CN104947126A - 一种镁合金清洗剂 - Google Patents

一种镁合金清洗剂 Download PDF

Info

Publication number
CN104947126A
CN104947126A CN201510411883.XA CN201510411883A CN104947126A CN 104947126 A CN104947126 A CN 104947126A CN 201510411883 A CN201510411883 A CN 201510411883A CN 104947126 A CN104947126 A CN 104947126A
Authority
CN
China
Prior art keywords
magnesium alloy
out system
clean
agent
cleaning agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510411883.XA
Other languages
English (en)
Other versions
CN104947126B (zh
Inventor
王修春
潘喜庆
张晶
伊希斌
王小军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
New Material Institute of Shandong Academy of Sciences
Original Assignee
New Material Institute of Shandong Academy of Sciences
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by New Material Institute of Shandong Academy of Sciences filed Critical New Material Institute of Shandong Academy of Sciences
Priority to CN201510411883.XA priority Critical patent/CN104947126B/zh
Publication of CN104947126A publication Critical patent/CN104947126A/zh
Application granted granted Critical
Publication of CN104947126B publication Critical patent/CN104947126B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种镁合金清洗剂，由以下浓度的组分组成：碱50～120g/L，添加剂5～50g/L，络合剂1～5g/L，润湿剂1～5g/L，余量为水。本发明的组分中没有强酸、铬酸盐以及氟化物，不会对环境造成污染，而且不会对镁合金造成过腐蚀，在对镁合金清洗干净彻底的基础上，不会对镁合金造成损害；本发明中添加剂能加快对油污和润滑剂的清洗速度，络合剂使清洗剂中的钙、镁、硅等离子保持稳定不产生絮状物，延长清洗剂的使用寿命。

