CN104972522A - Recycled equal-width butting-joint composite board plain panel production method and product - Google Patents
Recycled equal-width butting-joint composite board plain panel production method and product Download PDFInfo
- Publication number
- CN104972522A CN104972522A CN201510391339.3A CN201510391339A CN104972522A CN 104972522 A CN104972522 A CN 104972522A CN 201510391339 A CN201510391339 A CN 201510391339A CN 104972522 A CN104972522 A CN 104972522A
- Authority
- CN
- China
- Prior art keywords
- product
- production method
- side pressure
- wide
- template
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a recycled equal-width butting-joint composite board plain panel production method and a product. The method is implemented as the following steps that a, abandoned building construction composite boards are purchased; b, small layer boards are sorted out according to types, and nails and surface impurities are removed; c, end cropping is conducted by a right angle trimming machine; d, a multifunctional multiple-blade saw is used for cutting the small layer boards into long strips with equal widths and thicknesses, and all the impurities on the surface layer are removed at the same time; e, the small layer boards are put into templates for being preliminarily jointed into shaping panels after being gummed by an automatic gumming machine, and a plurality of solid wood middle skins are pasted on the width direction to serve as ribs; f, the shaping panels together with the templates are put into an all-round side pressure hot press in a layered mode for being subjected to synchronous hot pressing and side pressing; g, flat grinding and sanding are conducted by a sander after cooling; h, the four edges are cut by a four-side trimming machine, and then the product is obtained. The product can be widely used in the industries of furniture, decoration, ornament and wooden doors and can also be used as a basal plate and the middle material of panels for other purposes.
Description
Technical field
The present invention relates to a kind of production method and product of sheet material, particularly relate to a kind of production method and the product that regenerate wide docking multilayer laminin plate.
Background technology
As everyone knows, current China furniture, dress is drilled, decoration, the raw material that timber industry uses use solid wood board usually, finger-jointed plate, glued board etc., and high-end sheet material is as solid wood board, splice plate, finger-jointed plate is very expensive, although the high-quality glued board at present between solid wood and composite board is pure wood products, because adopting conventional art, process and structure fabrication, product quality can not meet the needs of people, and to there is a lot of discarded multi-layer sheet in existing building woodworking be not recycled utilization, the direct burning had, cause air environmental pollution on the one hand, bring again the significant wastage of timber resources on the other hand.
Summary of the invention
The object of the invention is to provide one can effectively reduce product cost, economize on resources, realize turning waste into wealth to overcome the deficiencies in the prior art, the production method of the strong regeneration protected forest resources wide docking multilayer laminin plate and product.Its concrete technical scheme is: a kind of production method regenerating wide docking multilayer laminin plate, follows these steps to carry out,
A, the discarded construction multi-layer sheet of purchase;
B, classification are picked out little laminate and remove nail, removal surface impurity;
C, use right angle bead cutter crop;
D, with multi-functional multiple blade saw the little laminate after crop be cut into the rectangular of wide uniform thickness and remove supracutaneous all impurity simultaneously;
E, be template with putting into after automatic glue spreaders gluing that template just spells, on width is pasted in several solid wood skin as rib;
F, put into four sides side pressure hot press synchronous hot pressing, side pressure together with template layering;
G, cooling after with sander sand flat, sanding;
H, cut four limits with four limit bead cutters and namely obtain product.
In said several solid wood, skin is as rib, and its quantity is 2-8 root.
Said in the synchronous hot pressing of four sides side pressure hot press, side pressure, its side pressure pressure is 6-16MPa, positive pressure pressure is 6-16MPa, temperature is 80-100 DEG C, the time is 4-15 minute.
As can be seen from technical scheme of the present invention, after little laminate in discarded construction multi-layer sheet carries out processing by method of the present invention, become the finished multi-layer plate with enough Strong degree, furniture can be widely used in, dress is drilled, decorated, timber industry, also can be used as substrate and the intermediate materials of other purposes sheet material.Can also cut into the rectangular sale that user needs, and cost ratio market like product is low, fullys meet the present invention and can effectively reduce product cost, economizes on resources, realize turning waste into wealth, the strong goal of the invention protected forest resources.
