CN105040249A - Heterogeneous fiber towel fabric and processing method thereof - Google Patents

Heterogeneous fiber towel fabric and processing method thereof Download PDF

Info

Publication number
CN105040249A
CN105040249A CN201510416074.8A CN201510416074A CN105040249A CN 105040249 A CN105040249 A CN 105040249A CN 201510416074 A CN201510416074 A CN 201510416074A CN 105040249 A CN105040249 A CN 105040249A
Authority
CN
China
Prior art keywords
raw material
towel fabric
terylene thread
cloth
silk
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510416074.8A
Other languages
Chinese (zh)
Inventor
钟海
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU BETTER CLEAN TEXTILE CO Ltd
Original Assignee
SUZHOU BETTER CLEAN TEXTILE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU BETTER CLEAN TEXTILE CO Ltd filed Critical SUZHOU BETTER CLEAN TEXTILE CO Ltd
Priority to CN201510416074.8A priority Critical patent/CN105040249A/en
Publication of CN105040249A publication Critical patent/CN105040249A/en
Pending legal-status Critical Current

Abstract

The invention discloses heterogeneous fiber towel fabric and a processing method thereof, and belongs to the technical field of knitted fabric. The heterogeneous fiber towel fabric comprises bottom yarn weave and surface yarn weave, the raw materials of the bottom yarn weave are 150D/144F DTY polyester yarns and 100D/48F FDY polyester yarns, the raw materials of the surface yarn weave are 150-300D/48-96F polyester cationic yarns, 150-300D/288F polyester yarns and 150-300D/72-144F polyester/polyamide compound yarns, the raw materials of the bottom yarn weave account for 32-38% of the towel fabric, and the raw materials of the surface yarn weave account for 62-68% of the towel fabric. The processing method comprises the steps of raw material selection, warping and weaving, splitting, dyeing, washing, dehydration, drying and shaping. After one-bath process dyeing is conducted, regular and color-gradient strip patterns with shade cycle alternation of one same color are formed at least one face of the towel fabric, the excellent stereoscopic feeling is embodied, the grade of a product is significantly promoted, and a good washable effect is embodied.

Description

Dissimilar fibers towel fabric and processing method thereof
Technical field
The invention belongs to knit fabric technical field, be specifically related to a kind of dissimilar fibers towel fabric, and relate to its processing method.
Background technology
The superfine fibre towel that towel, particularly surface are formed with pile loop both can be used as daily living article as kitchen, can be used for again public place as teahouse, beverage and even hotel and wineshop, etc.In order to give towel certain aesthetic feeling, usually the towel fabric being used for making towel is formed double-colored and even more rich colors.
As is known in the industry, the color of towel fabric is formed with colouring method usually in fabric process, such as when towel fabric will be made to possess the color and luster of two kinds or more, then to complete and through the dyeing stage by stage of twice or more after fibrillation at weaving process, one of self-evident shortcoming of this method, due to cannot by single bath process namely cannot with formation two kinds or more of once dyeing and there is the clearly demarcated color and luster of stereovision, thus technological process is tediously long and affect the working (machining) efficiency of towel fabric; Two, because dyestuff consumption is large, be thus unfavorable for embodying economizing on resources and ensureing the cheapness of towel fabric; Three, because the quantity of number of times and the color and luster of dyeing is in the relation of following in sb's footsteps, again because dyeing is what to carry out in the dye bath of heating, be thus unfavorable for reduction energy consumption; Four, because dyeing can exist colour contamination situation stage by stage, dyestuff when once dyeing after so-called colour contamination situation refers to can produce interference effect to the front color and luster once dyeed, and makes towel fabric occur look flower, final impact, as the quality of finished product towel, even causes defective product.
