CN105171989B - 一种塑料制品加工用脱模剂 - Google Patents
一种塑料制品加工用脱模剂 Download PDFInfo
- Publication number
- CN105171989B CN105171989B CN201510599092.4A CN201510599092A CN105171989B CN 105171989 B CN105171989 B CN 105171989B CN 201510599092 A CN201510599092 A CN 201510599092A CN 105171989 B CN105171989 B CN 105171989B
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- maleic acid
- releasing agent
- ethanol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种塑料制品加工用脱模剂，涉及塑料制品加工技术领域，由如下重量份数的原料制成：马来酸改性松香树脂90‑100份、煅烧硅藻土20‑25份、白云石粉12‑16份、腻子粉12‑16份、菱镁矿粉10‑15份、牛脂10‑15份、棕榈油8‑12份、凡士林8‑12份、纳米二氧化钛6‑10份、环氧改性有机硅树脂5‑8份、柠檬酸三丁酯5‑8份、乙醇55‑65份、水250‑300份。本发明所制脱模剂气味和毒性小，涂覆于模具后能形成一层表面光滑均匀的薄膜，尺寸精确无误，并且具有较强的耐高温性、耐化学性和耐污染性，不会被成型原料溶解，不易附着灰尘，有益于提高产品质量。
Description
技术领域：
本发明涉及塑料制品加工技术领域，具体涉及一种塑料制品加工用脱模剂。
背景技术：
塑料制品是采用塑料为主要原料加工而成的生活用品、工业用品的统称。包括以塑料为原料的注塑、吸塑等所有工艺的制品。塑料制品生产一般包括塑料的配料、成型、机械加工、接合、修饰和装配等。后四个工序是在塑料已成型为制品或半制品后进行的，又称为塑料二次加工。其中，成型是塑料加工的关键环节，是将各种形态的塑料(粉、粒料、溶液或分散体)制成所需形状的制品或坯件。
在成型环节中，模具起着至关重要的作用，其表面状态和尺寸精度直接影响产品质量。由于模具一般以合金材料制成，在塑料制品成型过程中，加热后的原料混合物易粘附于模具表面形成一层粘膜，称为型模污垢。如不对型模污垢进行清理，将会增加废品率；如进行清理，将会降低生产效率和增加人工投入。
发明内容：
本发明所要解决的技术问题在于提供一种耐高温、耐化学性强且脱模效果好的塑料制品加工用脱模剂。
本发明所要解决的技术问题采用以下的技术方案来实现：
一种塑料制品加工用脱模剂，由如下重量份数的原料制成：
马来酸改性松香树脂90-100份、煅烧硅藻土20-25份、白云石粉12-16份、腻子粉12-16份、菱镁矿粉10-15份、牛脂10-15份、棕榈油8-12份、凡士林8-12份、纳米二氧化钛6-10份、环氧改性有机硅树脂5-8份、柠檬酸三丁酯5-8份、乙醇55-65份、水250-300份；
其制备方法如下：
(1)先将牛脂、棕榈油和凡士林加入水中，分散均匀后加热至70-80℃保温搅拌10-15min，然后加入白云石粉、腻子粉和菱镁矿粉，混合均匀，即得物料I；
(2)将煅烧硅藻土和纳米二氧化钛分散于乙醇中，静置15-20min后加入环氧改性有机硅树脂和柠檬酸三丁酯，混合均匀，即得物料II；
(3)向物料I加入马来酸改性松香树脂，混合均匀后于微波频率2450MHz、功率600-800W下微波处理10-15min，随后冷却降温至30-40℃后加入物料II，混合物加入球磨机中球磨至细度小于0.1mm即可。
所述马来酸改性松香树脂使用前需要经过纳米硼酸铝处理，具体步骤为：先将35-40份马来酸改性松香树脂溶解于50-60松节油中，再加入3-6份纳米硼酸铝，分散均匀后在超声频率22kHz、温度45-50℃下超声处理25-30min即可。马来酸改性松香树脂经过处理后不仅提高了成膜性能，而且缩短了漆膜的固化时间。
所述煅烧硅藻土使用前需要经过羧甲基壳聚糖和氧化铝纤维处理，具体步骤为：先将40-50份煅烧硅藻土和5-8份羧甲基壳聚糖分散于乙醇中，然后在超声频率22kHz、温度55-60℃下超声处理25-30min，超声结束后将溶液浓缩至乙醇含量10-15％，再加入2-3份氧化铝纤维，研磨15-20min，最后经烘干、粉碎成粉末即可。煅烧硅藻土作为填料，其改性处理有利于提高漆膜的附着力和硬度。
本发明的有益效果是：本发明所制脱模剂气味和毒性小，涂覆于模具后能形成一层表面光滑均匀的薄膜，尺寸精确无误，并且具有较强的耐高温性、耐化学性和耐污染性，不会被成型原料溶解，不易附着灰尘，有益于提高产品质量。
