CN103409073A - Moisture-proof environment-friendly shoe polish and preparation method thereof - Google Patents
Moisture-proof environment-friendly shoe polish and preparation method thereof Download PDFInfo
- Publication number
- CN103409073A CN103409073A CN2013103528058A CN201310352805A CN103409073A CN 103409073 A CN103409073 A CN 103409073A CN 2013103528058 A CN2013103528058 A CN 2013103528058A CN 201310352805 A CN201310352805 A CN 201310352805A CN 103409073 A CN103409073 A CN 103409073A
- Authority
- CN
- China
- Prior art keywords
- parts
- shoe polish
- oil
- mixture
- environmental protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of household chemicals, and especially relates to a moisture-proof environment-friendly shoe polish and a preparation method thereof. The shoe polish comprises the raw materials of, by weight: 10-30 parts of turpentine, 1-10 parts of dibutyl phthalate, 5-10 parts of asphalt paint, 1-5 parts of nitrobenzene, 5-15 parts of titanium dioxide, 15-30 parts silicone oil, 20-40 parts of paraffin wax , 10-20 parts beeswax, 10-20 parts of lanolin, 5-10 parts of glycerol, 1-5 parts of magnesium stearate, 0.01-0.1 parts of bentonite, 1-10 parts of a fungicide, 0.5-5 parts of lavender oil, and 15-30 parts of deionized water. The shoe polish has good moisture-proof effect, and can prevent a leather shoe mold phenomenon during a storage and maintenance process. Also, the shoe polish has a refreshing smell, and is environment-friendly.
Description
Technical field
The present invention relates to the daily chemicals technical field, particularly a kind of moistureproof environmental protection shoe polish and preparation method thereof.
Background technology
Leather shoes are the favorite a kind of footwear of people, are that the employing natural leather is that the main raw material manufacture obtains.Whether wearing well of leather shoes, one side is the quality of leather shoes, is on the other hand its maintenance.
Shoe polish is a kind of in order to polish, to repair leather shoes, and strengthens the product of its anti-waterpower, and after shoe polish was coated on leather shoes upper, solvent evaporates, stayed the cere that one deck is thin, can reach blast, effect attractive in appearance.
When leather shoes are not worn, should take in time, and coat shoe polish, leather shoes are played to the maintenance effect.But in atmospheric moisture very large season, such as plum rain season, existing shoe polish product effect is difficult to leather shoes are played to moistureproof maintenance effect, and mildew easily appears in leather shoe surface, and simultaneously, the smell of existing shoe polish is pungent.
Summary of the invention
To the deficiencies in the prior art, technical problem to be solved by this invention is for above: provide a kind of can be moistureproof, footwear that again can environmental protection, the shoe polish of smell delicate fragrance.The technical scheme adopted is:
A kind of moistureproof environmental protection shoe polish, made by the following raw material according to the weight part meter: 10～30 parts, turps, 1～10 part of dibutyl phthalate, 5～10 parts of bituminous varnishs, 1～5 part, oil of mirbane, 5～15 parts of titanium dioxide, 15～30 parts of silicone oil, 20～40 parts, paraffin, 10～20 parts, beeswax, 10～20 parts, lanolin, 5～10 parts of glycerine, 1～5 part of Magnesium Stearate, 0.01～0.1 part of wilkinite, 1～10 part of mould inhibitor, 0.5～5 part of Herba Lysimachiae foenumgraeci quintessence oil, 15～30 parts of deionized waters.
Further, described moistureproof environmental protection shoe polish, made by the following raw material according to the weight part meter: 15～25 parts, turps, 1～5 part of dibutyl phthalate, 5～7 parts of bituminous varnishs, 2.5～5 parts, oil of mirbane, 5～10 parts of titanium dioxide, 20～25 parts of silicone oil, 25～35 parts, paraffin, 10～15 parts, beeswax, 10～15 parts, lanolin, 7～10 parts of glycerine, 1～2.5 part of Magnesium Stearate, 0.01～0.05 part of wilkinite, 1～5 part of mould inhibitor, 1～2.5 part of Herba Lysimachiae foenumgraeci quintessence oil, 20～25 parts of deionized waters.
Further, described moistureproof environmental protection shoe polish, mould inhibitor is phenol or Pentachlorophenol.
Further, the preparation method of described moistureproof environmental protection shoe polish comprises following steps:
(1) while turps, dibutyl phthalate, bituminous varnish, oil of mirbane, silicone oil, paraffin, beeswax, lanolin are heated, stir under 115～125 ℃, after melting, obtain mixture A;
(2) by titanium dioxide, glycerine, Magnesium Stearate, deionized water, heating under 70～80 ℃, stirring, mixing, obtain mixture B;
(3) mixture B is added in mixture A, stir, mix, let cool to 80～90 ℃, add wilkinite, mould inhibitor, Herba Lysimachiae foenumgraeci quintessence oil, stir, obtain.
