CN105153896A - Home security window prime paint and preparation method thereof - Google Patents
Home security window prime paint and preparation method thereof Download PDFInfo
- Publication number
- CN105153896A CN105153896A CN201510590647.9A CN201510590647A CN105153896A CN 105153896 A CN105153896 A CN 105153896A CN 201510590647 A CN201510590647 A CN 201510590647A CN 105153896 A CN105153896 A CN 105153896A
- Authority
- CN
- China
- Prior art keywords
- parts
- preparation
- home security
- hours
- security window
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a home security window prime paint and a preparation method thereof, relating to the technical field of home decoration material production. The invention is characterized in that the home security window prime paint is prepared from the following materials in parts by weight: 17 parts of polyester acrylate, 3 parts of antimony trioxide, 6 parts of sodium pentaborate, 4 parts of phthalate, 10 parts of epoxy acrylate, 3 parts of nonyl phenol, 5 parts of nano attapulgite, 2 parts of iron oxide red powder, 5 parts of high-density polyethylene resin and 3 parts of glycerate. The prime paint has the advantages of reasonable method, reasonable proportioning and favorable connectivity, and is convenient to operate.
Description
Technical field:
The present invention relates to house decoration material produce technical field, be specifically related to a kind of home security window priming paint and preparation method thereof.
Background technology:
Common burglary-resisting window kind is divided by material: have stainless steel burglary-resisting window, color steel burglary-resisting window, iron skill burglary-resisting window, aluminum alloy anti-theft window, zinc steel burglary-resisting window, steel plastic compount burglary-resisting window etc.; Divide by using function and have fixed anti-theft window and mobilizable Multifunction sliding antitheft window.According to national Eleventh Five-Year Development Plan planning outline, set up the fundamental policy of energy-saving and environmental protection, conservation-minded society, wherein building energy conservation is listed in the most important thing of constructing economical society.And building doors and windows accounts for about 50% of whole building energy conservation, visible door and window is the key point of building energy conservation.Under the prerequisite that this product is vigorously advocated in country just, summarize that ordinary window is not incubated, not heat insulation, non-anti-theft, ventilation is little, the dizzy danger of high building, clean the windows dangerous, to install anti-theft net additional disorderly and unsystematic, facilitate robber, have impact on the shortcomings such as neighborhood.Anti-theft louver not only solves these problems, and functionally to do again further perfect, and have passed national construction engineering quality and detect, and meets the requirement of national building energy conservation completely.
In life now, burglary-resisting window not only wants excellent property, and its outward appearance is all very important with being convenient to degree of cleaning, has the many burglary-resisting window time for a long time easily to fall paint, or wiping after touching and just have very serious scratch, is also unacceptable so for consumers.
Summary of the invention:
Technical problem to be solved by this invention be to overcome existing technological deficiency provide a kind of method rationally, reasonable ratio, a kind of home security window priming paint that easy to operate, connectivity is good and preparation method thereof.
Technical problem to be solved by this invention adopts following technical scheme to realize:
A kind of home security window priming paint and preparation method thereof, is characterized in that: be made up of the material of following weight part,
Polyester acrylate 17 parts, antimonous oxide 3 parts, sodium pentaborate 6 parts, phthalic ester 4 parts, epoxy acrylate 10 parts, nonylphenol 3 parts, nano-attapulgite 5 parts, ferric oxide red powder 2 parts, high-density polyethylene resin 5 parts, glycerate 3 parts;
Its preparation method comprises,
Polyester acrylate, antimonous oxide, sodium pentaborate, phthalic ester, nonylphenol are put into stainless steel cauldron and are warming up to 240 DEG C by I, start stirring reaction, a coreaction 4 hours;
Oxypropylene acid esters, nano-attapulgite, ferric oxide red powder, high-density polyethylene resin are put into stainless steel cauldron by II, are warming up to 200 DEG C, start stirring reaction, a coreaction 3 hours;
III starts working II after 1 hour in I work, after then completing at the same time, the material in I and II is put into a new reactor, with the intensification stirring reaction 4 hours of 45 DEG C/h, reacts and adds glycerate after one hour;
IV after III step completes, and is taken out by material, and shakes mixing 20 minutes, then extruded by twin screw extruder, temperature controls at 100 DEG C, has then extruded rear material left 10 minutes, then put into pulverizer lapping powder and be broken into 190-225 object powder, packaging warehouse-in.
Beneficial effect of the present invention is: coating has a variety of; there is suspension liquid state; there are liquid also have particle or pulverulence; the processing of particle or pulverulence is more convenient and result of use is more good; and different materials is processed by various steps such as reaction, concussion, mixing; make the performance of product more excellent, and the service efficiency of material also can improve, and so just makes product more outstanding.The inventive method rationally, reasonable ratio, easy to operate, connectivity good.
Embodiment:
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, setting forth the present invention further below.
A kind of home security window priming paint and preparation method thereof, is characterized in that: be made up of the material of following weight part,
Polyester acrylate 17 parts, antimonous oxide 3 parts, sodium pentaborate 6 parts, phthalic ester 4 parts, epoxy acrylate 10 parts, nonylphenol 3 parts, nano-attapulgite 5 parts, ferric oxide red powder 2 parts, high-density polyethylene resin 5 parts, glycerate 3 parts;
Its preparation method comprises,
Polyester acrylate, antimonous oxide, sodium pentaborate, phthalic ester, nonylphenol are put into stainless steel cauldron and are warming up to 240 DEG C by I, start stirring reaction, a coreaction 4 hours;
Oxypropylene acid esters, nano-attapulgite, ferric oxide red powder, high-density polyethylene resin are put into stainless steel cauldron by II, are warming up to 200 DEG C, start stirring reaction, a coreaction 3 hours;
III starts working II after 1 hour in I work, after then completing at the same time, the material in I and II is put into a new reactor, with the intensification stirring reaction 4 hours of 45 DEG C/h, reacts and adds glycerate after one hour;
IV after III step completes, and is taken out by material, and shakes mixing 20 minutes, then extruded by twin screw extruder, temperature controls at 100 DEG C, has then extruded rear material left 10 minutes, then put into pulverizer lapping powder and be broken into 190-225 object powder, packaging warehouse-in.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (1)
1. home security window priming paint and preparation method thereof, is characterized in that: be made up of the material of following weight part,
Polyester acrylate 17 parts, antimonous oxide 3 parts, sodium pentaborate 6 parts, phthalic ester 4 parts, epoxy acrylate 10 parts, nonylphenol 3 parts, nano-attapulgite 5 parts, ferric oxide red powder 2 parts, high-density polyethylene resin 5 parts, glycerate 3 parts;
Its preparation method comprises,
Polyester acrylate, antimonous oxide, sodium pentaborate, phthalic ester, nonylphenol are put into stainless steel cauldron and are warming up to 240 DEG C by I, start stirring reaction, a coreaction 4 hours;
Oxypropylene acid esters, nano-attapulgite, ferric oxide red powder, high-density polyethylene resin are put into stainless steel cauldron by II, are warming up to 200 DEG C, start stirring reaction, a coreaction 3 hours;
III starts working II after 1 hour in I work, after then completing at the same time, the material in I and II is put into a new reactor, with the intensification stirring reaction 4 hours of 45 DEG C/h, reacts and adds glycerate after one hour;
IV after III step completes, and is taken out by material, and shakes mixing 20 minutes, then extruded by twin screw extruder, temperature controls at 100 DEG C, has then extruded rear material left 10 minutes, then put into pulverizer lapping powder and be broken into 190-225 object powder, packaging warehouse-in.