具体实施方式：
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
实施例1
(1)先将10份牛脂、8份棕榈油和8份凡士林加入250份水中，分散均匀后加热至70-75℃保温搅拌10min，然后加入12份白云石粉、12份腻子粉和10份菱镁矿粉，混合均匀，即得物料I；
(2)将20份煅烧硅藻土和6份纳米二氧化钛分散于55份乙醇中，静置15min后加入8份环氧改性有机硅树脂和5份柠檬酸三丁酯，混合均匀，即得物料II；
(3)向物料I加入90份马来酸改性松香树脂，混合均匀后于微波频率2450MHz、功率600W下微波处理10min，随后冷却降温至30-35℃后加入物料II，混合物加入球磨机中球磨至细度小于0.1mm即可。
马来酸改性松香树脂的预处理：先将35份马来酸改性松香树脂溶解于60松节油中，再加入5份纳米硼酸铝，分散均匀后在超声频率22kHz、温度45-50℃下超声处理30min即可。
煅烧硅藻土的预处理：先将50份煅烧硅藻土和8份羧甲基壳聚糖分散于乙醇中，然后在超声频率22kHz、温度55-60℃下超声处理30min，超声结束后将溶液浓缩至乙醇含量10-15％，再加入3份氧化铝纤维，研磨15min，最后经烘干、粉碎成粉末即可。
实施例2
(1)先将12份牛脂、10份棕榈油和10份凡士林加入300份水中，分散均匀后加热至70-75℃保温搅拌15min，然后加入14份白云石粉、13份腻子粉和12份菱镁矿粉，混合均匀，即得物料I；
(2)将25份煅烧硅藻土和8份纳米二氧化钛分散于60份乙醇中，静置20min后加入7份环氧改性有机硅树脂和6份柠檬酸三丁酯，混合均匀，即得物料II；
(3)向物料I加入95份马来酸改性松香树脂，混合均匀后于微波频率2450MHz、功率800W下微波处理15min，随后冷却降温至35-40℃后加入物料II，混合物加入球磨机中球磨至细度小于0.1mm即可。
本实施例中马来酸改性松香树脂和煅烧硅藻土的预处理方法同实施例1。
实施例3
(1)先将15份牛脂、12份棕榈油和8份凡士林加入300份水中，分散均匀后加热至75-80℃保温搅拌15min，然后加入16份白云石粉、12份腻子粉和12份菱镁矿粉，混合均匀，即得物料I；
(2)将25份煅烧硅藻土和8份纳米二氧化钛分散于65份乙醇中，静置20min后加入8份环氧改性有机硅树脂和5份柠檬酸三丁酯，混合均匀，即得物料II；
(3)向物料I加入100份马来酸改性松香树脂，混合均匀后于微波频率2450MHz、功率800W下微波处理15min，随后冷却降温至35-40℃后加入物料II，混合物加入球磨机中球磨至细度小于0.1mm即可。
本实施例中马来酸改性松香树脂和煅烧硅藻土的预处理方法同实施例1。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (2)
1.一种塑料制品加工用脱模剂，其特征在于，由如下重量份数的原料制成：
马来酸改性松香树脂90-100份、煅烧硅藻土20-25份、白云石粉12-16份、腻子粉12-16份、菱镁矿粉10-15份、牛脂10-15份、棕榈油8-12份、凡士林8-12份、纳米二氧化钛6-10份、环氧改性有机硅树脂5-8份、柠檬酸三丁酯5-8份、乙醇55-65份、水250-300份；
其制备方法如下：
(1)先将牛脂、棕榈油和凡士林加入水中，分散均匀后加热至70-80℃保温搅拌10-15min，然后加入白云石粉、腻子粉和菱镁矿粉，混合均匀，即得物料I；
(2)将煅烧硅藻土和纳米二氧化钛分散于乙醇中，静置15-20min后加入环氧改性有机硅树脂和柠檬酸三丁酯，混合均匀，即得物料II；
(3)向物料I加入马来酸改性松香树脂，混合均匀后于微波频率2450MHz、功率600-800W下微波处理10-15min，随后冷却降温至30-40℃后加入物料II，混合物加入球磨机中球磨至细度小于0.1mm即可；
所述马来酸改性松香树脂使用前需要经过纳米硼酸铝处理，具体步骤为：先将35-40份马来酸改性松香树脂溶解于50-60份松节油中，再加入3-6份纳米硼酸铝，分散均匀后在超声频率22kHz、温度45-50℃下超声处理25-30min即可。
2.根据权利要求1所述的塑料制品加工用脱模剂，其特征在于：所述煅烧硅藻土使用前需要经过羧甲基壳聚糖和氧化铝纤维处理，具体步骤为：先将40-50份煅烧硅藻土和5-8份羧甲基壳聚糖分散于乙醇中，然后在超声频率22kHz、温度55-60℃下超声处理25-30min，超声结束后将溶液浓缩至乙醇含量10-15％，再加入2-3份氧化铝纤维，研磨15-20min，最后经烘干、粉碎成粉末即可。