CN105110684A - 一种混凝土改性剂及其混凝土 - Google Patents

一种混凝土改性剂及其混凝土 Download PDF

Info

Publication number
CN105110684A
CN105110684A CN201510542888.6A CN201510542888A CN105110684A CN 105110684 A CN105110684 A CN 105110684A CN 201510542888 A CN201510542888 A CN 201510542888A CN 105110684 A CN105110684 A CN 105110684A
Authority
CN
China
Prior art keywords
parts
concrete
powder
modifying agent
modifier
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510542888.6A
Other languages
English (en)
Inventor
叶飚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi Lu Jia Bridge Survey And Design Co Ltd
Original Assignee
Guangxi Lu Jia Bridge Survey And Design Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi Lu Jia Bridge Survey And Design Co Ltd filed Critical Guangxi Lu Jia Bridge Survey And Design Co Ltd
Priority to CN201510542888.6A priority Critical patent/CN105110684A/zh
Publication of CN105110684A publication Critical patent/CN105110684A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种混凝土改性剂及其混凝土，属于混凝土技术领域。所述混凝土改性剂包括如下重量份数的原料：煤灰粉5～10份、二氧化硅粉2～6份、石膏粉2～6份、格雷斯纤维5～10份、钢纤维2～6份、钙粉3～9份、分散性乳胶粉1～9份、丙烯酸乳液1～5份、碳酸钙1～5份、硫酸锌1～5份、硼酸钠5～10份和聚丙烯酰胺4～12份。本发明的混凝土改性剂，能提高混凝土的韧性、抗压强度和使用年限，采用本发明的混凝土改性剂制成的混凝土抗拉、抗折、抗裂性能好，且价格低廉、生产工艺简单、成本低，适合规模化生产。