The invention has the beneficial effects as follows:
(1) the present invention has good moisture-proof role, can prevent from Signs of Mould occurring in the maintenance of leather shoes storage;
(2) smell delicate fragrance of the present invention, environmental protection.
Embodiment
According to the weight proportion in table 1, prepare each component raw material.
The weight proportion of table 1 embodiment 1～embodiment 4
The preparation method is:
Embodiment 1
(1) by turps, dibutyl phthalate, bituminous varnish, oil of mirbane, silicone oil, paraffin, beeswax, lanolin under 115 ℃ while heating, stirring, after melting, obtain mixture A;
(2) by titanium dioxide, glycerine, Magnesium Stearate, deionized water, heating under 70 ℃, stirring, mixing, obtain mixture B;
(3) mixture B is added in mixture A, stir, mix, let cool to 80 ℃, add wilkinite, phenol, Herba Lysimachiae foenumgraeci quintessence oil, stir, obtain.
Embodiment 2
(1) by turps, dibutyl phthalate, bituminous varnish, oil of mirbane, silicone oil, paraffin, beeswax, lanolin under 125 ℃ while heating, stirring, after melting, obtain mixture A;
(2) by titanium dioxide, glycerine, Magnesium Stearate, deionized water, heating under 80 ℃, stirring, mixing, obtain mixture B;
(3) mixture B is added in mixture A, stir, mix, let cool to 90 ℃, add wilkinite, Pentachlorophenol, Herba Lysimachiae foenumgraeci quintessence oil, stir, obtain.
Embodiment 3
(1) by turps, dibutyl phthalate, bituminous varnish, oil of mirbane, silicone oil, paraffin, beeswax, lanolin under 118 ℃ while heating, stirring, after melting, obtain mixture A;
(2) by titanium dioxide, glycerine, Magnesium Stearate, deionized water, heating under 75 ℃, stirring, mixing, obtain mixture B;
(3) mixture B is added in mixture A, stir, mix, let cool to 85 ℃, add wilkinite, phenol, Herba Lysimachiae foenumgraeci quintessence oil, stir, obtain.
Embodiment 4
(1) by turps, dibutyl phthalate, bituminous varnish, oil of mirbane, silicone oil, paraffin, beeswax, lanolin under 120 ℃ while heating, stirring, after melting, obtain mixture A;
(2) by titanium dioxide, glycerine, Magnesium Stearate, deionized water, heating under 78 ℃, stirring, mixing, obtain mixture B;
(3) mixture B is added in mixture A, stir, mix, let cool to 88 ℃, add wilkinite, Pentachlorophenol, Herba Lysimachiae foenumgraeci quintessence oil, stir, obtain.
Claims (4)
1. moistureproof environmental protection shoe polish is characterized in that: made by the following raw material according to the weight part meter:
10～30 parts, turps
1～10 part of dibutyl phthalate
5～10 parts of bituminous varnishs
1～5 part, oil of mirbane
5～15 parts of titanium dioxide
15～30 parts of silicone oil
20～40 parts, paraffin
10～20 parts, beeswax
10～20 parts, lanolin
5～10 parts of glycerine
1～5 part of Magnesium Stearate
0.01～0.1 part of wilkinite
1～10 part of mould inhibitor
0.5～5 part of Herba Lysimachiae foenumgraeci quintessence oil
15～30 parts of deionized waters.
2. moistureproof environmental protection shoe polish according to claim 1 is characterized in that: made by the following raw material according to the weight part meter:
15～25 parts, turps
1～5 part of dibutyl phthalate
5～7 parts of bituminous varnishs
2.5～5 parts, oil of mirbane
5～10 parts of titanium dioxide
20～25 parts of silicone oil
25～35 parts, paraffin
10～15 parts, beeswax
10～15 parts, lanolin
7～10 parts of glycerine
1～2.5 part of Magnesium Stearate
0.01～0.05 part of wilkinite
1～5 part of mould inhibitor
1～2.5 part of Herba Lysimachiae foenumgraeci quintessence oil
20～25 parts of deionized waters.
3. moistureproof environmental protection shoe polish according to claim 1 and 2, it is characterized in that: mould inhibitor is phenol or Pentachlorophenol.
4. method for preparing moistureproof environmental protection shoe polish claimed in claim 1, it is characterized in that: the preparation method comprises following steps:
(1) while turps, dibutyl phthalate, bituminous varnish, oil of mirbane, silicone oil, paraffin, beeswax, lanolin are heated, stir under 115～125 ℃, after melting, obtain mixture A;
(2) by titanium dioxide, glycerine, Magnesium Stearate, deionized water, heating under 70～80 ℃, stirring, mixing, obtain mixture B;
(3) mixture B is added in mixture A, stir, mix, let cool to 80～90 ℃, add wilkinite, mould inhibitor, Herba Lysimachiae foenumgraeci quintessence oil, stir, obtain.