CN105131547A - 一种聚碳酸酯组合物及其制备方法 - Google Patents
一种聚碳酸酯组合物及其制备方法 Download PDFInfo
- Publication number
- CN105131547A CN105131547A CN201510539899.9A CN201510539899A CN105131547A CN 105131547 A CN105131547 A CN 105131547A CN 201510539899 A CN201510539899 A CN 201510539899A CN 105131547 A CN105131547 A CN 105131547A
- Authority
- CN
- China
- Prior art keywords
- bat wool
- polycarbonate
- component
- glass
- polycarbonate compositions
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (11)