CN105602320A - Bottom protective paint for needle valve manufacture - Google Patents
Bottom protective paint for needle valve manufacture Download PDFInfo
- Publication number
- CN105602320A CN105602320A CN201610099286.2A CN201610099286A CN105602320A CN 105602320 A CN105602320 A CN 105602320A CN 201610099286 A CN201610099286 A CN 201610099286A CN 105602320 A CN105602320 A CN 105602320A
- Authority
- CN
- China
- Prior art keywords
- parts
- needle valve
- minutes
- protective paint
- bottom protective
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses bottom protective paint for needle valve manufacture and relates to the technical field of valve processing and production. The bottom protective paint is characterized by being prepared from, by weight, 7 parts of epoxy resin, 5 parts of titanium dioxide, 7 parts of organic silicon resin, 1 part of hexamethyl phosphoric triamide, 1 part of alkenyl succinate, 1.5 parts of resorcinol, 0.5 part of disodium edetate, 2 parts of corn starch, 0.5 part of stearic acid, 0.5 part of sodium acetate, 3 parts of tertiary butyl paradiphenol, 1 part of sebacic dihydrazide, 1 part of 8-hydroxyquinoline, 2 parts of defoaming agent and 3.5 parts of adhesive. According to the bottom protective paint, the method is reasonable, operation is convenient, and the ratio is reasonable.
Description
Technical field:
The present invention relates to valve processing technical field, be specifically related to the bottom guarantor that a kind of needle valve is manufacturedProtect coating.
Background technology:
Valve (valve) is the control assembly in fluid delivery system, have cut-off, adjusting, water conservancy diversion,Prevent the functions such as adverse current, voltage stabilizing, shunting or overflow pressure relief.
For the valve of fluid control systems, from the simplest stop valve to very complicated robot control system(RCS)Various valves used, its kind and specification are quite various. Valve can be used for controlling air, water, steam,The stream of all kinds fluids such as various Korrosionsmediums, mud, oil product, liquid metal and radiating mediumMoving. Valve is also divided into cast iron valve according to material, cast steel valve, stainless valve (201,304,316Deng), chrome-molybdenum steel valve, Chrominm-molybdenum-vanadium steel valve, dual phase steel valve, Plastic valve, the nonstandard customized valve that waitsMaterial.
And because valve easily suffers destruction and the corrosion of extraneous factor, some coating in the process usingQuality be not very good, cause the valve even fracture that gets rusty easily, like this to bringing greatlyTrouble.
Summary of the invention:
Technical problem to be solved by this invention is to overcome existing technological deficiency provides a kind of method to closeThe protective underlayer coating that reason, a kind of needle valve easy to operate, reasonable mixture ratio are manufactured.
Technical problem to be solved by this invention adopts following technical scheme to realize:
The protective underlayer coating that needle valve is manufactured, is characterized in that: by the material system of following weight portionBecome,
7 parts of epoxy resin, 5 parts of titanium dioxides, 7 parts of organic siliconresins, 1 part of HMPA, thiazolinyl1 part of succinate, 1.5 parts of resorcinols, 0.5 part of disodium ethylene diamine tetraacetate, 2 parts of cornstarch, hard0.5 part of resin acid, 0.5 part of sodium acetate, the tert-butyl group are to 3 parts of biphenol, 1 part of sebacic dihydrazide, 8-hydroxyl1 part, quinoline, 2 parts of defoamers, 3.5 parts, reason mixture;
Comprise following preparation process,
I is put into successively disintegrating apparatus by above-mentioned material and is pulverized, stirs, mixes according to conventional method,Put into a kind of material every 1 minute, after all discharging, continue to mix 20 minutes;
II is taken out mixed material and put into heater and is heated to 240-280 DEG C, heating 30-39Minute;
III is put into calcining furnace by the material after heating and is calcined 3.5 hours according to conventional method;
Reactor put into by the material after calcining by IV, little with 4 of the intensification stirring reactions of 100 DEG C/hTime, react and within latter 30 minutes, added reasonable mixture;
V is taken out material, and shakes mixing 20 minutes, then extrudes temperature by double screw extruderDegree is controlled at 125 DEG C, has then extruded rear material and has left standstill 10 minutes, then puts into pulverizer and grindsBe ground into 190-225 object powder, packaging warehouse-in;
Described reason mixture is made up of the material of following weight portion,
2 parts of the roots of fangji, 3 parts of the barks of eucommia, 4 parts of the shell of areca nuts, 7 parts of the roots of bidentate achyranthes, 9 parts of lophatherum graciles, 2 parts of the stem piths of the rice-paper plant, the bighead atractylodes rhizome 3Part, 4 parts of phoenix-tail ferns, 8 parts of cordate houttuynias, 1 part, gypsum, 3 parts of brush-cherry seeds, 1 part of croton, 3 parts of corn stigmas,3 parts of cortex acanthopanacis, 2 parts of radix cynanchi atratis;
Preparation method: after above-mentioned material is cleaned totally with clear water, dry in the place that is placed on ventilation,Then putting into disintegrating apparatus is ground into Powdered, for subsequent use according to conventional method.
Beneficial effect of the present invention is: a series of material of interpolation can make coating play protection productEffect, can increase the life-span, make material more wear-resisting, corrosion-resistant, and add Chinese medicine can in and materialToxin in material, make staff ensure when in use its health, and the cost of material is not high.The inventive method is reasonable, easy to operate, reasonable mixture ratio.
