CN103976489A - Method for making butyronitrile anti-skid fully-impregnated safety port glove - Google Patents
Method for making butyronitrile anti-skid fully-impregnated safety port glove Download PDFInfo
- Publication number
- CN103976489A CN103976489A CN201410146137.8A CN201410146137A CN103976489A CN 103976489 A CN103976489 A CN 103976489A CN 201410146137 A CN201410146137 A CN 201410146137A CN 103976489 A CN103976489 A CN 103976489A
- Authority
- CN
- China
- Prior art keywords
- gloves
- steeping
- skidding
- preparation
- butyronitrile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for making a butyronitrile anti-skid fully-impregnated safety port glove. The method comprises the steps of material preparation, glue mixing, soaking and drying. The surface of the glove produced by adopting the method in the technical scheme is frosted, so that the defects of slippage of the butyronitrile glove due to water and oil are effectively overcome, the application field of the butyronitrile glove is better expanded, and the working safety of a user is better protected.
Description
Technical field
The present invention relates to the manufacture method of rubber gloves, relate to specifically a kind of butyronitrile anti-skidding entirely soak safe mouthful
The preparation method of gloves.
Background technology
Existing butyronitrile safety mouthful gloves are widely used in the industries such as petrochemical industry, paint printing, agriculture and animal husbandry, automobile mechanical maintenance; There is lightly sensitive, soft comfortable wear-resisting heat-insulation warm keeping, oil stain preventing function, acid and alkali-resistance, the performance such as anticorrosive.After impregnation, be divided into and partly soak and entirely soak two kinds, but be all smooth with regard to surperficial surface smoothness, therefore existing common butyronitrile gloves easily skids running into after water or oil, causes a lot of inconvenience to people's work.
Summary of the invention
The technical problem to be solved in the present invention is for the deficiencies in the prior art, and a kind of water or oil of meeting is provided
The anti-skidding preparation method who entirely soaks safety mouthful gloves of rear non-slip butyronitrile.
For addressing the above problem, the present invention by the following technical solutions: a kind of butyronitrile is anti-skidding soaks the preparation method of safety mouthful gloves entirely, it is characterized in that: comprise the following steps:
(1), get the raw materials ready, get NBR latex, blowing agent, thickener and water-based PU resin for subsequent use;
(2), impregnation, NBR latex and thickener are joined in liquid mixing agitator and carry out an impregnation, obtain single-steeping glue; NBR latex, blowing agent and water-based PU are joined in liquid mixing agitator and carry out secondary impregnation, obtain double-steeping glue;
(3), dipping, first gloves embryo is immersed in single-steeping glue and carries out single-steeping, then immerse and in double-steeping glue, carry out double-steeping;
(4), dry, gloves complete double-steeping are entered to drying baker and dry and obtain product.
Below further improvement of the present invention:
NBR latex in step (1): blowing agent: thickener: the mass ratio=100:2:1:5 of water-based PU resin.
Further improve:
When an impregnation, control liquid mixing agitator rotating speed 30 rad/min, mixing time is half an hour.
Further improve:
The rotating speed of controlling liquid mixing agitator when secondary impregnation is 30 rad/min, and mixing time is half an hour.
Further improve:
First prebake conditions gloves embryo before single-steeping, prebake conditions temperature is controlled at 22-26 DEG C, after preliminary drying completes, gloves embryo is enclosed within on fingerprint, and baking, makes gloves embryo temperature reach 40 DEG C, is then immersed in single-steeping glue, enters into preliminary drying district preliminary drying after whirl coating, even glue.
Further improve:
Gloves embryo after double-steeping is carried out to whirl coating, the operation of even glue.
Further improve:
Described baking step comprises dries for the first time and dries for the second time, first dries for the first time, after then drying for the second time, obtains product.
Further improve:
While oven dry for the first time, controlling temperature is 60 DEG C, and baking time is 30 minutes.
Further improve:
While oven dry for the second time, controlling temperature is 120 DEG C, and baking time is 60-80 minute.
Further improve:
Described blowing agent is the mixed solution of sodium acid carbonate and water, and wherein the mass ratio of sodium acid carbonate and water is 1:10; Described thickener is casein.
The glove surface that the present invention adopts the preparation method of technique scheme to produce is frosted shape, has effectively improved the shortcoming that butyronitrile gloves and water and oil skid, and has better opened up the application of butyronitrile gloves, and has better protected user's work safety.
Detailed description of the invention
Embodiment, the anti-skidding preparation method who entirely soaks safety mouthful gloves of a kind of butyronitrile, comprises the following steps:
1, get the raw materials ready: NBR latex, blowing agent, thickener and water-based PU resin, wherein NBR latex: blowing agent: thickener: the mass ratio=100:2:1:5 of water-based PU resin.
Described NBR latex is southern Supreme Being's NBR latex of import, canned, and mass concentration is 44%.
Described blowing agent is the mixed solution of sodium acid carbonate and water, and wherein the mass ratio of sodium acid carbonate and water is 1:10.
Described thickener is casein.
