CN105165892A - 一种适用于卫生用纸的抗菌组合物的制备工艺 - Google Patents
一种适用于卫生用纸的抗菌组合物的制备工艺 Download PDFInfo
- Publication number
- CN105165892A CN105165892A CN201510576635.0A CN201510576635A CN105165892A CN 105165892 A CN105165892 A CN 105165892A CN 201510576635 A CN201510576635 A CN 201510576635A CN 105165892 A CN105165892 A CN 105165892A
- Authority
- CN
- China
- Prior art keywords
- chitosan derivatives
- titanium oxide
- applicable
- bactericidal composition
- nano titanium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种适用于卫生用纸的抗菌组合物的制备工艺，针对现有纸品内单一抗菌剂存在的缺陷，由壳聚糖衍生物、纳米二氧化钛、在戊二醛的固化作用交联而成抗菌组合物，本发明的抗菌组合物，不仅克服了单独使用壳聚糖衍生物时对纸品柔韧度的影响，而且还克服了单独使用纳米二氧化钛进行抗菌时钛对光的敏感程度而造成的抗菌效果变差。本发明所得到的抗菌衍生不仅具有较好的稳定性、且使用时抗菌的效果在壳聚糖和二氧化钛的共同作用下大大增强，同时还具有良好的缓释性能。
Description
技术领域
本发明涉及一种纸品添加剂，尤其是涉及一种适用于卫生用纸的抗菌组合物的制备工艺。
背景技术
随着人们生活品质的提高，对生活用纸的品质和功能性有了越来越高的要求，由于目前生活用纸对杀菌要求同样很高，采用在纸张表面直接涂布杀菌剂以提高纸张的抗菌性能这种方法带来的弊端就是降低了纸张的柔软度和舒适度。使用该类纸张擦拭皮肤时，往往会由于摩擦力过大而引起皮肤疼痛、擦红或者其他的不适宜症状，一种既能保证杀菌效果又不影响柔软度且抗菌更为广谱、稳定性好的新型抗菌组合物的研究值得探讨。
发明内容
发明目的：为了解决现有技术中所存在的的问题，本发明提出了一种。
技术方案：为达以上目的，本发明采取以下技术方案：一种适用于卫生用纸的抗菌组合物的制备工艺，包括以下步骤：
（1）原料组成：原料包括壳聚糖衍生物、纳米二氧化钛、戊二醛、添加了二烷基苯磺酸钠和硬脂酸钠的混合油；按照以下配比准备：壳聚糖衍生物与纳米二氧化钛的质量百分比为：壳聚糖衍生物60～80％，纳米二氧化钛20～40％；戊二醛与壳聚糖衍生物的摩尔比为2:1～3:1；，混合油的添加量为壳聚糖衍生物与纳米二氧化钛总量的12%～25%；
（2）壳聚糖衍生物的制备：将壳聚糖衍生物中各组分按以下配比混合置于反应容器中：壳聚糖与异丙醇、NaOH、氯乙酸的质量比为1∶3:2:5，反应温度为25～70℃，反应时间为4～8h；
（3）将上述制备完成的壳聚糖衍生物与纳米二氧化钛混合后超生分散1.5-2.5h后得水相混合物；
（4）在上述水相混合物中加入混合油；得到水油混合物；
（5）配制质量浓度为25%的戊二醛水溶液，在上述水油混合物加入戊二醛水溶液后搅拌反应5-9h；即可制得所需抗菌组合物。
更为优选的，所述纳米二氧化钛的晶型为锐钛矿型，其粒子直径为9-15nm。
更进一步的，所述壳聚糖衍生物与二氧化钛的反应质量比控制在1:0.02～1:0.04。
更进一步的，所述混合油由体积比为4:1的矿物油和石蜡油组成。
