CN103820040A - Adhesive for solid wood floors and preparation method of adhesive - Google Patents
Adhesive for solid wood floors and preparation method of adhesive Download PDFInfo
- Publication number
- CN103820040A CN103820040A CN201410104226.6A CN201410104226A CN103820040A CN 103820040 A CN103820040 A CN 103820040A CN 201410104226 A CN201410104226 A CN 201410104226A CN 103820040 A CN103820040 A CN 103820040A
- Authority
- CN
- China
- Prior art keywords
- sodium bicarbonate
- parts
- adhesive
- add
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses adhesive for solid wood floors and a preparation method thereof. The adhesive comprises the following components in parts by weight: 20-30 parts of vinyl acetate, 10-20 parts of butyl acrylate, 3-5 parts of polyvinyl alcohol, 0.1-0.3 part of sodium carboxymethyl cellulose, 0.2-0.4 part of sodium bicarbonate, 3-5 parts of isopropyl alcohol, 0.1-0.3 part of paraben, 0.2-0.4 part of ethylene glycol dimethacrylate and 40-60 parts of water. The preparation method of the adhesive comprises the following steps: (1) adding the polyvinyl alcohol to the water, heating, then adding the isopropyl alcohol and the ethylene glycol dimethacrylate, and uniformly stirring; (2) cooling, adding the vinyl acetate and the butyl acrylate, protecting by using nitrogen, and uniformly stirring and dispersing; (3) heating, adding other components except for the sodium bicarbonate, and uniformly stirring; and (4) cooling to room temperature, adding the sodium bicarbonate, adjusting a pH value to 5.5, and filtering, thus obtaining the finished product.
Description
Technical field
The invention belongs to adhesive technology field, more specifically relate to a kind of solid wooden floor board tackiness agent and preparation method thereof.
Background technology
Solid wooden floor board is the floor decorative material forming after natural timber drying, processing.Natural wood texture and colour image that it presents, give nature, soft, the texture that is rich in avidity, becomes the ideal material of the ground surface finishings such as bedroom, parlor, study simultaneously due to the characteristic that it is cool in summer and warm in winter, sense of touch is good.
Solid wooden floor board when mounted, conventionally need to be by adhesive bonds on the ground, and therefore, the quality of adhesive quality has affected the result of use of solid wooden floor board largely.
Summary of the invention
The object of the invention is to overcome the deficiency that prior art exists, a kind of solid wooden floor board tackiness agent is provided.
Another object of the present invention is to provide the preparation method of this solid wooden floor board tackiness agent.
For achieving the above object, the present invention has taked following technical scheme:
A kind of solid wooden floor board tackiness agent, in weight part, composed of the following components:
Vinyl acetate: 20～30, butyl acrylate: 10～20, polyvinyl alcohol: 3～5,
Xylo-Mucine: 0.1～0.3, sodium bicarbonate: 0.2～0.4,
Virahol: 3～5, nipagin esters: 0.1～0.3,
Ethylene glycol dimethacrylate: 0.2～0.4, water: 40～60.
Described solid wooden floor board production of adhesive technique is:
(1) polyvinyl alcohol is added to the water, is heated to 80～90 ℃, then add Virahol and ethylene glycol dimethacrylate, stir;
(2) be cooled to 60～70 ℃, add vinyl acetate and butyl acrylate, with nitrogen protection, dispersed with stirring is even;
(3) be warming up to 80～90 ℃, add all the other components except sodium bicarbonate, stir;
(4) be cooled to room temperature, add sodium bicarbonate, regulate PH to 5.5, after filtration, get final product to obtain finished product.
Compared with prior art, the present invention has following beneficial effect:
(1) cohesive strength is large, water-fast, moisture resistivity is good;
(2) nontoxic free from extraneous odour, security is good, easy construction, moderate cost.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described.
Embodiment 1
A kind of solid wooden floor board tackiness agent, in weight part, composed of the following components:
Vinyl acetate: 20, butyl acrylate: 10, polyvinyl alcohol: 3,
Xylo-Mucine: 0.1, sodium bicarbonate: 0.2, Virahol: 3,
Nipagin esters: 0.1, ethylene glycol dimethacrylate: 0.2, water: 40.
Embodiment 2
A kind of solid wooden floor board tackiness agent, in weight part, composed of the following components:
Vinyl acetate: 30, butyl acrylate: 20, polyvinyl alcohol: 5,
Xylo-Mucine: 0.3, sodium bicarbonate: 0.4, Virahol: 5,
Nipagin esters: 0.3, ethylene glycol dimethacrylate: 0.4, water: 60.
Embodiment 3
A kind of solid wooden floor board tackiness agent, in weight part, composed of the following components:
Vinyl acetate: 25, butyl acrylate: 16, polyvinyl alcohol: 4,
Xylo-Mucine: 0.2, sodium bicarbonate: 0.3, Virahol: 4,
Nipagin esters: 0.2, ethylene glycol dimethacrylate: 0.3, water: 50.
Described solid wooden floor board production of adhesive technique is:
(1) polyvinyl alcohol is added to the water, is heated to 80～90 ℃, then add Virahol and ethylene glycol dimethacrylate, stir;
(2) be cooled to 60～70 ℃, add vinyl acetate and butyl acrylate, with nitrogen protection, dispersed with stirring is even;
(3) be warming up to 80～90 ℃, add all the other components except sodium bicarbonate, stir;
(4) be cooled to room temperature, add sodium bicarbonate, regulate PH to 5.5, after filtration, get final product to obtain finished product.
The present invention decorates wood floors for cement flooring, can in the time of room temperature, construct; Before construction, should clean out the dirt on cement flooring and wood floors surface, at cement flooring and wood floors surface gluing simultaneously, exert pressure, completely curing after 12 hours.
Claims (2)
1. a solid wooden floor board tackiness agent, is characterized in that, in weight part, composed of the following components:
Vinyl acetate: 20～30, butyl acrylate: 10～20, polyvinyl alcohol: 3～5,
Xylo-Mucine: 0.1～0.3, sodium bicarbonate: 0.2～0.4,
Virahol: 3～5, nipagin esters: 0.1～0.3,
Ethylene glycol dimethacrylate: 0.2～0.4, water: 40～60.
2. the preparation method of a kind of solid wooden floor board tackiness agent claimed in claim 1, is characterized in that, comprises following technological step:
(1) polyvinyl alcohol is added to the water, is heated to 80～90 ℃, then add Virahol and ethylene glycol dimethacrylate, stir;
(2) be cooled to 60～70 ℃, add vinyl acetate and butyl acrylate, with nitrogen protection, dispersed with stirring is even;
(3) be warming up to 80～90 ℃, add all the other components except sodium bicarbonate, stir;
(4) be cooled to room temperature, add sodium bicarbonate, regulate PH to 5.5, after filtration, get final product to obtain finished product.