-400转/分的速度搅拌8-10分钟后加入混合粉料，以500-600转/分的速度搅拌20-30分钟得到混合浆料，最后将混合浆料泵入喷雾干燥设备中，控制进风温度 120-150℃、出风温度 80-100℃，即可制成增效剂。
2.根据权利要求1所述一种轻质多孔吸音的保温砂浆，其特征在于，由以下具体步骤制成：首先将蜂窝煤渣、火山渣、碳化硅混合后研磨40-50分钟，形成200-300目粉末，然后与其他剩余成分混合，加入到双轴卧式搅拌釜中，以300-400转/分钟匀速搅拌15-20分钟，包装即得到保温砂浆预拌料。
CN201510283120.1A 2015-05-29 2015-05-29 一种轻质多孔吸音的保温砂浆及其制备方法 Pending CN104909627A (zh)