CN104961937A - 一种耐老化橡胶材料 - Google Patents
一种耐老化橡胶材料 Download PDFInfo
- Publication number
- CN104961937A CN104961937A CN201510358617.5A CN201510358617A CN104961937A CN 104961937 A CN104961937 A CN 104961937A CN 201510358617 A CN201510358617 A CN 201510358617A CN 104961937 A CN104961937 A CN 104961937A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber material
- rubber
- ageing
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐老化橡胶材料,涉及橡胶生产技术领域,所述橡胶材料包括以下组份(重量份):丁晴橡胶85-95、氧化锌6-10份,硬脂酸2-5份,有机蒙脱土3-8份,硫化剂5-8份,促进剂1-3份,耐磨炭黑N330 10-18份,碳酸钙15-20份和石蜡2-4份,本发明是以丁腈橡胶为主体胶料,再配以其他辅料,通过优选各个组份的配比,制备出的橡胶材料耐磨性能优异,耐老化性能好,其力学性能也较高,可承受较大程度的撞击和拉扯,且原料来源广泛,成本低廉。
Description
技术领域
本发明涉及橡胶生产技术领域,具体涉及一种耐老化橡胶材料。
背景技术
丁腈橡胶(NBR)因其耐油性好,物理机械性能优异,已被广泛用于制造各种耐油制品,如O型环、软管、垫圈以及燃料箱衬胶、油罐衬里、织物涂层、管螺纹保护层以及电线包皮、胶粘剂、橡胶手套、食品包装用薄膜等领域。目前,世界上有 30 多个国家生产 NBR,应用领域广阔,NBR 最大的消费是生产耐油胶管制品以及阻燃运输带,消费量约占 NBR 总消费量的50%。但是它也有一些缺点限制了丁腈橡胶在更广泛的领域使用,如耐臭氧、耐天候老化性,耐热老化性比较差,所以在一些需要耐侯耐老化的环境下就不能使用 NBR 作为基础材料,为此需要针对 NBR 现有的缺点进行改性以增加其使用领域。
鉴于现有技术的不足,需要对现有的丁晴橡胶材料进行改进。
发明内容
本发明所要解决的问题是提供一种耐老化性能好,成本低廉的耐老化橡胶材料。
为了实现上述目的,本发明采取的技术方案为:所提供的一种耐老化橡胶材料,所述橡胶材料包括以下组份(重量份):丁晴橡胶85-95、氧化锌6-10份,硬脂酸2-5份,有机蒙脱土3-8份,硫化剂5-8份,促进剂1-3份,耐磨炭黑N330 10-18份,碳酸钙15-20份和石蜡2-4份。
优选的,所述橡胶材料包括以下组份(重量份):丁晴橡胶85、氧化锌8份,硬脂酸3份,有机蒙脱土5份,硫化剂7份,促进剂2份,耐磨炭黑N330 12份,碳酸钙6份和石蜡3份。
优选的,所述轻烧镁粉中活性氧化镁的镁含量(质量分数)为60—80%。
优选的,所述丁腈橡胶为丙烯腈型固体胶,所述丙烯腈型固体胶中含的丙烯腈含量为 25-30wt%。
采用本发明的技术方案,本发明是以丁腈橡胶为主体胶料,再配以其他辅料,通过优选各个组份的配比,制备出的橡胶材料耐磨性能优异,耐老化性能好,其力学性能也较高,可承受较大程度的撞击和拉扯,且原料来源广泛,成本低廉。
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施方式,进一步阐述本发明。
实施例1:
一种耐老化橡胶材料,所述橡胶材料包括以下组份(重量份):丁晴橡胶85、氧化锌8份,硬脂酸3份,有机蒙脱土5份,硫化剂7份,促进剂2份,耐磨炭黑N330 12份,碳酸钙6份和石蜡3份。
基于上述,本发明是以丁腈橡胶为主体胶料,再配以其他辅料,通过优选各个组份的配比,制备出的橡胶材料耐磨性能优异,耐老化性能好,其力学性能也较高,可承受较大程度的撞击和拉扯,且原料来源广泛,成本低廉。
显然本发明具体实现并不受上述方式的限制,只要采用了本发明的方法构思和技术方案进行的各种非实质性的改进,或未经改进将本发明的构思和技术方案直接应用于其它场合的,均在本发明的保护范围之内。
Claims (3)
1. 一种耐老化橡胶材料,其特征在于,所述橡胶材料包括以下组份(重量份):丁晴橡胶85-95、氧化锌6-10份,硬脂酸2-5份,有机蒙脱土3-8份,硫化剂5-8份,促进剂1-3份,耐磨炭黑N330 10-18份,碳酸钙15-20份和石蜡2-4份。
2.根据权利要求1所述的一种耐老化橡胶材料,其特征在于,所述橡胶材料包括以下组份(重量份):丁晴橡胶85、氧化锌8份,硬脂酸3份,有机蒙脱土5份,硫化剂7份,促进剂2份,耐磨炭黑N330 12份,碳酸钙6份和石蜡3份。
3. 根据权利要求1或2所述的一种耐老化橡胶材料,其特征在于,所述丁腈橡胶为丙烯腈型固体胶,所述丙烯腈型固体胶中含的丙烯腈含量为 25-30wt%。