CN105058522A - Regeneration multilayer solid wood finger joint plate production method and product - Google Patents

Regeneration multilayer solid wood finger joint plate production method and product Download PDF

Info

Publication number
CN105058522A
CN105058522A CN201510391356.7A CN201510391356A CN105058522A CN 105058522 A CN105058522 A CN 105058522A CN 201510391356 A CN201510391356 A CN 201510391356A CN 105058522 A CN105058522 A CN 105058522A
Authority
CN
China
Prior art keywords
pressure
solid wood
cold
cut
template
Prior art date
Application number
CN201510391356.7A
Other languages
Chinese (zh)
Inventor
何龙江
何政
Original Assignee
南充市嘉陵区森利木业加工厂
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 南充市嘉陵区森利木业加工厂 filed Critical 南充市嘉陵区森利木业加工厂
Priority to CN201510391356.7A priority Critical patent/CN105058522A/en
Publication of CN105058522A publication Critical patent/CN105058522A/en

Abstract

The invention discloses a regeneration multilayer solid wood finger joint plate production method and product; the method comprises the following steps: purchasing waste building construction battens; removing nails and surface impurity; using a right angle edge trimmer to cut heads, classifying the battens according to thickness, and drying the battens; using a comb machine to cut heads and comb; coating glue on a combed tooth flank; using an automatic length expander to splice and expand the length, and cutting the material to a preset length; using a multifunctional multi-blade saw to define width and thickness, and removing surface impurities; using an automatic spreading machine to glue; splicing the material into a mould board in a template, and the template and the mould board are layered and enter a multilayer four-side side-pressure hot press for synchronization hot pressing, thus forming a moulding plate; using a sander to define thickness, flatten, and polish; using a four-side edge trimmer to cut the moulding plate according to preset sizes, thus obtaining plain panels; using an automatic double-face laminator to glue a plurality of plain panels according to different product thickness requirements of a user, overlapping the plain panels into a cold press for cold pressing formation, and using the four-side edge trimmer to cut four edges, thus obtaining the product.

Description

The production method of regeneration multi-layer solid wood finger-jointed plate and product

Technical field

The present invention relates to a kind of production method and product of sheet material, particularly relate to a kind of production method and the product that regenerate multi-layer solid wood finger-jointed plate.

Background technology

As everyone knows, current China furniture, dress is drilled, decoration, the raw material that timber industry uses use solid wood board usually, finger-jointed plate, glued board etc., and high-end sheet material is as solid wood board, splice plate, finger-jointed plate is very expensive, although the high-quality glued board at present between solid wood and composite board is pure wood products, because adopting conventional art, process and structure fabrication, product quality can not meet the needs of people, and to there is a lot of waste wood in existing building woodworking be not recycled utilization, the direct burning had, cause air environmental pollution on the one hand, bring again the significant wastage of timber resources on the other hand.

Summary of the invention

The object of the invention is to provide one can effectively reduce product cost, economize on resources, realize turning waste into wealth to overcome the deficiencies in the prior art, the production method of the strong regeneration multi-layer solid wood finger-jointed plate protected forest resources and product.Its concrete technical scheme is: a kind of production method regenerating multi-layer solid wood finger-jointed plate, follows these steps to carry out,

A, the discarded construction batten of purchase;

B, go nail, remove surface impurity;

C, use right angle bead cutter crop, by thickness classification, dry;

D, use rack shaper crop, comb;

E, on the flank of tooth combed out gluing;

F, with automatic lengthening machine splicing spreading, and by the length of regulation;

G, with multi-functional multiple blade saw fixed width, fixed thick, removing epidermis impurity;

H, use automatic glue spreaders gluing;

I, on cold spelling machine, be paved into desired profiled sheeting, by side pressure initial shaping, then clamp broadside with sizing clamp bar, then take off from cold spelling machine, place after 2-8 hour, allow glue fully bond, taking off sizing clamp bar after sclerosis becomes profiled sheeting; Or template is spliced in template, entering the synchronous hot pressing of multilayer four sides side pressure hot press together with template layering becomes profiled sheeting;

J, with sander fixed thick, sand flat, sanding;

K, the size being cut into regulation with four limit bead cutters obtain plain plate;

L, according to the different requirements of user to product thickness, by several plain plates by after automatic double-sided gluing machine applying glue, overlap puts into cold press cold moudling together;

M, cut four limits with four limit bead cutters and namely obtain product.