Description

一种镁合金清洗剂
技术领域
本发明属于镁合金的表面处理技术领域，具体涉及一种镁合金清洗剂。
背景技术
镁合金是目前使用最轻的金属材料，是重要的有色金属材料。具有密度低，比强度和比刚度高，减震性、电磁屏蔽和抗辐射能力强，易切削加工和回收等一系列优点，被誉为“21世纪绿色工程材料”。镁合金压铸造件被广泛应用于汽车制造、航天航空、通讯、光学仪器和计算机制造业。
由于镁合金易被腐蚀，所以，需要在镁合金的表面涂上具有高耐腐蚀性能的防护层。镁合金表面防护处理前要对镁合金工件进行预处理，以保证工件的表面无油无锈，并且平整光洁。目前镁合金的预处理剂为铬酸盐、氟化物以及强酸等物质，除了易对环境造成严重污染外，强酸还容易导致镁合金过腐蚀。专利201210538283.6提出了一种废镁合金表面涂层的清洗方法，采用强碱性溶液清除废镁合金表面固着有机涂层。
发明内容
本发明的目的在于提供一种镁合金清洗剂，它能较快地去除镁合金表面的氧化膜、腐蚀产物、油和润滑剂等污物，且不会对镁合金表面造成损害。
为了解决以上技术问题，本发明的技术方案为：
一种镁合金清洗剂，由以下浓度的组分组成：碱50～120g/L，添加剂5～50g/L，络合剂1～5g/L，润湿剂1～5g/L，余量为水。
优选的，所述镁合金清洗剂，由以下浓度的组分组成：碱70g/L，添加剂20g/L，络合剂2g/L，润湿剂3g/L，余量为水。
优选的，所述碱为氢氧化钠和氢氧化钾中的一种或两种。
优选的，所述添加剂为磷酸钠、硅酸钠和焦磷酸钠中的一种或两种。
优选的，所述络合剂为乙二胺四乙酸二钠、柠檬酸钠和酒石酸钠中的一种或两种。
优选的，所述润湿剂为十二烷基苯磺酸钠、脂肪醇聚氧乙烯醚硫酸钠和烷基酚聚氧乙烯醚中的一种或两种
所述镁合金清洗剂的使用方法：将待清洗处理的镁合金工件放入50～100℃的镁合金清洗剂中浸泡5～30分钟，将浸泡后的镁合金工件用清水漂净，即可。
本发明的有益技术效果为：
1、本发明的组分中没有强酸、铬酸盐以及氟化物，不会对环境造成污染，而且不会对镁合金造成过腐蚀，在对镁合金清洗干净彻底的基础上，不会对镁合金造成损害；
2、本发明中添加剂能加快对油污和润滑剂的清洗速度，提高工作效率，络合剂使清洗剂中的钙、镁、硅等离子保持稳定不产生絮状物，延长清洗剂的使用寿命。
具体实施方式
实施例1
一种镁合金清洗剂，由以下浓度的组分组成：氢氧化钠70g/L、磷酸钠20g/L、柠檬酸钠2g/L、十二烷基苯磺酸钠2g/L、烷基酚聚氧乙烯醚3g/L。
将待清洗处理的镁合金工件放入50℃的镁合金清洗剂中浸泡15分钟，浸泡后的镁合金工件用清水漂净，清洗后镁合金光亮清洁。
实施例2
一种镁合金清洗剂，由以下浓度的组分组成：氢氧化钠120g/L、硅酸钠5g/L、乙二胺四乙酸二钠1g/L、十二烷基苯磺酸钠0.4g/L、脂肪醇聚氧乙烯醚硫酸钠0.6g/L。
将待清洗处理的镁合金工件放入80℃的镁合金清洗剂中浸泡10分钟，浸泡后的镁合金工件用清水漂净，清洗后镁合金光亮清洁。
实施例3
一种镁合金清洗剂，由以下浓度的组分组成：氢氧化钾50g/L、焦磷酸钠50g/L、酒石酸钠1g/L、十二烷基苯磺酸钠5g/L。
将待清洗处理的镁合金工件放入80℃的镁合金清洗剂中浸泡30分钟，浸泡后的镁合金工件用清水漂净，清洗后镁合金光亮清洁。
实施例4
一种镁合金清洗剂，由以下浓度的组分组成：氢氧化钾120g/L、磷酸钠5g/L、柠檬酸钠0.5g/L、酒石酸钠0.5g/L、脂肪醇聚氧乙烯醚硫酸钠1g/L。
将待清洗处理的镁合金工件放入90℃的镁合金清洗剂中浸泡10分钟，浸泡后的镁合金工件用清水漂净，清洗后镁合金光亮清洁。
实施例5
一种镁合金清洗剂，由以下浓度的组分组成：氢氧化钠30g/L、氢氧化钾30g/L、硅酸钠2g/L、焦磷酸钠3g/L、乙二胺四乙酸二钠2g/L、酒石酸钠3g/L、烷基酚聚氧乙烯醚3g/L。
将待清洗处理的镁合金工件放入85℃的镁合金清洗剂中浸泡5分钟，浸泡后的镁合金工件用清水漂净，清洗后镁合金光亮清洁。
实施例6
一种镁合金清洗剂，由以下浓度的组分组成：氢氧化钠45g/L、氢氧化钾45g/L、焦磷酸钠5g/L、柠檬酸钠5g/L、十二烷基苯磺酸钠1g/L、脂肪醇聚氧乙烯醚硫酸钠1g/L、烷基酚聚氧乙烯醚1g/L。
将待清洗处理的镁合金工件放入90℃的镁合金清洗剂中浸泡10分钟，浸泡后的镁合金工件用清水漂净，清洗后镁合金光亮清洁。
实施例7
一种镁合金清洗剂，由以下浓度的组分组成：氢氧化钠50g/L、氢氧化钾70g/L、硅酸钠50g/L、酒石酸钠5g/L、脂肪醇聚氧乙烯醚硫酸钠1g/L、烷基酚聚氧乙烯醚2g/L。
将待清洗处理的镁合金工件放入88℃的镁合金清洗剂中浸泡15分钟，浸泡后的镁合金工件用清水漂净，清洗后镁合金光亮清洁。
实施例8
一种镁合金清洗剂，由以下浓度的组分组成：氢氧化钠20g/L、氢氧化钾30g/L、磷酸钠30g/L、硅酸钠20g/L、乙二胺四乙酸二钠5g/L、十二烷基苯磺酸钠1g/L、烷基酚聚氧乙烯醚4g/L。
将待清洗处理的镁合金工件放入100℃的镁合金清洗剂中浸泡5分钟，浸泡后的镁合金工件用清水漂净，清洗后镁合金光亮清洁。
上述虽然对本发明的具体实施方式进行了描述，但并非对本发明保护范围的限制，所属领域技术人员应该明白，在本发明的技术方案的基础上，本领域技术人员不需要付出创造性劳动即可做出的各种修改或变形仍在本发明的保护范围以内。

Claims (7)

1.一种镁合金清洗剂，其特征在于：由以下浓度的组分组成：碱50～120g/L，添加剂5～50g/L，络合剂1～5g/L，润湿剂1～5g/L，余量为水。
2.根据权利要求1所述的镁合金清洗剂，其特征在于：所述镁合金清洗剂，由以下浓度的组分组成：碱70g/L，添加剂20g/L，络合剂2g/L，润湿剂3g/L，余量为水。
3.根据权利要求2所述的镁合金清洗剂，其特征在于：所述碱为氢氧化钠和氢氧化钾中的一种或两种。
4.根据权利要求3所述的镁合金清洗剂，其特征在于：所述添加剂为磷酸钠、硅酸钠和焦磷酸钠中的一种或两种。
5.根据权利要求4所述的镁合金清洗剂，其特征在于：所述络合剂为乙二胺四乙酸二钠、柠檬酸钠和酒石酸钠中的一种或两种。
6.根据权利要求5所述的镁合金清洗剂，其特征在于：所述润湿剂为十二烷基苯磺酸钠、脂肪醇聚氧乙烯醚硫酸钠和烷基酚聚氧乙烯醚中的一种或两种 。
7.根据权利要求1-6任一所述镁合金清洗剂的使用方法：将待清洗处理的镁合金工件放入50～100℃的镁合金清洗剂中浸泡5～30分钟，将浸泡后的镁合金工件用清水漂净，即可。
CN201510411883.XA 2015-07-14 2015-07-14 一种镁合金清洗剂 Active CN104947126B (zh)