CN103535927B - A kind of latex temperature-dependent mechanical embossing gloves and preparation technology thereof - Google Patents
A kind of latex temperature-dependent mechanical embossing gloves and preparation technology thereof Download PDFInfo
- Publication number
- CN103535927B CN103535927B CN201310536861.7A CN201310536861A CN103535927B CN 103535927 B CN103535927 B CN 103535927B CN 201310536861 A CN201310536861 A CN 201310536861A CN 103535927 B CN103535927 B CN 103535927B
- Authority
- CN
- China
- Prior art keywords
- gloves
- temperature
- impregnation
- dependent mechanical
- mechanical embossing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of latex temperature-dependent mechanical embossing gloves and preparation technology thereof, comprise the following steps: successively through getting the raw materials ready, impregnation, impregnation, temperature-dependent mechanical embossing, oven dry, washing and baking operation again.Described impregnation operation, after gloves embryo is inserted in fingerprint, fingerprint temperature is increased to 70 DEG C, immerse 1-2s in the impregnated resin that impregnation operation obtains again, even glue 2 times, described temperature-dependent mechanical embossed cotton, be by impregnation after gloves facies palmaris enter on figuratum template down, carry out temperature-dependent mechanical embossing 5s, and then through drying, washing and baking operation again, obtained latex temperature-dependent mechanical embossing gloves.Adopt the product that present invention process is produced; mechanical graining is carried out after the inner impregnation of palm; better improve gripping power and protection; coating can prevent entering of liquid; obtained gloves quality softness, lightly sensitive, good permeability; wear indefatigability for a long time, be particularly suitable for machinery industry operation.
Description
Technical field
The present invention relates to a kind of protective gloves and preparation technology thereof, particularly a kind of latex temperature-dependent mechanical embossing gloves and preparation technology thereof.
Background technology
Along with the reinforcement of mankind's sense of self-protection, require also more and more higher to the safeguard function of safety protection glove, application number 201110001374.1, denomination of invention is a kind of manufacture method of gum dipping safety protection gloves, disclose a kind of methyl alcohol first gloves base dipping being added calcium nitrate, then Dipped latex makes impregnation safety gloves; Application number 200810021536.6, denomination of invention: the patent of invention of antislip gumming gloves and production method thereof, discloses a kind of before dipping process, first carries out a production technology for pearl process to gloves base, obtained antislip gumming gloves, the protective gloves of applicable garden management.But the problems such as said method all exists the inner gripping power of gloves palm and protection is inadequate.
Summary of the invention
The object of this invention is to provide the inner gripping power of a kind of raising palm and protection, the latex temperature-dependent mechanical embossing gloves in use better preventing liquid from entering and preparation technology thereof.
For reaching above object, the technical scheme that the present invention takes is: a kind of preparation technology of latex temperature-dependent mechanical embossing gloves, is characterized in that: comprise the following steps: successively through getting the raw materials ready, impregnation, impregnation, temperature-dependent mechanical embossing, oven dry, washing and baking operation again.
Below the further improvement to technique scheme:
Described procedure for preparation, raw material is natural emulsion, thickener and heat sensitizer.
Described natural emulsion mass concentration is 61%; Described thickener is casein, and consumption is 5 ‰ of natural emulsion; Described heat sensitizer is zinc ammonium complex ion, and consumption is 2% of natural emulsion.
Described impregnation operation, after gloves embryo is inserted in fingerprint, fingerprint temperature is increased to 70 DEG C, then immerse in impregnated resin that impregnation operation obtains, and control the impregnation degree of depth, the impregnation time is 1-2s, even glue 2 times.
In described impregnation operation, the impregnation degree of depth is for count 3.5 ± 0.5cm from thumb tip.
In described impregnation operation, the impregnation degree of depth is for count 11 ± 1.5cm from thumb tip.
Described temperature-dependent mechanical embossed cotton, be by impregnation after gloves facies palmaris enter on figuratum template down, carry out temperature-dependent mechanical embossing 5s.
Described impregnation operation joins in liquid mixing agitator by natural emulsion, heat sensitizer and thickener in the ratio in procedure for preparation, controls rotating speed 100 r/min, stirs half an hour, obtain impregnated resin.
