CN105195514A - 一种铜箔冷轧方法 - Google Patents

一种铜箔冷轧方法 Download PDF

Info

Publication number
CN105195514A
CN105195514A CN201510704610.4A CN201510704610A CN105195514A CN 105195514 A CN105195514 A CN 105195514A CN 201510704610 A CN201510704610 A CN 201510704610A CN 105195514 A CN105195514 A CN 105195514A
Authority
CN
China
Prior art keywords
copper foil
cooled
cold
cold rolling
copper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510704610.4A
Other languages
English (en)
Inventor
邓义增
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuxi Hebang Metal Products Co Ltd
Original Assignee
Wuxi Hebang Metal Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuxi Hebang Metal Products Co Ltd filed Critical Wuxi Hebang Metal Products Co Ltd
Priority to CN201510704610.4A priority Critical patent/CN105195514A/zh
Publication of CN105195514A publication Critical patent/CN105195514A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种铜箔冷轧方法。该方法包括如下步骤：（1）铜带在400-600℃下保温1-3小时后，淬入PAG淬火液中冷却；（2）将步骤（1）冷却后的铜带在250-280℃下保温0.5-1.5小时后，冷却至室温；（3）经步骤（2）处理的铜带在冷轧机上冷轧，得到铜箔。与现有方法相比，本发明在保持相当的强度下，能明显改善铜箔的塑料，提高延伸率。

Description

一种铜箔冷轧方法
技术领域
本发明涉及一种铜箔冷轧方法。
背景技术
传统铜箔冷轧时由于晶粒破碎容易出现硬化，塑性明显下降的问题，导致铜箔强度高而延伸率低。为克服该问题，现有技术提出在冷轧前进行退火处理，虽然能一定程度的减轻塑性下降的问题，但延伸率提高有限。
发明内容
本发明要解决的技术问题是克服现有的缺陷，提供了一种铜箔冷轧方法。
为了解决上述技术问题，本发明提供了如下的技术方案：
一种铜箔冷轧方法，包括如下步骤：
（1）铜带在400-600℃下保温1-3小时后，淬入PAG淬火液中冷却；
（2）将步骤（1）冷却后的铜带在250-280℃下保温0.5-1.5小时后，冷却至室温；
（3）经步骤（2）处理的铜带在冷轧机上冷轧，得到铜箔。
进一步，步骤（3）冷轧时一次压下率为10-90%。
与现有方法相比，本发明在保持相当的强度下，能明显改善铜箔的塑性，提高延伸率。
具体实施方式
以下对本发明的优选实施例进行说明，应当理解，此处所描述的优选实施例仅用于说明和解释本发明，并不用于限定本发明。
实施例1
（1）将0.15mm的铜带在450℃（氮气气氛）下保温3小时后，迅速淬入PAG（聚烷撑乙二醇）淬火液中冷却；
（2）将步骤（1）冷却后的铜带在250℃（氮气气氛）下保温0.5小时后，冷却至室温；
（3）将步骤（2）冷却后的铜带上冷轧机，一道冷轧至0.10mm，所得铜箔的延伸率为15.1%，抗拉强度206MPa。
实施例2
（1）将0.15mm的铜带在500℃（氨气气氛）下保温2.5小时后，迅速淬入PAG淬火液中冷却；
（2）将步骤（1）冷却后的铜带在260℃（氮气气氛）下保温1小时后，冷却至室温；
（3）将步骤（2）冷却后的铜带上冷轧机，一道冷轧至0.08mm，所得铜箔的延伸率为14.8%，抗拉强度209MPa。
实施例3
（1）将0.15mm的铜带在600℃（真空度为0.092MPa）下保温1.5小时后，迅速淬入PAG淬火液中冷却；
（2）将步骤（1）冷却后的铜带在280℃（真空度为0.092MPa）下保温1.5小时后，冷却至室温；
（3）将步骤（2）冷却后的铜带上冷轧机，一道冷轧至0.04mm，所得铜箔的延伸率为15.3%，抗拉强度210MPa。
对比例
（1）将0.15mm的铜带在600℃（真空度为0.092MPa）下保温4小时后，冷却至室温；
（2）将步骤（1）冷却后的铜带上冷轧机，一道冷轧至0.04mm，所得铜箔的延伸率为11.2%，抗拉强度212MPa。
本发明所述的PAG淬火液购自恒鑫化工，型号THIF-502。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (2)

1.一种铜箔冷轧方法，包括如下步骤：
（1）铜带在400-600℃下保温1-3小时后，淬入PAG淬火液中冷却；
（2）将步骤（1）冷却后的铜带在250-280℃下保温0.5-1.5小时后，冷却至室温；
（3）经步骤（2）处理的铜带在冷轧机上冷轧，得到铜箔。
2.根据权利要求1所述的铜箔冷轧方法，其特征在于，步骤（3）冷轧时一次压下率为10-90%。
CN201510704610.4A 2015-10-27 2015-10-27 一种铜箔冷轧方法 Pending CN105195514A (zh)