Described water-based PU resin is import Korea S water-based PU resin, 100Kg/ bucket, and mass concentration is 50%.
2, impregnation:
An impregnation: NBR latex and thickener are joined in liquid mixing agitator by the consumption of step 1, control rotating speed 30 rad/min, stir half an hour, obtain single-steeping glue;
Secondary impregnation: NBR latex, blowing agent and water-based PU are joined in liquid mixing agitator by the consumption of step 1, control rotating speed 30 rad/min, stir half an hour, obtain double-steeping glue.
3, dipping:
Single-steeping: first prebake conditions gloves embryo, prebake conditions temperature is controlled at 22-26 DEG C, after having toasted, gloves embryo is enclosed within on fingerprint, baking, makes gloves embryo temperature reach 40 DEG C, then be immersed in the single-steeping glue in step 2, whirl coating gets rid of unnecessary glue 10 times, evener glue is uniformly distributed glue 3 times, avoids occurring glue beans, enter afterwards preliminary drying district and dry 20 minutes, preliminary drying district temperature is controlled at 80 DEG C;
Double-steeping: the gloves that single-steeping is completed are immersed in the double-steeping glue obtaining in step 2 again, and whirl coating gets rid of unnecessary glue 5 times, and even glue is uniformly distributed glue 3 times, avoids occurring glue beans.
4, dry:
Gloves complete double-steeping in step 3 are entered to drying baker, dry for the first time, temperature 60 C, time 30 minutes, and then dry for the second time, 120 DEG C of temperature, time 60-80 minute, obtain product.
The gloves that the present invention adopts above-mentioned steps to make, meet or exceed national standard, wherein sizing material adhesive force (peel strength) is 40N, glue face thickness is 2mm, glue face tearing strength meets and exceeds level Four (>=75N), glue face is wear-resistant power >=8000rad, reaches level Four level, and glue face ageing resistace reaches 1 grade of product requirement.
Claims (10)
1. the anti-skidding preparation method who entirely soaks safety mouthful gloves of butyronitrile, is characterized in that: comprise the following steps:
(1), get the raw materials ready, get NBR latex, blowing agent, thickener and water-based PU resin for subsequent use;
(2), impregnation, NBR latex and thickener are joined in liquid mixing agitator and carry out an impregnation, obtain single-steeping glue; NBR latex, blowing agent and water-based PU are joined in liquid mixing agitator and carry out secondary impregnation, obtain double-steeping glue;
(3), dipping, first gloves embryo is immersed in single-steeping glue and carries out single-steeping, then immerse and in double-steeping glue, carry out double-steeping;
(4), dry, gloves complete double-steeping are entered to drying baker and dry and obtain product.
2. the anti-skidding preparation method who entirely soaks safety mouthful gloves of a kind of butyronitrile according to claim 1, is characterized in that: NBR latex in step (1): blowing agent: thickener: the mass ratio=100:2:1:5 of water-based PU resin.
3. the anti-skidding preparation method who entirely soaks safety mouthful gloves of a kind of butyronitrile according to claim 1, is characterized in that: when an impregnation, control liquid mixing agitator rotating speed 30 rad/min, mixing time is half an hour.
4. the anti-skidding preparation method who entirely soaks safety mouthful gloves of a kind of butyronitrile according to claim 3, is characterized in that: the rotating speed of controlling liquid mixing agitator when secondary impregnation is 30 rad/min, and mixing time is half an hour.
5. the anti-skidding preparation method who entirely soaks safety mouthful gloves of a kind of butyronitrile according to claim 1, it is characterized in that: first prebake conditions gloves embryo before single-steeping, prebake conditions temperature is controlled at 22-26 DEG C, after preliminary drying completes, gloves embryo is enclosed within on fingerprint, baking, make gloves embryo temperature reach 40 DEG C, be then immersed in single-steeping glue, after whirl coating, even glue, enter into preliminary drying district preliminary drying.
6. the anti-skidding preparation method who entirely soaks safety mouthful gloves of a kind of butyronitrile according to claim 5, is characterized in that: the gloves embryo after double-steeping carries out whirl coating, the operation of even glue.
7. the anti-skidding preparation method who entirely soaks safety mouthful gloves of a kind of butyronitrile according to claim 1, is characterized in that: described baking step comprises dries for the first time and dry for the second time, first dries for the first time, after then drying for the second time, obtains product.
8. the anti-skidding preparation method who entirely soaks safety mouthful gloves of a kind of butyronitrile according to claim 7, is characterized in that: while oven dry for the first time, controlling temperature is 60 DEG C, and baking time is 30 minutes.
9. the anti-skidding preparation method who entirely soaks safety mouthful gloves of a kind of butyronitrile according to claim 8, is characterized in that: while oven dry for the second time, controlling temperature is 120 DEG C, and baking time is 60-80 minute.
10. the anti-skidding preparation method who entirely soaks safety mouthful gloves of a kind of butyronitrile according to claim 1, is characterized in that: described blowing agent is the mixed solution of sodium acid carbonate and water, and wherein the mass ratio of sodium acid carbonate and water is 1:10; Described thickener is casein.