CN105130381B - 一种编织篮陶瓷制品用土及其制作工艺 - Google Patents

一种编织篮陶瓷制品用土及其制作工艺 Download PDF

Info

Publication number
CN105130381B
CN105130381B CN201510533693.5A CN201510533693A CN105130381B CN 105130381 B CN105130381 B CN 105130381B CN 201510533693 A CN201510533693 A CN 201510533693A CN 105130381 B CN105130381 B CN 105130381B
Authority
CN
China
Prior art keywords
kaolin
ceramic
woven basket
soil
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510533693.5A
Other languages
English (en)
Other versions
CN105130381A (zh
Inventor
林建华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MYINGFA CERAMIC Co Ltd DEHUA FUJIAN
Original Assignee
MYINGFA CERAMIC Co Ltd DEHUA FUJIAN
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MYINGFA CERAMIC Co Ltd DEHUA FUJIAN filed Critical MYINGFA CERAMIC Co Ltd DEHUA FUJIAN
Priority to CN201510533693.5A priority Critical patent/CN105130381B/zh
Publication of CN105130381A publication Critical patent/CN105130381A/zh
Application granted granted Critical
Publication of CN105130381B publication Critical patent/CN105130381B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种编织篮陶瓷制品用土及其制作工艺，由南平透辉石、广西滑石、龙岩高岭土、大田高岭土、漳平高岭土和福州腊石按照质量比制备而成，将原料按照配比放入球磨机中充分研磨，经筛网过滤放入储浆槽中陈腐，通过练泥机抽出空气，用练泥机炼制多次，经过压滤机压制成泥饼，用卡板叠放陈腐1个月即可。本发明编织篮陶瓷制品用土，组分简单，配比合理，利用本发明用土进行烧制编织篮陶瓷制品，较一般编织篮陶瓷制品原料的烧制温度降低很多，因此其能耗低，成本低，而且烧制出的编织篮陶瓷制品硬度强，质量过硬，不易损坏。

Description

一种编织篮陶瓷制品用土及其制作工艺
技术领域
本发明涉及陶瓷工艺品制作技术领域，具体是一种编织篮陶瓷制品用土及其制作工艺。
背景技术
目前，陶瓷工艺品的原料配方以及烧制工艺已经很成熟，制造出来的产品也存在很多优点；但是现有的编织篮陶瓷制品还存在诸多的缺点，由于编织篮陶瓷制品采用的原料组分过多，成分复杂，因此在烧制过程中，需要很高的烧制温度才能达到工艺要求，因此能耗高，成本也高，烧制出的产品硬度高，容易损坏，因此需要对现有的陶瓷成分进行改进，以降低其成本，提高质量。
发明内容
本发明的目的在于提供一种编织篮陶瓷制品用土及其制作工艺，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：
一种编织篮陶瓷制品用土，由以下原料按照质量百分比制作而成：南平透辉石15～25％，广西滑石15～25％，龙岩高岭土12～18％，大田高岭土12～18％，漳平高岭土12～18％，福州腊石12～18％。
作为本发明进一步的方案：具体由以下原料按照质量百分比制作而成：南平透辉石20％，广西滑石20％，龙岩高岭土15％，大田高岭土15％，漳平高岭土15％，福州腊石15％。
一种编织篮陶瓷制品用土的制作工艺，具体制作步骤如下：将上述原料按照配比放入球磨机中，充分研磨12～15h，经200～250目筛网过滤，放入大型储浆槽中，陈腐3～5天，通过练泥机抽出空气，用练泥机炼制2～3次，经过压滤机压制成泥饼，用卡板叠放陈腐1个月，即可。
与现有技术相比，本发明的有益效果是：本发明编织篮陶瓷制品用土，组分简单，配比合理，利用本发明用土进行烧制编织篮陶瓷制品，其烧制温度在1150～1200℃即可，较一般编织篮陶瓷制品原料的烧制温度降低很多，因此其能耗低，成本低，而且烧制出的编织篮陶瓷制品硬度强，质量过硬，不易损坏。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
编织篮陶瓷制品用土，由以下原料按照质量百分比制作而成：南平透辉石15～25％，广西滑石15～25％，龙岩高岭土12～18％，大田高岭土12～18％，漳平高岭土12～18％，福州腊石12～18％。
实施例2
编织篮陶瓷制品用土，具体由以下原料按照质量百分比制作而成：南平透辉石20％，广西滑石20％，龙岩高岭土15％，大田高岭土15％，漳平高岭土15％，福州腊石15％。
实施例3
编织篮陶瓷制品用土，由以下原料按照质量百分比制作而成：南平透辉石15～25％，广西滑石15～25％，龙岩高岭土12～18％，大田高岭土12～18％，漳平高岭土12～18％，福州腊石12～18％。
上述实施例中编织篮陶瓷制品用土的制作工艺，具体制作步骤如下：将上述原料按照配比放入球磨机中，充分研磨12～15h，经200～250目筛网过滤，放入大型储浆槽中，陈腐3～5天，通过练泥机抽出空气，用练泥机炼制2～3次，经过压滤机压制成泥饼，用卡板叠放陈腐1个月，即可。
采用上述的原料烧制编织篮陶瓷制品，其烧制温度在1150～1200℃即可，能耗低，成本低，硬度强，质量过硬，符合国家标准。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。

Claims (3)

1.一种编织篮陶瓷制品用土，其特征在于，由以下原料按照质量百分比制作而成：南平透辉石15～25％，广西滑石15～25％，龙岩高岭土12～18％，大田高岭土12～18％，漳平高岭土12～18％，福州腊石12～18％。
2.根据权利要求1所述的编织篮陶瓷制品用土，其特征在于，具体由以下原料按照质量百分比制作而成：南平透辉石20％，广西滑石20％，龙岩高岭土15％，大田高岭土15％，漳平高岭土15％，福州腊石15％。
3.一种如权利要求1或2所述的编织篮陶瓷制品用土的制作工艺，其特征在于，具体制作步骤如下：将上述原料按照配比放入球磨机中，充分研磨12～15h，经200～250目筛网过滤，放入大型储浆槽中，陈腐3～5天，通过练泥机抽出空气，用练泥机炼制2～3次，经过压滤机压制成泥饼，用卡板叠放陈腐1个月，即可。
CN201510533693.5A 2015-08-27 2015-08-27 一种编织篮陶瓷制品用土及其制作工艺 Active CN105130381B (zh)