CN104974673A - Shoe polish - Google Patents

Abstract

The invention discloses shoe polish comprising the following components: carnauba wax, microcrystalline wax, white pine oil, dimethyl silicone oil, stearic acid, triethanolamine, fatty alcohol-polyoxyethylene ether, sodium hexametaphosphate, sodium oleoyl amino fatty acid, a preservative A26, a butadiene resin film-forming agent, a pigment and deionized water. When the shoe polish is used for polishing shoes, the shoe polish can form a wax film being excellent in waterproof performance after shoes being uniformly wiped by a clean soft cloth, so that the shoes are durable in glossiness. The wax film also has an excellent wiping resistant performance.

Description

A kind of shoe polish

Technical field

The present invention relates to a kind of chemical products, particularly a kind of ointment shape shoe cream.

Background technology

Shoe polish is a kind of in order to polish, to repair leather shoes or leather boots, and strengthens the product of its anti-waterpower, can extend the life-span of footwear.Shoe polish is wax oil or paste normally, is the preparation that a kind of wiping leather shoe surface makes it clean light, and have liquid state, semisolid, solid-state dividing, main component is all wax.Leather shoes need routine maintenance, the light of guarantee leather, or the leather shoes newly bought, and because it is in making processes, due to infrared rays baking, can lose grease and the moisture of leather shoes inside.Footwear main body of oil is wax and oil, when shoe polish wiped Tu on leather after, oil can be seeped in skin, and to protect the plump and soft of leather, wax is trapped on vamp and forms very thin one deck cere, can play water proof anti-soil and protection vamp effect.Then by the wiping of footwear cloth, wax layer is made to have good smooth finish.

Summary of the invention

The object of the invention is the cere water resisting property after solving shoe polish wiping poor, the problem that the foreign material such as some koniology make gloss impermanent is easily adsorbed on surface.

The technical solution used in the present invention is: a kind of shoe polish, it is characterized in that comprising component carnauba wax, Microcrystalline Wax, white pine oil, dimethyl silicone oil, stearic acid, trolamine, fatty alcohol-polyoxyethylene ether, Sodium hexametaphosphate 99, oleoyl amino acid sodium, sanitas A26, butadiene resin membrane-forming agent, pigment and deionized water, each component in mass ratio example is: 20:15:3:7:18:1.2:6.8:0.08:1.9:0.49:1:2:23.6;

Making step:

(1), in belt stirrer and heatable reactor add carnauba wax, Microcrystalline Wax, stearic acid, dimethyl silicone oil and white pine oil, be heated to 80-85 DEG C, stir after each component is all dissolved;

(2), in the container of the agitator of another said function, add deionized water, trolamine, fatty alcohol-polyoxyethylene ether, sanitas A26, oleoyl amino acid sodium, be heated to 70-75 DEG C;

(3), under constantly stirring the mixed solution of step 2 gained is added in the mixed solution of step 1 gained, then add Sodium hexametaphosphate 99, butadiene resin membrane-forming agent and pigment and stir and namely make finished product, canned after being cooled to 40 DEG C.

The invention has the beneficial effects as follows: use this shoe polish to brush, wipe the cere water resisting property evenly with the soft cloth of cleaning excellent, vamp is for a long time bright and clean; Cere also has good erasibility.

Embodiment

Embodiment 1:

(1), in belt stirrer and heatable reactor add 20kg carnauba wax, 15kg Microcrystalline Wax, 18kg stearic acid, 7kg dimethyl silicone oil and 3kg white pine oil, be heated to 80-85 DEG C, stir after each component is all dissolved;

(2), in the container of the agitator of another said function, add 23.6kg ionized water, 1.2kg trolamine, 6.8kg fatty alcohol-polyoxyethylene ether, 0.49kg sanitas A26,1.9kg oleoyl amino acid sodium, be heated to 70-75 DEG C;

(3), under constantly stirring the mixed solution of step 2 gained is added in the mixed solution of step 1 gained, then add 0.08kg Sodium hexametaphosphate 99,1kg butadiene resin membrane-forming agent and 2kg pigment and stir and namely make finished product, canned after being cooled to 40 DEG C.

Embodiment 2:

(1), in belt stirrer and heatable reactor add 20kg carnauba wax, 15kg Microcrystalline Wax, 20kg stearic acid, 7.5kg dimethyl silicone oil and 3kg white pine oil, be heated to 80-85 DEG C, stir after each component is all dissolved;

(2), in the container of the agitator of another said function, add 27.7kg ionized water, 1.25kg trolamine, 7.5kg fatty alcohol-polyoxyethylene ether, 0.61kg sanitas A26,2.6kg oleoyl amino acid sodium, be heated to 70-75 DEG C;

(3), under constantly stirring the mixed solution of step 2 gained is added in the mixed solution of step 1 gained, then add 1kg Sodium hexametaphosphate 99,1kg butadiene resin membrane-forming agent and 2kg pigment and stir and namely make finished product, canned after being cooled to 40 DEG C.

Embodiment 3:

(1), in belt stirrer and heatable reactor add 20kg carnauba wax, 15kg Microcrystalline Wax, 22kg stearic acid, 8kg dimethyl silicone oil and 3kg white pine oil, be heated to 80-85 DEG C, stir after each component is all dissolved;

(2), in the container of the agitator of another said function, add 32kg ionized water, 1.33kg trolamine, 8.6kg fatty alcohol-polyoxyethylene ether, 0.78kg sanitas A26,3.2kg oleoyl amino acid sodium, be heated to 70-75 DEG C;

(3), under constantly stirring the mixed solution of step 2 gained is added in the mixed solution of step 1 gained, then add 1.02kg Sodium hexametaphosphate 99,1kg butadiene resin membrane-forming agent and 2kg pigment and stir and namely make finished product, canned after being cooled to 40 DEG C.

Above embodiments of the present invention are described, but the invention is not restricted to above-mentioned embodiment, in the ken that art those of ordinary skill possesses, can also make a variety of changes under the prerequisite not departing from present inventive concept.

Claims (1)

1. a shoe polish, it is characterized in that comprising component carnauba wax, Microcrystalline Wax, white pine oil, dimethyl silicone oil, stearic acid, trolamine, fatty alcohol-polyoxyethylene ether, Sodium hexametaphosphate 99, oleoyl amino acid sodium, sanitas A26, butadiene resin membrane-forming agent, pigment and deionized water, each component in mass ratio example is: 20:15:3:7:18:1.2:6.8:0.08:1.9:0.49:1:2:23.6;

Making step:

(1), in belt stirrer and heatable reactor add carnauba wax, Microcrystalline Wax, stearic acid, dimethyl silicone oil and white pine oil, be heated to 80-85 DEG C, stir after each component is all dissolved;

(2), in the container of the agitator of another said function, add deionized water, trolamine, fatty alcohol-polyoxyethylene ether, sanitas A26, oleoyl amino acid sodium, be heated to 70-75 DEG C;

(3), under constantly stirring the mixed solution of step 2 gained is added in the mixed solution of step 1 gained, then add Sodium hexametaphosphate 99, butadiene resin membrane-forming agent and pigment and stir and namely make finished product, canned after being cooled to 40 DEG C.