Detailed description of the invention:
For technological means, creation characteristic that the present invention is realized, reach object and effect is easy to understandSeparate, below further set forth the present invention.
The protective underlayer coating that needle valve is manufactured, is characterized in that: by the material system of following weight portionBecome,
7 parts of epoxy resin, 5 parts of titanium dioxides, 7 parts of organic siliconresins, 1 part of HMPA, thiazolinyl1 part of succinate, 1.5 parts of resorcinols, 0.5 part of disodium ethylene diamine tetraacetate, 2 parts of cornstarch, hard0.5 part of resin acid, 0.5 part of sodium acetate, the tert-butyl group are to 3 parts of biphenol, 1 part of sebacic dihydrazide, 8-hydroxyl1 part, quinoline, 2 parts of defoamers, 3.5 parts, reason mixture;
Comprise following preparation process,
I is put into successively disintegrating apparatus by above-mentioned material and is pulverized, stirs, mixes according to conventional method,Put into a kind of material every 1 minute, after all discharging, continue to mix 20 minutes;
II is taken out mixed material and put into heater and is heated to 240-280 DEG C, heating 30-39Minute;
III is put into calcining furnace by the material after heating and is calcined 3.5 hours according to conventional method;
Reactor put into by the material after calcining by IV, little with 4 of the intensification stirring reactions of 100 DEG C/hTime, react and within latter 30 minutes, added reasonable mixture;
V is taken out material, and shakes mixing 20 minutes, then extrudes temperature by double screw extruderDegree is controlled at 125 DEG C, has then extruded rear material and has left standstill 10 minutes, then puts into pulverizer and grindsBe ground into 190-225 object powder, packaging warehouse-in;
Described reason mixture is made up of the material of following weight portion,
2 parts of the roots of fangji, 3 parts of the barks of eucommia, 4 parts of the shell of areca nuts, 7 parts of the roots of bidentate achyranthes, 9 parts of lophatherum graciles, 2 parts of the stem piths of the rice-paper plant, the bighead atractylodes rhizome 3Part, 4 parts of phoenix-tail ferns, 8 parts of cordate houttuynias, 1 part, gypsum, 3 parts of brush-cherry seeds, 1 part of croton, 3 parts of corn stigmas,3 parts of cortex acanthopanacis, 2 parts of radix cynanchi atratis;
Preparation method: after above-mentioned material is cleaned totally with clear water, dry in the place that is placed on ventilation,Then putting into disintegrating apparatus is ground into Powdered, for subsequent use according to conventional method.
More than show and described general principle of the present invention and principal character and advantage of the present invention. One's own professionThe technical staff of industry should understand, and the present invention is not restricted to the described embodiments, above-described embodiment and explanationThat in book, describes just illustrates principle of the present invention, without departing from the spirit and scope of the present invention,The present invention also has various changes and modifications, and these changes and improvements all fall into claimed model of the present inventionIn enclosing. The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (3)
1. the protective underlayer coating that needle valve is manufactured, is characterized in that: by the material of following weight portionMake,
7 parts of epoxy resin, 5 parts of titanium dioxides, 7 parts of organic siliconresins, 1 part of HMPA,1 part of alkenyl succinic acid ester, 1.5 parts of resorcinols, 0.5 part of disodium ethylene diamine tetraacetate, cornstarch 2Part, 0.5 part of stearic acid, 0.5 part of sodium acetate, the tert-butyl group are to 3 parts of biphenol, sebacic dihydrazide 1Part, 1 part of oxine, 2 parts of defoamers, 3.5 parts, reason mixture.
2. the protective underlayer coating that a kind of needle valve according to claim 1 is manufactured, is characterized in that:Comprise following preparation process,
I is put into successively disintegrating apparatus by above-mentioned material and is pulverized, stirs, mixes according to conventional method,Put into a kind of material every 1 minute, after all discharging, continue to mix 20 minutes;
II is taken out mixed material and put into heater and is heated to 240-280 DEG C, heating 30-39Minute;
III is put into calcining furnace by the material after heating and is calcined 3.5 hours according to conventional method;
Reactor put into by the material after calcining by IV, little with 4 of the intensification stirring reactions of 100 DEG C/hTime, react and within latter 30 minutes, added reasonable mixture;
V is taken out material, and shakes mixing 20 minutes, then extrude by double screw extruder,Temperature is controlled at 125 DEG C, has then extruded rear material and has left standstill 10 minutes, then puts into pulverizer and grindsAbrasive dust is broken into 190-225 object powder, packaging warehouse-in.
3. the protective underlayer coating that a kind of needle valve according to claim 1 is manufactured, is characterized in that: instituteState reason mixture and made by the material of following weight portion,
2 parts of the roots of fangji, 3 parts of the barks of eucommia, 4 parts of the shell of areca nuts, 7 parts of the roots of bidentate achyranthes, 9 parts of lophatherum graciles, 2 parts of the stem piths of the rice-paper plant, the bighead atractylodes rhizome 3Part, 4 parts of phoenix-tail ferns, 8 parts of cordate houttuynias, 1 part, gypsum, 3 parts of brush-cherry seeds, 1 part of croton, 3 parts of corn stigmas,3 parts of cortex acanthopanacis, 2 parts of radix cynanchi atratis;
Preparation method: after above-mentioned material is cleaned totally with clear water, dry in the place that is placed on ventilation,Then putting into disintegrating apparatus is ground into Powdered, for subsequent use according to conventional method.