CN107740554A - Solid wood stone plastic floor and preparation method thereof - Google Patents
Solid wood stone plastic floor and preparation method thereof Download PDFInfo
- Publication number
- CN107740554A CN107740554A CN201710917476.5A CN201710917476A CN107740554A CN 107740554 A CN107740554 A CN 107740554A CN 201710917476 A CN201710917476 A CN 201710917476A CN 107740554 A CN107740554 A CN 107740554A
- Authority
- CN
- China
- Prior art keywords
- solid wood
- stone
- base layer
- molding base
- plastic floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of solid wood stone plastic floor and preparation method thereof.The solid wood stone plastic floor includes stone molding base layer and solid wood epidermis, and the solid wood epidermis is by melt viscosity together on the stone molding base layer.Solid wood stone plastic floor of the present invention, glued on stone molding base layer and set solid wood epidermis so that product seems very naturally, overall structure is close with solid wooden floor board, while has the fragrance of solid wood, more green as a result of solid wood as epidermis.Because solid wood beneath epidermal layers are stone molding base layers, it has preferable water proofing property and stability, and solid wood epidermis is only the relatively thin Rotating fields of floor surface, and therefore, whole flooring product possesses good water resistance.
Description
Technical field
The present invention relates to technical field of floor, more particularly to a kind of solid wood stone plastic floor and preparation method thereof.
Background technology
Solid wooden floor board is the main product of domestic market, and it has the texture and fragrance of solid wood, but solid wooden floor board is present
The problem of water proofing property difference, in the plum rain season of south China, solid wooden floor board is easy to make moist and buckling deformation or damage occurs.Stone
It is that it has preferable water proofing property and stability using stone flour, polyvinyl chloride as floor made of primary raw material to mould floor, but not enough
Environmental protection.
The content of the invention
The invention aims to solve the above problems, there is provided a kind of solid wood stone plastic floor, it combines solid wooden floor board
With the advantage of stone plastic floor, the problem of can solve the problem that floor water proofing property difference, and environmentally friendly raw material is used, it is more green.
In order to achieve the above object, the present invention provides a kind of solid wood stone plastic floor, including stone molding base layer and solid wood epidermis
Layer, the solid wood epidermis is by melt viscosity together on the stone molding base layer.
In one embodiment of the invention, the thickness of the solid wood epidermis is 0.6mm-2.0mm.
In one embodiment of the invention, the thickness of the stone molding base layer is 2.5mm-7.0mm.
In one embodiment of the invention, the stone molding base layer is mainly made up of the raw material of following parts by weight：Polyvinyl chloride
40-60 parts, calcium carbonate 80-120 parts, calcium-zinc composite stabilizing agent 6-8 parts, stearic acid 0.7-0.8 parts, Tissuemat E 0.6-0.8 parts,
Acrylic polymer 4-6 parts, haloflex 4-6 parts.
In one embodiment of the invention, the stone molding base layer is formed towards the surface of solid wood epidermis by frosted processing
Rough surface, hot-melt are overlayed on the rough surface.
In one embodiment of the invention, the solid wood epidermis upper surface is coated with marine glue.
The present invention also provides a kind of preparation method of solid wood stone plastic floor, for the solid wood stone described in any of the above embodiment
Floor is moulded, the preparation method comprises the following steps：
According to the formula mixing stone molding base layer raw material of stone molding base layer, by five temperature-controlled areas to mixed original
Material is heated, and then by mould shape slice, and by the pressure roller of one group of control thickness, obtains the stone modeling base of predetermined thickness
Material layer；
Frosted processing is carried out to the surface of stone molding base layer, rough surface is formed it into, in stone molding base layer
Rough surface coating hot-melt adhesive, solid wood epidermis is fitted on the stone molding base layer for scribbling PUR, you can obtain
Solid wood stone plastic floor.
In one embodiment of the invention, the temperature of five temperature-controlled areas is followed successively by：First 175-205 DEG C of area, the secondth area
170-205 DEG C, the 3rd 155-185 DEG C of area, the 4th 150-180 DEG C of area, the 5th 160-190 DEG C of area.
Compared with prior art, the beneficial effect of the technical program is：
Solid wood stone plastic floor of the present invention, glued on stone molding base layer and set solid wood epidermis so that product seems very certainly
So, overall structure is close with solid wooden floor board, while has the fragrance of solid wood, greener as a result of solid wood as epidermis
Colour circle is protected.Because solid wood beneath epidermal layers are stone molding base layers, it has preferable a water proofing property and stability, and solid wood epidermis
Only it is the relatively thin Rotating fields of floor surface, therefore, whole flooring product possesses good water resistance.
