CN105176423A - 一种无卤环保绿色胶黏剂及其制备方法 - Google Patents
一种无卤环保绿色胶黏剂及其制备方法 Download PDFInfo
- Publication number
- CN105176423A CN105176423A CN201510722982.XA CN201510722982A CN105176423A CN 105176423 A CN105176423 A CN 105176423A CN 201510722982 A CN201510722982 A CN 201510722982A CN 105176423 A CN105176423 A CN 105176423A
- Authority
- CN
- China
- Prior art keywords
- sizing agent
- halogen
- ethyl acetate
- agent
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种无卤环保绿色胶黏剂及其制备方法，由以下重量百分比的原料组成：胶黏剂主剂30%～40%；蓝油墨1%～3%；黄油墨3%～9%；固化剂3%～4%；余量为乙酸乙酯；所述胶黏剂主剂的重量百分比组成为：丙烯酸丁酯15%、丙烯酸异辛酯13%、甲基丙烯酸4%、甲基丙烯酸羟乙酯6%、甲基丙烯酸甲酯6%、N-羟甲基丙烯酰胺7%、BPO？0.5%、乙酸乙酯48.5%。本发明的胶黏剂粘结力强，无卤、低毒，且颜色稳定。该制备方法简单，添加成分少，不添加抗沉淀剂、消泡剂、乳化剂等助剂，生产成本低，制备条件温和、环保。本发明的胶黏剂与色母油墨的连接剂结构相似，能很好的相容到一起。不会出现颜色析出和胶黏剂残胶的不良问题。
Description
技术领域
本发明公开了一种胶黏剂，具体涉及一种无卤环保绿色胶黏剂及其制备方法。
背景技术
自20世纪50年代初至今的60多年间，特别是自20世纪80年代初至今的约30年间，保护膜的发展快速，并且向着多元化，功能性的方向发展。
在加工过程当中起到制程保护、转贴和排废的保护膜越来越多。各种功能性的保护膜也是越来越受到人们的重视。目前市场上一些带颜色的保护膜大多上在膜上产生的。但是原膜的颜色大多是比较单一的几种，并且这种原膜的厚薄稳定性都很差，在高温下还会出现颜色渗出的异常。胶水带颜色的保护膜很少。偶尔有带颜色胶水，也是用来做胶带一类的产品。颜色一类的添加剂对胶黏剂本身的粘性和稳定性都有很大程度的破坏。
发明内容
本发明目的是提供一种无卤环保绿色胶黏剂，解决现有的颜色一类的添加剂对胶黏剂本身的粘性和稳定性造成破坏的问题。
本发明的技术方案为：一种无卤环保绿色胶黏剂，由以下重量百分比的原料组成：
胶黏剂主剂30%～40%；
蓝油墨1%～3%；
黄油墨3%～9%；
固化剂3%～4%；
余量为乙酸乙酯；
所述胶黏剂主剂的重量百分比组成为：丙烯酸丁酯15%、丙烯酸异辛酯13%、甲基丙烯酸4%、甲基丙烯酸羟乙酯6%、甲基丙烯酸甲酯6%、N-羟甲基丙烯酰胺7%、BPO0.5%、乙酸乙酯48.5%。
进一步地，蓝油墨的重量百分比组成为：酞青蓝色粉40%、聚丙烯酸酯树脂30%、碳酸钙3%、硫酸钡2%、流平剂4%、多异氰酸酯类固化剂0.02%，余量为乙酸乙酯。
进一步地，所述黄油墨的重量百分比组成为：无卤黄色粉40%、聚丙烯酸酯树脂30%、碳酸钙3%、硫酸钡2%、流平剂4%、多胺类固化剂0.02%，余量为乙酸乙酯。
