CN104497895A - Novel wood floor adhesive - Google Patents
Novel wood floor adhesive Download PDFInfo
- Publication number
- CN104497895A CN104497895A CN201410691621.9A CN201410691621A CN104497895A CN 104497895 A CN104497895 A CN 104497895A CN 201410691621 A CN201410691621 A CN 201410691621A CN 104497895 A CN104497895 A CN 104497895A
- Authority
- CN
- China
- Prior art keywords
- parts
- adhesive
- tackiness agent
- cyanoacrylate
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel wood floor adhesive. The adhesive is prepared by using the following raw materials, by weight, 5-10 parts of sodium polyacrylate, 0.5-1.7 parts of titanium dioxide, 1.5-3 parts of ethyl alpha-cyanoacrylate, 2.5-4.3 parts of alkyl polyglycoside, 1.5-2.8 parts of steam-exploded lignin, 1.2-3.6 parts of polyethylidene maleic acid, 0.5-1.2 parts of sodium diacetate and 0.9-2.2 parts of guanidine hydrochloride. Compared with present adhesives, the adhesive disclosed in the invention has the advantages of strong adhesion, no shedding, easily available raw materials, simple preparation technology, no benzene or aldehyde, non-toxicity, harmlessness, environmental protection, low carbon, high solid content, small shrinkage, good initial tack, fast drying speed, freeze resistance and easy gluing.
Description
Technical field
The present invention relates to a kind of wood flooring tackiness agent, belong to building material field.
Background technology
Solid wooden floor board is the floor decorative material of formation after natural timber drying, processing.The natural wood texture that it presents and colour image, give nature, soft, the texture that is rich in avidity, become the ideal material of the ground surface finishings such as bedroom, parlor, study simultaneously due to the characteristic that it is cool in summer and warm in winter, sense of touch is good.Solid wooden floor board in use, often needs at its surface adhesion some decorative pattern, pigment etc., therefore needs to use tackiness agent.But existing sizing agent exists stickiness difference, easily come off and high in cost of production shortcoming.
Summary of the invention
For the deficiency that prior art exists, technical problem to be solved by this invention is, provides a kind of wood flooring tackiness agent, and can to bond some decorative pattern, pigment etc. at floor surface, stickiness is strong, and difficult drop-off is with low cost.
For solving the problems of the technologies described above, the technical scheme that the present invention takes is, a kind of wood flooring tackiness agent,
Be made up of the raw material of following parts by weight: sodium polyacrylate 5-10 part, titanium dioxide 0.5-1.7 part, alpha-cyanoacrylate second fat 1.5-3 part, alkyl polyglycoside 2.5-4.3 part, steam explosion xylogen 1.5-2.8 part, poly-polyethylene toxilic acid 1.2-3.6 part, sodium Diacetate 0.5-1.2 part and Guanidinium hydrochloride 0.9-2.2 part.
Optimize, above-mentioned wood flooring tackiness agent, be made up of the raw material of following parts by weight:
Sodium polyacrylate 8 parts, titanium dioxide 1.3 parts, 2.3 parts, alpha-cyanoacrylate second fat, alkyl polyglycoside 3.8 parts, steam explosion xylogen 1.5-2.82.1 part, poly-polyethylene toxilic acid 2.5 parts, sodium Diacetate 0.8 part and Guanidinium hydrochloride 1.8 parts.
Tackiness agent of the present invention is compared with existing tackiness agent, and cohesive force is strong, be not easy to come off, raw material is easy to get, preparation technology is simple; Without benzene, without aldehyde, nontoxic, harmless, environmental protection, low-carbon (LC), also have that solid content is high, shrinking percentage is little, tack is good, a rate of drying advantage such as antifreeze, easy gluing soon.
Embodiment
embodiment 1
The present invention is a kind of wood flooring tackiness agent, is made up of the raw material of following parts by weight:
Sodium polyacrylate 5 parts, titanium dioxide 0.5 part, 1.5 parts, alpha-cyanoacrylate second fat, alkyl polyglycoside 2.5 parts, 1.5 parts, steam explosion xylogen, poly-polyethylene toxilic acid 1.2 parts, sodium Diacetate 0.5 part and Guanidinium hydrochloride 0.9 part.
embodiment 2
The present invention is a kind of wood flooring tackiness agent, is made up of the raw material of following parts by weight:
Sodium polyacrylate 10 parts, titanium dioxide 1.7 parts, 3 parts, alpha-cyanoacrylate second fat, alkyl polyglycoside 4.3 parts, 2.8 parts, steam explosion xylogen, poly-polyethylene toxilic acid 3.6 parts, sodium Diacetate 1.2 parts and Guanidinium hydrochloride 2.2 parts.
embodiment 3
The present invention is a kind of wood flooring tackiness agent, is made up of the raw material of following parts by weight:
Sodium polyacrylate 8 parts, titanium dioxide 1.3 parts, 2.3 parts, alpha-cyanoacrylate second fat, alkyl polyglycoside 3.8 parts, steam explosion xylogen 1.5-2.82.1 part, poly-polyethylene toxilic acid 2.5 parts, sodium Diacetate 0.8 part and Guanidinium hydrochloride 1.8 parts.
Tackiness agent of the present invention is compared with existing tackiness agent, and cohesive force is strong, be not easy to come off, raw material is easy to get, preparation technology is simple; Without benzene, without aldehyde, nontoxic, harmless, environmental protection, low-carbon (LC), also have that solid content is high, shrinking percentage is little, tack is good, a rate of drying advantage such as antifreeze, easy gluing soon.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned citing; those skilled in the art; in essential scope of the present invention, the change made, remodeling, interpolation or replacement, all should belong to protection scope of the present invention.
Claims (2)
1. a wood flooring tackiness agent, is characterized in that: be made up of the raw material of following parts by weight:
Sodium polyacrylate 5-10 part, titanium dioxide 0.5-1.7 part, alpha-cyanoacrylate second fat 1.5-3 part, alkyl polyglycoside 2.5-4.3 part, steam explosion xylogen 1.5-2.8 part, poly-polyethylene toxilic acid 1.2-3.6 part, sodium Diacetate 0.5-1.2 part and Guanidinium hydrochloride 0.9-2.2 part.
2. wood flooring tackiness agent according to claim 1, is characterized in that:
Be made up of the raw material of following parts by weight: sodium polyacrylate 8 parts, titanium dioxide 1.3 parts, 2.3 parts, alpha-cyanoacrylate second fat, alkyl polyglycoside 3.8 parts, steam explosion xylogen 1.5-2.82.1 part, poly-polyethylene toxilic acid 2.5 parts, sodium Diacetate 0.8 part and Guanidinium hydrochloride 1.8 parts.