CN105150300A - Production method and product for regeneration multilayer solid wood finger joint composite board - Google Patents
Production method and product for regeneration multilayer solid wood finger joint composite board Download PDFInfo
- Publication number
- CN105150300A CN105150300A CN201510391360.3A CN201510391360A CN105150300A CN 105150300 A CN105150300 A CN 105150300A CN 201510391360 A CN201510391360 A CN 201510391360A CN 105150300 A CN105150300 A CN 105150300A
- Authority
- CN
- China
- Prior art keywords
- solid wood
- template
- side pressure
- cold
- pressure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production method and product for a regeneration multilayer solid wood finger joint composite board. The production method comprises the following steps that waste battens and multilayer boards of building operation are purchased; pegs and surface impurities are removed; the battens are made into finger joint solid wood boards; selected big laminates are made into finger joint multilayer boards; small laminates are made into butt joint multilayer boards with uniform width and multilayer splice boards with uniform width; then multiple sheets of boards pass through an automatic double-face glue machine according to the different requirements of thickness of the product required by customers, and are placed in a cold pressing machine in an overlapped mode to be cold pressed and formed together after sizing; and a four-edge trimmer is used for trimming the four edges and the product is obtained. The product can be widely used in industries of furniture, decoration, ornament and wooden doors, and can serve as a base plate for a panel with other purposes. The aims of effectively reducing the production cost, saving resources, achieving the transformation from waste to wealth and effectively protecting forest resources are completely reached.
Description
Technical field
The present invention relates to a kind of production method and product of sheet material, particularly relate to a kind of production method and the product that regenerate multi-layer solid wood finger-jointed composite board.
Background technology
As everyone knows, current China furniture, dress is drilled, decoration, the raw material that timber industry uses use solid wood board usually, finger-jointed plate, glued board etc., and high-end sheet material is as solid wood board, splice plate, finger-jointed plate is very expensive, although the high-quality glued board at present between solid wood and composite board is pure wood products, because adopting conventional art, process and structure fabrication, product quality can not meet the needs of people, and to there is a lot of waste wood in existing building woodworking be not recycled utilization, the direct burning had, cause air environmental pollution on the one hand, bring again the significant wastage of timber resources on the other hand.
Summary of the invention
The object of the invention is to provide one can effectively reduce product cost, economize on resources, realize turning waste into wealth to overcome the deficiencies in the prior art, the production method of the strong regeneration multi-layer solid wood finger-jointed composite board protected forest resources and product.Its concrete technical scheme is: a kind of production method regenerating multi-layer solid wood finger-jointed composite board, follows these steps to carry out,
A, purchase discarded construction batten, composite plate;
Batten, large and small laminate are picked out in b, classification, and remove nail, removal surface impurity;
C, to the batten right angle bead cutter crop selected, by thickness classification, dry; With rack shaper crop, comb; Gluing on the flank of tooth combed out; With automatic lengthening machine splicing spreading, and by the length specified; With multi-functional multiple blade saw fixed width, fixed thick, removing epidermis impurity; Use automatic glue spreaders gluing; Cold spelling machine is paved into desired profiled sheeting, by side pressure initial shaping, then clamps broadside with sizing clamp bar, then take off from cold spelling machine, place after 2-8 hour, allow glue fully bond, taking off sizing clamp bar after sclerosis becomes profiled sheeting; Or template is spliced in template, entering the synchronous hot pressing of multilayer four sides side pressure hot press together with template layering becomes profiled sheeting; With sander fixed thick, sand flat, sanding; The size being cut into regulation with four limit bead cutters obtains finger-joint wood plate;
D, to the large laminate selected with automatically wide be machined to wide rectangular; Wide rectangular two ends rack shaper is cut flat, comb; The flank of tooth combed out is connected into rectangular and to rectangular comb after gluing with automatic spreading rack shaper; By the length of full-automatic lengthening machine by regulation; Docked rectangular for the polylith of fixed length by teeth groove on cold plate joggling apparatus, four sides pressurization, keeps the regular hour to be combined into profiled sheeting; Profiled sheeting used hot press hot pressing, flatten, compress; Cooled profiled sheeting, by the fixed thick sanding of sander, removes top layer impurity; Four limit bead cutters are cut into the size of regulation, obtain finger multilayer laminin plate;
E, to the little laminate right angle bead cutter crop selected; With multi-functional multiple blade saw the little laminate after crop be cut into the rectangular of wide uniform thickness and remove supracutaneous all impurity simultaneously; Be template with putting into after automatic glue spreaders gluing that template just spells, on width is pasted in several solid wood skin as rib; The synchronous hot pressing of four sides side pressure hot press, side pressure is put into together with template layering; After cooling with sander sand flat, sanding; Cut four limits with four limit bead cutters and namely obtain wide docking multilayer laminin plate; Not wide little laminate right angle bead cutter crop; With multi-functional multiple blade saw by trimming, fixed thick and remove supracutaneous all impurity simultaneously; Spread out in solid wood into template after skin gluing with automatic glue spreaders, then the multi-layer sheet after aforementioned processing put into template and just spell as template, on width is pasted in several solid wood skin as rib; The synchronous hot pressing of four sides side pressure hot press, side pressure is put into together with template layering; After cooling with sander sand flat, sanding; Cut four limits with four limit bead cutters and namely obtain splicing multilayer laminin plate;
F, according to the different requirements of user to product thickness, by solid wood board and several plain plates by after automatic double-sided gluing machine applying glue, overlap puts into cold press cold moudling together;
G, cut four limits with four limit bead cutters and namely obtain product.
