CN103059741A - Waterproof bright shoe polish and preparation method thereof - Google Patents
Waterproof bright shoe polish and preparation method thereof Download PDFInfo
- Publication number
- CN103059741A CN103059741A CN 201110325168 CN201110325168A CN103059741A CN 103059741 A CN103059741 A CN 103059741A CN 201110325168 CN201110325168 CN 201110325168 CN 201110325168 A CN201110325168 A CN 201110325168A CN 103059741 A CN103059741 A CN 103059741A
- Authority
- CN
- China
- Prior art keywords
- parts
- heating
- beeswax
- preparation
- melting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses waterproof bright shoe polish and a preparation method of the shoe polish. The shoe polish comprises the following components in parts by weight: 10-15 parts of beewax, 5-10 parts of spermaceti wax, 20-40 parts of turpentine oil, 1-5 parts of asphalt paint, 1-5 parts of borax powder, 1-4 parts of gas carbon black, 1-4 parts of prussian blue and 1-4 parts of prussian blue. The shoe polish prepared by steps such as heating and melting, stirring the raw materials and the like is coated on a vamp, so that the vamp can be effectively protected from soaking by rain, and therefore, the shoe polish has strong gloss and waterproof performance.
Description
Technical field
The present invention relates to a kind of leather shoe brightener and preparation method thereof, more particularly, the present invention relates to a kind of waterproof bright shoe cream and preparation method thereof.
Background technology
When selecting leather shoes, note five aspects: sole, leather, ventilation property, external form, size.Sole wherein: leather sole has cortex and colloid two large classes.At the bottom of the measured leather shoes of matter, surface-brightening is level and smooth, and color even is consistent, does not have oil mark, stain and scar, and thickness is even; With the finger bullet, the sound is clear and melodious, and it is very solid that fingerprint is felt.This sole is pliable and tough plentiful, and tensile strength is large, and wear resistance is strong.The measured colloid sole of matter, smooth surface is consistent, and decorative pattern is neat, and each decorative pattern corner should be distinct complete.From the side, tangent plane uniform and delicate inclusion-free is without the size particles tissue, without the became uneven phenomenon; Touch with hand, preferably toughness and elasticity sensation should be arranged.If gluing leather shoes will check that whether the base side end is bonding tight, smooth, can not have the space, lose the glue phenomenon.Leather: leather shoe surface has two kinds of smooth leather and reverse leathers.The measured smooth musculus cutaneus footwear of matter, the grain even thickness, sliding flat careful, there are not wrinkle and scar; Luminance brightness, color even are consistent, and color and luster is bright, bright-coloured, does not have light and shade and deep mixed phenomenon.The pressure that press...withes one's finger surface, it is evenly tiny wrinkle to occur, and behind the relieving finger, microgroove disappears immediately; The fingerprint soft feel is lubricated, and springiness is not stiff, and the thickness of leather is evenly appropriate.The measured reverse side leather shoes of matter, surperficial fine hair is soft, even, solid colour, without thick macrofiber and oil mark stain, nothing is wrinkle and scar obviously, and touch perception is identical with light musculus cutaneus footwear.Ventilation property: the ventilation property with synthetic leather in the leather shoes is the poorest.General natural leather leather shoes ventilation property is better, and wherein especially take pig leather as best, because the pigskin pore is than thick several times of ox-hide pore, the pore eye is also much bigger, and sweat gas is easily discharged.But leather is attractive in appearance not as ox-hide.External form: except selecting the pattern that you like, note also whether the pin code of suture is even, whether two shoes full symmetric.Then with toe cap towards oneself, lie on the sales counter, whether the point of contact of checking half sole place and sales counter in the central position of half sole.If any deviation, be through the easy lateral deviation that occurs on the pin, cause the footwear distortion.Size: select leather shoes take comfortable as principle.Generally say, can expand into fully when width is stressed with instep; Length is not pressed from both sides with tiptoe and is not pushed up, and pin does not slide in footwear as well during walking.