Brief description of the drawings
Fig. 1 is the structural representation of an embodiment of solid wood stone plastic floor of the present invention.
Embodiment
Below in conjunction with the accompanying drawings, by specific embodiment, clear, complete description is carried out to technical scheme.
It refer to shown in Fig. 1, the present invention provides a kind of solid wood stone plastic floor, including stone molding base layer 1 and solid wood epidermis
2, the solid wood epidermis 2 is by melt viscosity together on the stone molding base layer 1.
Solid wood stone plastic floor of the present invention, glued on stone molding base layer 1 and set solid wood epidermis 2 so that product seems very
Naturally, overall structure is close with solid wooden floor board, while has the fragrance of solid wood, as a result of solid wood as epidermis, more
It is green.Because the lower section of solid wood epidermis 2 is stone molding base layer 1, it has preferable a water proofing property and stability, and solid wood table
Cortex 1 is only the relatively thin Rotating fields of floor surface, and therefore, whole flooring product possesses good water resistance.
The thickness of the solid wood epidermis 2 is 0.6mm-2.0mm.
The thickness of the stone molding base layer 1 is 2.5mm-7.0mm.
The stone molding base layer is mainly made up of the raw material of following parts by weight：Polyvinyl chloride 40-60 parts, calcium carbonate 80-120
Part, calcium-zinc composite stabilizing agent 6-8 parts, stearic acid 0.7-0.8 parts, Tissuemat E 0.6-0.8 parts, acrylic polymer 4-6
Part, haloflex 4-6 parts.Stone molding base layer has preferable stability made from the composition of raw materials, its expansion rate and contraction
Rate is not susceptible to warpage all than relatively low.
The stone molding base layer 1 forms rough surface towards the surface of solid wood epidermis 2 by frosted processing, heat
Melten gel is coated on the rough surface.Frosted processing is carried out to stone molding base layer 1 can cause PUR more uniformly
Surface coated on stone molding base layer 1, so as to which solid wood epidermis 2 preferably can fit together with stone molding base layer 1.
Further, the upper surface of solid wood epidermis 2 is coated with marine glue so that floor has more preferable water proofing property
Energy.
The present invention also provides a kind of preparation method of solid wood stone plastic floor, for preparing the reality described in any of the above embodiment
Wooden stone plastic floor, the preparation method comprise the following steps：
According to the formula mixing stone molding base layer raw material of stone molding base layer, by five temperature-controlled areas to mixed original
Material is heated, and the temperature of five temperature-controlled areas is followed successively by：First 175-205 DEG C of area, the second 170-205 DEG C of area, the 3rd area
155-185 DEG C, the 4th 150-180 DEG C of area, the 5th 160-190 DEG C of area.Then pass through mould shape slice, and pass through one group of control
The pressure roller of thickness, obtain the stone molding base layer of predetermined thickness.
Frosted processing is carried out to the surface of stone molding base layer, rough surface is formed it into, in stone molding base layer
Rough surface coating hot-melt adhesive, solid wood epidermis is fitted on the stone molding base layer for scribbling PUR, you can obtain
Solid wood stone plastic floor.
Embodiment 1
A kind of solid wood stone plastic floor, including stone molding base layer and solid wood epidermis, the solid wood epidermis pass through PUR
It is bonded on the stone molding base layer.The solid wood epidermis upper surface is coated with marine glue.The thickness of the solid wood epidermis
For 0.6mm.The thickness of the stone molding base layer is 2.5mm.
Above-described solid wood stone plastic floor is prepared by the following method：
Stone molding base layer raw material is mixed according to the component of following parts by weight：40 parts of polyvinyl chloride, 80 parts of calcium carbonate, calcium zinc is answered
Close 6 parts of stabilizer, 0.7 part of stearic acid, 0.6 part of Tissuemat E, 4 parts of acrylic polymer, 4 parts of haloflex.By
Five temperature-controlled areas are heated to mixed raw material, and the temperature of five temperature-controlled areas is followed successively by：First 175 DEG C of area,
Second 170 DEG C of area, the 3rd 155 DEG C of area, the 4th 150 DEG C of area, the 5th 160 DEG C of area.Then mould shape slice is passed through, and by one
The pressure roller of group control thickness, obtains the stone molding base layer of predetermined thickness.
Frosted processing is carried out to the surface of stone molding base layer, rough surface is formed it into, in stone molding base layer
Rough surface coating hot-melt adhesive, solid wood epidermis is fitted on the stone molding base layer for scribbling PUR, you can obtain
Solid wood stone plastic floor.
