CN105086541A - Heat-resistant fire-resistant paint - Google Patents
Heat-resistant fire-resistant paint Download PDFInfo
- Publication number
- CN105086541A CN105086541A CN201510620868.6A CN201510620868A CN105086541A CN 105086541 A CN105086541 A CN 105086541A CN 201510620868 A CN201510620868 A CN 201510620868A CN 105086541 A CN105086541 A CN 105086541A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat
- resistant
- fire
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses heat-resistant fire-resistant paint which comprises the following components in parts by weight: 120-160 parts of phenolic resin, 80-100 parts of methacrylic acid-2-hydroxyethyl, 40-60 parts of methyl methacrylate, 80-160 parts of butyrolactone, 40-60 parts of zinc borate, 20-40 parts of aluminum hydroxide, 18-24 parts of phosphotriester, 16-18 parts of antimonous oxide, 6-12 parts of an asbestos fiber, 10-20 parts of graphite nodules and 12-28 parts of vanadium trioxide. The heat-resistant fire-resistant paint is simple to produce, and non-toxic raw materials are adopted for production; the heat-resistant fire-resistant paint is good in using effect and environment-friendly; a coating formed by the heat-resistant fire-resistant paint is high in heat-insulating property.
Description
Technical field
The present invention relates to a kind of technical field of chemical article, be specifically related to a kind of heat and flame coating.
Background technology
The effect of coating in production and life is very large; widespread use and every field; the film that coating is formed can play decoration, protection and beautiful effect to object; although current most of coating on the market makes simply, price is cheap but function ratio is more single simultaneously; can only simply as the use of decoration; and in the operating environment that some are special, can not meeting needed for people of simple coating.
Summary of the invention
Object of the present invention provides a kind of heat and flame coating, solves one or more in above-mentioned prior art problem.
According to an aspect of the present invention, a kind of heat and flame coating, comprises the component of following weight part, 120 ~ 160 parts, resol, Jia base Bing Xi Suan ?2 ?hydroxyl ethyl ester 80 ~ 100 parts, methyl methacrylate 40 ~ 60 parts, butyrolactone 80 ~ 160 parts, zinc borate 40 ~ 60 parts, 20 ~ 40 parts, aluminium hydroxide, phosphotriester 18 ~ 24 parts, antimonous oxide 16 ~ 18 parts, fibrous magnesium silicate 6 ~ 12 parts, graphite pebbles 10 ~ 20 parts, vanadous oxide 12 ~ 28 parts.
A kind of heat and flame coating provided by the invention, makes simple, and the raw materials for production of employing are selected avirulent, and the result of use of coating is good, environmental protection, and paint coatings has good heat-insulating property.
Embodiment
Embodiment 1
By 120 parts, resol, Jia base Bing Xi Suan ?2 ?hydroxyl ethyl ester 80 parts, methyl methacrylate 40 parts, butyrolactone 80 parts, zinc borate 40 parts, 20 parts, aluminium hydroxide, phosphotriester 18 parts, antimonous oxide 16 parts, fibrous magnesium silicate 6 parts, graphite pebbles 10 parts, vanadous oxide 12 parts puts into reactor, continuous stirring, mixes complete post-heating to 75 DEG C, namely obtains product after uniform stirring.
Embodiment 2
By 140 parts, resol, Jia base Bing Xi Suan ?2 ?hydroxyl ethyl ester 90 parts, methyl methacrylate 50 parts, butyrolactone 120 parts, zinc borate 50 parts, 30 parts, aluminium hydroxide, phosphotriester 21 parts, antimonous oxide 17 parts, fibrous magnesium silicate 9 parts, graphite pebbles 15 parts, vanadous oxide 20 parts puts into reactor, continuous stirring, mixes complete post-heating to 75 DEG C, namely obtains product after uniform stirring.
Embodiment 3
By 160 parts, resol, Jia base Bing Xi Suan ?2 ?hydroxyl ethyl ester 100 parts, methyl methacrylate 60 parts, butyrolactone 160 parts, zinc borate 60 parts, 40 parts, aluminium hydroxide, phosphotriester 24 parts, antimonous oxide 18 parts, fibrous magnesium silicate 12 parts, graphite pebbles 20 parts, vanadous oxide 28 parts puts into reactor, continuous stirring, mixes complete post-heating to 75 DEG C, namely obtains product after uniform stirring.
The above is only optimal way of the present invention; it should be pointed out that to those skilled in the art, without departing from the concept of the premise of the invention; can also make some similar distortion and improvement, these also should be considered as within protection scope of the present invention.
Claims (1)
1. a heat and flame coating, is characterized in that: the component comprising following weight part,
120 ~ 160 parts, resol, Jia base Bing Xi Suan ?2 ?hydroxyl ethyl ester 80 ~ 100 parts, methyl methacrylate 40 ~ 60 parts, butyrolactone 80 ~ 160 parts, zinc borate 40 ~ 60 parts, 20 ~ 40 parts, aluminium hydroxide, phosphotriester 18 ~ 24 parts, antimonous oxide 16 ~ 18 parts, fibrous magnesium silicate 6 ~ 12 parts, graphite pebbles 10 ~ 20 parts, vanadous oxide 12 ~ 28 parts.