Saidly on cold spelling machine, carry out side pressure, its pressure is 8-16MPa, the time is 5-15 minute.
Said in the synchronous hot pressing of multilayer four sides side pressure hot press, its side pressure pressure is 8-16MPa, positive pressure pressure is 8-16MPa, temperature is 100-180 DEG C, and the time is 10-30 minute.
Said in cold press cold moudling, its pressure is 8-15MPa, and the time is 2-8 hour.
Said carry out on cold plate joggling apparatus cold spelling sizing, its pressure is 6-15MPa, the time is 4-15 minute.
In said several solid wood, skin is as rib, and its quantity is 2-8 root.
As can be seen from technical scheme of the present invention, after discarded construction batten, multi-layer sheet carry out processing by method of the present invention, become the solid wood composite board with enough Strong degree, furniture can be widely used in, dress is drilled, decorated, timber industry, also can be used as the substrate of other purposes sheet material.Can also cut into the rectangular sale that user needs, and cost ratio market like product is low, fullys meet the present invention and can effectively reduce product cost, economizes on resources, realize turning waste into wealth, the strong goal of the invention protected forest resources.
Detailed description of the invention
Embodiment 1, a kind of production method regenerating multi-layer solid wood finger-jointed composite board, follow these steps to carry out,
A, purchase discarded construction batten, composite plate;
Batten, large and small laminate are picked out in b, classification, and remove nail, removal surface impurity;
C, to the batten right angle bead cutter crop selected, by thickness classification, dry; With rack shaper crop, comb; Gluing on the flank of tooth combed out; With automatic lengthening machine splicing spreading, and by the length specified; With multi-functional multiple blade saw fixed width, fixed thick, removing epidermis impurity; Use automatic glue spreaders gluing; Cold spelling machine is paved into desired profiled sheeting, by side pressure (pressure be 8MPa, time be 15 minutes) initial shaping, then clamps broadside with sizing clamp bar, take off from cold spelling machine again, place after 8 hours, allow glue fully bond, taking off sizing clamp bar after sclerosis becomes profiled sheeting; Or template is spliced in template, entering multilayer four sides side pressure hot press synchronous hot pressing (side pressure pressure is 8MPa, positive pressure pressure is 8MPa, temperature is 100 DEG C, and the time is 30 minutes) together with template layering becomes profiled sheeting; With sander fixed thick, sand flat, sanding; The size being cut into regulation with four limit bead cutters obtains finger-joint wood plate;
D, to the large laminate selected with automatically wide be machined to wide rectangular; Wide rectangular two ends rack shaper is cut flat, comb; The flank of tooth combed out is connected into rectangular and to rectangular comb after gluing with automatic spreading rack shaper; By the length of full-automatic lengthening machine by regulation; Docked rectangular for the polylith of fixed length by teeth groove on cold plate joggling apparatus, four sides pressurization, keep the regular hour (its pressure be 6MPa, time be 15 minutes) to be combined into profiled sheeting; Profiled sheeting used hot press hot pressing, flatten, compress (side pressure pressure is 8MPa, positive pressure pressure is 8MPa, temperature is 100 DEG C, and the time is 30 minutes); Cooled profiled sheeting, by the fixed thick sanding of sander, removes top layer impurity; Four limit bead cutters are cut into the size of regulation, obtain finger multilayer laminin plate;
E, to the little laminate right angle bead cutter crop selected; With multi-functional multiple blade saw the little laminate after crop be cut into the rectangular of wide uniform thickness and remove supracutaneous all impurity simultaneously; Be template with putting into after automatic glue spreaders gluing that template just spells, on width is pasted in two solid woods skin as rib; Four sides side pressure hot press synchronous hot pressing, side pressure (side pressure pressure is 8MPa, positive pressure pressure is 8MPa, temperature is 100 DEG C, and the time is 30 minutes) is put into together with template layering; After cooling with sander sand flat, sanding; Cut four limits with four limit bead cutters and namely obtain wide docking multilayer laminin plate; Not wide little laminate right angle bead cutter crop; With multi-functional multiple blade saw by trimming, fixed thick and remove supracutaneous all impurity simultaneously; Spread out in solid wood into template after skin gluing with automatic glue spreaders, then the multi-layer sheet after aforementioned processing put into template and just spell as template, on width is pasted in two solid woods skin as rib; Four sides side pressure hot press synchronous hot pressing, side pressure (side pressure pressure is 8MPa, positive pressure pressure is 8MPa, temperature is 100 DEG C, and the time is 30 minutes) is put into together with template layering; After cooling with sander sand flat, sanding; Cut four limits with four limit bead cutters and namely obtain splicing multilayer laminin plate;
