CN104985651A - Producing method and product of regeneration solid wood finger joint laminated board - Google Patents
Producing method and product of regeneration solid wood finger joint laminated board Download PDFInfo
- Publication number
- CN104985651A CN104985651A CN201510391436.2A CN201510391436A CN104985651A CN 104985651 A CN104985651 A CN 104985651A CN 201510391436 A CN201510391436 A CN 201510391436A CN 104985651 A CN104985651 A CN 104985651A
- Authority
- CN
- China
- Prior art keywords
- machine
- solid wood
- side pressure
- waste
- battens
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a producing method and product of a regeneration solid wood finger joint laminated board. The producing method comprises the following steps that waste battens for building construction are purchased; nails and surface impurities are removed; the ends of the waste battens are cut through a right-angle edge cutting machine, and the waste battens are classified according the thickness and dried; the ends of the waste battens are cut and combed through a comb machine; the toothed surfaces, obtained through combing, of the waste battens are coated with glue; the waste battens are spliced and lengthened through an automatic lengthening machine and cut to a regulated length; a multifunctional multi-blade saw is used for fixing the width and the thickness of the waste battens and removing surface impurities; an automatic glue coating machine is used for gluing; the waste battens are laid on a cold splicing machine to form needed formed boards, specifically, shaping clamp bars are used for clamping wide edges of the formed boards after side pressure primary shaping, then the formed boards are taken off from the cold splicing machine and stored for 2-8 hours, and the formed boards are formed by taking off the shaping clamp bars after full bonding of glue and hardening; or the waste battens are spliced in a template to form the formed boards, specifically, the waste battens and the template together enter a multilayer four-faced side pressure heat press in a laminated mode for synchronous hot pressing to form the formed boards; a sanding machine is used for thickness fixing, sand-flattening and sanding; a four-side edge cutting machine is used for cutting edges, and therefore the product is obtained.
Description
Technical field
The present invention relates to a kind of production method and product of sheet material, particularly relate to a kind of production method and the product that regenerate solid wood finger-jointed plate.
Background technology
As everyone knows, current China furniture, dress is drilled, decoration, the raw material that timber industry uses use solid wood board usually, finger-jointed plate, glued board etc., and high-end sheet material is as solid wood board, splice plate, finger-jointed plate is very expensive, although the high-quality glued board at present between solid wood and composite board is pure wood products, because adopting conventional art, process and structure fabrication, product quality can not meet the needs of people, and to there is a lot of waste wood in existing building woodworking be not recycled utilization, the direct burning had, cause air environmental pollution on the one hand, bring again the significant wastage of timber resources on the other hand.
Summary of the invention
The object of the invention is to provide one can effectively reduce product cost, economize on resources, realize turning waste into wealth to overcome the deficiencies in the prior art, the production method of the strong regeneration solid wood finger-jointed plate protected forest resources and product.Its concrete technical scheme is: a kind of production method regenerating solid wood finger-jointed plate, follows these steps to carry out:
A, the discarded construction batten of purchase;
B, go nail, remove surface impurity;
C, use right angle bead cutter crop, by thickness classification, dry;
D, use rack shaper crop, comb;
E, on the flank of tooth combed out gluing;
F, with automatic lengthening machine splicing spreading, and by the length of regulation;
G, with multi-functional multiple blade saw fixed width, fixed thick, removing epidermis impurity;
H, use automatic glue spreaders gluing;
I, on cold spelling machine, be paved into desired profiled sheeting, by side pressure initial shaping, then clamp broadside with sizing clamp bar, then take off from cold spelling machine, place after 2-8 hour, allow glue fully bond, taking off sizing clamp bar after sclerosis becomes profiled sheeting; Or template is spliced in template, entering the synchronous hot pressing of multilayer four sides side pressure hot press together with template layering becomes profiled sheeting;
J, with sander fixed thick, sand flat, sanding;
K, namely obtain product with after four limit bead cutter trimmings.
Saidly on cold spelling machine, carry out side pressure, its pressure is 8-16MPa, the time is 5-15 minute.
Said in the synchronous hot pressing of multilayer four sides side pressure hot press, its side pressure pressure is 8-16MPa, positive pressure pressure is 8-16MPa, temperature is 100-180 DEG C, and the time is 10-30 minute.
As can be seen from technical scheme of the present invention, after discarded construction batten carries out processing by method of the present invention, become the solid wood board with enough Strong degree, furniture can be widely used in, dress is drilled, decorated, timber industry, also can be used as the substrate of other purposes sheet material.Can also cut into the rectangular sale that user needs, and cost ratio market like product is low, fullys meet the present invention and can effectively reduce product cost, economizes on resources, realize turning waste into wealth, the strong goal of the invention protected forest resources.