The TECHNICAL INFORMATION SOURCES of towel fabric and production method thereof can be seen in disclosed Chinese patent literature, typical recommend to have " Ultrahigh-elasticityextensible extensible towel and manufacture method thereof " as CN103015001B, the towel cloth that this patent formula obtains is particularly suitable for carwash industry (specifically can see the 0015th section, description) because having the elasticity of excellence.Especially, because the ground of this patent formula is coated through have employed low elastic polyester filament/superelevation bullet thick dawn spandex thread, low elastic polyester filament/superelevation bullet thick dawn spandex thread wrap yarn adopts (140-210) D/(1-24) the superelevation bullet spandex thread of F is as inner core, ground weft have employed low elastic polyester filament, front looped pile warp is Cationic Dyeable Pet fabric of island-in-sea type composite superfine terylene thread, reverse side looped pile through be ordinary polyester fabric of island-in-sea type composite superfine terylene thread (warp and front looped pile warp, the arrangement ratio of reverse side looped pile warp is 2: 1: 1 or 2: 2: 2), so when adopting the secondary color dyeing of cation dyes single bath process low temperature dye, the depth that can obtain the positive and negative of towel and front and reverse side is heterochromatic, specifically by cation dyes, Cationic Dyeable Pet fabric of island-in-sea type composite superfine terylene thread is dyed dark color, and ordinary polyester fabric of island-in-sea type composite superfine terylene thread can be dyed to the light color of same colour system because of staining.
Although above-mentioned patent formula gives the enlightenment (front color and luster is significantly deeper than back side color and luster) utilizing fiber of different nature to be able to obtain the color and luster with the different depth in two sides in one-bath dyeing to look rate of the eating difference (namely to the sensitive difference of dyestuff) of same dyestuff, but, the dyeing towel cloth that this patent formula obtains only can form single color and luster on same surface and cannot embody the double-colored of circulation gradual change or multicolour effect, namely the front of towel fabric and/or the existing regular periodicity gradient color effect repeatedly of back side bulk cannot be made, and gradient color effect sets off towel fabric third dimension exactly and promote fabric class and use and embody the key factor of added value.So-called gradient color refer to by homogencous dyes and the same surface presentation depth relying on one-bath dyeing and make towel fabric alternately namely by dark and shallow cycle alternation and the well-bedded homochromy strip pattern of color and luster.But be showed no all technology enlightenments being formed the towel fabric with aforementioned style in China and foreign countries' patent and non-patent literature disclosed in up to now.
For above-mentioned prior art, the applicant has done positive and useful exploration, have found the way solved the problems of the technologies described above, and defines technical scheme described below.
Summary of the invention
Top priority of the present invention is that providing a kind of contributes to being formed the gradient color strip pattern of regular depth cycle alternation and use the third dimension and the dissimilar fibers towel fabric of remarkable improving product class that embody excellence.
Another task of the present invention is the processing method providing a kind of dissimilar fibers towel fabric, and this processing method can ensure comprehensive embodiment of the described technique effect of described dissimilar fibers towel fabric and have the strong and washable effect of dyeing COLOR FASTNESS.
For having embodied top priority of the present invention, technical scheme provided by the invention is: a kind of dissimilar fibers towel fabric, comprise bottom silk organization and surface silk organization, the raw material of described bottom silk organization is the DTY terylene thread of 150D/144F and the FDY terylene thread of 100D/48F; The raw material of described surface silk organization be 150-300D/48-96F entirely wash CATION silk, the terylene thread of 150-300D/288F and the polyamide composite filaments of 150-300D/72-144F; The mass percent that the raw material of described bottom silk organization is shared in described towel fabric is 32-38%, and the mass percent of the raw material of described surface silk organization shared by towel fabric is 62-68%.
In a specific embodiment of the present invention, the DTY terylene thread of described 150D/144F and the FDY terylene thread of the described 100D/48F mass percent shared by the raw material of described bottom silk organization is respectively 1/2nd of described 32-38%; CATION silk, the terylene thread of 150-300D/288F and the polyamide composite filaments of the 150-300D/72-144F mass percent shared in the raw material of described surface silk organization of entirely washing of described 150-300D/48-96F is respectively 1/3rd of described 62-68%.