Embodiment 2
A kind of solid wood stone plastic floor, including stone molding base layer and solid wood epidermis, the solid wood epidermis pass through PUR
It is bonded on the stone molding base layer.The solid wood epidermis upper surface is coated with marine glue.The thickness of the solid wood epidermis
For 1.0mm.The thickness of the stone molding base layer is 3.0mm.
Above-described solid wood stone plastic floor is prepared by the following method：
Stone molding base layer raw material is mixed according to the component of following parts by weight：50 parts of polyvinyl chloride, 110 parts of calcium carbonate, calcium zinc
6 parts of compound stabilizer, 0.7 part of stearic acid, 0.6 part of Tissuemat E, 4 parts of acrylic polymer, 4 parts of haloflex.Through
Cross five temperature-controlled areas to heat mixed raw material, the temperature of five temperature-controlled areas is followed successively by：First area 180
DEG C, the second 175 DEG C of area, the 3rd 165 DEG C of area, the 4th 160 DEG C of area, the 5th 170 DEG C of area.Then pass through mould shape slice, and pass through
The pressure roller of one group of control thickness is crossed, obtains the stone molding base layer of predetermined thickness.
Frosted processing is carried out to the surface of stone molding base layer, rough surface is formed it into, in stone molding base layer
Rough surface coating hot-melt adhesive, solid wood epidermis is fitted on the stone molding base layer for scribbling PUR, you can obtain
Solid wood stone plastic floor.
Embodiment 3
A kind of solid wood stone plastic floor, including stone molding base layer and solid wood epidermis, the solid wood epidermis pass through PUR
It is bonded on the stone molding base layer.The solid wood epidermis upper surface is coated with marine glue.The thickness of the solid wood epidermis
For 1.0mm.The thickness of the stone molding base layer is 5.0mm.
Above-described solid wood stone plastic floor is prepared by the following method：
Stone molding base layer raw material is mixed according to the component of following parts by weight：60 parts of polyvinyl chloride, 120 parts of calcium carbonate, calcium zinc
8 parts of compound stabilizer, 0.8 part of stearic acid, 0.8 part of Tissuemat E, 6 parts of acrylic polymer, 6 parts of haloflex.Through
Cross five temperature-controlled areas to heat mixed raw material, the temperature of five temperature-controlled areas is followed successively by：First area 205
DEG C, the second 205 DEG C of area, the 3rd 185 DEG C of area, the 4th 180 DEG C of area, the 5th 190 DEG C of area.Then pass through mould shape slice, and pass through
The pressure roller of one group of control thickness is crossed, obtains the stone molding base layer of predetermined thickness.
Frosted processing is carried out to the surface of stone molding base layer, rough surface is formed it into, in stone molding base layer
Rough surface coating hot-melt adhesive, solid wood epidermis is fitted on the stone molding base layer for scribbling PUR, you can obtain
Solid wood stone plastic floor.
Embodiment 4
A kind of solid wood stone plastic floor, including stone molding base layer and solid wood epidermis, the solid wood epidermis pass through PUR
It is bonded on the stone molding base layer.The solid wood epidermis upper surface is coated with marine glue.The thickness of the solid wood epidermis
For 1.5mm.The thickness of the stone molding base layer is 6.0mm.
Above-described solid wood stone plastic floor is prepared by the following method：
Stone molding base layer raw material is mixed according to the component of following parts by weight：50 parts of polyvinyl chloride, 110 parts of calcium carbonate, calcium zinc
7 parts of compound stabilizer, 0.7 part of stearic acid, 0.7 part of Tissuemat E, 5 parts of acrylic polymer, 5 parts of haloflex.Through
Cross five temperature-controlled areas to heat mixed raw material, the temperature of five temperature-controlled areas is followed successively by：First area 191
DEG C, the second 188 DEG C of area, the 3rd 170 DEG C of area, the 4th 165 DEG C of area, the 5th 175 DEG C of area.Then pass through mould shape slice, and pass through
The pressure roller of one group of control thickness is crossed, obtains the stone molding base layer of predetermined thickness.
Frosted processing is carried out to the surface of stone molding base layer, rough surface is formed it into, in stone molding base layer
Rough surface coating hot-melt adhesive, solid wood epidermis is fitted on the stone molding base layer for scribbling PUR, you can obtain
Solid wood stone plastic floor.
Embodiment 5
A kind of solid wood stone plastic floor, including stone molding base layer and solid wood epidermis, the solid wood epidermis pass through PUR
It is bonded on the stone molding base layer.The solid wood epidermis upper surface is coated with marine glue.The thickness of the solid wood epidermis
For 2.0mm.The thickness of the stone molding base layer is 7.0mm.