Detailed description of the invention
Embodiment 1, a kind of production method regenerating solid wood finger-jointed plate, follow these steps to carry out,
A, the discarded construction batten of purchase;
B, go nail, remove surface impurity;
C, use right angle bead cutter crop, by thickness classification, dry;
D, use rack shaper crop, comb;
E, on the flank of tooth combed out gluing;
F, with automatic lengthening machine splicing spreading, and by the length of regulation;
G, with multi-functional multiple blade saw fixed width, fixed thick, removing epidermis impurity;
H, use automatic glue spreaders gluing;
I, on cold spelling machine, be paved into desired profiled sheeting, by side pressure (its pressure be 8MPa, time be 15 minutes) initial shaping, then clamp broadside with sizing clamp bar, take off from cold spelling machine again, place after 8 hours, allow glue fully bond, taking off sizing clamp bar after sclerosis becomes profiled sheeting; Or template is spliced in template, entering multilayer four sides side pressure hot press synchronous hot pressing (its side pressure pressure is 8MPa, positive pressure pressure is 8MPa, temperature is 100 DEG C, and the time is 30 minutes) together with template layering becomes profiled sheeting;
J, with sander fixed thick, sand flat, sanding;
K, namely obtain product with after four limit bead cutter trimmings.
Embodiment 2, a kind of production method regenerating solid wood finger-jointed plate, follow these steps to carry out,
A, the discarded construction batten of purchase;
B, go nail, remove surface impurity;
C, use right angle bead cutter crop, by thickness classification, dry;
D, use rack shaper crop, comb;
E, on the flank of tooth combed out gluing;
F, with automatic lengthening machine splicing spreading, and by the length of regulation;
G, with multi-functional multiple blade saw fixed width, fixed thick, removing epidermis impurity;
H, use automatic glue spreaders gluing;
I, on cold spelling machine, be paved into desired profiled sheeting, by side pressure (its pressure be 12MPa, time be 10 minutes) initial shaping, then clamp broadside with sizing clamp bar, take off from cold spelling machine again, place after 5 hours, allow glue fully bond, taking off sizing clamp bar after sclerosis becomes profiled sheeting; Or template is spliced in template, entering multilayer four sides side pressure hot press synchronous hot pressing (its side pressure pressure is 12MPa, positive pressure pressure is 12MPa, temperature is 140 DEG C, and the time is 20 minutes) together with template layering becomes profiled sheeting;
J, with sander fixed thick, sand flat, sanding;
K, namely obtain product with after four limit bead cutter trimmings.
Embodiment 3, a kind of production method regenerating solid wood finger-jointed plate, follow these steps to carry out,
A, the discarded construction batten of purchase;
B, go nail, remove surface impurity;
C, use right angle bead cutter crop, by thickness classification, dry;
D, use rack shaper crop, comb;
E, on the flank of tooth combed out gluing;
F, with automatic lengthening machine splicing spreading, and by the length of regulation;
G, with multi-functional multiple blade saw fixed width, fixed thick, removing epidermis impurity;
H, use automatic glue spreaders gluing;
I, on cold spelling machine, be paved into desired profiled sheeting, by side pressure (its pressure be 16MPa, time be 5 minutes) initial shaping, then clamp broadside with sizing clamp bar, take off from cold spelling machine again, place after 2 hours, allow glue fully bond, taking off sizing clamp bar after sclerosis becomes profiled sheeting; Or template is spliced in template, entering multilayer four sides side pressure hot press synchronous hot pressing (its side pressure pressure is 16MPa, positive pressure pressure is 16MPa, temperature is 180 DEG C, and the time is 10 minutes) together with template layering becomes profiled sheeting;
J, with sander fixed thick, sand flat, sanding;
K, namely obtain product with after four limit bead cutter trimmings.
Claims (4)
1. regenerate a production method for solid wood finger-jointed plate, it is characterized in that: follow these steps to carry out,
A, the discarded construction batten of purchase;
B, go nail, remove surface impurity;
C, use right angle bead cutter crop, by thickness classification, dry;
D, use rack shaper crop, comb;
E, on the flank of tooth combed out gluing;
F, with automatic lengthening machine splicing spreading, and by the length of regulation;
G, with multi-functional multiple blade saw fixed width, fixed thick, removing epidermis impurity;
H, use automatic glue spreaders gluing;
I, on cold spelling machine, be paved into desired profiled sheeting, by side pressure initial shaping, then clamp broadside with sizing clamp bar, then take off from cold spelling machine, place after 2-8 hour, allow glue fully bond, taking off sizing clamp bar after sclerosis becomes profiled sheeting; Or template is spliced in template, entering the synchronous hot pressing of multilayer four sides side pressure hot press together with template layering becomes profiled sheeting;
J, with sander fixed thick, sand flat, sanding;
K, namely obtain product with after four limit bead cutter trimmings.
2. a kind of production method regenerating solid wood finger-jointed plate according to claim 1, is characterized in that: saidly on cold spelling machine, carry out side pressure, and its pressure is 8-16MPa, the time is 5-15 minute.
3. a kind of production method regenerating solid wood finger-jointed plate according to claim 1, it is characterized in that: said in the synchronous hot pressing of multilayer four sides side pressure hot press, its side pressure pressure is 8-16MPa, positive pressure pressure is 8-16MPa, temperature is 100-180 DEG C, and the time is 10-30 minute.
4. regenerate a solid wood finger-jointed plate, it is characterized in that: the product that method according to claim 1 obtains.