For having embodied another task of the present invention, technical scheme provided by the invention has been: a kind of processing method of dissimilar fibers towel fabric, comprises the following steps:
A) raw material is selected, choose the DTY terylene thread of 150D/144F and the FDY terylene thread of the 100D/48F raw material as bottom silk organization, that chooses 150D-300D/48-96F washs CATION silk, the terylene thread of 150-300D/288F and the polyamide composite filaments of the 150-300D/72-144F raw material as surface silk organization simultaneously entirely, the mass percent that the raw material of described bottom silk organization is shared in described towel fabric is 32-38%, and the mass percent of the raw material of described surface silk organization shared by towel fabric is 62-68%, obtain raw material;
B) warping and weaving, first by by steps A) raw material that obtains carries out warping, wherein, the raw material of surface silk organization, L4: form one group with the order arrangement of entirely washing CATION silk, the terylene thread of 1 to 24 150-300D/288F and the polyamide composite filaments of 1 to 24 150-300D/72-144F of 1 to 24 150-300D/48-96F and circulate according to this, the raw material of bottom silk organization, the DTY terylene thread of L2:150D/144F, the FDY terylene thread of L3:100D/48F, be put to loom after completing warping again weave, obtain grey cloth;
C) fibrillation, to by step B) the grey cloth fibrillation that obtains and control the technological parameter of fibrillation, obtain waiting to dye cloth;
D) dye, to by step C) obtain wait to dye cloth and dye, and control the technological parameter of dyeing, obtain stained clot-h;
E) wash, dehydration and dry, to by step D) stained clot-h that obtains washes, carries out dewatering and drying, obtain undetermined type cloth after washing;
F) shape, by by step e) the undetermined type cloth that obtains introduces setting machine sizing and controls setting temperature and control the gait of march of cloth, going out setting machine, rolling, obtain dissimilar fibers towel fabric.
In another specific embodiment of the present invention, step B) described in be woven as and make through braiding or weft knitting is weaved.
In another specific embodiment of the present invention, step C) described in the technological parameter of control fibrillation refer to: to being furnished with heater and filling the liquid caustic soda adding 0.1-0.14g/L in the fibrillation groove of water, the mass percent concentration of this liquid caustic soda is 10-14%, described grey cloth is introduced in fibrillation groove, and keep 35-45min at the temperature of 110-120 DEG C.
In another specific embodiment of the present invention, step D) described in the technological parameter of control dyeing be: first in dyeing container, add dyestuff a) 0.015-0.025g/L, dyestuff b) 0.003-0.0036g/L and dyestuff c) 0.002-0.003g/L, introducing dye bath dyeing of dying cloth is waited again by described, dyeing temperature controls as 120-140 DEG C, and dyeing time controls as 25-35min.
Also have in a specific embodiment of the present invention, step e) described in time of washing be 15-30min, the temperature of described oven dry is 130-140 DEG C, and the gait of march of the cloth when drying is 15-20m/min.
More of the present invention and in a specific embodiment, step F) described in control setting temperature be 155-165 DEG C by setting temperature, the gait of march of described control cloth is 25-40m/min by the gait of march of cloth.
In an of the present invention and then specific embodiment, described dyestuff a), b) and c) is cation dyes.
More of the present invention and in a specific embodiment, described dyestuff a) for S-GL is bright blue, described dyestuff b) for CRE sapphire blue, described dyestuff c) be that 6GF is yellow.
Owing to being selected by the raw material of surface silk organization, technical scheme provided by the invention has used that 150-300D/48-96F's wash CATION silk, the terylene thread of 150-300D/288F and the polyamide composite filaments of 150-300D/72-144F entirely, and because these three kinds of silks belong to the different dissimilar fibers silk of dye uptake, thus can be formed the gradient color strip pattern of regular depth cycle alternation by same color at least one side of towel fabric after one-bath dyeing, both excellent third dimension can have been embodied, again can the class of remarkable improving product; The processing method provided can ensure excellent COLOR FASTNESS and use the good washable effect of embodiment.
