CN105001722A - Waterborne multi-color coating with good weatherability - Google Patents
Waterborne multi-color coating with good weatherability Download PDFInfo
- Publication number
- CN105001722A CN105001722A CN201410598936.9A CN201410598936A CN105001722A CN 105001722 A CN105001722 A CN 105001722A CN 201410598936 A CN201410598936 A CN 201410598936A CN 105001722 A CN105001722 A CN 105001722A
- Authority
- CN
- China
- Prior art keywords
- parts
- good weatherability
- coating
- zinc
- calcined kaolin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a waterborne multi-color coating with good weatherability. The coating is composed of the following raw materials, by weight, 25-28 parts of styrolized polyester resin, 30-40 parts of a fluoro-silicon emulsion, 6-8 parts of calcined kaolin, 4-6 parts of ethylene glycol monobutyl ether, 12-14 parts of color paste, 0.8-1.2 parts of a preservative, 0.5-0.8 part of zinc tetroxy chromate, 1.5-1.8 parts of 30% sodium metaphosphate, 0.3-0.5 part of leaded zinc oxide, 0.2-0.5 part of an antifoaming agent, 0.3-0.6 part of titanium dioxide, 2.5-4.5 parts of a dispersant and 50-60 parts of water. The coating belongs to a high-grade decorative material. The coating has lucid and lively colors, has a strong three-dimensional sense, has oil painting characteristic, is nontoxic and odorless, has good weatherability and excellent properties, and can be applied by the use of a brush or a roller.
Description
Technical field
The present invention relates to decorative paint field, specifically belong to a kind of good weatherability aqueous colorful paint.
Background technology
Paint is that one firmly can cover body surface, plays protection, decoration, mark and the chemical mixture coating of other special purposes.Paint is thickness oil colour, inflammable in not dry situation, water insoluble, is slightly soluble in fat, dissolves in alcohol, aldehyde, ether, benzene, alkane, be soluble in gasoline, kerosene, diesel oil.
Kind is painted much in present market, but various paint is all made up of filmogen (various resin), solvent, pigment, siccative, additive.Common paint makes solvent with gasoline usually, and epoxy iron red shop primer is containing a small amount of dimethylbenzene, and dipping lacquer mainly containing toluene, also has a small amount of benzene, very large on human body impact.
Summary of the invention
The object of this invention is to provide a kind of good weatherability aqueous colorful paint, belong to high-grade finishing material, its color is lucid and lively, and stereoscopic sensation is strong, is rich in oil painting characteristic, has nontoxic, odorless, good weatherability, excellent performance feature, can brush, can roller coating.
The technical solution used in the present invention is as follows:
A good weatherability aqueous colorful paint, by weight, is made up of following raw material:
Styrenated polyesters resin 25-28, fluoro-silicone emulsion 30-40, calcined kaolin 6-8, butyl glycol ether 4-6, mill base 12-14, sanitas 0.8-1.2, zinc tetroxy chromate 0.5-0.8,30% sodium-metaphosphate 1.5-1.8, leaded zinc 0.3-0.5, defoamer 0.2-0.5, titanium dioxide 0.3-0.6, dispersion agent 2.5-4.5, water 50-60; Its concrete preparation method is as follows: in high-speed dispersing kettle, add water, styrenated polyesters resin, calcined kaolin, zinc tetroxy chromate, 30% sodium-metaphosphate, dispersion agent, the defoamer of 1/4th successively, stirring reaction 45-50 minute at 85-90 DEG C, then each raw material of residue is added, be reduced to 30-40 DEG C, 800-1000 rev/min of dispersed with stirring 38-45 minute, obtains this paint.
A kind of good weatherability aqueous colorful paint, by weight, be made up of following raw material: styrenated polyesters resin 26, fluoro-silicone emulsion 35, calcined kaolin 7, butyl glycol ether 5, mill base 13, sanitas 1, zinc tetroxy chromate 0.7,30% sodium-metaphosphate 1.6, leaded zinc 0.4, defoamer 0.4, titanium dioxide 0.5, dispersion agent 3, water 55.
Starting material of the present invention adopt styrenated polyesters resin, fluoro-silicone emulsion as film coalescence aid, not containing the objectionable impurities such as formaldehyde and trimethylbenzene, take water as solvent, coating chemical stability is good, can construct on the surface of humidity, has excellent tack, there is high resistance alkalescence, directly can be used as priming paint, floating coat, its color is lucid and lively, stereoscopic sensation is strong, be rich in oil painting characteristic, there is nontoxic, odorless, good weatherability, excellent performance feature, can brush, can roller coating.
Embodiment
A kind of good weatherability aqueous colorful paint, by weight, be made up of following raw material: styrenated polyesters resin 26, fluoro-silicone emulsion 35, calcined kaolin 7, butyl glycol ether 5, mill base 13, sanitas 1, zinc tetroxy chromate 0.7,30% sodium-metaphosphate 1.6, leaded zinc 0.4, defoamer 0.4, titanium dioxide 0.5, dispersion agent 3, water 55; Its concrete preparation method is as follows: in high-speed dispersing kettle, add water, styrenated polyesters resin, calcined kaolin, zinc tetroxy chromate, 30% sodium-metaphosphate, dispersion agent, the defoamer of 1/4th successively, stirring reaction 45-50 minute at 85-90 DEG C, then each raw material of residue is added, be reduced to 30-40 DEG C, 800-1000 rev/min of dispersed with stirring 38-45 minute, obtains this paint.
Claims (2)
1. a good weatherability aqueous colorful paint, by weight, is characterized in that, is made up of following raw material:
Styrenated polyesters resin 25-28, fluoro-silicone emulsion 30-40, calcined kaolin 6-8, butyl glycol ether 4-6, mill base 12-14, sanitas 0.8-1.2, zinc tetroxy chromate 0.5-0.8,30% sodium-metaphosphate 1.5-1.8, leaded zinc 0.3-0.5, defoamer 0.2-0.5, titanium dioxide 0.3-0.6, dispersion agent 2.5-4.5, water 50-60; Its concrete preparation method is as follows: in high-speed dispersing kettle, add water, styrenated polyesters resin, calcined kaolin, zinc tetroxy chromate, 30% sodium-metaphosphate, dispersion agent, the defoamer of 1/4th successively, stirring reaction 45-50 minute at 85-90 DEG C, then each raw material of residue is added, be reduced to 30-40 DEG C, 800-1000 rev/min of dispersed with stirring 38-45 minute, obtains this paint.
2. good weatherability aqueous colorful paints according to claim 1, it is characterized in that, be made up of following raw material: styrenated polyesters resin 26, fluoro-silicone emulsion 35, calcined kaolin 7, butyl glycol ether 5, mill base 13, sanitas 1, zinc tetroxy chromate 0.7,30% sodium-metaphosphate 1.6, leaded zinc 0.4, defoamer 0.4, titanium dioxide 0.5, dispersion agent 3, water 55.