Description

一种混凝土改性剂及其混凝土
技术领域
本发明涉及一种混凝土改性剂及其混凝土，属于混凝土技术领域。
背景技术
混凝土，简称为“砼”，通常是指用水泥作胶凝材料，砂、石作集料，与水按一定比例配合，经搅拌所得。混凝土具有原料丰富，价格低廉，生产工艺简单的特点，使其使用范围十分广泛，不仅在各种土木工程中使用，就是造船业、机械工业、海洋的开发、地热工程等，混凝土也是重要的材料。
混凝土在实际工程中应用中，经常暴露于各种较为严酷的环境，如环境周围腐蚀性介质的侵入，环境温湿度的变化、冻融循环破坏以及部分混凝土工程经常处于重荷载磨损等，这些外部条件将会严重影响混凝土的使用寿命。因此，需要在混凝土中添加保护剂对混凝土进行保护作用，现有的混凝土改性剂存在功能单一、对混凝土的保养效果差的技术不足。
发明内容
本发明的目的是弥补现有技术的不足，提供一种混凝土改性剂及其混凝土。本发明的混凝土改性剂能提高混凝土的韧性、抗压强度和使用年限，采用本发明的混凝土改性剂制成的混凝土抗拉、抗折、抗裂性能好。
本发明解决上述技术问题的技术方案如下：一种混凝土改性剂，包括如下重量份数的原料：煤灰粉5～10份、二氧化硅粉2～6份、石膏粉2～6份、格雷斯纤维5～10份、钢纤维2～6份、钙粉3～9份、分散性乳胶粉1～9份、丙烯酸乳液1～5份、碳酸钙1～5份、硫酸锌1～5份、硼酸钠5～10份和聚丙烯酰胺4～12份。
在上述技术方案的基础上，本发明还可以做如下改进。
进一步，包括如下重量份数的原料：煤灰粉7份、二氧化硅粉4份、石膏粉4份、格雷斯纤维7份、钢纤维4份、钙粉6份、分散性乳胶粉5份、丙烯酸乳液3份、碳酸钙3份、硫酸锌3份、硼酸钠7份和聚丙烯酰胺8份。
进一步，所述膨润土为钠基膨润土。
进一步，所述二氧化硅粉为纳米二氧化硅粉。
进一步，所述钢纤维的长度为1～40mm。
进一步，所述分散性乳胶粉的成膜温度≥0℃。
一种混凝土，包含如上任意一项所述的混凝土改性剂。
在上述技术方案的基础上，本发明还可以做如下改进。
进一步，所述混凝土改性剂的质量为混凝土质量的5～10wt％。
本发明的有益效果是：
(1)本发明的混凝土改性剂,能提高混凝土的韧性、抗压强度和使用年限。
(2)采用本发明的混凝土改性剂制成的混凝土抗拉、抗折、抗裂性能好。
(3)本发明的价格低廉、生产工艺简单、成本低，适合规模化生产。
具体实施方式
以下结合具体实施例对本发明的原理和特征进行描述，所举实例只用于解释本发明，并非用于限定本发明的范围。
实施例1：
一种混凝土改性剂，包括如下重量份数的原料：煤灰粉5份、二氧化硅粉6份、石膏粉2份、格雷斯纤维10份、钢纤维2份、钙粉9份、分散性乳胶粉1份、丙烯酸乳液5份、碳酸钙1份、硫酸锌5份、硼酸钠5份和聚丙烯酰胺12份，其中，所述膨润土为钠基膨润土，所述二氧化硅粉为纳米二氧化硅粉，所述钢纤维的长度为1～40mm，所述分散性乳胶粉的成膜温度≥0℃。
一种混凝土，包含如上所述的混凝土改性剂，所述混凝土改性剂的质量为混凝土质量的5wt％。
实施例2：
一种混凝土改性剂，包括如下重量份数的原料：煤灰粉7份、二氧化硅粉4份、石膏粉4份、格雷斯纤维7份、钢纤维4份、钙粉6份、分散性乳胶粉5份、丙烯酸乳液3份、碳酸钙3份、硫酸锌3份、硼酸钠7份和聚丙烯酰胺8份，其中，所述膨润土为钠基膨润土，所述二氧化硅粉为纳米二氧化硅粉，所述钢纤维的长度为1～40mm，所述分散性乳胶粉的成膜温度≥0℃。
一种混凝土，包含如上所述的混凝土改性剂，所述混凝土改性剂的质量为混凝土质量的7wt％。
实施例3：
一种混凝土改性剂，包括如下重量份数的原料：煤灰粉10份、二氧化硅粉2份、石膏粉6份、格雷斯纤维5份、钢纤维6份、钙粉3份、分散性乳胶粉9份、丙烯酸乳液1份、碳酸钙5份、硫酸锌1份、硼酸钠10份和聚丙烯酰胺4份，其中，所述膨润土为钠基膨润土，所述二氧化硅粉为纳米二氧化硅粉，所述钢纤维的长度为1～40mm，所述分散性乳胶粉的成膜温度≥0℃。
一种混凝土，包含如上所述的混凝土改性剂，所述混凝土改性剂的质量为混凝土质量的10wt％。
以上所述仅为本发明的较佳实施例，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (8)

1.一种混凝土改性剂，其特征在于，包括如下重量份数的原料：煤灰粉5～10份、二氧化硅粉2～6份、石膏粉2～6份、格雷斯纤维5～10份、钢纤维2～6份、钙粉3～9份、分散性乳胶粉1～9份、丙烯酸乳液1～5份、碳酸钙1～5份、硫酸锌1～5份、硼酸钠5～10份和聚丙烯酰胺4～12份。
2.根据权利要求1所述的一种混凝土改性剂，其特征在于，包括如下重量份数的原料：煤灰粉7份、二氧化硅粉4份、石膏粉4份、格雷斯纤维7份、钢纤维4份、钙粉6份、分散性乳胶粉5份、丙烯酸乳液3份、碳酸钙3份、硫酸锌3份、硼酸钠7份和聚丙烯酰胺8份。
3.根据权利要求1或2所述的一种混凝土改性剂，其特征在于，所述膨润土为钠基膨润土。
4.根据权利要求1或2所述的一种混凝土改性剂，其特征在于，所述二氧化硅粉为纳米二氧化硅粉。
5.根据权利要求1或2所述的一种混凝土改性剂，其特征在于，所述钢纤维的长度为1～40mm。
6.根据权利要求1或2所述的一种混凝土改性剂，其特征在于，所述分散性乳胶粉的成膜温度≥0℃。
7.一种混凝土，其特征在于，包含权利要求1-6任意一项所述的混凝土改性剂。
8.根据权利要求7所述的混凝土，其特征在于，所述混凝土改性剂的质量为混凝土质量的5～10wt％。
CN201510542888.6A 2015-08-31 2015-08-31 一种混凝土改性剂及其混凝土 Pending CN105110684A (zh)