更进一步的，所述混合油中二烷基苯磺酸钠和硬脂酸钠的添加量分别为5g/L和3g/L。
更进一步的，所述水相混合物与油相混合物的体积比为1:3-1:15。
更进一步的，所述步骤（3）中水油混合物应室温静置30-45min待用。
有益效果：本发明提供的一种适用于卫生用纸的抗菌组合物的制备工艺，针对现有纸品内单一抗菌剂存在的缺陷，由壳聚糖衍生物、纳米二氧化钛、在戊二醛的固化作用交联而成抗菌组合物，本发明的抗菌组合物，不仅克服了单独使用壳聚糖衍生物时对纸品柔韧度的影响，而且还克服了单独使用纳米二氧化钛进行抗菌时钛对光的敏感程度而造成的抗菌效果变差。本发明所得到的抗菌衍生不仅具有较好的稳定性、且使用时抗菌的效果在壳聚糖和二氧化钛的共同作用下大大增强，同时还具有良好的缓释性能。
具体实施方式
实施例1：
一种适用于卫生用纸的抗菌组合物的制备工艺，包括以下步骤：
（1）原料组成：原料包括壳聚糖衍生物、纳米二氧化钛、戊二醛、添加了二烷基苯磺酸钠和硬脂酸钠的混合油；按照以下配比准备：壳聚糖衍生物与纳米二氧化钛的质量百分比为：壳聚糖衍生物60％，纳米二氧化钛20％；戊二醛与壳聚糖衍生物的摩尔比为2:1；混合油的添加量为壳聚糖衍生物与纳米二氧化钛总量的12%；
（2）壳聚糖衍生物的制备：将壳聚糖衍生物中各组分按以下配比混合置于反应容器中：壳聚糖与异丙醇、NaOH、氯乙酸的质量比为1∶3:2:5，反应温度为25℃，反应时间为4h；
（3）将上述制备完成的壳聚糖衍生物与纳米二氧化钛混合后超生分散1.5h后得水相混合物；
（4）在上述水相混合物中加入混合油；得到水油混合物；
（5）配制质量浓度为25%的戊二醛水溶液，在上述水油混合物加入戊二醛水溶液后搅拌反应5h；即可制得所需抗菌组合物。
其中，所述纳米二氧化钛的晶型为锐钛矿型，其粒子直径为9nm；所述壳聚糖衍生物与二氧化钛的反应质量比控制在1:0.02；所述混合油由体积比为4:1的矿物油和石蜡油组成；所述混合油中二烷基苯磺酸钠和硬脂酸钠的添加量分别为5g/L和3g/L；所述水相混合物与油相混合物的体积比为1:3；所述步骤（3）中水油混合物应室温静置30min待用。
实施例2：
一种适用于卫生用纸的抗菌组合物的制备工艺，包括以下步骤：
（1）原料组成：原料包括壳聚糖衍生物、纳米二氧化钛、戊二醛、添加了二烷基苯磺酸钠和硬脂酸钠的混合油；按照以下配比准备：壳聚糖衍生物与纳米二氧化钛的质量百分比为：壳聚糖衍生物80％，纳米二氧化钛40％；戊二醛与壳聚糖衍生物的摩尔比为3:1；混合油的添加量为壳聚糖衍生物与纳米二氧化钛总量的25%；
（2）壳聚糖衍生物的制备：将壳聚糖衍生物中各组分按以下配比混合置于反应容器中：壳聚糖与异丙醇、NaOH、氯乙酸的质量比为1∶3:2:5，反应温度为25℃，反应时间为8h；
（3）将上述制备完成的壳聚糖衍生物与纳米二氧化钛混合后超生分散2.5h后得水相混合物；
（4）在上述水相混合物中加入混合油；得到水油混合物；
（5）配制质量浓度为25%的戊二醛水溶液，在上述水油混合物加入戊二醛水溶液后搅拌反应9h；即可制得所需抗菌组合物。
其中，所述纳米二氧化钛的晶型为锐钛矿型，其粒子直径为15nm；所述壳聚糖衍生物与二氧化钛的反应质量比控制在1:0.04；所述混合油由体积比为4:1的矿物油和石蜡油组成；所述混合油中二烷基苯磺酸钠和硬脂酸钠的添加量分别为5g/L和3g/L；所述水相混合物与油相混合物的体积比为1:3；所述步骤（3）中水油混合物应室温静置45min待用。
实施例3：
一种适用于卫生用纸的抗菌组合物的制备工艺，包括以下步骤：
（1）原料组成：原料包括壳聚糖衍生物、纳米二氧化钛、戊二醛、添加了二烷基苯磺酸钠和硬脂酸钠的混合油；按照以下配比准备：壳聚糖衍生物与纳米二氧化钛的质量百分比为：壳聚糖衍生物70％，纳米二氧化钛30％；戊二醛与壳聚糖衍生物的摩尔比为2.5:1；混合油的添加量为壳聚糖衍生物与纳米二氧化钛总量的20%；
