CN105001383A - 一种高强度树脂模具 - Google Patents
一种高强度树脂模具 Download PDFInfo
- Publication number
- CN105001383A CN105001383A CN201510416107.9A CN201510416107A CN105001383A CN 105001383 A CN105001383 A CN 105001383A CN 201510416107 A CN201510416107 A CN 201510416107A CN 105001383 A CN105001383 A CN 105001383A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- amine curing
- emulsifying agent
- curing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种高强度树脂模具，该模具材料按如下重量比配制：E51、E44或E42牌号中的任何一种环氧树脂为100；聚醚型聚氨酯为20-23；聚苯硫醚为10；酚醛树脂为15；二苯胺为12；聚磷酸铵为10；丙烯酸酯为55；增塑剂为5-25；胺类固化剂为5-20；H.L.B值13至15的乳化剂为5-40；水为150-250；细度为100目-1000目的填料为300-600。采用本发明的模具材料制作的高强度树脂模具作用寿命得以延长，不仅可以在夏天保持刚性，还能在寒冷的冬天保持韧性，使用温度范围广，强度高，耐腐蚀性强。
Description
技术领域
本发明涉及树脂模具领域，具体是一种高强度树脂模具。
背景技术
陶瓷压力注浆模具在工作时要承受最高压力为1.5MPa的泥浆的上万次交变应力作用，其温度为40℃左右；还要承受清洗时氧化剂的侵蚀。因此，制作陶瓷压力注浆成型模具的微通孔材料必须具有良好的耐湿热性、耐化学侵蚀性、较高的机械强度及良好的韧性。
然而随着季节的更替，有些地方冬天和夏天的温度差异很大，夏天温度过高，模具容易软化，而冬天温度过低，模具又会变得很硬很脆，非常容易发生破碎。
发明内容
本发明旨在提供一种高强度树脂模具，以满足不同温度环境下的工作需求。
为实现上述目的，本发明提供如下技术方案：一种高强度树脂模具，该模具材料按如下重量比配制：E51、E44或E42牌号中的任何一种环氧树脂为100；聚醚型聚氨酯为20-23；聚苯硫醚为10；酚醛树脂为15；二苯胺为12；聚磷酸铵为10；丙烯酸酯为55；增塑剂为5-25；胺类固化剂为5-20；H.L.B值13至15的乳化剂为5-40；水 为150-250；细度为100目-1000目的填料为300-600。
模具材料按如下重量比配制：环氧树脂E51为100；聚醚型聚氨酯为20；聚苯硫醚为10；酚醛树脂为15；二苯胺为12；聚磷酸铵为10；丙烯酸酯为55；增塑剂为22；胺类固化剂为14；H.L.B值13的乳化剂为35；水为180；细度为325目的填料为560。
所述增塑剂选用邻苯二甲酸二丁酯，胺类固化剂选用二乙烯三胺，乳化剂选用脂肪醇聚氧乙烯醚或烷基酚聚氧乙烯醚O/W型乳化剂，填料选用石英粉。
与现有技术相比，本发明的有益效果是：采用本发明的模具材料制作的高强度树脂模具作用寿命得以延长，不仅可以在夏天保持刚性，还能在寒冷的冬天保持韧性，使用温度范围广，强度高，耐腐蚀性强。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例一
一种高强度树脂模具，该模具材料按如下重量比配制：E51、E44或E42牌号中的任何一种环氧树脂为100；聚醚型聚氨酯为20-23；聚苯硫醚为10；酚醛树脂为15；二苯胺为12；聚磷酸铵为10；丙烯酸酯为55；增塑剂为5-25；胺类固化剂为5-20；H.L.B值13至15 的乳化剂为5-40；水为150-250；细度为100目-1000目的填料为300-600。
实施例二
模具材料按如下重量比配制：环氧树脂E51为100；聚醚型聚氨酯为20；聚苯硫醚为10；酚醛树脂为15；二苯胺为12；聚磷酸铵为10；丙烯酸酯为55；增塑剂为22；胺类固化剂为14；H.L.B值13的乳化剂为35；水为180；细度为325目的填料为560。
所述增塑剂选用邻苯二甲酸二丁酯，胺类固化剂选用二乙烯三胺，乳化剂选用脂肪醇聚氧乙烯醚或烷基酚聚氧乙烯醚O/W型乳化剂，填料选用石英粉。
先将环氧树脂、聚醚型聚氨酯为、聚苯硫醚为、酚醛树脂为、二苯胺为、聚磷酸铵为、丙烯酸酯、邻苯二甲酸二丁酯搅拌均匀，再加入二乙烯三胺作为固化剂搅拌均匀，然后加入H.L.B值13的脂肪醇聚氧乙烯醚或烷基酚聚氧乙烯醚O/W型乳化剂搅拌均匀，再加入水搅拌形成均匀乳液，最后加入填料搅拌均匀形成料浆，将料浆注入模型中。在常温下，环氧树脂固化后，脱模并通过预先设置在固化物中的孔道用水冲去可溶物，即形成微孔材料，其外形为预定地模具形状。采用本发明的模具材料制作的高强度树脂模具作用寿命得以延长，不仅可以在夏天保持刚性，还能在寒冷的冬天保持韧性，使用温度范围广，强度高，耐腐蚀性强。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其 他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
Claims (3)
1.一种高强度树脂模具，其特征在于，该模具材料按如下重量比配制：E51、E44或E42牌号中的任何一种环氧树脂为100；聚醚型聚氨酯为20-23；聚苯硫醚为10；酚醛树脂为15；二苯胺为12；聚磷酸铵为10；丙烯酸酯为55；增塑剂为5-25；胺类固化剂为5-20；H.L.B值13至15的乳化剂为5-40；水为150-250；细度为100目-1000目的填料为300-600。
2.根据权利要求1所述的一种高强度树脂模具，其特征在于，模具材料按如下重量比配制：环氧树脂E51为100；聚醚型聚氨酯为20；聚苯硫醚为10；酚醛树脂为15；二苯胺为12；聚磷酸铵为10；丙烯酸酯为55；增塑剂为22；胺类固化剂为14；H.L.B值13的乳化剂为35；水为180；细度为325目的填料为560。
3.根据权利要求1或2所述的一种高强度树脂模具，其特征在于，所述增塑剂选用邻苯二甲酸二丁酯，胺类固化剂选用二乙烯三胺，乳化剂选用脂肪醇聚氧乙烯醚或烷基酚聚氧乙烯醚O/W型乳化剂，填料选用石英粉。