Accompanying drawing explanation
Fig. 1 is the process chart of the inventive method.
Fig. 2 is that the inventive method is by the fabric construction schematic diagram making the dissimilar fibers towel fabric of acquisition through braiding.
Fig. 3 is the inventive method is weaved the dissimilar fibers towel fabric of acquisition fabric construction schematic diagram by weft knitting.
Detailed description of the invention
embodiment 1:
Refer to Fig. 1 and Fig. 2, process the dissimilar fibers towel fabric of fabric construction as shown in Figure 2 by step as shown in Figure 1.
A) raw material is selected, choose the DTY terylene thread of 150D/144F and the FDY terylene thread of the 100D/48F raw material as bottom silk organization, the mass percent that the raw material of this bottom silk organization is shared in towel fabric is 38%, that chooses 150D/48F washs CATION silk simultaneously entirely, the terylene thread of 150D/288F and the polyamide composite filaments of 150D/72F are as the raw material of surface silk organization, the mass percent that the raw material of this surface silk organization is shared in towel fabric is 62%, wherein: the DTY terylene thread of described 150D/144F and the FDY terylene thread of 100D/48F respectively account for described 38% 1/2nd in the raw material of bottom silk organization, namely respectively 19% is accounted for, described 150D/48F washs CATION silk entirely, the terylene thread of 150D/288F and the polyamide composite filaments three of 150D/72F respectively account for described 62% 1/3rd at the raw material of surface silk organization, namely respectively 20.666% is accounted for, obtain raw material,
B) warping and weaving, first by by steps A) raw material that obtains is preferably but not adopt the model of being produced by Jiangsu Province, China Changzhou City No.8 Textile Machinery Plant to be that GE203 type computer-controlled high speed warping machines carries out warping with being definitely limited to, the technological parameter of warping is, the raw material of surface silk organization: L4 washs CATION silk entirely with 8 150D/48F's, the order of the polyamide composite filaments of the terylene thread of 8 150D/288F and 8 150D/72F is arranged in one group and circulates according to this, the raw material of bottom silk organization, the DTY terylene thread of L2:150D/144F, the FDY terylene thread of L3:100D/48F, be put to loom after completing warping make through braiding, obtain grey cloth, loom described in this step preferably adopts to be produced by Changde Textile Machinery Co., Ltd. of Hunan China province and the model of selling is that GE2-28M/C-136E24 type is through weft knitting machines,
C) fibrillation, to by step B) the grey cloth fibrillation that obtains, the technological parameter of this fibrillation is as follows: to being furnished with heater and filling in the fibrillation groove (i.e. fibrillation container) of water that to add mass percent concentration be add 0.14g in the every premium on currency of 0.14g/L(of 10%) liquid caustic soda, grey cloth is introduced in fibrillation groove, and at 120 DEG C, keep 35min, go out fibrillation groove, obtain waiting to dye cloth;
D) dye, to by step C) obtain wait to dye cloth and dye, the technological parameter of this dyeing is: in dyeing container, first add dyestuff a) namely adds in the bright blue 0.015g/L(of S-GL and every premium on currency and add 0.15g, below duplicate), dyestuff b) and the sapphire blue 0.0033g/L of CRE and dyestuff c) i.e. the yellow 0.003g/L of 6GF, introducing dye bath dyeing of dying cloth is waited again by described, it is 140 DEG C that dyeing temperature controls, and dyeing time controls, for 25min, to obtain stained clot-h;
E) wash, dewater and dry, to by step D) stained clot-h that obtains adopts centrifugal dehydrator dehydration, wash after dehydration, washing time is 20min, introducing the model of preferably being produced by plump dyeing and finishing machinery Co., Ltd of Jiangsu Province, China Jiangyin City after washing is FR-III type drying machine drying, bake out temperature is 130 DEG C, and the gait of march of cloth is 15m/min, obtains undetermined type cloth;
F) shape, by by step e) the undetermined type cloth that obtains introduces and preferably to be produced by Shengzhou, Shaoxin City of Zhejiang Province, China province municipal one-tenth dyeing machine Science and Technology Ltd. and the model of selling is ZAMB768 type setting machine shapes, setting temperature is 160 DEG C, the gait of march of cloth is 32m/min, go out setting machine, rolling, obtains fabric construction dissimilar fibers towel fabric as shown in Figure 2.When this dissimilar fibers towel fabric being made towel, so open cut down and merge by edge machine tape edge by driving sanction machine, concrete as: by the specification driving sanction machine and cut into 40 × 40 ㎝, bound off by serger again and make, obtain towel, under this towel using state side toward the outside have light blue, navy blue and more these three kinds of color and lusters of navy blue be one group and gradient color strip blue color patterns in regular cycle alternation (being alternately repeatedly).