And speak of in the maintenance of leather shoes, polish shoes oil everybody can, but only do with oneself idea, tend to occur all mistakes, not only do not have the effect of protecting leather shoes, can damage to some extent leather shoes on the contrary.Leather shoes are polished for the first time, should carry out before wearing new footwear, do not stain in the dirty situation at leather shoes to begin, and can keep well color and luster and the light of leather shoes.In wearing process, per two to three days needs shoe polishes once later on.And different cortex just need to be selected different shoe polish.Water dyes skin: the most handy colourless shoe polish, or sheep oil smears, preferably also is to use cotton, do not use brush.Buff: had better not oil with brush, best with cotton, can not damage shoes.Clean the shoes cleaning before oiling, do not wash with water, with half wet cloth dust is cleaned up, again shoe polish is squeezed on cotton, on surface, smear again.Dynamics is not too big when smearing, and grasps rhythm, smears a little more for a long time, and color even is all right by the time.Cured skin: all cured skins all can not be gone up shoe polish, otherwise are can variable color, in case and variable color just become and not return original color, arranging at ordinary times is exactly to wipe clean all right with clean cotton.Coat of paint: coat of paint is to have shown lacquer, the skin that hardness is large, does not need to smear shoe polish, and it is all right to dab dust with soft cloth at ordinary times, will note protection in the time of dress.The frosted skin: frosted skin and anti-suede are same natures, brush totally with hairbrush at ordinary times, and along a direction brush, just with the spray of frosted skin nursing agent, the place of then putting ventilation is dried in the shade all right every about a week in the time of brush.
Publication number is CN 1195686, open day discloses a kind of Quick polishing shoe cream for the Chinese patent literature of 1998.10.14, it is characterized in that: it is comprised of following component: synthetic wax 2-25 part, polysiloxane liquid 5-60 part, tensio-active agent 0.5-20 part, water 10-50 part, dyestuff 0.1-2.5, antifreeze component 2-15 part.This shoe cream formula is unreasonable, and light enhancing effect is poor, and shoe polish be coated on the leather shoes volatile, can not waterproof, vamp is easily spent.
Summary of the invention
It is poor that the present invention is intended to solve above-mentioned shoe polish light enhancing effect, and shoe polish be coated on the leather shoes volatile, can not waterproof, vamp is the problem of flower easily, provides a kind of light enhancing effect good, and waterproof bright shoe cream that can waterproof and preparation method thereof.
In order to realize the foregoing invention purpose, the technical solution used in the present invention is as follows:
The waterproof bright shoe cream is characterized in that: the component that comprises following parts by weight: beeswax 10-15 part
Spermaceti 5-10 part turps 20-40 part
Bituminous varnish 1-5 part
Borax powder 1-5 part
Gas-produced black 1-4 part
Prussian blue 1-4 part
Oil of mirbane 1-4 part.
The preparation method of waterproof bright shoe cream is characterized in that: comprise following processing step: A, take by weighing the beeswax water proof heating of formula ratio first, after its melting, the borax powder of formula ratio is added in the beeswax solution, constantly be stirred to the glue shape;
B, with the spermaceti heating and melting of formula ratio, then the bituminous varnish of formula ratio is added in the spermaceti of melting and fully stirs, again solution is added in the beeswax solution;
C, add the gas-produced black of formula ratio and Prussian blue, and continue to stir, add at last oil of mirbane and stir.
It is 10-20 ℃ in the heating and melting temperature described in the steps A.
It is 15-25 ℃ in the heating and melting temperature described in the step B.
The useful technique effect that the present invention brings is mainly manifested in the following aspects:
One, the beeswax that adopts in the waterproof bright shoe cream prescription provided by the invention is yellow, fallow or yellow-white, and is opaque or sub-translucent, smooth surface; Body is lighter, wax, and the section sand shape is pinched and can be softened with hand rubbing; Honey sample fragrance is arranged, and it is little sweet to distinguish the flavor of, and cooperates greatly soaking of strong resistance rainwater of turps.
Two, the turps that adopts in the waterproof bright shoe cream prescription provided by the invention is the liquid that clear, colorless has aromatising flavour, and relative density is 0.86～0.87, and refractive index is 1.4670～1.4710; Turps is water insoluble, but volatile drying; Belong to the secondary inflammable liquid, 32 ℃ of flash-points, 235 ℃ of spontaneous ignition temperatures; Turps itself is no acidic, but is subjected to extraneous oxygenizement to form free acid.Spread upon on the leather shoes and can effectively prevent soaking of sealing, leather shoes are not totally spent, the cooperation beeswax can the Effective Raise water-repellancy.
Three, the bituminous varnish that adopts in the waterproof bright shoe cream prescription provided by the invention has good thermotolerance, and time of drying is short, and favorable anti-corrosion effect.
