CN105131567A - 一种聚氨酯橡胶ptmeg-f复合材料及其制备方法 - Google Patents

一种聚氨酯橡胶ptmeg-f复合材料及其制备方法 Download PDF

Info

Publication number
CN105131567A
CN105131567A CN201510516515.1A CN201510516515A CN105131567A CN 105131567 A CN105131567 A CN 105131567A CN 201510516515 A CN201510516515 A CN 201510516515A CN 105131567 A CN105131567 A CN 105131567A
Authority
CN
China
Prior art keywords
agent
ptmeg
urethanes
rubber composite
adopts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510516515.1A
Other languages
English (en)
Inventor
黄文鹏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510516515.1A priority Critical patent/CN105131567A/zh
Publication of CN105131567A publication Critical patent/CN105131567A/zh
Pending legal-status Critical Current

Abstract

本发明涉及复合材料及其制备领域，特别涉及一种聚氨酯橡胶PTMEG-F橡胶复合材料，包括聚醚多元醇（PPG）、异氰酸酯（MDI）、交联剂以及发泡助济组成，其中发泡助剂包括催化剂、助剂类、水、表面活性剂、三异氰酸酯、促硫剂、发泡剂、内润滑剂、外润滑剂、着色剂，采用这种制备方法使用本发明比传统硬橡胶密度低、尺寸稳定、并且可大大节省材料。

Description

一种聚氨酯橡胶PTMEG-F复合材料及其制备方法
技术领域
本发明涉及复合材料及其制备领域，特别涉及一种聚氨酯橡胶PTMEG-F复合材料及其制备方法。
背景技术
现有橡胶发泡材料通常采用偶氮类(如偶氮而甲酰胺)、4，4一氧化双苯磺酰肼、二亚硝基五次甲基四胺等化学发泡剂作为发泡剂，通过控制发泡剂的用量来控制发泡材料的发泡(膨胀)倍率(即尺寸大小)，其缺点是发泡材料尺寸难控制，且发泡后的材料收缩率大，尺寸容易变化，并且模具倍率的计算困难。若采用硬橡胶(不发泡橡胶)虽然成型后尺寸稳定，但是密度大，耗材量大，造成资源的浪费。
发明内容
为了克服现有技术中存在的上述不足之处，本发明的目的在于提供一种比传统硬橡胶密度低、尺寸稳定、并且可大大节省材料的聚氨酯橡胶PTMEG-F复合材料及其制备方法。
为了达到上述之目的，本发明采用如下具体技术方案：一种聚氨酯橡胶PTMEG-F复合材料，包括聚醚多元醇（PPG）、异氰酸酯（MDI）、交联剂以及发泡助济组成，其中发泡助剂包括催化剂、助剂类、水、表面活性剂、三异氰酸酯、促硫剂、发泡剂、内润滑剂、外润滑剂、着色剂。
所述橡胶复合材料各组分的质量百分比为：50%-70%聚醚多元醇（PPG）、18%-50%异氰酸酯（MDI）、6%-9%交联剂、1-3%催化剂、4-5%助剂类、0.9-2%水、1-10%表面活性剂、1-4%三异氰酸酯、1-3%促硫剂、2-4%发泡剂、1-3%内润滑剂、2-3%外润滑剂、1-10%着色剂。
所述交联剂采用1.4丁二醇或已二醇。
所述交联剂采用HQEE(4-羟乙基氧乙基-1-羟乙基苯二醚)
所述催化剂采用金属类的辛酸亚锡、二丁基锡二月桂酸酯和乙酸汞。
所述催化剂采用非金属类的三亚乙基二胺或二甲基乙醇胺。
所述发泡剂采用偶氮二甲酰胺或碳酸氢钠。
所述内润滑剂采用油酸酰胺，所述外润滑剂采用亚乙基双硬脂酰胺（EBS）。
所述着色剂采用色粉或色母。
所述聚氨酯橡胶PTMEG-F复合材料的其制备方法包含以下步骤：
1）将聚醚多元醇（PPG）、异氰酸酯（MDI）、交联剂以及发泡助济，通过计量泵计量加入混合器中进行预混合。
2）当温度反应到90—100℃时进入双螺杆挤出机，把温度控制在90℃，在挤出机末段的时候，通过粉体喂料机计量加入混合发泡助剂，其中发泡助剂包括催化剂、助剂类、水、表面活性剂、三异氰酸酯、促硫剂、发泡剂、内润滑剂、外润滑剂、着色剂。
3）发泡助剂与聚醚多元醇（PPG）、异氰酸酯（MDI）、交联剂通过栓螺杆挤压充分混合，从机头挤出，通过水下切粒机切.
4）再经风干、筛选，最后成橡胶复合原料料。
本发明具有以下突出优点和效果：比传统硬橡胶密度低、尺寸稳定、并且可大大节省材料的橡胶复合材料及其制备方法。
附图说明
图1为本发明的工艺流程图。
下面结合附图对本发明作进一步的详细说明。
具体实施方式
实施例1
一种聚氨酯橡胶PTMEG-F复合材料，包括聚醚多元醇（PPG）、异氰酸酯（MDI）、交联剂以及发泡助济组成，其中发泡助剂包括催化剂、助剂类、水、表面活性剂、三异氰酸酯、促硫剂、发泡剂、内润滑剂、外润滑剂、着色剂。
所述橡胶复合材料各组分的质量百分比为：50%-70%聚醚多元醇（PPG）、18%-50%异氰酸酯（MDI）、6%-9%交联剂、1-3%催化剂、4-5%助剂类、0.9-2%水、1-10%表面活性剂、1-4%三异氰酸酯、1-3%促硫剂、2-4%发泡剂、1-3%内润滑剂、2-3%外润滑剂、1-10%着色剂。
所述交联剂采用1.4丁二醇或已二醇。
所述交联剂采用HQEE(4-羟乙基氧乙基-1-羟乙基苯二醚)
所述催化剂采用金属类的辛酸亚锡、二丁基锡二月桂酸酯和乙酸汞。
所述催化剂采用非金属类的三亚乙基二胺或二甲基乙醇胺。
所述发泡剂采用偶氮二甲酰胺或碳酸氢钠。
所述内润滑剂采用油酸酰胺，所述外润滑剂采用亚乙基双硬脂酰胺（EBS）。
所述着色剂采用色粉或色母。
所述聚氨酯橡胶PTMEG-F复合材料的其制备方法包含以下步骤：
1）将聚醚多元醇（PPG）、异氰酸酯（MDI）、交联剂以及发泡助济，通过计量泵计量加入混合器中进行预混合。
2）当温度反应到90—100℃时进入双螺杆挤出机，把温度控制在90℃，在挤出机末段的时候，通过粉体喂料机计量加入混合发泡助剂，其中发泡助剂包括催化剂、助剂类、水、表面活性剂、三异氰酸酯、促硫剂、发泡剂、内润滑剂、外润滑剂、着色剂。
3）发泡助剂与聚醚多元醇（PPG）、异氰酸酯（MDI）、交联剂通过栓螺杆挤压充分混合，从机头挤出，通过水下切粒机切。
4）再经风干、筛选，最后成橡胶复合原料料。