（2）壳聚糖衍生物的制备：将壳聚糖衍生物中各组分按以下配比混合置于反应容器中：壳聚糖与异丙醇、NaOH、氯乙酸的质量比为1∶3:2:5，反应温度为25℃，反应时间为6h；
（3）将上述制备完成的壳聚糖衍生物与纳米二氧化钛混合后超生分散2h后得水相混合物；
（4）在上述水相混合物中加入混合油；得到水油混合物；
（5）配制质量浓度为25%的戊二醛水溶液，在上述水油混合物加入戊二醛水溶液后搅拌反应7h；即可制得所需抗菌组合物。
其中，所述纳米二氧化钛的晶型为锐钛矿型，其粒子直径为9nm；所述壳聚糖衍生物与二氧化钛的反应质量比控制在1:0.02；所述混合油由体积比为4:1的矿物油和石蜡油组成；所述混合油中二烷基苯磺酸钠和硬脂酸钠的添加量分别为5g/L和3g/L；所述水相混合物与油相混合物的体积比为1:3；所述步骤（3）中水油混合物应室温静置30min待用。
使用上述实施例1-3的一种适用于卫生用纸的抗菌组合物的制备方法，针对现有纸品内单一抗菌剂存在的缺陷，由壳聚糖衍生物、纳米二氧化钛、在戊二醛的固化作用交联而成抗菌组合物，本发明的抗菌组合物，不仅克服了单独使用壳聚糖衍生物时对纸品柔韧度的影响，而且还克服了单独使用纳米二氧化钛进行抗菌时钛对光的敏感程度而造成的抗菌效果变差。本发明所得到的抗菌衍生不仅具有较好的稳定性、且使用时抗菌的效果在壳聚糖和二氧化钛的共同作用下大大增强，同时还具有良好的缓释性能。
应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以作出若干改进，这些改进也应视为本发明的保护范围。
Claims (7)
1.一种适用于卫生用纸的抗菌组合物的制备工艺，其特征在于包括以下步骤：
（1）原料组成：原料包括壳聚糖衍生物、纳米二氧化钛、戊二醛、添加了二烷基苯磺酸钠和硬脂酸钠的混合油；按照以下配比准备：壳聚糖衍生物与纳米二氧化钛的质量百分比为：壳聚糖衍生物60～80％，纳米二氧化钛20～40％；戊二醛与壳聚糖衍生物的摩尔比为2:1～3:1；，混合油的添加量为壳聚糖衍生物与纳米二氧化钛总量的12%～25%；
（2）壳聚糖衍生物的制备：将壳聚糖衍生物中各组分按以下配比混合置于反应容器中：壳聚糖与异丙醇、NaOH、氯乙酸的质量比为1∶3:2:5，反应温度为25～70℃，反应时间为4～8h；
（3）将上述制备完成的壳聚糖衍生物与纳米二氧化钛混合后超生分散1.5-2.5h后得水相混合物；
（4）在上述水相混合物中加入混合油；得到水油混合物；
（5）配制质量浓度为25%的戊二醛水溶液，在上述水油混合物加入戊二醛水溶液后搅拌反应5-9h；即可制得所需抗菌组合物。
2.根据权利要求1所述的适用于卫生用纸的抗菌组合物的制备工艺，其特征在于：所述纳米二氧化钛的晶型为锐钛矿型，其粒子直径为9-15nm。
3.根据权利要求1所述的适用于卫生用纸的抗菌组合物的制备工艺，其特征在于：所述壳聚糖衍生物与二氧化钛的反应质量比控制在1:0.02～1:0.04。
4.根据权利要求1所述的适用于卫生用纸的抗菌组合物的制备工艺，其特征在于：所述混合油由体积比为4:1的矿物油和石蜡油组成。
5.根据权利要求1所述的适用于卫生用纸的抗菌组合物的制备工艺，其特征在于：所述混合油中二烷基苯磺酸钠和硬脂酸钠的添加量分别为5g/L和3g/L。
6.根据权利要求8所述的适用于卫生用纸的抗菌组合物的制备工艺：其特征在于：所述水相混合物与油相混合物的体积比为1:3-1:15。
7.根据权利要求8所述的适用于卫生用纸的抗菌组合物的制备工艺：其特征在于：所述步骤（3）中水油混合物应室温静置30-45min待用。