embodiment 2:
Only by steps A) in the raw material of bottom silk organization and the mass percent shared in towel fabric of the FDY terylene thread of the DTY silk of 150D/144F and 100D/48F change 32% into, by 150D/48F entirely wash that CATION silk uses 300D/96F instead entirely wash CATION silk, the terylene thread of 150D/288F is used instead the terylene thread of 300D/288F, and the polyamide composite filaments of 150D/72F is used instead the polyamide composite filaments of 300D/144F, and the mass percent that the raw material of surface silk organization is shared in towel raw material changes 68% into, the DTY terylene thread of 150D/144F and the FDY terylene thread of 100D/48F respectively account for described 32% 1/2nd in the raw material of bottom silk organization, namely respectively 16% is accounted for, 300D/96F washs CATION silk entirely, the terylene thread of 300D/288F and the polyamide composite filaments three of 300D/144F respectively account for described 68% 1/3rd in the raw material of surface silk organization, namely respectively 22.66% is accounted for, only by step B) the raw material of surface silk organization: L4 is arranged in one group with the order of entirely washing CATION silk, the terylene thread of 24 300D/288F and the polyamide composite filaments of 24 300D/144F of 24 300D/96F and circulates according to this, only by step c) in the consumption of liquid caustic soda change 0.1% into, and change the mass percent concentration of liquid caustic soda into 14%, temperature changed into 115 DEG C, the retention time will change 40min into, only by step D) described in the bright blue consumption of S-GL change 0.025g/L into, change consumption sapphire blue for CRE into 0.003g/L, change the consumption of 6GF Huang into 0.002g/L, dyeing temperature is changed into 120 DEG C, change dyeing time into 35min, only by step e) in washing time change 30min into, bake out temperature is changed into 140 DEG C, and changes the gait of march of cloth into 20m/mi, only by step F) in setting temperature change 155 DEG C into, and change the gait of march of cloth into 25m/min.All the other are all with the description to embodiment 1.
embodiment 3:
Only by steps A) in the raw material of bottom silk organization and the mass percent shared in towel fabric of the FDY terylene thread of the DTY silk of 150D/144F and 100D/48F change 35% into, CATION silk is entirely washed by 150D/48F, the terylene thread of 300D/288F and the polyamide composite filaments of 300D/144F are as the raw material of surface silk organization, and the mass percent that the raw material of surface silk organization is shared in towel raw material changes 65% into, the DTY terylene thread of 150D/144F and the FDY terylene thread of 100D/48F respectively account for described 35% 1/2nd in the raw material of bottom silk organization, namely respectively 17.5% is accounted for, 150D/48F washs CATION silk entirely, the terylene thread of 300D/288F and the polyamide composite filaments three of 300D/144F respectively account for described 65% 1/3rd in the raw material of surface silk organization, namely respectively 21.66% is accounted for, only by step B) the raw material of surface silk organization: L4 is arranged in one group with the order of entirely washing CATION silk, the terylene thread of 5 300D/288F and the polyamide composite filaments of 5 300D/144F of 5 150D/48F and circulates according to this, only by step c) in the consumption of liquid caustic soda change 0.12% into, and change the mass percent concentration of liquid caustic soda into 12%, temperature changed into 110 DEG C, the retention time will change 45min into, only by step D) described in the bright blue consumption of S-GL change 0.018g/L into, change consumption sapphire blue for CRE into 0.0036g/L, change the consumption of 6GF Huang into 0.0025g/L, dyeing temperature is changed into 130 DEG C, change dyeing time into 30min, only by step e) in washing time change 15min into, bake out temperature is changed into 135 DEG C, and changes the gait of march of cloth into 18m/mi, only by step F) in setting temperature change 165 DEG C into, and change the gait of march of cloth into 40m/min.All the other are all with the description to embodiment 1.
