CN105172473A - 一种环保的箱包滚轮 - Google Patents
一种环保的箱包滚轮 Download PDFInfo
- Publication number
- CN105172473A CN105172473A CN201510574514.2A CN201510574514A CN105172473A CN 105172473 A CN105172473 A CN 105172473A CN 201510574514 A CN201510574514 A CN 201510574514A CN 105172473 A CN105172473 A CN 105172473A
- Authority
- CN
- China
- Prior art keywords
- roller
- compound
- luggage
- environmental protection
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及箱包的生产加工领域,更具体地说涉及一种环保的箱包滚轮,其特征在于:所述的滚筒内部为混合物,所述的混合物外通过胶粘剂粘有合金层,所述的混合物包括下列重量份的组分:秸秆50-60份、木屑30-40份、废纸浆20-30份、PVC40-50份,本发明中采用回收的秸秆、木屑、废纸浆和PVC,节约了大量能源,这种混合物会有一定的弹性和聚合力,外粘一层合金层又增强了其耐腐蚀能力,本发明环保,且降低了成本。
Description
技术领域:
本发明涉及箱包的生产加工领域,更具体地说涉及一种环保的箱包滚轮。
背景技术:
人们外出旅游或出差时会经常携带各种箱包以盛放物品,拉杆箱包因其省力、方便等优点而受到人们的喜爱;更因其便捷、大容量以及结实耐用等特点成为人们出差旅行必不可少的装备。目前制作拉杆箱包滚轮所用的材质主要有:硬塑料、铝合金等。硬塑料滚轮强度差,时间长了容易老化变脆导致破裂,纯铝合金制造造价较为昂贵。
发明内容:
本发明所要解决的技术问题在于克服现有的技术缺陷提供一种环保的箱包滚轮。
本发明所要解决的技术问题采用以下的技术方案来实现:
一种环保的箱包滚轮,其特征在于:所述的滚筒内部为混合物,所述的混合物外通过胶粘剂粘有合金层,所述的混合物包括下列重量份的组分:秸秆50-60份、木屑30-40份、废纸浆20-30份、PVC40-50份。
进一步的,所述的胶粘剂为聚氯乙烯、聚苯乙烯、丙烯酸树脂、尼龙的一种或一种以上的混合物。
进一步的,所述的合金层厚度为一毫米。
一种环保的箱包滚轮的制作方式,其特征在于包括下列步骤:
(1)将秸秆和木屑通过粉碎机粉碎成粉状混合物;
(2)将废纸浆加热干燥,至水分含量低于1%,然后和步骤(1)得到的混合物混合;
(3)将PVC加热融化,加热温度为240℃,待呈液状时,边加热边搅拌,然后加入步骤(2)得到的混合物,均匀搅拌;
(4)将步骤(3)得到的液状混合物注入模具中冷却定型;
(5)将定型后的模具外涂刷胶粘剂,然后胶粘合金层。
本发明中采用回收的秸秆、木屑、废纸浆和PVC,节约了大量能源,这种混合物会有一定的弹性和聚合力,外粘一层合金层又增强了其耐腐蚀能力,本发明环保,且降低了成本。
具体实施方式:
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
实施例1:一种环保的箱包滚轮,其特征在于:所述的滚筒内部为混合物,所述的混合物外通过胶粘剂粘有合金层,所述的混合物包括下列重量份的组分:秸秆60份、木屑40份、废纸浆30份、PVC50份。
胶粘剂为聚氯乙烯。
实施例2:一种环保的箱包滚轮,其特征在于:所述的滚筒内部为混合物,所述的混合物外通过胶粘剂粘有合金层,所述的混合物包括下列重量份的组分:秸秆50份、木屑30份、废纸浆20份、PVC40份。
胶粘剂为聚苯乙烯和丙烯酸树脂的混合物。
合金层厚度为一毫米。
一种环保的箱包滚轮的制作方式,其特征在于包括下列步骤:
(1)将秸秆和木屑通过粉碎机粉碎成粉状混合物;
(2)将废纸浆加热干燥,至水分含量低于1%,然后和步骤(1)得到的混合物混合;
(3)将PVC加热融化,加热温度为240℃,待呈液状时,边加热边搅拌,然后加入步骤(2)得到的混合物,均匀搅拌;
(4)将步骤(3)得到的液状混合物注入模具中冷却定型;
(5)将定型后的模具外涂刷胶粘剂,然后胶粘合金层。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (4)
1.一种环保的箱包滚轮,其特征在于:所述的滚筒内部为混合物,所述的混合物外通过胶粘剂粘有合金层,所述的混合物包括下列重量份的组分:秸秆50-60份、木屑30-40份、废纸浆20-30份、PVC40-50份。
2.根据权利要求1所述的一种环保的箱包滚轮,其特征在于:所述的胶粘剂为聚氯乙烯、聚苯乙烯、丙烯酸树脂、尼龙的一种或一种以上的混合物。
3.根据权利要求1所述的一种环保的箱包滚轮,其特征在于:所述的合金层厚度为一毫米。
4.一种环保的箱包滚轮的制作方式,其特征在于包括下列步骤:
(1)将秸秆和木屑通过粉碎机粉碎成粉状混合物;
(2)将废纸浆加热干燥,至水分含量低于1%,然后和步骤(1)得到的混合物混合;
(3)将PVC加热融化,加热温度为240℃,待呈液状时,边加热边搅拌,然后加入步骤(2)得到的混合物,均匀搅拌;
(4)将步骤(3)得到的液状混合物注入模具中冷却定型;
(5)将定型后的模具外涂刷胶粘剂,然后胶粘合金层。