CN104530794A - Non-intumescent latex fireproof paint - Google Patents

Abstract

The invention discloses a non-intumescent latex fireproof paint which comprises the following components in parts by weight: 40-60 parts of polyisobutyl ester, 20-40 parts of aluminum hydroxide, 12-24 parts of phosphotriester, 12-18 parts of antimony trioxide, 4-12 parts of asbestos fiber, 20-30 parts of graphite nodule, 16-18 parts of vanadium trioxide, 10-20 parts of azo-dicarbonamide, 4-12 parts of benzoperoxide, 12-24 parts of isopropanol, 4-8 parts of isopropyl acrylate and 8-12 parts of butyl acetate. The non-intumescent latex fireproof paint disclosed by the invention is simple to prepare, adopts nontoxic production raw materials, and has the advantages of favorable use effect and environmental protection. The paint coating can not be self-ignited, and can release fire-extinguishing gas and isolate air under the condition of flame or high temperature, thereby achieving the goal of fire resistance.

Description

Non-expansive latex fire-retardant paint

Technical field

The present invention relates to a kind of technical field of chemical article, be specifically related to Non-expansive latex fire-retardant paint.

Background technology

The effect of coating in production and life is very large; widespread use and every field; the film that coating is formed can play decoration, protection and beautiful effect to object; although current most of coating on the market makes simply, price is cheap but function ratio is more single simultaneously; can only simply as the use of decoration; and in the operating environment that some are special, can not meeting needed for people of simple coating.

Summary of the invention

Object of the present invention provides Non-expansive latex fire-retardant paint, solves one or more in above-mentioned prior art problem.

According to an aspect of the present invention, Non-expansive latex fire-retardant paint, comprises the component of following weight part,

Poly-isobutyl ester 40 ~ 60 parts, 20 ~ 40 parts, aluminium hydroxide, phosphotriester 12 ~ 24 parts, antimonous oxide 12 ~ 18 parts, fibrous magnesium silicate 4 ~ 12 parts, graphite pebbles 20 ~ 30 parts, vanadous oxide 16 ~ 18 parts, azodicarbonamide 10 ~ 20 parts, benzoyl peroxide 4 ~ 12 parts, Virahol 12 ~ 24 parts, isopropyl acrylate 4 ~ 8 parts, butylacetate 8 ~ 12 parts.

Non-expansive latex fire-retardant paint provided by the invention, makes simple, and the raw materials for production of employing are selected avirulent, the result of use of coating is good, environmental protection, and paint coatings is difficult to own combustion, can fire-suppressant gas be discharged and air-isolation simultaneously under flame or high temperature, thus reach fp object.

Embodiment

Embodiment 1

Isobutyl ester 40 parts will be gathered, 20 parts, aluminium hydroxide, phosphotriester 12 parts, antimonous oxide 12 parts, fibrous magnesium silicate 4 parts, graphite pebbles 20 parts, vanadous oxide 16 parts, azodicarbonamide 10 parts, benzoyl peroxide 4 parts, Virahol 12 parts, isopropyl acrylate 4 parts, butylacetate 8 parts puts into reactor, constantly stirs, mix complete post-heating to 65 DEG C, after uniform stirring, namely obtain product.

Embodiment 2

Isobutyl ester 50 parts will be gathered, 30 parts, aluminium hydroxide, phosphotriester 18 parts, antimonous oxide 15 parts, fibrous magnesium silicate 8 parts, graphite pebbles 25 parts, vanadous oxide 17 parts, azodicarbonamide 15 parts, benzoyl peroxide 8 parts, Virahol 18 parts, isopropyl acrylate 6 parts, butylacetate 10 parts puts into reactor, constantly stirs, mix complete post-heating to 65 DEG C, after uniform stirring, namely obtain product.

Embodiment 3

Isobutyl ester 60 parts will be gathered, 40 parts, aluminium hydroxide, phosphotriester 24 parts, antimonous oxide 18 parts, fibrous magnesium silicate 12 parts, graphite pebbles 30 parts, vanadous oxide 18 parts, azodicarbonamide 20 parts, benzoyl peroxide 12 parts, Virahol 24 parts, isopropyl acrylate 8 parts, butylacetate 12 parts puts into reactor, constantly stirs, mix complete post-heating to 65 DEG C, after uniform stirring, namely obtain product.

The above is only optimal way of the present invention; it should be pointed out that to those skilled in the art, without departing from the concept of the premise of the invention; can also make some similar distortion and improvement, these also should be considered as within protection scope of the present invention.

Claims (1)

1. Non-expansive latex fire-retardant paint, is characterized in that: the component comprising following weight part,

Poly-isobutyl ester 40 ~ 60 parts, 20 ~ 40 parts, aluminium hydroxide, phosphotriester 12 ~ 24 parts, antimonous oxide 12 ~ 18 parts, fibrous magnesium silicate 4 ~ 12 parts, graphite pebbles 20 ~ 30 parts, vanadous oxide 16 ~ 18 parts, azodicarbonamide 10 ~ 20 parts, benzoyl peroxide 4 ~ 12 parts, Virahol 12 ~ 24 parts, isopropyl acrylate 4 ~ 8 parts, butylacetate 8 ~ 12 parts.