CN105086744A - Crack-resistant woodenware paint - Google Patents
Crack-resistant woodenware paint Download PDFInfo
- Publication number
- CN105086744A CN105086744A CN201410598938.8A CN201410598938A CN105086744A CN 105086744 A CN105086744 A CN 105086744A CN 201410598938 A CN201410598938 A CN 201410598938A CN 105086744 A CN105086744 A CN 105086744A
- Authority
- CN
- China
- Prior art keywords
- parts
- crack
- resistant
- woodenware paint
- ethylene glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses crack-resistant woodenware paint. The crack-resistant woodenware paint, by weight, 30-40 parts of E-20 epoxy resin, 3.5-5.5 parts of short-oil alkyd resin, 1.5-2.0 parts of dioctyl phthalate, 5-8 parts of glycol, 10-12 parts of ultrafine powdered steatile, 0.3-1.2 parts of ethylene glycol ethyl ether, 0.2-0.5 parts of sodium hexametaphosphate, 0.3-3.0 parts of polyamide, 4-6 parts of silica fine sand, 0.4-1.5 parts of amide-modified hydrogenated castor oil, 5-7 parts of carbon black, 4-6 parts of silicon powder, 12-15 parts of acrylic acid emulsion and 46-50 parts of water. The crack-resistant woodenware paint utilizes cheap raw materials and contains less harmful chemical products. The dried crack-resistant woodenware paint can form a continuous coating, and the coating has good elongation percentage, breaking strength, acid resistance, base resistance, excellent weatherability, excellent crack resistance and no environmental pollution.
Description
Technical field
The present invention relates to decorative paint field, specifically belong to a kind of cracking resistance woodenware paint.
Background technology
Paint is that one firmly can cover body surface, plays protection, decoration, mark and the chemical mixture coating of other special purposes.Paint is thickness oil colour, inflammable in not dry situation, water insoluble, is slightly soluble in fat, dissolves in alcohol, aldehyde, ether, benzene, alkane, be soluble in gasoline, kerosene, diesel oil.
Kind is painted much in present market, but various paint is all made up of filmogen (various resin), solvent, pigment, siccative, additive.Common paint makes solvent with gasoline usually, and epoxy iron red shop primer is containing a small amount of dimethylbenzene, and dipping lacquer mainly containing toluene, also has a small amount of benzene, very large on human body impact.
Summary of the invention
The object of this invention is to provide a kind of cracking resistance woodenware paint, the prices of raw and semifnished materials are low, Harmful chemicals consumption is few, successional coating can be formed after paint drying, paint coating has good unit elongation and breaking tenacity, acidproof, alkali resistance good, have excellent weather resistance, the excellent property of cracking resistance, non-environmental-pollution.
The technical solution used in the present invention is as follows:
A cracking resistance woodenware paint, by weight, is made up of following raw material:
E-20 epoxy resin 30-40, short oil alkyd 3.5-5.5, dioctyl phthalate (DOP) 1.5-2.0, ethylene glycol 5-8, superfine talcum powder 10-12, ethylene glycol ethyl ether 0.3-1.2, Sodium hexametaphosphate 99 0.2-0.5, polymeric amide 0.3-3.0, silicon-dioxide fine sand 4-6, amide modifications hydrogenated castor oil 0.4-1.5, carbon black 5-7, silica flour 4-6, ACRYLIC EMULSION 12-15, water 46-50;
Its concrete preparation method is as follows:
By above-mentioned weight part, ACRYLIC EMULSION and Sodium hexametaphosphate 99, water are carried out suction header tank after pre-emulsification, another header tank of suction after E-20 epoxy resin, short oil alkyd, ethylene glycol water dissolution, two header tanks enter steel basin in the mode dripped simultaneously, and in steel basin, temperature controls at 70-80 degree, control rate of addition, reaction mass is dripped off at 2-3.5h, is then incubated 1-1.5h, then cool, cool rear and the abundant mix and blend of all the other raw materials, to obtain final product.
The present invention with E-20 epoxy resin for film coalescence aid, dimethylbenzene zero adds, the prices of raw and semifnished materials are low, Harmful chemicals consumption is few, successional coating can be formed after paint drying, paint coating has good unit elongation and breaking tenacity, acidproof, alkali resistance good, has excellent weather resistance, the excellent property of cracking resistance, non-environmental-pollution.
Embodiment
A cracking resistance woodenware paint, by weight, is made up of following raw material:
E-20 epoxy resin 30-40, short oil alkyd 3.5-5.5, dioctyl phthalate (DOP) 1.5-2.0, ethylene glycol 5-8, superfine talcum powder 10-12, ethylene glycol ethyl ether 0.3-1.2, Sodium hexametaphosphate 99 0.2-0.5, polymeric amide 0.3-3.0, silicon-dioxide fine sand 4-6, amide modifications hydrogenated castor oil 0.4-1.5, carbon black 5-7, silica flour 4-6, ACRYLIC EMULSION 12-15, water 46-50;
Its concrete preparation method is as follows:
By above-mentioned weight part, ACRYLIC EMULSION and Sodium hexametaphosphate 99, water are carried out suction header tank after pre-emulsification, another header tank of suction after E-20 epoxy resin, short oil alkyd, ethylene glycol water dissolution, two header tanks enter steel basin in the mode dripped simultaneously, and in steel basin, temperature controls at 70-80 degree, control rate of addition, reaction mass is dripped off at 2-3.5h, is then incubated 1-1.5h, then cool, cool rear and the abundant mix and blend of all the other raw materials, to obtain final product.
Claims (1)
1. a cracking resistance woodenware paint, by weight, is characterized in that, is made up of following raw material:
E-20 epoxy resin 30-40, short oil alkyd 3.5-5.5, dioctyl phthalate (DOP) 1.5-2.0, ethylene glycol 5-8, superfine talcum powder 10-12, ethylene glycol ethyl ether 0.3-1.2, Sodium hexametaphosphate 99 0.2-0.5, polymeric amide 0.3-3.0, silicon-dioxide fine sand 4-6, amide modifications hydrogenated castor oil 0.4-1.5, carbon black 5-7, silica flour 4-6, ACRYLIC EMULSION 12-15, water 46-50;
Its concrete preparation method is as follows:
By above-mentioned weight part, ACRYLIC EMULSION and Sodium hexametaphosphate 99, water are carried out suction header tank after pre-emulsification, another header tank of suction after E-20 epoxy resin, short oil alkyd, ethylene glycol water dissolution, two header tanks enter steel basin in the mode dripped simultaneously, and in steel basin, temperature controls at 70-80 degree, control rate of addition, reaction mass is dripped off at 2-3.5h, is then incubated 1-1.5h, then cool, cool rear and the abundant mix and blend of all the other raw materials, to obtain final product.