Detailed description of the invention
Embodiment 1, a kind of production method regenerating wide docking multilayer laminin plate, follow these steps to carry out,
A, the discarded construction multi-layer sheet of purchase;
B, classification are picked out little laminate and remove nail, removal surface impurity;
C, use right angle bead cutter crop;
D, with multi-functional multiple blade saw the little laminate after crop be cut into the rectangular of wide uniform thickness and remove supracutaneous all impurity simultaneously;
E, be template with putting into after automatic glue spreaders gluing that template just spells, on width is pasted in two solid woods skin as rib;
F, to put into four sides side pressure hot press synchronous hot pressing, side pressure (side pressure pressure is 6MPa, positive pressure pressure is 6MPa, temperature is 80 DEG C, time be 15 minutes) together with template layering;
G, cooling after with sander sand flat, sanding;
H, cut four limits with four limit bead cutters and namely obtain product.
Embodiment 2, a kind of production method regenerating wide docking multilayer laminin plate, follow these steps to carry out,
A, the discarded construction multi-layer sheet of purchase;
B, classification are picked out little laminate and remove nail, removal surface impurity;
C, use right angle bead cutter crop;
D, with multi-functional multiple blade saw the little laminate after crop be cut into the rectangular of wide uniform thickness and remove supracutaneous all impurity simultaneously;
E, be template with putting into after automatic glue spreaders gluing that template just spells, on width is pasted in 5 solid woods skin as rib;
F, to put into four sides side pressure hot press synchronous hot pressing, side pressure (side pressure pressure is 11MPa, positive pressure pressure is 11MPa, temperature is 90 DEG C, time be 10 minutes) together with template layering;
G, cooling after with sander sand flat, sanding;
H, cut four limits with four limit bead cutters and namely obtain product.
Embodiment 3, a kind of production method regenerating wide docking multilayer laminin plate, follow these steps to carry out,
A, the discarded construction multi-layer sheet of purchase;
B, classification are picked out little laminate and remove nail, removal surface impurity;
C, use right angle bead cutter crop;
D, with multi-functional multiple blade saw the little laminate after crop be cut into the rectangular of wide uniform thickness and remove supracutaneous all impurity simultaneously;
E, be template with putting into after automatic glue spreaders gluing that template just spells, on width is pasted in 8 solid woods skin as rib;
F, to put into four sides side pressure hot press synchronous hot pressing, side pressure (side pressure pressure is 16MPa, positive pressure pressure is 16MPa, temperature is 100 DEG C, time be 4 minutes) together with template layering;
G, cooling after with sander sand flat, sanding;
H, cut four limits with four limit bead cutters and namely obtain product.
Claims (4)
1. regenerate a production method for wide docking multilayer laminin plate, it is characterized in that: follow these steps to carry out,
A, the discarded construction multi-layer sheet of purchase;
B, classification are picked out little laminate and remove nail, removal surface impurity;
C, use right angle bead cutter crop;
D, with multi-functional multiple blade saw the little laminate after crop be cut into the rectangular of wide uniform thickness and remove supracutaneous all impurity simultaneously;
E, be template with putting into after automatic glue spreaders gluing that template just spells, on width is pasted in several solid wood skin as rib;
F, put into four sides side pressure hot press synchronous hot pressing, side pressure together with template layering;
G, cooling after with sander sand flat, sanding;
H, cut four limits with four limit bead cutters and namely obtain product.
2. a kind of production method regenerating wide docking multilayer laminin plate according to claim 1, it is characterized in that: in said several solid wood, skin is as rib, its quantity is 2-8 root.
3. a kind of production method regenerating wide docking multilayer laminin plate according to claim 1, it is characterized in that: said in the synchronous hot pressing of four sides side pressure hot press, side pressure, its side pressure pressure is 6-16MPa, positive pressure pressure is 6-16MPa, temperature is 80-100 DEG C, the time is 4-15 minute.
4. regenerate a wide docking multilayer laminin plate, it is characterized in that: the product that method according to claim 1 obtains.