Saidly on cold spelling machine, carry out side pressure, its pressure is 8-16MPa, the time is 5-15 minute.

Said in the synchronous hot pressing of multilayer four sides side pressure hot press, its side pressure pressure is 8-16MPa, positive pressure pressure is 8-16MPa, temperature is 100-180 DEG C, and the time is 10-30 minute.

Said in cold press cold moudling, its pressure is 8-15MPa, and the time is 2-6 hour.

As can be seen from technical scheme of the present invention, after discarded construction batten carries out processing by method of the present invention, become the solid wood board with enough Strong degree, furniture can be widely used in, dress is drilled, decorated, timber industry, also can be used as the substrate of other purposes sheet material.Can also cut into the rectangular sale that user needs, and cost ratio market like product is low, fullys meet the present invention and can effectively reduce product cost, economizes on resources, realize turning waste into wealth, the strong goal of the invention protected forest resources.

Detailed description of the invention

Embodiment 1, a kind of production method regenerating multi-layer solid wood finger-jointed plate, follow these steps to carry out,

A, the discarded construction batten of purchase;

B, go nail, remove surface impurity;

C, use right angle bead cutter crop, by thickness classification, dry;

D, use rack shaper crop, comb;

E, on the flank of tooth combed out gluing;

F, with automatic lengthening machine splicing spreading, and by the length of regulation;

G, with multi-functional multiple blade saw fixed width, fixed thick, removing epidermis impurity;

H, use automatic glue spreaders gluing;

I, on cold spelling machine, be paved into desired profiled sheeting, by side pressure (its pressure be 8MPa, time be 15 minutes) initial shaping, then clamp broadside with sizing clamp bar, take off from cold spelling machine again, place after 8 hours, allow glue fully bond, taking off sizing clamp bar after sclerosis becomes profiled sheeting; Or template is spliced in template, entering multilayer four sides side pressure hot press synchronous hot pressing (its side pressure pressure is 8MPa, positive pressure pressure is 8MPa, temperature is 100 DEG C, and the time is 30 minutes) together with template layering becomes profiled sheeting;

J, with sander fixed thick, sand flat, sanding;

K, the size being cut into regulation with four limit bead cutters obtain plain plate;

L, according to the different requirements of user to product thickness, by several plain plates by after automatic double-sided gluing machine applying glue, overlap puts into cold press cold moudling together, and its pressure is 8MPa, and the time is 6 hours;

M, cut four limits with four limit bead cutters and namely obtain product.

Embodiment 2, a kind of production method regenerating multi-layer solid wood finger-jointed plate, follow these steps to carry out,

A, the discarded construction batten of purchase;

B, go nail, remove surface impurity;

C, use right angle bead cutter crop, by thickness classification, dry;

D, use rack shaper crop, comb;

E, on the flank of tooth combed out gluing;

F, with automatic lengthening machine splicing spreading, and by the length of regulation;

G, with multi-functional multiple blade saw fixed width, fixed thick, removing epidermis impurity;

H, use automatic glue spreaders gluing;

I, on cold spelling machine, be paved into desired profiled sheeting, by side pressure (its pressure be 12MPa, time be 10 minutes) initial shaping, then clamp broadside with sizing clamp bar, take off from cold spelling machine again, place after 5 hours, allow glue fully bond, taking off sizing clamp bar after sclerosis becomes profiled sheeting; Or template is spliced in template, entering multilayer four sides side pressure hot press synchronous hot pressing (its side pressure pressure is 12MPa, positive pressure pressure is 12MPa, temperature is 140 DEG C, and the time is 20 minutes) together with template layering becomes profiled sheeting;

J, with sander fixed thick, sand flat, sanding;

K, the size being cut into regulation with four limit bead cutters obtain plain plate;

L, according to the different requirements of user to product thickness, by several plain plates by after automatic double-sided gluing machine applying glue, overlap puts into cold press cold moudling together, and its pressure is 12MPa, and the time is 4 hours;

M, cut four limits with four limit bead cutters and namely obtain product.