Above-described solid wood stone plastic floor is prepared by the following method：
Stone molding base layer raw material is mixed according to the component of following parts by weight：55 parts of polyvinyl chloride, 115 parts of calcium carbonate, calcium zinc
7 parts of compound stabilizer, 0.7 part of stearic acid, 0.8 part of Tissuemat E, 4 parts of acrylic polymer, 4 parts of haloflex.Through
Cross five temperature-controlled areas to heat mixed raw material, the temperature of five temperature-controlled areas is followed successively by：First area 200
DEG C, the second 195 DEG C of area, the 3rd 182 DEG C of area, the 4th 175 DEG C of area, the 5th 185 DEG C of area.Then pass through mould shape slice, and pass through
The pressure roller of one group of control thickness is crossed, obtains the stone molding base layer of predetermined thickness.
Frosted processing is carried out to the surface of stone molding base layer, rough surface is formed it into, in stone molding base layer
Rough surface coating hot-melt adhesive, solid wood epidermis is fitted on the stone molding base layer for scribbling PUR, you can obtain
Solid wood stone plastic floor.
Comparative example 1
A kind of wood floor, its thickness are identical with the solid wood stone plastic floor of embodiment 1.
The performance on the floor of embodiment 1-5 and comparative example 1 is detected, test result is as shown in table 1 below.
Expansion rate is tested：50 DEG C of floor expansion rate is determined using precision high temperature roaster HQ-WG-550.
Shrinkage factor is tested：80 DEG C of floor shrinkage factor is determined using precision high temperature roaster HQ-WG-550.
Table 1
It was found from upper table 1, the present embodiment 1-5 stone plastic floor have with solid wooden floor board identical wood grain and fragrance,
And water proofing property is preferable, there is relatively low expansion rate, shrinkage factor, performance is more stablized.
Although the present invention is disclosed as above with preferred embodiment, it is not for limiting the present invention, any this area
Technical staff without departing from the spirit and scope of the present invention, may be by the methods and technical content of the disclosure above to this hair
Bright technical scheme makes possible variation and modification, therefore, every content without departing from technical solution of the present invention, according to the present invention
Any simple modifications, equivalents, and modifications made to above example of technical spirit, belong to technical solution of the present invention
Protection domain.
Claims (8)
1. a kind of solid wood stone plastic floor, it is characterised in that including stone molding base layer and solid wood epidermis, the solid wood epidermis leads to
PUR is crossed to be bonded on the stone molding base layer.
2. solid wood stone plastic floor according to claim 1, it is characterised in that the thickness of the solid wood epidermis is 0.6mm-
2.0mm。
3. solid wood stone plastic floor according to claim 1, it is characterised in that the thickness of the stone molding base layer is 2.5mm-
7.0mm。
4. solid wood stone plastic floor according to claim 1, it is characterised in that the stone molding base layer is mainly by following weight
The raw material of part is made：Polyvinyl chloride 40-60 parts, calcium carbonate 80-120 parts, calcium-zinc composite stabilizing agent 6-8 parts, stearic acid 0.7-0.8
Part, Tissuemat E 0.6-0.8 parts, acrylic polymer 4-6 parts, haloflex 4-6 parts.
5. solid wood stone plastic floor according to claim 1, it is characterised in that the stone molding base layer is towards solid wood epidermis
Surface form rough surface by frosted processing, hot-melt is overlayed on the rough surface.
6. solid wood stone plastic floor according to claim 1, it is characterised in that the solid wood epidermis upper surface is coated with anti-
Glue.
7. a kind of preparation method of solid wood stone plastic floor, for preparing any described solid wood stone plastic floors of claim 1-6, its
It is characterised by, the preparation method comprises the following steps：
According to the formula mixing stone molding base layer raw material of stone molding base layer, mixed raw material is entered by five temperature-controlled areas
Row heating, then by mould shape slice, and by the pressure roller of one group of control thickness, obtain the stone molding base of predetermined thickness
Layer；
Frosted processing is carried out to the surface of stone molding base layer, rough surface is formed it into, in the bumps of stone molding base layer
Uneven surface coating hot-melt adhesive, solid wood epidermis is fitted on the stone molding base layer for scribbling PUR, you can obtain solid wood
Stone plastic floor.
8. the preparation method of solid wood stone plastic floor according to claim 7, it is characterised in that the temperature of five temperature-controlled areas
Degree is followed successively by：First 175-205 DEG C of area, the second 170-205 DEG C of area, the 3rd 155-185 DEG C of area, the 4th 150-180 DEG C of area, the 5th
160-190 DEG C of area.