进一步地，多异氰酸酯类固化剂为拜耳L-75固化剂。
进一步地，所述固化剂为甲苯多异氰酸酯。
一种无卤环保绿色胶黏剂的制备方法，包括如下步骤：
（1）调制色料：量取蓝油墨和黄油墨，加入两种油墨总重量的两倍重量的乙酸乙酯，搅拌均匀后过500目晒网；
（2）配置胶黏剂主剂：量取胶黏剂主剂，并加入胶黏剂主剂总重量的20%的乙酸乙酯稀释，搅拌均匀；
（3）将固化剂用乙酸乙酯稀释后加入步骤（2）配置好的胶黏剂主剂中，搅拌10-20分钟后后加入步骤（1）制备的色料，继续搅拌20～30分钟，即得成品。
本发明与现有技术相比具有如下优点：
1、本发明的胶黏剂粘结力强，无卤、低毒，且颜色稳定。该制备方法简单，添加成分少，不添加抗沉淀剂、消泡剂、乳化剂等助剂，生产成本低，制备条件温和、环保。
2、本发明的胶黏剂与色母油墨的连接剂结构相似，均为丙烯酸酯类，根据相似相容原理，胶黏剂和油墨树脂混溶，油墨树脂包裹颜料，再通过固化剂交联成网状结构，能很好的相容到一起，不会出现颜色析出和胶黏剂残胶的不良问题。
具体实施方式
实施例1
一种无卤环保绿色胶黏剂，由以下重量百分比的原料组成：
胶黏剂主剂30%；
蓝油墨3%；
黄油墨3%；
固化剂3%；
余量为乙酸乙酯；
所述胶黏剂主剂的重量百分比组成为：丙烯酸丁酯15%、丙烯酸异辛酯13%、甲基丙烯酸4%、甲基丙烯酸羟乙酯6%、甲基丙烯酸甲酯6%、N-羟甲基丙烯酰胺7%、BPO0.5%、乙酸乙酯48.5%。蓝油墨的重量百分比组成为：酞青蓝色粉40%、聚丙烯酸酯树脂30%、碳酸钙3%、硫酸钡2%、流平剂4%、多异氰酸酯类固化剂0.02%，余量为乙酸乙酯。所述黄油墨的重量百分比组成为：无卤黄色粉40%、聚丙烯酸酯树脂30%、碳酸钙3%、硫酸钡2%、流平剂4%、多胺类固化剂0.02%，余量为乙酸乙酯。多异氰酸酯类固化剂为拜耳L-75固化剂。所述固化剂为甲苯多异氰酸酯。
制备方法如下：
（1）调制色料：量取蓝油墨和黄油墨，加入两种油墨总重量的两倍重量的乙酸乙酯，搅拌均匀后过500目晒网；
（2）配置胶黏剂主剂：量取胶黏剂主剂，并加入胶黏剂主剂总重量的20%的乙酸乙酯稀释，搅拌均匀；
（3）将固化剂用乙酸乙酯稀释后加入步骤（2）配置好的胶黏剂主剂中，搅拌10-20分钟后后加入步骤（1）制备的色料，继续搅拌20～30分钟，即得成品。
实施例2
一种无卤环保绿色胶黏剂，由以下重量百分比的原料组成：
胶黏剂主剂40%；
蓝油墨1%；
黄油墨9%；
固化剂3%%；
余量为乙酸乙酯；
所述胶黏剂主剂的重量百分比组成为：丙烯酸丁酯15%、丙烯酸异辛酯13%、甲基丙烯酸4%、甲基丙烯酸羟乙酯6%、甲基丙烯酸甲酯6%、N-羟甲基丙烯酰胺7%、BPO0.5%、乙酸乙酯48.5%。蓝油墨的重量百分比组成为：酞青蓝色粉40%、聚丙烯酸酯树脂30%、碳酸钙3%、硫酸钡2%、流平剂4%、多异氰酸酯类固化剂0.02%，余量为乙酸乙酯。黄油墨的重量百分比组成为：无卤黄色粉40%、聚丙烯酸酯树脂30%、碳酸钙3%、硫酸钡2%、流平剂4%、多胺类固化剂0.02%，余量为乙酸乙酯。多异氰酸酯类固化剂为拜耳L-75固化剂。所述固化剂为甲苯多异氰酸酯。
制备方法如下：
（1）调制色料：量取蓝油墨和黄油墨，加入两种油墨总重量的两倍重量的乙酸乙酯，搅拌均匀后过500目晒网；
（2）配置胶黏剂主剂：量取胶黏剂主剂，并加入胶黏剂主剂总重量的20%的乙酸乙酯稀释，搅拌均匀；