Embodiment 3, a kind of production method regenerating multi-layer solid wood finger-jointed plate, follow these steps to carry out,

A, the discarded construction batten of purchase;

B, go nail, remove surface impurity;

C, use right angle bead cutter crop, by thickness classification, dry;

D, use rack shaper crop, comb;

E, on the flank of tooth combed out gluing;

F, with automatic lengthening machine splicing spreading, and by the length of regulation;

G, with multi-functional multiple blade saw fixed width, fixed thick, removing epidermis impurity;

H, use automatic glue spreaders gluing;

I, on cold spelling machine, be paved into desired profiled sheeting, by side pressure (its pressure be 16MPa, time be 5 minutes) initial shaping, then clamp broadside with sizing clamp bar, take off from cold spelling machine again, place after 2 hours, allow glue fully bond, taking off sizing clamp bar after sclerosis becomes profiled sheeting; Or template is spliced in template, entering multilayer four sides side pressure hot press synchronous hot pressing (its side pressure pressure is 16MPa, positive pressure pressure is 16MPa, temperature is 180 DEG C, and the time is 10 minutes) together with template layering becomes profiled sheeting;

J, with sander fixed thick, sand flat, sanding;

K, the size being cut into regulation with four limit bead cutters obtain plain plate;

L, according to the different requirements of user to product thickness, by several plain plates by after automatic double-sided gluing machine applying glue, overlap puts into cold press cold moudling together, and its pressure is 15MPa, and the time is 2 hours;

M, cut four limits with four limit bead cutters and namely obtain product.

Claims (5)

1. regenerate a production method for multi-layer solid wood finger-jointed plate, it is characterized in that: follow these steps to carry out,
A, the discarded construction batten of purchase;
B, go nail, remove surface impurity;
C, use right angle bead cutter crop, by thickness classification, dry;
D, use rack shaper crop, comb;
E, on the flank of tooth combed out gluing;
F, with automatic lengthening machine splicing spreading, and by the length of regulation;
G, with multi-functional multiple blade saw fixed width, fixed thick, removing epidermis impurity;
H, use automatic glue spreaders gluing;
I, on cold spelling machine, be paved into desired profiled sheeting, by side pressure initial shaping, then clamp broadside with sizing clamp bar, then take off from cold spelling machine, place after 2-8 hour, allow glue fully bond, taking off sizing clamp bar after sclerosis becomes profiled sheeting; Or template is spliced in template, entering the synchronous hot pressing of multilayer four sides side pressure hot press together with template layering becomes profiled sheeting;
J, with sander fixed thick, sand flat, sanding;
K, the size being cut into regulation with four limit bead cutters obtain plain plate;
L, according to the different requirements of user to product thickness, by several plain plates by after automatic double-sided gluing machine applying glue, overlap puts into cold press cold moudling together;
M, cut four limits with four limit bead cutters and namely obtain product.
2. a kind of production method regenerating solid wood finger-jointed plate according to claim 1, is characterized in that: saidly on cold spelling machine, carry out side pressure, and its pressure is 8-16MPa, the time is 5-15 minute.
3. a kind of production method regenerating solid wood finger-jointed plate according to claim 1, it is characterized in that: said in the synchronous hot pressing of multilayer four sides side pressure hot press, its side pressure pressure is 8-16MPa, positive pressure pressure is 8-16MPa, temperature is 100-180 DEG C, and the time is 10-30 minute.
4. a kind of production method regenerating solid wood finger-jointed plate according to claim 1, it is characterized in that: said in cold press cold moudling, its pressure is 8-15MPa, and the time is 2-6 hour.
5. regenerate a solid wood finger-jointed plate, it is characterized in that: the product that method according to claim 1 obtains.
CN201510391356.7A 2015-07-07 2015-07-07 Regeneration multilayer solid wood finger joint plate production method and product CN105058522A (en)