CN104945686A - 一种敏感农药用易降解型壳聚糖基包覆膜以及制备方法 - Google Patents
一种敏感农药用易降解型壳聚糖基包覆膜以及制备方法 Download PDFInfo
- Publication number
- CN104945686A CN104945686A CN201510402569.5A CN201510402569A CN104945686A CN 104945686 A CN104945686 A CN 104945686A CN 201510402569 A CN201510402569 A CN 201510402569A CN 104945686 A CN104945686 A CN 104945686A
- Authority
- CN
- China
- Prior art keywords
- chitosan
- succinyl
- stirred
- afterwards
- covering film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种敏感农药用易降解型壳聚糖基包覆膜,其特征在于,该组合物包括由下列重量份的原料:N-琥珀酰壳聚糖20-30、聚乳酸2-3、丙交酯1-2、改性多介质孔海藻酸钠1.2-1.6、过硫酸铵0.4-0.8、N、N’-亚双基双丙烯酰胺0.6-0.8、改性多孔葡聚糖1-2、纤维素二醋酸酯0.5-0.7、聚己内酯0.8-1、有机溶剂5-6、脂肪醇聚氧乙烯醚0.7-0.9、适量的浓度1%的醋酸溶液以及适量的水。本发明通过加入改性多介质孔海藻酸钠分散剂改性N-琥珀酰壳聚糖,增加了N-琥珀酰壳聚糖对敏药物的吸附性,通过改性多孔葡聚糖和丙交酯制得的改性葡聚糖交联剂实现各包覆膜层材料的交联混合,进而制备包覆膜,增加了包覆膜材料的敏感药物的透过性。
Description
技术领域
本发明属于农药用包覆膜领域,具体地说是涉及一种敏感农药用易降解型壳聚糖基包覆膜以及制备方法。
背景技术
农药是农作物健康生长的保证,但是农药的易挥发以及刺鼻的难闻的味道使得农药在喷洒过程中极易给工作人 员造成伤害,每年出现的在工作中农药中毒造成生命伤亡的案例不计其数,因此发展一种农药包覆膜,使得农药进行一定程度的包覆,减缓农药功能的发挥但又不影响功能作用及其重要。壳聚糖作为一种天然大分子多糖,具有来源广泛、无毒、无味、良好的生物相容性和生物降解和良好的抗菌性等性能特征,并且其降解产物无毒;在壳聚糖分子结构中存在大量的游离氨基酸,是天然多糖中少见的带正电荷的高分子化合物,可以结合其它高分子化合物实现天然功能性物质的包覆,进而实现预想的功能。
发明内容
为解决上述技术问题,本发明的目的是提供一种敏感农药用易降解型壳聚糖基包覆膜以及制备方法。
为达到上述目的,本发明所采取的技术方案为:
一种敏感农药用易降解型壳聚糖基包覆膜,其特征在于,该组合物包括由下列重量份的原料:N-琥珀酰壳聚糖20-30、聚乳酸2-3、丙交酯1-2、改性多介质孔海藻酸钠1.2-1.6、过硫酸铵0.4-0.8、N、N’-亚双基双丙烯酰胺0.6-0.8、改性多孔葡聚糖1-2、纤维素二醋酸酯0.5-0.7、聚己内酯0.8-1、有机溶剂5-6、脂肪醇聚氧乙烯醚0.7-0.9、适量的浓度1%的醋酸溶液以及适量的水。
一种敏感农药用易降解型壳聚糖基包覆膜,其特征在于,包括以下步骤:
(1)取聚乳酸并加入7-9倍的水加热80℃搅拌至均匀,之后缓慢加入N-琥珀酰壳聚糖,升温至80℃加热搅拌完全溶解,之后加入改性多介质孔海藻酸钠,搅拌至均匀后得改性N-琥珀酰壳聚糖溶液备用;
(2)取有机溶剂加热75℃搅拌至均匀,之后缓慢加入过硫酸铵、N、N’-亚双基双丙烯酰胺、纤维素二醋酸酯、聚己内酯、升温至80℃加热搅拌完全溶解,之后加入脂肪醇聚氧乙烯醚,搅拌至均匀后得混合溶液备用;
(3)将改性多孔葡聚糖和丙交酯在高温下180-200℃下共混制得改性葡聚糖交联剂备用;
(4)将改性N-琥珀酰壳聚糖溶液、混合溶液、改性葡聚糖交联剂混合,通过磁力搅拌至均匀,高压低温脱水份含量为总重量的4-6%,之后进行-3~0℃的冷冻2-3h,得胶冻状包覆材料备用;
(5)取胶冻状包覆材料在室温下加入总重量2-3倍的浓度1%的醋酸溶液,浸泡1-2min后即得。
本发明的有益效果:
本发明通过加入改性多介质孔海藻酸钠分散剂改性N-琥珀酰壳聚糖,增加了N-琥珀酰壳聚糖对敏药物的吸附性,通过改性多孔葡聚糖和丙交酯制得的改性葡聚糖交联剂实现各包覆膜层材料的交联混合,进而制备包覆膜,增加了包覆膜材料的敏感药物的透过性。
