CN105177602A - 一种合金表面除锈工艺 - Google Patents

一种合金表面除锈工艺 Download PDF

Info

Publication number
CN105177602A
CN105177602A CN201510732607.3A CN201510732607A CN105177602A CN 105177602 A CN105177602 A CN 105177602A CN 201510732607 A CN201510732607 A CN 201510732607A CN 105177602 A CN105177602 A CN 105177602A
Authority
CN
China
Prior art keywords
cleaning
minutes
alloy surface
surface derusting
workpiece
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510732607.3A
Other languages
English (en)
Inventor
鲁一军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510732607.3A priority Critical patent/CN105177602A/zh
Publication of CN105177602A publication Critical patent/CN105177602A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种合金表面除锈工艺，包括以下步骤：a、去渣；b、清洗，用5～10MPa水压清洗3～5分钟；c、制备处理液；d、处理液对合金工件在50～70℃条件下进行酸性处理10～15分钟；e、清洗，用10～20MPa水压清洗5～10分钟；f、干燥，将工件进行真空干燥，干燥温度为70～90℃。本发明合金表面除锈工艺，工序简单、操作方便且表面清洗效果好，利于工件批量清洗。

Description

一种合金表面除锈工艺
技术领域
本发明涉及一种金属表面除锈工艺，特别涉及一种合金表面除锈工艺。
背景技术
金属长期风吹雨打表面易氧化就会生锈，合金金属由于表面加入特殊元素起到一定抗锈作用。但是表面还是会产生点点锈斑，如果不及时锈斑就会扩大，从而影响合金金属的使用质量。
发明内容
【1】要解决的技术问题
本发明要解决的技术问题是提供一种操作简单、方便快捷并且修复质量好的合金表面除锈工艺。
【2】解决问题的技术方案
一种合金表面除锈工艺，其特征在于，包括以下步骤：
a、去渣；
b、清洗，用5～10MPa水压清洗3～5分钟；
c、制备处理液；
d、处理液对合金工件在50～70℃条件下进行酸性处理10～15分钟；
e、清洗，用10～20MPa水压清洗5～10分钟；
f、干燥，将工件进行真空干燥，干燥温度为70～90℃。
进一步的，在步骤c中，所述处理液为盐酸15-20％、氟化氢铵19-24％。
【3】有益效果
本发明一种合金表面除锈工艺，工序简单、操作方便且表面清洗效果好，利于工件批量清洗。
具体实施方式
下面详细介绍本发明实施例。
一种合金表面除锈工艺，其特征在于，包括以下步骤：
a、去渣；
b、清洗，用5～10MPa水压清洗3～5分钟；
c、制备处理液；
d、处理液对合金工件在50～70℃条件下进行酸性处理10～15分钟；
e、清洗，用10～20MPa水压清洗5～10分钟；
f、干燥，将工件进行真空干燥，干燥温度为70～90℃。
在步骤c中，所述处理液为盐酸15-20％、氟化氢铵19-24％。
本发明一种合金表面除锈工艺，工序简单、操作方便且表面清洗效果好，利于工件批量清洗。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (2)

1.一种合金表面除锈工艺，其特征在于，包括以下步骤：
a、去渣；
b、清洗，用5～10MPa水压清洗3～5分钟；
c、制备处理液；
d、处理液对合金工件在50～70℃条件下进行酸性处理10～15分钟；
e、清洗，用10～20MPa水压清洗5～10分钟；
f、干燥，将工件进行真空干燥，干燥温度为70～90℃。
2.如权利要求1所述的一种合金表面除锈工艺，其特征在于：在步骤c中，所述处理液为盐酸15-20％、氟化氢铵19-24％。
CN201510732607.3A 2015-11-02 2015-11-02 一种合金表面除锈工艺 Pending CN105177602A (zh)