Embodiment
Embodiment 1
The waterproof bright shoe cream is characterized in that: the component that comprises following parts by weight: 10 parts in beeswax
20 parts in 5 parts of turps of spermaceti
1 part of bituminous varnish
1 part in borax powder
1 part of gas-produced black
Prussian blue 1 part
1 part in oil of mirbane.
Embodiment 2
The waterproof bright shoe cream is characterized in that: the component that comprises following parts by weight: 12 parts in beeswax
30 parts in 8 parts of turps of spermaceti
3 parts of bituminous varnishs
3 parts in borax powder
3 parts of gas-produced blacks
Prussian blue 3 parts
3 parts in oil of mirbane.
Embodiment 3
The waterproof bright shoe cream is characterized in that: the component that comprises following parts by weight: 15 parts in beeswax
40 parts in 10 parts of turps of spermaceti
5 parts of bituminous varnishs
5 parts in borax powder
4 parts of gas-produced blacks
Prussian blue 4 parts
4 parts in oil of mirbane.
Embodiment 4
The preparation method of waterproof bright shoe cream is characterized in that: comprise following processing step: A, take by weighing 10 parts of beeswax water proof heating first, after its melting, 1 part of borax powder is added in the beeswax solution, constantly be stirred to the glue shape;
B, with 5 parts of spermaceti heating and meltings, then 1 part of bituminous varnish is added in the spermaceti of melting and fully stirs, again solution is added in the beeswax solution;
C, to add 1 part of gas-produced black and 1 part Prussian blue, and continue to stir, and adds at last 1 part of oil of mirbane and stir.
It is 10 ℃ in the heating and melting temperature described in the steps A.
It is 15 ℃ in the heating and melting temperature described in the step B.
Embodiment 5
The preparation method of waterproof bright shoe cream is characterized in that: comprise following processing step: A, take by weighing 12 parts of beeswax water proof heating first, after its melting, 3 parts of borax powder are added in the beeswax solution, constantly be stirred to the glue shape;
B, with 8 parts of spermaceti heating and meltings, then 3 parts of bituminous varnishs are added in the spermaceti of melting and fully stir, again solution is added in the beeswax solution;
C, to add 3 parts of gas-produced blacks and 3 parts Prussian blue, and continue to stir, and adds at last 3 parts of oil of mirbane and stir.
It is 15 ℃ in the heating and melting temperature described in the steps A.
It is 20 ℃ in the heating and melting temperature described in the step B.
Embodiment 6
The preparation method of waterproof bright shoe cream is characterized in that: comprise following processing step: A, take by weighing 15 parts of beeswax water proof heating first, after its melting, 5 parts of borax powder are added in the beeswax solution, constantly be stirred to the glue shape;
B, with 10 parts of spermaceti heating and meltings, then 5 parts of bituminous varnishs are added in the spermaceti of melting and fully stir, again solution is added in the beeswax solution;
C, to add 4 parts of gas-produced blacks and 4 parts Prussian blue, and continue to stir, and adds at last 4 parts of oil of mirbane and stir.
It is 20 ℃ in the heating and melting temperature described in the steps A.
It is 25 ℃ in the heating and melting temperature described in the step B.
Claims (4)
1. the waterproof bright shoe cream is characterized in that: the component that comprises following parts by weight: beeswax 10-15 part
Spermaceti 5-10 part turps 20-40 part
Bituminous varnish 1-5 part
Borax powder 1-5 part
Gas-produced black 1-4 part
Prussian blue 1-4 part
Oil of mirbane 1-4 part.
2. the preparation method of described waterproof bright shoe cream according to claim 1, it is characterized in that: comprise following processing step: A, take by weighing the beeswax water proof heating of formula ratio first, after its melting, in the borax powder adding beeswax solution with formula ratio, constantly be stirred to the glue shape;
B, with the spermaceti heating and melting of formula ratio, then the bituminous varnish of formula ratio is added in the spermaceti of melting and fully stirs, again solution is added in the beeswax solution;
C, add the gas-produced black of formula ratio and Prussian blue, and continue to stir, add at last oil of mirbane and stir.
3. the preparation method of described waterproof bright shoe cream according to claim 2 is characterized in that: be 10-20 ℃ in the heating and melting temperature described in the steps A.
4. the preparation method of described waterproof bright shoe cream according to claim 2 is characterized in that: be 15-25 ℃ in the heating and melting temperature described in the step B.