F, according to the different requirements of user to product thickness, by solid wood board and several plain plates by after automatic double-sided gluing machine applying glue, overlap puts into cold press cold moudling together;
G, cut four limits with four limit bead cutters and namely obtain product.
Embodiment 2, a kind of production method regenerating multi-layer solid wood finger-jointed composite board, follow these steps to carry out,
A, purchase discarded construction batten, composite plate;
Batten, large and small laminate are picked out in b, classification, and remove nail, removal surface impurity;
C, to the batten right angle bead cutter crop selected, by thickness classification, dry; With rack shaper crop, comb; Gluing on the flank of tooth combed out; With automatic lengthening machine splicing spreading, and by the length specified; With multi-functional multiple blade saw fixed width, fixed thick, removing epidermis impurity; Use automatic glue spreaders gluing; Cold spelling machine is paved into desired profiled sheeting, by side pressure (pressure be 12MPa, time be 10 minutes) initial shaping, then clamps broadside with sizing clamp bar, take off from cold spelling machine again, place after 5 hours, allow glue fully bond, taking off sizing clamp bar after sclerosis becomes profiled sheeting; Or template is spliced in template, entering multilayer four sides side pressure hot press synchronous hot pressing (side pressure pressure is 12MPa, positive pressure pressure is 12MPa, temperature is 140 DEG C, and the time is 20 minutes) together with template layering becomes profiled sheeting; With sander fixed thick, sand flat, sanding; The size being cut into regulation with four limit bead cutters obtains finger-joint wood plate;
D, to the large laminate selected with automatically wide be machined to wide rectangular; Wide rectangular two ends rack shaper is cut flat, comb; The flank of tooth combed out is connected into rectangular and to rectangular comb after gluing with automatic spreading rack shaper; By the length of full-automatic lengthening machine by regulation; Docked rectangular for the polylith of fixed length by teeth groove on cold plate joggling apparatus, four sides pressurization, keep the regular hour (its pressure be 10MPa, time be 10 minutes) to be combined into profiled sheeting; Profiled sheeting used hot press hot pressing, flatten, compress (side pressure pressure is 12MPa, positive pressure pressure is 12MPa, temperature is 140 DEG C, and the time is 20 minutes); Cooled profiled sheeting, by the fixed thick sanding of sander, removes top layer impurity; Four limit bead cutters are cut into the size of regulation, obtain finger multilayer laminin plate;
E, to the little laminate right angle bead cutter crop selected; With multi-functional multiple blade saw the little laminate after crop be cut into the rectangular of wide uniform thickness and remove supracutaneous all impurity simultaneously; Be template with putting into after automatic glue spreaders gluing that template just spells, on width is pasted in 5 solid woods skin as rib; Four sides side pressure hot press synchronous hot pressing, side pressure (side pressure pressure is 12MPa, positive pressure pressure is 12MPa, temperature is 140 DEG C, and the time is 20 minutes) is put into together with template layering; After cooling with sander sand flat, sanding; Cut four limits with four limit bead cutters and namely obtain wide docking multilayer laminin plate; Not wide little laminate right angle bead cutter crop; With multi-functional multiple blade saw by trimming, fixed thick and remove supracutaneous all impurity simultaneously; Spread out in solid wood into template after skin gluing with automatic glue spreaders, then the multi-layer sheet after aforementioned processing put into template and just spell as template, on width is pasted in 5 solid woods skin as rib; Four sides side pressure hot press synchronous hot pressing, side pressure (side pressure pressure is 12MPa, positive pressure pressure is 12MPa, temperature is 140 degree, and the time is 20 minutes) is put into together with template layering; After cooling with sander sand flat, sanding; Cut four limits with four limit bead cutters and namely obtain splicing multilayer laminin plate;
F, according to the different requirements of user to product thickness, by solid wood board and several plain plates by after automatic double-sided gluing machine applying glue, overlap puts into cold press cold moudling together;
G, cut four limits with four limit bead cutters and namely obtain product.
