CN105199403A - 一种沥青路面材料及制备方法 - Google Patents

一种沥青路面材料及制备方法 Download PDF

Info

Publication number
CN105199403A
CN105199403A CN201510667272.1A CN201510667272A CN105199403A CN 105199403 A CN105199403 A CN 105199403A CN 201510667272 A CN201510667272 A CN 201510667272A CN 105199403 A CN105199403 A CN 105199403A
Authority
CN
China
Prior art keywords
asphalt pavement
petroleum resin
pavement material
pigment
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510667272.1A
Other languages
English (en)
Other versions
CN105199403B (zh
Inventor
张桂忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Dashan Road&bridge Engineering Co ltd
Original Assignee
Heze Hainuo Intellectual Property Service Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Heze Hainuo Intellectual Property Service Co Ltd filed Critical Heze Hainuo Intellectual Property Service Co Ltd
Priority to CN201510667272.1A priority Critical patent/CN105199403B/zh
Publication of CN105199403A publication Critical patent/CN105199403A/zh
Application granted granted Critical
Publication of CN105199403B publication Critical patent/CN105199403B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及沥青路面材料,按照重量份数计,包括:基础油30-50份、C5石油树脂15-40份、C9石油树脂20-45份、改性组分5-15份、阳离子慢裂乳化剂0.5-3份、颜料1-15份、水20-45份。其制备方法包括步骤:1)将基础油加热到160-180℃,添加C5石油树脂、C9石油树脂、颜料、改性组分,搅拌;2)把水加热到50-70℃,向热水中添加阳离子慢裂乳化剂,搅拌;3)将步骤1)与步骤2)所得物质混合并进行剪切研磨。本材料只需要桶包装或罐车运输,使用前后无需加热,常温下即可与石料拌合使用,极大的简化了彩色沥青混合料的制备过程,使彩色路面的施工变的极为简单方便。

Description

一种沥青路面材料及制备方法
技术领域
本发明涉及改性沥青,特别涉及一种沥青路面材料及制备方法。
背景技术
目前沥青主要采用脱色沥青进行调和,常温下呈固态,而运输或使用时高温加热,变为粘稠液态,反复加热影响沥青的性能。
彩色沥青路面对城市美化和城市交通起到至关重要的作用,其应用广泛,开发一种常温下为液态的彩色沥青,意义重大。
发明内容
本发明为了弥补现有技术的不足,提供了一种沥青路面材料及制备方法,该材料常温下为可流动液态,可常温运输,在常温下即可与石料拌合使用,然后进行路面的摊铺、碾压施工,实现冷拌冷铺,极大的简化了彩色沥青路面的铺筑过程,使彩色路面的施工变的更为简单方便。
本发明是通过如下技术方案实现的:
一种沥青路面材料,按照重量份数计,包括:基础油20-70份、C5石油树脂10-50份、C9石油树脂10-50份、改性组分2-20份、阳离子慢裂乳化剂0.1-5份、颜料0.5-20份、水10-60份;所述改性组分由SBS改性剂和聚乙烯醇组成。聚乙烯醇可以提高产品存储的稳定性。
作为优选,按照重量份数计,包括:基础油35-45份、C5石油树脂20-30份、C9石油树脂28-35份、改性组分8-12份、阳离子慢裂乳化剂1-2份、颜料5-10份、水28-35份。
优选的,所述基础油为矿物类油。
优选的,所述SBS改性剂与聚乙烯醇的质量比为2:1-1:1。
作为优选,所述颜料为无机颜料,所述无机颜料为铁红颜料、铬绿颜料、铁绿颜料、钛白颜料、铬黄颜料中的至少一种。
作为优选方案,所述阳离子慢裂乳化剂为酰胺型慢裂快凝型阳离子沥青乳化剂。
所述的沥青路面材料的制备方法,包括以下步骤:1)将基础油加热到160-180℃,添加C5石油树脂、C9石油树脂、颜料、改性组分,搅拌;2)把水加热到50-70℃,向热水中添加阳离子慢裂乳化剂,搅拌;3)将步骤1)所得物质与步骤2)所得物质混合并进行剪切研磨得沥青路面材料。
作为优选,步骤2)中把水加热到60℃。
本发明的有益效果:
本材料为冷施工彩色乳化改性沥青材料,本材料在运输中只需要简单地桶包装或罐车运输,使用时无需加热,在常温下即可与石料拌合使用,然后进行路面的摊铺、碾压施工,极大的简化了彩色沥青混合料的制备过程,使彩色路面的施工变的极为简单方便;另外,用水作为溶剂,避免了环境污染,降低了材料的制作成本。
具体实施方式
实施例1
沥青路面材料的制备方法,包括以下步骤:
1)将30kg矿物类油加热到160℃,添加15kgC5石油树脂、20kgC9石油树脂、1kg铁红颜料、3kg热塑性弹性体SBS和2kg聚乙烯醇(平均分子量16000-20000),搅拌1小时;
2)把水加热到50℃,20kg该热水中添加0.5kg酰胺型阳离子慢裂快凝型乳化剂,搅拌10分钟;
3)将步骤1)所得物质与步骤2)所得物质混合并进行剪切研磨即得产品。
实施例2:
沥青路面材料的制备方法,包括以下步骤:
1)将50kg矿物类油加热到180℃,添加40kgC5石油树脂、45kgC9石油树脂、15kg铁绿颜料、8kg热塑性弹性体SBS和7kg聚乙烯醇(平均分子量16000-20000),搅拌1.5小时;
2)把水加热到70℃,45kg该热水中添加3kg酰胺型阳离子慢裂快凝型乳化剂,搅拌15分钟;
3)将步骤1)所得物质与步骤2)所得物质混合并进行剪切研磨即得产品。
实施例3:
沥青路面材料的制备方法,包括以下步骤:
1)将40kg矿物类油加热到170℃,添加27kgC5石油树脂、33kgC9石油树脂、8kg铬绿颜料、5kg热塑性弹性体SBS和5kg聚乙烯醇(平均分子量16000-20000),搅拌1小时;
2)把水加热到60℃,33kg该热水中添加1.8kg酰胺型阳离子慢裂快凝型乳化剂,搅拌10分钟;
3)将步骤1)所得物质与步骤2)所得物质混合并进行剪切研磨即得产品。
实施例4:
沥青路面材料的制备方法,包括以下步骤:
1)将35kg矿物类油加热到170℃,添加20kgC5石油树脂、28kgC9石油树脂、5kg铬黄颜料、4kg热塑性弹性体SBS和4kg聚乙烯醇(平均分子量16000-20000),搅拌1小时;
2)把水加热到60℃,28kg该热水中添加1kg阳离子慢裂快凝型乳化剂,搅拌10分钟;
3)将步骤1)所得物质与步骤2)所得物质混合并进行剪切研磨即得产品。
实施例5:
沥青路面材料的制备方法,包括以下步骤:
1)将45kg矿物类油加热到170℃,添加30kgC5石油树脂、35kgC9石油树脂、10kg铁红颜料、6kg热塑性弹性体SBS和6kg聚乙烯醇(平均分子量16000-20000),搅拌1小时;
2)把水加热到60℃,35kg该热水中添加2kg阳离子慢裂快凝型乳化剂,搅拌10分钟;
3)将步骤1)所得物质与步骤2)所得物质混合并进行剪切研磨即得产品。
实施例6:
沥青路面材料的制备方法,包括以下步骤:
1)将40kg矿物类油加热到170℃,添加25kgC5石油树脂、31kgC9石油树脂、5kg铁红颜料和2kg钛白颜料、5kg热塑性弹性体SBS和5kg聚乙烯醇(平均分子量16000-20000),搅拌1小时;
2)把水加热到60℃,33kg该热水中添加1.5kg阳离子慢裂型乳化剂,搅拌10分钟;
3)将步骤1)所得物质与步骤2)所得物质混合并进行剪切研磨即得产品。
实施例7:
沥青路面材料的制备方法,包括以下步骤:
1)将36kg矿物类油加热到170℃,添加18kgC5石油树脂、26kgC9石油树脂、6kg铬黄颜料、5kg热塑性弹性体SBS和3kg聚乙烯醇(平均分子量16000-20000),搅拌1小时;
2)把水加热到60℃,40kg该热水中添加2kg阳离子慢裂快凝型乳化剂,搅拌10分钟;
3)将步骤1)所得物质与步骤2)所得物质混合并进行剪切研磨即得产品。
实施例8:
沥青路面材料的制备方法,包括以下步骤:
1)将41kg荷荷巴油加热到170℃,添加23kgC5石油树脂、20kgC9石油树脂、8kg铬绿颜料、6kg热塑性弹性体SBS和6kg聚乙烯醇(平均分子量16000-20000),搅拌1小时;
2)把水加热到60℃,35kg该热水中添加1.5kg阳离子慢裂快凝型乳化剂,搅拌10分钟;
3)将步骤1)所得物质与步骤2)所得物质混合并进行剪切研磨即得产品。

