CN104860585A - 一种防水混凝土及其制备方法 - Google Patents

一种防水混凝土及其制备方法 Download PDF

Info

Publication number
CN104860585A
CN104860585A CN201510212978.9A CN201510212978A CN104860585A CN 104860585 A CN104860585 A CN 104860585A CN 201510212978 A CN201510212978 A CN 201510212978A CN 104860585 A CN104860585 A CN 104860585A
Authority
CN
China
Prior art keywords
parts
water
concrete
minute
waterproof
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510212978.9A
Other languages
English (en)
Inventor
朱安会
马洪章
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Xin Run Type Material Co Ltd
Original Assignee
Anhui Xin Run Type Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Xin Run Type Material Co Ltd filed Critical Anhui Xin Run Type Material Co Ltd
Priority to CN201510212978.9A priority Critical patent/CN104860585A/zh
Publication of CN104860585A publication Critical patent/CN104860585A/zh
Pending legal-status Critical Current

Abstract

一种防水混凝土,由下列重量份的原料制成:橡胶粉20-30、聚丙烯纤维20-30、氯化锌3-4、氯化镁3-4、氧化钙6-8、E环氧树脂10-15、邻苯二甲酸二丁酯2-3、砂270-300、水泥160-170、石子500-530、水适量、助剂20-30;本发明混凝土防水性能好,抗渗等级高,还具有较高的强度;通过使用助剂,增加了混凝土的抗拉、抗折、抗压强度和密实性,能够散发香气,防蛀防腐蚀,增强了防锈、防水、防渗性能,减水性、可塑性和可泵送效果好;该混凝土成本低廉,耐久性提高,适合大规模工业化生产。

Description

一种防水混凝土及其制备方法
技术领域
本发明属于建筑材料领域,特别涉及一种防水混凝土及其制备方法。
背景技术
混凝土具有原料丰富,价格低廉,生产工艺简单的特点,因而使其用量越来越大。同时混凝土还具有抗压强度高,耐久性好,强度等级范围宽等特点。这些特点使其使用范围十分广泛,不仅在各种土木工程中使用,就是造船业,机械工业,海洋的开发,地热工程等,混凝土也是重要的材料。
随着混凝土组成材料的不断发展,人们对对混凝土的性能要求不仅仅局限于抗压强度,而是在立足强度的基础上,更加注重混凝土的耐久性、变形性能、防火抗爆性能、防渗水性能、韧性、耐腐蚀性、保温性、健康环保性以及降低成本等等综合指标的平衡和协调。混凝土各项性能指标的要求比以前更明确、细化和具体。同时,建筑设备水平的提升,新型施工工艺的不断涌现和推广,使混凝土技术适应了不同的设计、施工和使用要求,发展很快。
混凝土还离不开混凝土用原材料的发展,离不开混凝土的工程应用对象的发展变化。因此,研制性能更加优异、功能更加强大、更适应新工艺、新建筑对象的混凝土就显得尤为重要。
发明内容
本发明的目的在于提供一种防水混凝土及其制备方法,该混凝土防水性能好,抗渗等级高,还具有较高的强度。
本发明的技术方案如下:
一种防水混凝土,其特征在于由下列重量份的原料制成:橡胶粉20-30、聚丙烯纤维20-30、氯化锌3-4、氯化镁3-4、氧化钙6-8、E环氧树脂10-15、邻苯二甲酸二丁酯2-3、砂270-300、水泥160-170、石子500-530、水适量、助剂20-30;
    所述助剂由下列重量份的原料制成:环氧丙烯酸酯2-3、丙烯酸甲酯2-3、季戊四醇1-2、丙烯腈2-3、庚酸烯丙酯2-3、丙烯酸乙酯1-2、橘子油0.4-0.6、苯并三氮唑1-2、三聚氰胺1-2、12-羟基硬脂酸锂1-2、钢纤维4-6、活性硅酸钙4-5、杏仁油1-1.7、三乙烯四胺0.2-0.3、全氟辛基磺酸钠0.6-0.9、苹果酸钠0.5-0.7、椰子油二乙醇酰胺0.5-0.8、过硫酸铵0.1-0.2、过硫酸钾0.1-0.2、水15-18、;制备方法为:将水、环氧丙烯酸酯、丙烯酸甲酯、季戊四醇、丙烯腈、庚酸烯丙酯、全氟辛基磺酸钠、苹果酸钠、椰子油二乙醇酰胺、苯并三氮唑、钢纤维混合,加热至70-80℃,加入过硫酸铵搅拌反应20-30分钟,再与其他剩余成分混合,加热至80-90℃,搅拌反应40-50分钟,即得。
所述的防水混凝土的制备方法,其特征在于包括以下步骤:
(1)将橡胶粉、氯化锌、氯化镁、E环氧树脂、邻苯二甲酸二丁酯混合,研磨20-30分钟,再与水混合,搅拌均匀,得到混合浆液;
(2)将聚丙烯纤维、氧化钙、砂、水泥、石子混合均匀,与第(1)步得到的混合浆液以及其他剩余成分混合均匀,搅拌反应8-12分钟,然后浇注,振捣;
(3)浇筑后在 5-25℃的潮湿环境中进行养护7-9天,即得。
本发明的有益效果
本发明混凝土防水性能好,抗渗等级高,还具有较高的强度;通过使用助剂,增加了混凝土的抗拉、抗折、抗压强度和密实性,能够散发香气,防蛀防腐蚀,增强了防锈、防水、防渗性能,减水性、可塑性和可泵送效果好;该混凝土成本低廉, 耐久性提高,适合大规模工业化生产。
具体实施方式
一种防水混凝土,由下列重量份(公斤)的原料制成:橡胶粉25、聚丙烯纤维25、氯化锌3.5、氯化镁3.5、氧化钙7、E环氧树脂13、邻苯二甲酸二丁酯2.5、砂280、水泥165、石子520、水适量、助剂25;
    所述助剂由下列重量份(公斤)的原料制成:环氧丙烯酸酯2.5、丙烯酸甲酯2.5、季戊四醇1.5、丙烯腈2.5、庚酸烯丙酯2.5、丙烯酸乙酯1.5、橘子油0.5、苯并三氮唑1.5、三聚氰胺1.5、12-羟基硬脂酸锂1.5、钢纤维5、活性硅酸钙4.5、杏仁油1.4、三乙烯四胺0.2、全氟辛基磺酸钠0.8、苹果酸钠0.6、椰子油二乙醇酰胺0.6、过硫酸铵0.2、过硫酸钾0.2、水16、;制备方法为:将水、环氧丙烯酸酯、丙烯酸甲酯、季戊四醇、丙烯腈、庚酸烯丙酯、全氟辛基磺酸钠、苹果酸钠、椰子油二乙醇酰胺、苯并三氮唑、钢纤维混合,加热至75℃,加入过硫酸铵搅拌反应25分钟,再与其他剩余成分混合,加热至85℃,搅拌反应45分钟,即得。
所述的防水混凝土的制备方法,包括以下步骤:
(1)将橡胶粉、氯化锌、氯化镁、E环氧树脂、邻苯二甲酸二丁酯混合,研磨25分钟,再与水混合,搅拌均匀,得到混合浆液;
(2)将聚丙烯纤维、氧化钙、砂、水泥、石子混合均匀,与第(1)步得到的混合浆液以及其他剩余成分混合均匀,搅拌反应9分钟,然后浇注,振捣;
(3)浇筑后在 10-20℃的潮湿环境中进行养护8天,即得。
实验数据:
该实施例的混凝土强度等级为C35,坍落度为18cm,抗压强度45MPa,抗折强度 16.6MPa,抗渗等级S10。