Gloves after temperature-dependent mechanical embossing are put into baking oven by described baking operation, carry out first time oven dry, temperature 80 DEG C, 15 minutes time; Described washing step, the gloves after being dried first time enter in soaked pond and carry out washing 15min; Described baking operation again, by the gloves after washing, carries out second time and dries, temperature 80-100 DEG C, time 60-80 minute.
The product prepared by preparation technology of latex temperature-dependent mechanical embossing gloves, technical indicator is as follows: adhesive force (peel strength): 40N; Thickness: glue face thickness 2mm; Tearing strength: meet and exceed level Four (>=75N); Wear-resistant power: >=2000 cycles, reaches tertiary effluent and puts down.
The present invention adopts above technical scheme, compared with prior art has the following advantages:
Adopt the gloves that present invention process is produced, carry out mechanical graining after the inner impregnation of palm, better improve gripping power and protection; Coating can prevent entering of liquid, and obtained gloves quality softness, lightly sensitive, good permeability, wear indefatigability for a long time, is particularly suitable for machinery industry operation.
Detailed description of the invention
Except as otherwise noted, the percentage adopted in the present invention is mass percent.
embodiment 1
A preparation technology for latex temperature-dependent mechanical embossing gloves, comprises the following steps:
(1) get the raw materials ready: natural emulsion, thickener, heat sensitizer;
Described natural emulsion is three, the Thailand tree board natural emulsion of import, 205Kg/ bucket, and mass concentration is 61%;
Thickener is casein, and consumption is 5 ‰ of natural emulsion;
Heat sensitizer is zinc ammonium complex ion, and consumption is 2% of natural emulsion, the adding of heat sensitizer is conducive to rear operation and carries out temperature-dependent mechanical embossing.
Through lot of experiments, thickener is casein, and consumption is 5 ‰ of natural emulsion; Heat sensitizer is zinc ammonium complex ion, and when consumption is 2% of natural emulsion, obtained product quality is best, therefore this proportioning preferred.
(2) impregnation: join in liquid mixing agitator in the ratio of step (1) by natural emulsion, heat sensitizer and thickener, controls rotating speed 100 r/min, stirs half an hour, obtains impregnated resin.
(3) impregnation: after gloves embryo is inserted in fingerprint; fingerprint temperature is increased to 70 DEG C; immerse the impregnated resin 1-2s that step (2) obtains again; the impregnation degree of depth is for count 3.5 ± 0.5cm from thumb tip; even glue 2 times; glue is uniformly distributed; avoid occurring glue beans; control the different impregnation degree of depth; the degree that obtained gloves are protected palm is different, and the impregnation degree of depth is darker, larger to the degree of palm protection; the impregnation degree of depth is product quality optimum obtained when counting 3.5 ± 0.5cm from thumb tip, therefore this technological parameter preferred.
(4) temperature-dependent mechanical embossing: enter on figuratum template down by the gloves facies palmaris after step (3) impregnation, carries out temperature-dependent mechanical embossing 5s, and after the inner impregnation of palm, mechanical graining better improves gripping power and protection.
(5) dry: the gloves that step (4) presses line are put into baking oven, carry out first time oven dry, temperature 80 DEG C, 15 minutes time.
(6) wash: the gloves after step (5) being dried enter in soaked pond and carry out washing 15min.
(7) dry: by the gloves after washing, then carry out second time and dry, temperature 80-100 DEG C, time 60-80 minute, obtain latex temperature-dependent mechanical embossing gloves product again.
As follows by the gloves specific targets of producing after present invention process:
Adhesive force (peel strength): 40N;
Thickness: glue face thickness 2mm;
Tearing strength: meet and exceed level Four (>=75N);
Wear-resistant power: >=2000 cycles, reaches tertiary effluent and puts down;
Anti-aging: ageing resistace reaches 1 grade of product requirement;
Pliability: soft;
Gas permeability: good air permeability.
embodiment 2
A preparation technology for latex temperature-dependent mechanical embossing gloves, comprises the following steps:
(1) get the raw materials ready: natural emulsion, thickener, heat sensitizer;
Described natural emulsion is three, the Thailand tree board natural emulsion of import, 205Kg/ bucket, and mass concentration is 61%;
Thickener is casein, and consumption is 5 ‰ of natural emulsion;
Heat sensitizer is zinc ammonium complex ion, and consumption is 2% of natural emulsion, the adding of heat sensitizer is conducive to rear operation and carries out temperature-dependent mechanical embossing.
