CN104962201A - 一种纳米瓷砖填孔剂 - Google Patents

一种纳米瓷砖填孔剂 Download PDF

Info

Publication number
CN104962201A
CN104962201A CN201510312618.6A CN201510312618A CN104962201A CN 104962201 A CN104962201 A CN 104962201A CN 201510312618 A CN201510312618 A CN 201510312618A CN 104962201 A CN104962201 A CN 104962201A
Authority
CN
China
Prior art keywords
ceramic tile
nanometer ceramic
agent
aqueous solution
spackling
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510312618.6A
Other languages
English (en)
Inventor
张振明
于民
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jinan Huichuan Ludox Factory
Original Assignee
Jinan Huichuan Ludox Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jinan Huichuan Ludox Factory filed Critical Jinan Huichuan Ludox Factory
Priority to CN201510312618.6A priority Critical patent/CN104962201A/zh
Publication of CN104962201A publication Critical patent/CN104962201A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种纳米瓷砖填孔剂，其为水溶液，水溶液中各组分及其质量配比为：硅溶胶30份；光亮剂0.02-0.05份；防水剂为1.5-2份；分散剂为0.2-0.5份。本发明的一种纳米瓷砖填孔剂能够明显提高瓷砖光泽度，可以使瓷砖光泽度达到90以上，防污能力强，与现有抛光液相比，至少降低10%的生产成本。

Description

一种纳米瓷砖填孔剂
技术领域
本发明涉及建筑装饰领域，具体涉及一种纳米瓷砖填孔剂。
背景技术
瓷砖，是以耐火的金属氧化物及半金属氧化物，经由研磨、混合、压制、施釉、烧结的过程，而形成之一种耐酸碱的瓷质或石质等建筑或装饰的材料，总称之为瓷砖。瓷砖有微晶石瓷砖、全抛釉瓷砖和普通抛光砖，其亮度(光泽度)均约为75。亮度达现有的抛光剂成本高，光度达不到，防污性能差。
发明内容
为解决上述问题，本发明提供了一种光泽度高，防污性强，成本低的纳米瓷砖填孔剂。
本发明通过以下技术实现：一种纳米瓷砖填孔剂，其为水溶液，水溶液中各组分及其质量配比为：硅溶胶30份；光亮剂0.02-0.05份；防水剂为1.5-2份；分散剂为0.2-0.5份。
优选的，所述光亮剂为烷基苯磺酸钠(ABS)。
优选的，所述防水剂为甲基硅酸钾或甲基硅酸钠。
优选的，所述甲基硅酸钾为pH7-9的中性甲基硅酸钾或中性甲基硅酸钠。
优选的，所述分散剂为壬基酚聚氧乙烯醚(NP-10)。
优选的，所述水溶液中各组分及其质量配比为：硅溶胶30份；光亮剂0.05份；防水剂为1.6份；分散剂为0.2份。
优选的，以硅溶胶的质量计，水溶液的质量体积浓度为15％。
优选的，所述水溶液中还包括有机硅消泡剂。
优选的，所述烷基苯磺酸钠可以为十二烷基苯磺酸钠。
另外，本发明的纳米瓷砖填孔剂还可以由以下组成方式：
100ml的质量体积分数(mg/ml)为30％的硅溶胶中加入(1)质量体积分数(mg/ml)的10％的光亮剂烷基苯磺酸钠0.5ml；(2)防水剂甲基硅酸钾或或甲基硅酸钠1.6ml；(3)分散剂壬基酚聚氧乙烯醚0.2ml；(4)100ml水(蒸馏水/纯净水)。
在加入的过程中不断搅拌使其充分均匀，后达到抛光剂浓度为15％。本发明可用于抛光地板砖/瓷砖(包括纳米瓷砖)，在稀释过程中如产生泡沫，需加入少许有机硅消泡剂。
本发明的具有以下优点：
1.明显提高瓷砖尤其是纳米瓷砖的光泽度，可以使瓷砖光泽度达到90以上。
2.防污能力提高。
3.与现有抛光液相比，至少降低10％的生产成本。
本发明的优选试验如下：
1.一种纳米瓷砖填孔剂(或称为抛光液)的浓度优选试验：
实验步骤：取100ml质量分数为30％(mg/ml)的硅溶胶，向其中依次加入0.5ml10％(mg/ml)的烷基苯磺酸钠，1.6ml的中性甲基硅酸和0.2ml壬基酚聚氧乙烯醚(NP-10)，在加入过程中边加边搅拌，使各组分充分混合均匀，以上混合液配置十份，用水调节抛光液的浓度分别达到5％、6％、8％、10％、11％、12％、13％、14％、15％以及17％，在稀释过程中如果产生泡沫，可加入少量有机硅消泡剂。使用雾化器将不同浓度的抛光液均匀喷涂于微粉砖上，用磨头打磨十次，用测光仪侧其表面光泽度，抛光液浓度与表面光泽度的关系如表1，由表1可见，抛光液浓度为15-17％时，表面光泽度最大，为92(60°)。
表1抛光液浓度与表面光泽度的关系
2.抛光次数优选试验：
使用雾化器将上述试验得到浓度为15％的抛光液均匀喷涂在瓷砖上，用磨头打磨，记录打磨次数和光泽度的关系。根据表2抛光液打磨次数与表面光泽度的关系，可见当打磨次数为12次和14次的时候，表面光泽度均为92.5，节约人力角度优选打磨次数为12次。
表2抛光液打磨次数与表面光泽度的关系
打磨次数 2 4 6 8 10 12 14
表面光泽度 70 76 82 88 92 92.5 92.5
3.放置时间及浓度测量
(1)把配制好抛光剂在温度5-40℃放置6个月没有沉淀或分层现象出现。
(2)浓度测量：一般用密度计测量在温度20-25℃时，抛光剂的浓度为15％时密度计读数为1.10g/㎝3。
4.市场流行同类产品对比
本发明的产品在同等打磨次数、同等含量的情况下平均比其它产品的光泽度高11-19度。而且只是同类产品的成本的90％左右。所以本产品有较高的使用和推广价值。
具体实施方式
实施例1
取100ml质量分数为30％的硅溶胶，向其中依次加入0.5ml10％的烷基苯磺酸钠，1.6ml中性甲基硅酸钾和0.2ml壬基酚聚氧乙烯醚，100ml水，在加入过程中边加边搅拌，使各组分充分混合均匀，用水调节抛光液的浓度为15％，此时，用密度计在20-25℃测量溶液，显示溶液密度为1.10g/㎝3，使用雾化器将抛光液喷涂于微粉砖上，打磨12次，用测光仪侧其表面光泽度为93。
实施例2
购买十种市场上流通的同类瓷砖，用测光仪侧其表面光泽度，记录如表3：
表3十种市场上流通的瓷砖的表面光泽度
瓷砖编号 A B C D E F G H I J
表面光泽度 76 78 74 79 76 77 80 82 81 80
将实施例1中的喷涂本发明的抛光液瓷砖与市场上流通的瓷砖的表面光泽度相比，发现使用本发明的抛光液的瓷砖的表面光泽度明显优于市场上流通的瓷砖的表面光泽度。
实施例3
将实施例1中的喷涂本发明的抛光液的瓷砖与实施例2中市场上流通的瓷砖分别树立于同一平面上，使瓷砖与水平面呈90°角直立，10天后，观察瓷砖表面的灰尘量，发现实施例1制得的瓷砖表面最光洁。

