CN104946043A - 一种汽车钢圈翻新用漆的制备方法 - Google Patents
一种汽车钢圈翻新用漆的制备方法 Download PDFInfo
- Publication number
- CN104946043A CN104946043A CN201510310835.1A CN201510310835A CN104946043A CN 104946043 A CN104946043 A CN 104946043A CN 201510310835 A CN201510310835 A CN 201510310835A CN 104946043 A CN104946043 A CN 104946043A
- Authority
- CN
- China
- Prior art keywords
- parts
- preparation
- steel ring
- paint
- automobile steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种汽车钢圈翻新用漆的制备方法,包括:将各组分按配比混匀后,进行酯化处理,得到所需汽车钢圈翻新用漆的制备方法。本发明所述汽车钢圈翻新用漆的制备方法,可以克服现有技术中易脱落、附着力差和喷涂不方便等缺陷,以实现不易脱落、附着力好和喷涂方便的优点。
Description
技术领域
本发明涉及汽车技术领域,具体地,涉及一种汽车钢圈翻新用漆的制备方法。
背景技术
汽车是一种高档消费品,随着人们生活水平的提高,对汽车产业也带来个更加有力的发展。日常生活中,汽车经常处于风吹日晒的环境中,一方面容易产生褪色、脱皮等损坏,另一方面也容易受到各种腐蚀,比如酸雨等。目前,各大汽车生产企业针对汽车面漆的研究日益深入,但是都没有一种有效地措施来防止汽车面漆的脱落,换句话说,汽车面漆的附着力需要有更大的提升才能更好的满足人们的要求。
在实现本发明的过程中,发明人发现现有技术中至少存在易脱落、附着力差和喷涂不方便等缺陷。
发明内容
本发明的目的在于,针对上述问题,提出一种汽车钢圈翻新用漆的制备方法,以实现不易脱落、附着力好和喷涂方便的优点。
为实现上述目的,本发明采用的技术方案是:一种汽车钢圈翻新用漆的制备方法,包括:
⑴按以下重量份数配比各组分:
超支化聚合物:9份;
金红石型二氧化钛:3份;
聚乙烯醇:12份;
聚二甲基硅氧烷:8份;
环氧树脂:28份;
丙烯酸树脂:36份;
颜料:20份;
乙酸乙酯:12份;
聚丙烯酸酯:15份;
润湿剂:4份;
云母粉:5份;
高岭土:8份;
乙醇:15份;
丙二醇:13份;
水:32份;
⑵将各组分按配比混匀后,进行酯化处理,得到所需汽车钢圈翻新用漆的制备方法。
本发明各实施例的汽车钢圈翻新用漆的制备方法,由于包括:将各组分按配比混匀后,进行酯化处理,得到所需汽车钢圈翻新用漆的制备方法;从而可以克服现有技术中易脱落、附着力差和喷涂不方便的缺陷,以实现不易脱落、附着力好和喷涂方便的优点。
本发明的其它特征和优点将在随后的说明书中阐述,并且,部分地从说明书中变得显而易见,或者通过实施本发明而了解。
下面通过实施例,对本发明的技术方案做进一步的详细描述。
具体实施方式
以下对本发明的优选实施例进行说明,应当理解,此处所描述的优选实施例仅用于说明和解释本发明,并不用于限定本发明。
根据本发明实施例,提供了一种汽车钢圈翻新用漆的制备方法,包括:
⑴按以下重量份数配比各组分:
超支化聚合物:9份;
金红石型二氧化钛:3份;
聚乙烯醇:12份;
聚二甲基硅氧烷:8份;
环氧树脂:28份;
丙烯酸树脂:36份;
颜料:20份;
乙酸乙酯:12份;
聚丙烯酸酯:15份;
润湿剂:4份;
云母粉:5份;
高岭土:8份;
乙醇:15份;
丙二醇:13份;
水:32份;
⑵将各组分按配比混匀后,进行酯化处理,得到所需汽车钢圈翻新用漆的制备方法。
经验证,本发明的技术方案所得产品,耐化学性能、耐气候性能、光泽度高同时附着力好,有效地提高汽车面漆与车身的附着力;抗紫外线吸收剂采用金红石型纳米氧化钛,抗紫外线效果优异,延长了面漆褪色周期。
最后应说明的是:以上所述仅为本发明的优选实施例而已,并不用于限制本发明,尽管参照前述实施例对本发明进行了详细的说明,对于本领域的技术人员来说,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (1)
1.一种汽车钢圈翻新用漆的制备方法,其特征在于,包括:
⑴按以下重量份数配比各组分:
超支化聚合物:9份;
金红石型二氧化钛:3份;
聚乙烯醇:12份;
聚二甲基硅氧烷:8份;
环氧树脂:28份;
丙烯酸树脂:36份;
颜料:20份;
乙酸乙酯:12份;
聚丙烯酸酯:15份;
润湿剂:4份;
云母粉:5份;
高岭土:8份;
乙醇:15份;
丙二醇:13份;
水:32份;
⑵将各组分按配比混匀后,进行酯化处理,得到所需汽车钢圈翻新用漆的制备方法。