Claims (10)

1.一种聚氨酯橡胶PTMEG-F橡胶复合材料，其特征在于：包括聚醚多元醇（PPG）、异氰酸酯（MDI）、交联剂以及发泡助济组成，其中发泡助剂包括催化剂、助剂类、水、表面活性剂、三异氰酸酯、促硫剂、发泡剂、内润滑剂、外润滑剂、着色剂。
2.根据权利要求1所述一种聚氨酯橡胶PTMEG-F橡胶复合材料，其特征在于：所述橡胶复合材料各组分的质量百分比为：50%-70%聚醚多元醇（PPG）、18%-50%异氰酸酯（MDI）、6%-9%交联剂、1-3%催化剂、4-5%助剂类、0.9-2%水、1-10%表面活性剂、1-4%三异氰酸酯、1-3%促硫剂、2-4%发泡剂、1-3%内润滑剂、2-3%外润滑剂、1-10%着色剂。
3.根据权利要求1所述一种聚氨酯橡胶PTMEG-F橡胶复合材料，其特征在于：所述交联剂采用1.4丁二醇或已二醇。
4.根据权利要求1所述一种聚氨酯橡胶PTMEG-F橡胶复合材料，其特征在于：所述交联剂采用4-羟乙基氧乙基-1-羟乙基苯二醚(HQEE)。
5.根据权利要求1所述一种聚氨酯橡胶PTMEG-F橡胶复合材料，其特征在于：所述催化剂采用金属类的辛酸亚锡、二丁基锡二月桂酸酯或乙酸汞。
6.根据权利要求1所述一种聚氨酯橡胶PTMEG-F橡胶复合材料，其特征在于：所述催化剂采用非金属类的三亚乙基二胺或二甲基乙醇胺。
7.根据权利要求1所述一种聚氨酯橡胶PTMEG-F橡胶复合材料，其特征在于：所述发泡剂采用偶氮二甲酰胺或碳酸氢钠。
8.根据权利要求1所述一种聚氨酯橡胶PTMEG-F橡胶复合材料，其特征在于：所述内润滑剂采用油酸酰胺，所述外润滑剂采用亚乙基双硬脂酰胺（EBS）。
9.根据权利要求1所述一种聚氨酯橡胶PTMEG-F橡胶复合材料，其特征在于：所述着色剂采用色粉或色母。
10.根据权利要求1所述一种聚氨酯橡胶PTMEG-F橡胶复合材料，其特征在于：所述橡胶复合材料的其制备方法包含以下步骤：
1）将聚醚多元醇（PPG）、异氰酸酯（MDI）、交联剂以及发泡助济，通过计量泵计量加入混合器中进行预混合；
2）当温度反应到90—100℃时进入双螺杆挤出机，把温度控制在90℃，在挤出机末段的时候，通过粉体喂料机计量加入混合发泡助剂，其中发泡助剂包括催化剂、助剂类、水、表面活性剂、三异氰酸酯、促硫剂、发泡剂、内润滑剂、外润滑剂、着色剂；
3）发泡助剂与聚醚多元醇（PPG）、异氰酸酯（MDI）、交联剂通过栓螺杆挤压充分混合，从机头挤出，通过水下切粒机切；
4）再经风干、筛选，最后成橡胶复合原料料。
CN201510516515.1A 2015-09-10 2015-09-10 一种聚氨酯橡胶ptmeg-f复合材料及其制备方法 Pending CN105131567A (zh)