Embodiment 3, a kind of production method regenerating multi-layer solid wood finger-jointed composite board, follow these steps to carry out,
A, purchase discarded construction batten, composite plate;
Batten, large and small laminate are picked out in b, classification, and remove nail, removal surface impurity;
C, to the batten right angle bead cutter crop selected, by thickness classification, dry; With rack shaper crop, comb; Gluing on the flank of tooth combed out; With automatic lengthening machine splicing spreading, and by the length specified; With multi-functional multiple blade saw fixed width, fixed thick, removing epidermis impurity; Use automatic glue spreaders gluing; Cold spelling machine is paved into desired profiled sheeting, by side pressure (pressure be 16MPa, time be 5 minutes) initial shaping, then clamps broadside with sizing clamp bar, take off from cold spelling machine again, place after 2 hours, allow glue fully bond, taking off sizing clamp bar after sclerosis becomes profiled sheeting; Or template is spliced in template, entering multilayer four sides side pressure hot press synchronous hot pressing (side pressure pressure is 16MPa, positive pressure pressure is 16MPa, temperature is 180 DEG C, and the time is 10 minutes) together with template layering becomes profiled sheeting; With sander fixed thick, sand flat, sanding; The size being cut into regulation with four limit bead cutters obtains finger-joint wood plate;
D, to the large laminate selected with automatically wide be machined to wide rectangular; Wide rectangular two ends rack shaper is cut flat, comb; The flank of tooth combed out is connected into rectangular and to rectangular comb after gluing with automatic spreading rack shaper; By the length of full-automatic lengthening machine by regulation; Docked rectangular for the polylith of fixed length by teeth groove on cold plate joggling apparatus, four sides pressurization, keep the regular hour (its pressure be 15MPa, time be 4 minutes) to be combined into profiled sheeting; Profiled sheeting used hot press hot pressing, flatten, compress (side pressure pressure is 16MPa, positive pressure pressure is 16MPa, temperature is 180 DEG C, and the time is 10 minutes); Cooled profiled sheeting, by the fixed thick sanding of sander, removes top layer impurity; Four limit bead cutters are cut into the size of regulation, obtain finger multilayer laminin plate;
E, to the little laminate right angle bead cutter crop selected; With multi-functional multiple blade saw the little laminate after crop be cut into the rectangular of wide uniform thickness and remove supracutaneous all impurity simultaneously; Be template with putting into after automatic glue spreaders gluing that template just spells, on width is pasted in 8 solid woods skin as rib; Four sides side pressure hot press synchronous hot pressing, side pressure (side pressure pressure is 16MPa, positive pressure pressure is 16MPa, temperature is 180 DEG C, and the time is 10 minutes) is put into together with template layering; After cooling with sander sand flat, sanding; Cut four limits with four limit bead cutters and namely obtain wide docking multilayer laminin plate; Not wide little laminate right angle bead cutter crop; With multi-functional multiple blade saw by trimming, fixed thick and remove supracutaneous all impurity simultaneously; Spread out in solid wood into template after skin gluing with automatic glue spreaders, then the multi-layer sheet after aforementioned processing put into template and just spell as template, on width is pasted in 8 solid woods skin as rib; Four sides side pressure hot press synchronous hot pressing, side pressure (side pressure pressure is 16MPa, positive pressure pressure is 16MPa, temperature is 180 DEG C, and the time is 10 minutes) is put into together with template layering; After cooling with sander sand flat, sanding; Cut four limits with four limit bead cutters and namely obtain splicing multilayer laminin plate;
F, according to the different requirements of user to product thickness, by solid wood board and several plain plates by after automatic double-sided gluing machine applying glue, overlap puts into cold press cold moudling together;
G, cut four limits with four limit bead cutters and namely obtain product.