（3）将固化剂用乙酸乙酯稀释后加入步骤（2）配置好的胶黏剂主剂中，搅拌10-20分钟后后加入步骤（1）制备的色料，继续搅拌20～30分钟，即得成品。
实施例3
一种无卤环保绿色胶黏剂，由以下重量百分比的原料组成：
胶黏剂主剂35%；
蓝油墨2%；
黄油墨5%；
固化剂3.5%；
余量为乙酸乙酯；
所述胶黏剂主剂的重量百分比组成为：丙烯酸丁酯15%、丙烯酸异辛酯13%、甲基丙烯酸4%、甲基丙烯酸羟乙酯6%、甲基丙烯酸甲酯6%、N-羟甲基丙烯酰胺7%、BPO0.5%、乙酸乙酯48.5%。蓝油墨的重量百分比组成为：酞青蓝色粉40%、聚丙烯酸酯树脂30%、碳酸钙3%、硫酸钡2%、流平剂4%、多异氰酸酯类固化剂0.02%，余量为乙酸乙酯。黄油墨的重量百分比组成为：无卤黄色粉40%、聚丙烯酸酯树脂30%、碳酸钙3%、硫酸钡2%、流平剂4%、多胺类固化剂0.02%，余量为乙酸乙酯。多异氰酸酯类固化剂为拜耳L-75固化剂。固化剂为甲苯多异氰酸酯。
制备方法如下：
（1）调制色料：量取蓝油墨和黄油墨，加入两种油墨总重量的两倍重量的乙酸乙酯，搅拌均匀后过500目晒网；
（2）配置胶黏剂主剂：量取胶黏剂主剂，并加入胶黏剂主剂总重量的20%的乙酸乙酯稀释，搅拌均匀；
（3）将固化剂用乙酸乙酯稀释后加入步骤（2）配置好的胶黏剂主剂中，搅拌10-20分钟后后加入步骤（1）制备的色料，继续搅拌20～30分钟，即得成品。
以上所述实施例仅表达了本申请的具体实施方式，其描述较为具体和详细，但并不能因此而理解为对本申请保护范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本申请技术方案构思的前提下，还可以做出若干变形和改进，这些都属于本申请的保护范围。
Claims (6)
1.一种无卤环保绿色胶黏剂，其特征在于，由以下重量百分比的原料组成：
胶黏剂主剂30%～40%；
蓝油墨1%～3%；
黄油墨3%～9%；
固化剂3%～4%；
余量为乙酸乙酯；
所述胶黏剂主剂的重量百分比组成为：丙烯酸丁酯15%、丙烯酸异辛酯13%、甲基丙烯酸4%、甲基丙烯酸羟乙酯6%、甲基丙烯酸甲酯6%、N-羟甲基丙烯酰胺7%、BPO0.5%、乙酸乙酯48.5%。
2.根据权利要求1所述的一种无卤环保绿色胶黏剂，其特征在于，蓝油墨的重量百分比组成为：酞青蓝色粉40%、聚丙烯酸酯树脂30%、碳酸钙3%、硫酸钡2%、流平剂4%、多异氰酸酯类固化剂0.02%，余量为乙酸乙酯。
3.根据权利要求1所述的一种无卤环保绿色胶黏剂，其特征在于，所述黄油墨的重量百分比组成为：无卤黄色粉40%、聚丙烯酸酯树脂30%、碳酸钙3%、硫酸钡2%、流平剂4%、多胺类固化剂0.02%，余量为乙酸乙酯。
4.根据权利要求1所述的一种无卤环保绿色胶黏剂，其特征在于，多异氰酸酯类固化剂为拜耳L-75固化剂。
5.根据权利要求1所述的一种无卤环保绿色胶黏剂，其特征在于，所述固化剂为甲苯多异氰酸酯。
6.根据权利要求1-5任一项所述的一种无卤环保绿色胶黏剂的制备方法，其特征在于，包括如下步骤：
（1）调制色料：量取蓝油墨和黄油墨，加入两种油墨总重量的两倍重量的乙酸乙酯，搅拌均匀后过500目晒网；
（2）配置胶黏剂主剂：量取胶黏剂主剂，并加入胶黏剂主剂总重量的20%的乙酸乙酯稀释，搅拌均匀；
（3）将固化剂用乙酸乙酯稀释后加入步骤（2）配置好的胶黏剂主剂中，搅拌10-20分钟后后加入步骤（1）制备的色料，继续搅拌20～30分钟，即得成品。