embodiment 4:
Only by steps A) in the raw material of surface silk organization change 300D/96F into entirely wash CATION silk, the terylene thread of 150D/288F and the polyamide composite filaments of 150D/72F, the mass percent that the raw material of bottom silk organization is shared in towel fabric changes 36% into, and the mass percent that the raw material of surface silk organization is shared in towel fabric changes 64% into; By step B) in L4 be arranged in one group with the polyamide composite filaments order of entirely washing CATION silk, the terylene thread of 12 150D/288F and 150D/72F of 12 300D/96F and circulate successively.All the other are all with the description to embodiment 1.
embodiment 5:
Ask for an interview Fig. 3 and continue composition graphs 1, processing the dissimilar fibers towel fabric of fabric construction as shown in Figure 3 by step as shown in Figure 1.
A) raw material is selected, choose the DTY terylene thread of 150D/144F and the FDY terylene thread of the 100D/48F raw material as bottom silk organization, the mass percent that the raw material of this bottom silk organization is shared in towel fabric is 34%, that chooses 150D/48F washs CATION silk simultaneously entirely, the terylene thread of 150D/288F and the polyamide composite filaments of 150D/72F are as the raw material of surface silk organization, the mass percent that the raw material of this surface silk organization is shared in towel fabric is 66%, wherein: the DTY terylene thread of described 150D/144F and the FDY terylene thread of 100D/48F respectively account for described 34% 1/2nd in the raw material of bottom silk organization, namely respectively 17% is accounted for, described 150D/48F washs CATION silk entirely, the terylene thread of 150D/288F and the polyamide composite filaments three of 150D/72F respectively account for described 66% 1/3rd at the raw material of surface silk organization, namely respectively 22% is accounted for, obtain raw material,
B) warping and weaving, first by by steps A) raw material that obtains is preferably but not adopt the model of being produced by Jiangsu Province, China Changzhou City No.8 Textile Machinery Plant to be that GE203 type conputer controlled adjustment warping machines carries out warping with being definitely limited to, the technological parameter of warping is, the raw material of surface silk organization: L4 is arranged in one group with the order of entirely washing CATION silk, the terylene thread of 10 150D/288F and the polyamide composite filaments of 10 150D/7F of 10 150D/48F and circulates according to this, L1; The terylene thread of 150D/144F is as the raw material of bottom silk organization, the DTY terylene thread of L2:150D/144F, the FDY terylene thread of L3:100D/48F, be put to loom weft braiding after completing warping make, obtain weft-knitted grey cloth, the loom described in this step preferably adopts to be produced by Changde Textile Machinery Co., Ltd. of Hunan China province and the model of selling is that GE2-28M/C-136E24 type is through weft knitting machines;
C) fibrillation, to by step B) the grey cloth fibrillation that obtains, the technological parameter of this fibrillation is as follows: to being furnished with heater and filling in the fibrillation groove (i.e. fibrillation container) of water that to add mass percent concentration be add 0.14g in the every premium on currency of 0.13g/L(of 13%) liquid caustic soda, grey cloth is introduced in fibrillation groove, and at 118 DEG C, keep 38min, go out fibrillation groove, obtain waiting to dye cloth;
D) dye, to by step C) obtain wait to dye cloth and dye, the technological parameter of this dyeing is: in dyeing container, first add dyestuff a) namely adds in the bright blue 0.022g/L(of S-GL and every premium on currency and add 0.022g, below duplicate), dyestuff b) and the sapphire blue 0.0032g/L of CRE and dyestuff c) i.e. the yellow 0.0026g/L of 6GF, introducing dye bath dyeing of dying cloth is waited again by described, it is 125 DEG C that dyeing temperature controls, and dyeing time controls, for 28min, to obtain stained clot-h;