Through lot of experiments, thickener is casein, and consumption is 5 ‰ of natural emulsion; Heat sensitizer is zinc ammonium complex ion, and when consumption is 2% of natural emulsion, obtained product quality is best, therefore this proportioning preferred.
(2) impregnation: join in liquid mixing agitator in the ratio of step (1) by natural emulsion, heat sensitizer and thickener, controls rotating speed 100 r/min, stirs half an hour, obtains impregnated resin.
(3) impregnation: after gloves embryo is inserted in fingerprint; fingerprint temperature is increased to 70 DEG C, then immerse the impregnated resin 1-2s that step (2) obtains; the impregnation degree of depth is for count 11 ± 1.5cm from thumb tip; even glue 2 times, makes glue be uniformly distributed, and avoids occurring glue beans; control the different impregnation degree of depth; the degree that obtained gloves are protected palm is different, and the impregnation degree of depth is darker, larger to the degree of palm protection.
(4) temperature-dependent mechanical embossing: enter on figuratum template down by the gloves facies palmaris after step (3) impregnation, carries out temperature-dependent mechanical embossing 5s.
(5) dry: the gloves that step (4) presses line are put into baking oven, carry out first time oven dry, temperature 80 DEG C, 15 minutes time.
(6) wash: the gloves after step (5) being dried enter in soaked pond and carry out washing 15min.
(7) dry: by the gloves after washing, then carry out second time and dry, temperature 80-100 DEG C, time 60-80 minute, obtain latex temperature-dependent mechanical embossing gloves again.
As follows by the gloves specific targets of producing after present invention process:
Adhesive force (peel strength): 40N;
Thickness: glue face thickness 2mm;
Tearing strength: meet and exceed level Four (>=75N);
Wear-resistant power: >=2000 cycles, reaches tertiary effluent and puts down;
Anti-aging: ageing resistace reaches 1 grade of product requirement;
Pliability: soft;
Gas permeability: good air permeability.
Adopt the gloves that present invention process is produced, carry out mechanical graining after the inner impregnation of palm, better improve gripping power and protection; Coating can prevent entering of liquid, and quality softness, lightly sensitive, good permeability, wear indefatigability for a long time, is particularly suitable for machinery industry operation.
Claims (2)
1. a preparation technology for latex temperature-dependent mechanical embossing gloves, is characterized in that: comprise the following steps:
(1) get the raw materials ready: natural emulsion, thickener, heat sensitizer;
Described natural emulsion is three, the Thailand tree board natural emulsion of import, 205Kg/ bucket, and mass concentration is 61%;
Thickener is casein, and consumption is 5 ‰ of natural emulsion;
Heat sensitizer is zinc ammonium complex ion, and consumption is 2% of natural emulsion;
(2) impregnation: join in liquid mixing agitator in the ratio of step (1) by natural emulsion, heat sensitizer and thickener, controls rotating speed 100 r/min, stirs half an hour, obtains impregnated resin;
(3) impregnation: after gloves embryo is inserted in fingerprint, fingerprint temperature is increased to 70 DEG C, then the impregnated resin 1-2s immersing that step (2) obtains, the impregnation degree of depth is for count 11 ± 1.5cm from thumb tip, and even glue 2 times, makes glue be uniformly distributed, and avoids occurring glue beans;
(4) temperature-dependent mechanical embossing: enter on figuratum template down by the gloves facies palmaris after step (3) impregnation, carries out temperature-dependent mechanical embossing 5s;
(5) dry: the gloves that step (4) presses line are put into baking oven, carry out first time oven dry, temperature 80 DEG C, 15 minutes time;
(6) wash: the gloves after step (5) being dried enter in soaked pond and carry out washing 15min;
(7) dry again: by the gloves after washing, then carry out second time and dry, temperature 80-100 DEG C, time 60-80 minute, obtained finished product.
2. the preparation technology of a kind of latex temperature-dependent mechanical embossing gloves according to claim 1, is characterized in that: adopt the product prepared by this preparation technology, technical indicator is as follows: adhesive force (peel strength): 40N; Thickness: glue face thickness 2mm; Tearing strength: meet and exceed level Four (>=75N); Wear-resistant power: >=2000 cycles, reaches tertiary effluent and puts down.