CN105086787A - 高丰满度抗刮哑光清面漆的配方及制备方法 - Google Patents
高丰满度抗刮哑光清面漆的配方及制备方法 Download PDFInfo
- Publication number
- CN105086787A CN105086787A CN201510448664.9A CN201510448664A CN105086787A CN 105086787 A CN105086787 A CN 105086787A CN 201510448664 A CN201510448664 A CN 201510448664A CN 105086787 A CN105086787 A CN 105086787A
- Authority
- CN
- China
- Prior art keywords
- components
- raw material
- preparation
- group raw
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了高丰满度抗刮哑光清面漆的配方及制备方法,它涉及油漆制备技术领域。先把甲组中第一组份逐步加入,高速分散均匀,然后搅拌机在1200-1600r/min下分散5-7min,加入二组份分散均匀,再加放入三组份搅拌机在高速1500-1700r/min下分散5-7min,加入四组份,最后边分散边加入五组份,搅拌机在高速1200-1600r/min分散3-6min,最后搅拌机在低速450-550r/min下脱泡5min,最后加入乙组原料充分搅拌均匀。它能克服现有技术的弊端,制备过程简单,制成的哑光清面漆抗刮性能好,丰满度好,固化剂要求较低,涂覆在产品上更加平整、光滑、细腻,并且不含有毒成分,环保。
Description
技术领域:
本发明涉及高丰满度抗刮哑光清面漆的配方及制备方法,属于油漆制备技术领域。
背景技术:
哑光清面漆采用自然成膜的方式,无需特殊工艺,在使用时由主剂+固化剂+稀释剂按照一定的比例配合然后喷涂,操作方便,被广泛应用于漆涂工艺中,但是现有的亚光情清面漆存在很大的缺陷就是抗刮性能差,并且丰满度差,固化剂要求较高。
发明内容:
针对上述问题,本发明要解决的技术问题是提供高丰满度抗刮哑光清面漆的配方及制备方法。
本发明的高丰满度抗刮哑光清面漆的配方及制备方法,它的配方包含两组原料,甲组原料和乙组原料,其中甲组原料和乙组原料的质量为:1:0.5;甲组原料包含四种组分:各个组分的成分及质量百分数为:一组份:短油度醇酸树脂12%-18%,大豆油改性醇酸树脂20%-30%,合成脂肪酸树脂18%-22%,醛酮树脂20%-25%,聚酰氨防沉剂0.3%-1.0%;二组份:分散剂0.1%-0.5%;三组份:消光剂5%-10%;四组份:醋酸丁酯3%-8%,环已酮2%-5%,二甲苯1%-4%;五组份:消泡剂0.2%-0.6%;流平剂0.2%-0.7%。
其中乙组原料的成分及质量百分数为:H﹒RB为25%-35%,L75为3%-45%,醋酸丁脂为25%-35%。
它的制备方法为:先把甲组中第一组份逐步加入,高速分散均匀,然后搅拌机在1200-1600r/min下分散5-7min,加入二组份分散均匀,再加放入三组份搅拌机在高速1500-1700r/min下分散5-7min,加入四组份,最后边分散边加入五组份,搅拌机在高速1200-1600r/min分散3-6min,最后搅拌机在低速450-550r/min下脱泡5min,最后加入乙组原料充分搅拌均匀。
本发明的有益效果:它能克服现有技术的弊端,制备过程简单,制成的哑光清面漆抗刮性能好,丰满度好,固化剂要求较低,涂覆在产品上更加平整、光滑、细腻,并且不含有毒成分,环保。
具体实施方式:
本具体实施方式采用以下技术方案:它的配方包含两组原料,甲组原料和乙组原料,其中甲组原料和乙组原料的质量为:1:0.5;甲组原料包含四种组分:各个组分的成分及质量百分数为:一组份:短油度醇酸树脂12%-18%,大豆油改性醇酸树脂20%-30%,合成脂肪酸树脂18%-22%,醛酮树脂20%-25%,聚酰氨防沉剂0.3%-1.0%;二组份:分散剂0.1%-0.5%;三组份:消光剂5%-10%;四组份:醋酸丁酯3%-8%,环已酮2%-5%,二甲苯1%-4%;五组份:消泡剂0.2%-0.6%;流平剂0.2%-0.7%。
其中乙组原料的成分及质量百分数为:H﹒RB为25%-35%,L75为3%-45%,醋酸丁脂为25%-35%。
它的制备方法为:先把甲组中第一组份逐步加入,高速分散均匀,然后搅拌机在1200-1600r/min下分散5-7min,加入二组份分散均匀,再加放入三组份搅拌机在高速1500-1700r/min下分散5-7min,加入四组份,最后边分散边加入五组份,搅拌机在高速1200-1600r/min分散3-6min,最后搅拌机在低速450-550r/min下脱泡5min,最后加入乙组原料充分搅拌均匀。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定 。
实施例:甲组原料和乙组原料的质量为:1:0.5,先把甲组中第一组份质量分数为:短油度醇酸树脂14.6%、大豆油改性醇酸树脂25%,合成脂肪酸树脂20%、醛酮树脂23%、聚酰氨防沉0.5%逐步加入搅拌机,高速分散均匀,然后搅拌机在1500r/min下分散5min,加入二组份分散剂0.3%分散均匀,再加放入三组份消光剂7%搅拌机在高速1700r/min下分散5min,加入四组份,醋酸丁酯4%、环已酮3%、二甲苯2%最后边分散边加入五组份消泡剂0.3%,流平剂0.3%,搅拌机在高速1500r/min分散6min,最后搅拌机在低速500r/min下脱泡5min,最后加入乙组原料30%的H﹒RB,40%的L75和30%的醋酸丁脂充分搅拌均匀即可。
本实施例中制成高丰满度抗刮哑光清面漆的检测指标:
粘度:2000±200cps/25℃
细度:<20um
表干:<45min
实干:<4h
光泽:30±5°
硬度:>2H
板面效果:平整、光滑、细腻。
Claims (3)
1.高丰满度抗刮哑光清面漆的配方及制备方法,其特征在于:它的配方包含两组原料,甲组原料和乙组原料,其中甲组原料和乙组原料的质量为:1:0.5;甲组原料包含四种组分:各个组分的成分及质量百分数为:一组份:短油度醇酸树脂12%-18%,大豆油改性醇酸树脂20%-30%,合成脂肪酸树脂18%-22%,醛酮树脂20%-25%,聚酰氨防沉剂0.3%-1.0%;二组份:分散剂0.1%-0.5%;三组份:消光剂5%-10%;四组份:醋酸丁酯3%-8%,环已酮2%-5%,二甲苯1%-4%;五组份:消泡剂0.2%-0.6%;流平剂0.2%-0.7%。
2.按照权利要求1所述的高丰满度抗刮哑光清面漆的配方,其特征在于:乙组原料的成分及质量百分数为:H﹒RB为25%-35%,L75为3%-45%,醋酸丁脂为25%-35%。
3.高丰满度抗刮哑光清面漆的配方及制备方法,其特征在于:它的制备方法为:先把甲组中第一组份逐步加入,高速分散均匀,然后搅拌机在1200-1600r/min下分散5-7min,加入二组份分散均匀,再加放入三组份搅拌机在高速1500-1700r/min下分散5-7min,加入四组份,最后边分散边加入五组份,搅拌机在高速1200-1600r/min分散3-6min,最后搅拌机在低速450-550r/min下脱泡5min,最后加入乙组原料充分搅拌均匀。