Claims (2)

1.一种防水混凝土,其特征在于由下列重量份的原料制成:橡胶粉20-30、聚丙烯纤维20-30、氯化锌3-4、氯化镁3-4、氧化钙6-8、E环氧树脂10-15、邻苯二甲酸二丁酯2-3、砂270-300、水泥160-170、石子500-530、水适量、助剂20-30;
    所述助剂由下列重量份的原料制成:环氧丙烯酸酯2-3、丙烯酸甲酯2-3、季戊四醇1-2、丙烯腈2-3、庚酸烯丙酯2-3、丙烯酸乙酯1-2、橘子油0.4-0.6、苯并三氮唑1-2、三聚氰胺1-2、12-羟基硬脂酸锂1-2、钢纤维4-6、活性硅酸钙4-5、杏仁油1-1.7、三乙烯四胺0.2-0.3、全氟辛基磺酸钠0.6-0.9、苹果酸钠0.5-0.7、椰子油二乙醇酰胺0.5-0.8、过硫酸铵0.1-0.2、过硫酸钾0.1-0.2、水15-18、;制备方法为:将水、环氧丙烯酸酯、丙烯酸甲酯、季戊四醇、丙烯腈、庚酸烯丙酯、全氟辛基磺酸钠、苹果酸钠、椰子油二乙醇酰胺、苯并三氮唑、钢纤维混合,加热至70-80℃,加入过硫酸铵搅拌反应20-30分钟,再与其他剩余成分混合,加热至80-90℃,搅拌反应40-50分钟,即得。
2.根据权利要求1所述的防水混凝土的制备方法,其特征在于包括以下步骤:
(1)将橡胶粉、氯化锌、氯化镁、E环氧树脂、邻苯二甲酸二丁酯混合,研磨20-30分钟,再与水混合,搅拌均匀,得到混合浆液;
(2)将聚丙烯纤维、氧化钙、砂、水泥、石子混合均匀,与第(1)步得到的混合浆液以及其他剩余成分混合均匀,搅拌反应8-12分钟,然后浇注,振捣;
(3)浇筑后在 5-25℃的潮湿环境中进行养护7-9天,即得。
CN201510212978.9A 2015-04-30 2015-04-30 一种防水混凝土及其制备方法 Pending CN104860585A (zh)