CN105176009A - 一种新型玻璃钢树脂 - Google Patents
一种新型玻璃钢树脂 Download PDFInfo
- Publication number
- CN105176009A CN105176009A CN201510485798.8A CN201510485798A CN105176009A CN 105176009 A CN105176009 A CN 105176009A CN 201510485798 A CN201510485798 A CN 201510485798A CN 105176009 A CN105176009 A CN 105176009A
- Authority
- CN
- China
- Prior art keywords
- reinforced plastic
- plastic resin
- novel glass
- glass fiber
- fiber reinforced
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新型玻璃钢树脂，所述一种新型玻璃钢树脂，按质量分数计，其组成为：聚酯树脂0.5-0.8份；丙酮0.002-0.005份；邻苯二甲酸二丁脂0.2-0.6份；过氧化甲乙酮0.01-0.06份；环烷酸钴0.01-0.03份；瓷粉0.02-0.1份；化石粉0.02-0.04份；钴0.3-0.6份；抗紫外线添加剂0.3-0.65份；氢氧化铝粉0.4-0.6份，本发明具有实现一种高质量、储存时间久、性能高的一种新型玻璃钢树脂。
Description
技术领域
本发明涉及一种新型玻璃钢树脂。
背景技术
钢玻璃具有玻璃的特性的同时也具有钢的特性，使玻璃钢的运用越来越广泛，涉及很多的领域其中玻璃钢格栅的运用率也是很高，玻璃钢是玻璃纤维和树脂等混合操作得来，目前市场上玻璃钢树脂产品也越来越多，对玻璃钢树脂进行质量的提升以及性能的优化是研发人员所面临的问题。
发明内容
本发明的目的是通过以下技术方案来实现一种高质量、储存时间久、性能高的一种新型玻璃钢树脂。
本发明的目的通过以下技术方案来实现：一种新型玻璃钢树脂，所述一种新型玻璃钢树脂，按质量分数计，其组成为：
聚酯树脂0.5-0.8份；
丙酮0.002-0.005份；
邻苯二甲酸二丁脂0.2-0.6份；
过氧化甲乙酮0.01-0.06份；
环烷酸钴0.01-0.03份；
瓷粉0.02-0.1份；
化石粉0.02-0.04份；
钴0.3-0.6份；
抗紫外线添加剂0.3-0.65份；
氢氧化铝粉0.4-0.6份；
本发明进一步改进在于：聚酯树脂为不饱和的。
本发明与现有技术相比具有以下优点：聚酯树脂为基本的反应物质，与丙酮、邻苯二甲酸二丁脂、过氧化甲乙酮、环烷酸钴、瓷粉、化石粉、钴、抗紫外线添加剂、氢氧化铝粉相互反应并且相对稳定；邻苯二甲酸二丁脂为其增塑剂，具有良好的柔软性主要是增加玻璃钢的韧性，并且具有良好的粘结性和防水性；过氧化甲乙酮凝固点零下20度，在130度温度中分解，使脂具有较强的耐水、耐油、耐酸碱腐蚀性和一定的耐热性；抗紫外线添加剂不仅具有抗紫外线的效果，还可以是玻璃钢具有抗老化的作用且效果稳定；氢氧化铝粉的抗酸作用较强而且效果持久，并且具有防火的作用且效果稳定。
具体实施方式：
为了加深对本发明的理解，下面将结合实例对本发明作进一步详述，该实施例仅用于解释本发明，并不构成对本发明保护范围的限定。
实验原料：聚酯树脂、丙酮、邻苯二甲酸二丁脂、过氧化甲乙酮、环烷酸钴、瓷粉、化石粉、钴、抗紫外线添加剂、氢氧化铝粉。
实验过程：配制时先将环烷酸钴放入聚酯树脂胶搅拌均匀后，接着依次放入邻苯二甲酸二丁脂、瓷粉、化石粉、钴、抗紫外线添加剂、氢氧化铝粉搅拌均匀后，加入丙酮以及放入过氧化甲乙酮搅拌均匀，配比比例视产品尺寸、温度、湿度等酌情掌握，一般温度高时过氧化甲乙酮含量低一些；产品尺寸大时过氧化甲乙酮含量低一些。
测试方法：将混合物树脂干固稳定后，分多个等量、质地相同的小样进行测验。
表一：
脱落层度测试：将混合物树脂涂抹在玻璃钢纤维上，等待树脂干固稳定后，抽取多个大小相同、质地相同的小样进行测验，将小样放入淡水中浸泡12h、放入含盐量5%的盐水中浸泡12h、高温烤箱中以及低温室内进行观察。
表二：
| 测验方式 | 实施咧1 | 实施咧2 | 实施咧3 | 实施咧4 | 实施咧5 | 实施咧6 |
| 盐水测试 | 表层微脱落 | 合格 | 合格 | 表层微脱落 | 优 | 表层微脱落 |
| 淡水测试 | 表层微脱落 | 合格 | 合格 | 合格 | 优 | 表层微脱落 |
| 耐温测试 | 表层有脱落 | 无脱落 | 无脱落 | 合格 | 优 | 表层有脱落 |
| 耐低温测试 | 表层有脱落 | 无脱落 | 合格 | 无脱落 | 优 | 表层有脱落 |
实验数据如下表示：
其中实施例5进行的盐水测试、淡水测试、耐温性测试以及耐低温性测试，结果是最为优异的。
储存时间测试：将配置好的树胶进行密封，置于15度的阴凉处分别放置8个月、10个月以及1年分别进行检测。
表三：
| 测试时间 | 实施例1 | 实施咧2 | 实施咧3 | 实施咧4 | 实施咧5 | 实施咧6 |
| 8个月 | 变质 | 表层变质 | 合格 | 变质 | 变质 | 合格 |
| 10个月 | 变质 | 变质 | 合格 | 部分变质 | 变质 | 合格 |
| 1年 | 变质 | 变质 | 合格 | 变质 | 变质 | 合格 |
实验数据如下：
实施例中，实施例3和实施例6是同样为合格的，其储存性是最好的。
黏度测试：抽取小样进行黏度检测，进行观记录。
表四：
| 黏度检测 | 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | 实施例6 |
| 状态 | 差 | 差 | 一般 | 优 | 合格 | 差 |
实验数据如下：
实施例中，实施例4的黏度检测最好，实施例3黏度测试为一般。
以上所述仅为说明本发明的实施方式，并不用于限制本发明，对于本领域的技术人员来说，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (2)
1.一种新型玻璃钢树脂，按质量分数计，其组成为：
聚酯树脂0.5-0.8份；
丙酮0.002-0.005份；
邻苯二甲酸二丁脂0.2-0.6份；
过氧化甲乙酮0.01-0.06份；
环烷酸钴0.01-0.03份；
瓷粉0.02-0.1份；
化石粉0.02-0.04份；
钴0.3-0.6份；
抗紫外线添加剂0.3-0.65份；
氢氧化铝粉0.4-0.6份。
2.根据权利要求1所述一种新型玻璃钢树脂，其特征在于：聚酯树脂为不饱和的。