Claims (8)

1.一种沥青路面材料,其特征在于,按照重量份数计,包括:基础油20-70份、C5石油树脂10-50份、C9石油树脂10-50份、改性组分2-20份、阳离子慢裂乳化剂0.1-5份、颜料0.5-20份、水10-60份;所述改性组分由SBS改性剂和聚乙烯醇组成。
2.如权利要求1所述的沥青路面材料,其特征在于:按照重量份数计,包括:基础油35-45份、C5石油树脂20-30份、C9石油树脂28-35份、改性组分8-12份、阳离子慢裂乳化剂1-2份、颜料5-10份、水28-35份。
3.如权利要求1所述的沥青路面材料,其特征在于:所述基础油为矿物类油。
4.如权利要求1所述的沥青路面材料及制备方法,其特征在于:所述SBS改性剂与聚乙烯醇的质量比为2:1-1:1。
5.如权利要求1所述的沥青路面材料,其特征在于:所述颜料为无机颜料,所述无机颜料为铁红颜料、铬绿颜料、铁绿颜料、钛白颜料、铬黄颜料中的至少一种。
6.如权利要求1所述的沥青路面材料,其特征在于:所述阳离子慢裂乳化剂为酰胺型慢裂快凝型阳离子沥青乳化剂。
7.一种如权利要求1-6中任一项所述的沥青路面材料的制备方法,其特征在于,包括以下步骤:1)将基础油加热到160-180℃,添加C5石油树脂、C9石油树脂、颜料、改性组分,搅拌;2)把水加热到50-70℃,向热水中添加阳离子慢裂乳化剂,搅拌;3)将步骤1)所得物质与步骤2)所得物质混合并进行剪切研磨得沥青路面材料。
8.如权利要求7所述的沥青路面材料的制备方法,其特征在于:步骤2)中把水加热到60℃。
CN201510667272.1A 2015-10-16 2015-10-16 一种沥青路面材料及制备方法 Active CN105199403B (zh)