Claims (7)
1. regenerate a production method for multi-layer solid wood finger-jointed composite board, it is characterized in that: follow these steps to carry out,
A, purchase discarded construction batten, composite plate;
Batten, large and small laminate are picked out in b, classification, and remove nail, removal surface impurity;
C, to the batten right angle bead cutter crop selected, by thickness classification, dry; With rack shaper crop, comb; Gluing on the flank of tooth combed out; With automatic lengthening machine splicing spreading, and by the length specified; With multi-functional multiple blade saw fixed width, fixed thick, removing epidermis impurity; Use automatic glue spreaders gluing; Cold spelling machine is paved into desired profiled sheeting, by side pressure initial shaping, then clamps broadside with sizing clamp bar, then take off from cold spelling machine, place after 2-8 hour, allow glue fully bond, taking off sizing clamp bar after sclerosis becomes profiled sheeting; Or template is spliced in template, entering the synchronous hot pressing of multilayer four sides side pressure hot press together with template layering becomes profiled sheeting; With sander fixed thick, sand flat, sanding; The size being cut into regulation with four limit bead cutters obtains finger-joint wood plate;
D, to the large laminate selected with automatically wide be machined to wide rectangular; Wide rectangular two ends rack shaper is cut flat, comb; The flank of tooth combed out is connected into rectangular and to rectangular comb after gluing with automatic spreading rack shaper; By the length of full-automatic lengthening machine by regulation; Docked rectangular for the polylith of fixed length by teeth groove on cold plate joggling apparatus, four sides pressurization, keeps the regular hour to be combined into profiled sheeting; Profiled sheeting used hot press hot pressing, flatten, compress; Cooled profiled sheeting, by the fixed thick sanding of sander, removes top layer impurity; Four limit bead cutters are cut into the size of regulation, obtain finger multilayer laminin plate;
E, to the little laminate right angle bead cutter crop selected; With multi-functional multiple blade saw the little laminate after crop be cut into the rectangular of wide uniform thickness and remove supracutaneous all impurity simultaneously; Be template with putting into after automatic glue spreaders gluing that template just spells, on width is pasted in several solid wood skin as rib; The synchronous hot pressing of four sides side pressure hot press, side pressure is put into together with template layering; After cooling with sander sand flat, sanding; Cut four limits with four limit bead cutters and namely obtain wide docking multilayer laminin plate; Not wide little laminate right angle bead cutter crop; With multi-functional multiple blade saw by trimming, fixed thick and remove supracutaneous all impurity simultaneously; Spread out in solid wood into template after skin gluing with automatic glue spreaders, then the multi-layer sheet after aforementioned processing put into template and just spell as template, on width is pasted in several solid wood skin as rib; The synchronous hot pressing of four sides side pressure hot press, side pressure is put into together with template layering; After cooling with sander sand flat, sanding; Cut four limits with four limit bead cutters and namely obtain splicing multilayer laminin plate;
F, according to the different requirements of user to product thickness, by solid wood board and several plain plates by after automatic double-sided gluing machine applying glue, overlap puts into cold press cold moudling together;
G, cut four limits with four limit bead cutters and namely obtain product.
2. a kind of production method regenerating multi-layer solid wood finger-jointed composite board according to claim 1, is characterized in that: saidly on cold spelling machine, carry out side pressure, and its pressure is 8-16MPa, the time is 5-15 minute.
3. a kind of production method regenerating multi-layer solid wood finger-jointed composite board according to claim 1, it is characterized in that: said in the synchronous hot pressing of multilayer four sides side pressure hot press, its side pressure pressure is 8-16MPa, positive pressure pressure is 8-16MPa, temperature is 100-180 DEG C, and the time is 10-30 minute.
4. a kind of production method regenerating multi-layer solid wood finger-jointed composite board according to claim 1, it is characterized in that: said in cold press cold moudling, its pressure is 8-15MPa, and the time is 2-8 hour.
5. a kind of production method regenerating multi-layer solid wood finger-jointed composite board according to claim 1, is characterized in that: said carry out on cold plate joggling apparatus cold spelling sizing, its pressure is 6-15MPa, the time is 4-15 minute.
6. a kind of production method regenerating multi-layer solid wood finger-jointed composite board according to claim 1, it is characterized in that: in said several solid wood, skin is as rib, its quantity is 2-8 root.
7. regenerate a multi-layer solid wood finger-jointed composite board, it is characterized in that: the product that method according to claim 1 obtains.