E) wash, dewater and dry, to by step D) stained clot-h that obtains adopts centrifugal dehydrator dehydration, wash after dehydration, washing time is 25min, introducing the model of preferably being produced by plump dyeing and finishing machinery Co., Ltd of Jiangsu Province, China Jiangyin City after washing is FR-III type drying machine drying, bake out temperature is 138 DEG C, and it is 19m/min that the ground of cloth enters speed, obtains undetermined type cloth;
F) shape, by by step e) the undetermined type cloth that obtains introduce preferably by Chinese Shengzhou municipal one-tenth dyeing machine Science and Technology Ltd. produce and the model of selling is ZAMB768 type setting machine shapes, setting temperature is 162 DEG C, the gait of march of cloth is 35m/min, go out setting machine, rolling, obtains fabric construction dissimilar fibers towel fabric as shown in Figure 3.When this dissimilar fibers towel fabric being made towel, so open cut down and merge by edge machine tape edge by driving sanction machine, concrete as: by the specification driving sanction machine and cut into 50 × 50 ㎝, bound off by serger again and make, obtain towel, enter under this towel using state with the side outside allusion quotation have light blue, navy blue and more these three kinds of color and lusters of navy blue be one group and gradient color strip blue color patterns in regular cycle alternation.
embodiment 6:
Relative to embodiment 5, only change as shown below: surface layer tissue and surface silk organization: L4 is one group putting in order entirely to wash CATION silk 150D/48F, terylene thread 150D/288F, entirely to wash CATION silk 150D/48F and polyamide composite filaments 150D/72F, every 16 rhizoids circulate, L1:150D/144F terylene thread, bottom fabric layer and bottom silk organization: L2:150D/144FDTY terylene thread, the FDY terylene thread of L3:100D/48F.All the other are all with the description to embodiment 5.
embodiment 7:
Relative to embodiment 6, only change as shown below: surface layer tissue and surface silk organization: L4 is one group putting in order entirely to wash CATION silk 150D/48F, terylene thread 150D/288F, entirely to wash CATION silk 150D/48F and polyamide composite filaments 150D/72F, every 9 rhizoids circulate, L1:150D/144F terylene thread, bottom fabric layer and bottom silk organization: L2:150D/144FDTY terylene thread, the FDY terylene thread of L3:100D/48F.All the other are all with the description to embodiment 5.

Claims (10)

1. a dissimilar fibers towel fabric, is characterized in that comprising bottom silk organization and surface silk organization, and the raw material of described bottom silk organization is the DTY terylene thread of 150D/144F and the FDY terylene thread of 100D/48F; The raw material of described surface silk organization be 150-300D/48-96F entirely wash CATION silk, the terylene thread of 150-300D/288F and the polyamide composite filaments of 150-300D/72-144F; The mass percent that the raw material of described bottom silk organization is shared in described towel fabric is 32-38%, and the mass percent of the raw material of described surface silk organization shared by towel fabric is 62-68%.
2. dissimilar fibers towel fabric according to claim 1, is characterized in that the DTY terylene thread of described 150D/144F and the mass percent of FDY terylene thread shared by the raw material of described bottom silk organization of described 100D/48F are respectively 1/2nd of described 32-38%; CATION silk, the terylene thread of 150-300D/288F and the polyamide composite filaments of the 150-300D/72-144F mass percent shared in the raw material of described surface silk organization of entirely washing of described 150-300D/48-96F is respectively 1/3rd of described 62-68%.