Claims (8)

1.一种纳米瓷砖填孔剂，其特征在于，其为水溶液，水溶液中各组分及其质量配比为：硅溶胶30份；光亮剂0.02-0.05份；防水剂为1.5-2份；分散剂为0.2-0.5份。
2.根据权利要求1所述的纳米瓷砖填孔剂，其特征在于，所述光亮剂为烷基苯磺酸钠。
3.根据权利要求1所述的纳米瓷砖填孔剂，其特征在于，所述防水剂为甲基硅酸钾或甲基硅酸钠。
4.根据权利要求3所述的纳米瓷砖填孔剂，其特征在于，所述甲基硅酸钾或甲基硅酸钠为pH7-9的中性甲基硅酸钾或或中性甲基硅酸钠。
5.根据权利要求1所述的纳米瓷砖填孔剂，其特征在于，所述分散剂为壬基酚聚氧乙烯醚。
6.根据权利要求1所述的纳米瓷砖填孔剂，其特征在于，所述水溶液中各组分及其质量配比为：硅溶胶30份；光亮剂0.05份；防水剂为1.6份；分散剂为0.2份。
7.根据权利要求1所述的纳米瓷砖填孔剂，其特征在于，以硅溶胶的质量计，水溶液的质量体积浓度为15%。
8.根据权利要求1所述的纳米瓷砖填孔剂，其特征在于，所述水溶液中还包括有机硅消泡剂。
CN201510312618.6A 2015-06-09 2015-06-09 一种纳米瓷砖填孔剂 Pending CN104962201A (zh)