3. a processing method for dissimilar fibers towel fabric as claimed in claim 1, is characterized in that comprising the following steps:
A) raw material is selected, choose the DTY terylene thread of 150D/144F and the FDY terylene thread of the 100D/48F raw material as bottom silk organization, that chooses 150D-300D/48-96F washs CATION silk, the terylene thread of 150-300D/288F and the polyamide composite filaments of the 150-300D/72-144F raw material as surface silk organization simultaneously entirely, the mass percent that the raw material of described bottom silk organization is shared in described towel fabric is 32-38%, and the mass percent of the raw material of described surface silk organization shared by towel fabric is 62-68%, obtain raw material;
B) warping and weaving, first by by steps A) raw material that obtains carries out warping, wherein, the raw material of surface silk organization, L4: form one group with the order arrangement of entirely washing CATION silk, the terylene thread of 1 to 24 150-300D/288F and the polyamide composite filaments of 1 to 24 150-300D/72-144F of 1 to 24 150-300D/48-96F and circulate according to this, the raw material of bottom silk organization, the DTY terylene thread of L2:150D/144F, the FDY terylene thread of L3:100D/48F, be put to loom after completing warping again weave, obtain grey cloth;
C) fibrillation, to by step B) the grey cloth fibrillation that obtains and control the technological parameter of fibrillation, obtain waiting to dye cloth;
D) dye, to by step C) obtain wait to dye cloth and dye, and control the technological parameter of dyeing, obtain stained clot-h;
E) wash, dehydration and dry, to by step D) stained clot-h that obtains washes, carries out dewatering and drying, obtain undetermined type cloth after washing;
F) shape, by by step e) the undetermined type cloth that obtains introduces setting machine sizing and controls setting temperature and control the gait of march of cloth, going out setting machine, rolling, obtain dissimilar fibers towel fabric.
4. the processing method of dissimilar fibers towel fabric according to claim 3, is characterized in that step B) described in be woven as and make or weft knitting is weaved through braiding.
5. the processing method of dissimilar fibers towel fabric according to claim 3, it is characterized in that step C) described in the technological parameter of control fibrillation refer to: to being furnished with heater and filling the liquid caustic soda adding 0.1-0.14g/L in the fibrillation groove of water, the mass percent concentration of this liquid caustic soda is 10-14%, described grey cloth is introduced in fibrillation groove, and keep 35-45min at the temperature of 110-120 DEG C.
6. the processing method of dissimilar fibers towel fabric according to claim 3, it is characterized in that step D) described in the technological parameter of control dyeing be: first in dyeing container, add dyestuff a) 0.015-0.025g/L, dyestuff b) 0.003-0.0036g/L and dyestuff c) 0.002-0.003g/L, introducing dye bath dyeing of dying cloth is waited again by described, dyeing temperature controls as 120-140 DEG C, and dyeing time controls as 25-35min.
7. the processing method of dissimilar fibers towel fabric according to claim 3, is characterized in that step e) described in time of washing be 15-30min, the temperature of described oven dry is 130-140 DEG C, and the gait of march of cloth when drying is 15-20m/min.
8. the processing method of dissimilar fibers towel fabric according to claim 3, it is characterized in that step F) described in control setting temperature be 155-165 DEG C by setting temperature, the gait of march of described control cloth is 25-40m/min by the gait of march of cloth.
9. the processing method of dissimilar fibers towel fabric according to claim 6, is characterized in that described dyestuff a), b) and c) is cation dyes.
10. the processing method of the dissimilar fibers towel fabric according to claim 6 or 9, is characterized in that described dyestuff a) for S-GL is bright blue, described dyestuff b) for CRE sapphire blue, described dyestuff c) be that 6GF is yellow.
CN201510416074.8A 2015-07-16 2015-07-16 Heterogeneous fiber towel fabric and processing method thereof Pending CN105040249A (en)