具体实施方式
下面结合具体实施例对本发明所述技术方案作进一步的说明。
实施例1:
本实施例所述敏感农药用易降解型壳聚糖基包覆膜,其特征在于,该组合物包括由下列重量份的原料:N-琥珀酰壳聚糖20、聚乳酸2、丙交酯1、改性多介质孔海藻酸钠1.2、过硫酸铵0.4、N、N’-亚双基双丙烯酰胺0.6、改性多孔葡聚糖1、纤维素二醋酸酯0.5、聚己内酯0.8、有机溶剂5、脂肪醇聚氧乙烯醚0.7、适量的浓度1%的醋酸溶液以及适量的水。
本实施例所述敏感农药用易降解型壳聚糖基包覆膜,其特征在于,包括以下步骤:
(1)取聚乳酸并加入7倍的水加热80℃搅拌至均匀,之后缓慢加入N-琥珀酰壳聚糖,升温至85℃加热搅拌完全溶解,之后加入改性多介质孔海藻酸钠,搅拌至均匀后得改性N-琥珀酰壳聚糖溶液备用;
(2)取有机溶剂加热75℃搅拌至均匀,之后缓慢加入过硫酸铵、N、N’-亚双基双丙烯酰胺、纤维素二醋酸酯、聚己内酯、升温至80℃加热搅拌完全溶解,之后加入脂肪醇聚氧乙烯醚,搅拌至均匀后得混合溶液备用;
(3)将改性多孔葡聚糖和丙交酯在高温下180℃下共混制得改性葡聚糖交联剂备用;
(4)将改性N-琥珀酰壳聚糖溶液、混合溶液、改性葡聚糖交联剂混合,通过磁力搅拌至均匀,高压低温脱水份含量为总重量的4%,之后进行-3℃的冷冻2h,得胶冻状包覆材料备用;
(5)取胶冻状包覆材料在室温下加入总重量2-3倍的浓度1%的醋酸溶液,浸泡1-2min后即得。
实施例2:
本实施例所述的敏感农药用易降解型壳聚糖基包覆膜,其特征在于,该组合物包括由下列重量份的原料:N-琥珀酰壳聚糖25、聚乳酸2.5、丙交酯1.5、改性多介质孔海藻酸钠1.4、过硫酸铵0.6、N、N’-亚双基双丙烯酰胺0.7、改性多孔葡聚糖1.5、纤维素二醋酸酯0.6、聚己内酯0.9、有机溶剂5.5、脂肪醇聚氧乙烯醚0.8、适量的浓度1%的醋酸溶液以及适量的水。
本实施例所述的敏感农药用易降解型壳聚糖基包覆膜,其特征在于,包括以下步骤:
(1)取聚乳酸并加入8倍的水加热80℃搅拌至均匀,之后缓慢加入N-琥珀酰壳聚糖,升温至85℃加热搅拌完全溶解,之后加入改性多介质孔海藻酸钠,搅拌至均匀后得改性N-琥珀酰壳聚糖溶液备用;
(2)取有机溶剂加热75℃搅拌至均匀,之后缓慢加入过硫酸铵、N、N’-亚双基双丙烯酰胺、纤维素二醋酸酯、聚己内酯、升温至80℃加热搅拌完全溶解,之后加入脂肪醇聚氧乙烯醚,搅拌至均匀后得混合溶液备用;
(3)将改性多孔葡聚糖和丙交酯在高温下190℃下共混制得改性葡聚糖交联剂备用;
(4)将改性N-琥珀酰壳聚糖溶液、混合溶液、改性葡聚糖交联剂混合,通过磁力搅拌至均匀,高压低温脱水份含量为总重量的4-6%,之后进行-2℃的冷冻2.5h,得胶冻状包覆材料备用;
(5)取胶冻状包覆材料在室温下加入总重量2-3倍的浓度1%的醋酸溶液,浸泡1-2min后即得。
实施例3:
本事实施例所述的敏感农药用易降解型壳聚糖基包覆膜,其特征在于,该组合物包括由下列重量份的原料:N-琥珀酰壳聚糖30、聚乳酸3、丙交酯2、改性多介质孔海藻酸钠1.6、过硫酸铵0.8、N、N’-亚双基双丙烯酰胺0.8、改性多孔葡聚糖2、纤维素二醋酸酯0.7、聚己内酯1、有机溶剂6、脂肪醇聚氧乙烯醚0.9、适量的浓度1%的醋酸溶液以及适量的水。
本实施例所述的敏感农药用易降解型壳聚糖基包覆膜,其特征在于,包括以下步骤:
(1)取聚乳酸并加入9倍的水加热80℃搅拌至均匀,之后缓慢加入N-琥珀酰壳聚糖,升温至85℃加热搅拌完全溶解,之后加入改性多介质孔海藻酸钠,搅拌至均匀后得改性N-琥珀酰壳聚糖溶液备用;
(2)取有机溶剂加热75℃搅拌至均匀,之后缓慢加入过硫酸铵、N、N’-亚双基双丙烯酰胺、纤维素二醋酸酯、聚己内酯、升温至80℃加热搅拌完全溶解,之后加入脂肪醇聚氧乙烯醚,搅拌至均匀后得混合溶液备用;
(3)将改性多孔葡聚糖和丙交酯在高温下200℃下共混制得改性葡聚糖交联剂备用;
(4)将改性N-琥珀酰壳聚糖溶液、混合溶液、改性葡聚糖交联剂混合,通过磁力搅拌至均匀,高压低温脱水份含量为总重量的4-6%,之后进行-1℃的冷冻3h,得胶冻状包覆材料备用;
(5)取胶冻状包覆材料在室温下加入总重量2-3倍的浓度1%的醋酸溶液,浸泡1-2min后即得。
Claims (2)
1.一种敏感农药用易降解型壳聚糖基包覆膜,其特征在于,该组合物包括由下列重量份的原料:N-琥珀酰壳聚糖20-30、聚乳酸2-3、丙交酯1-2、改性多介质孔海藻酸钠1.2-1.6、过硫酸铵0.4-0.8、N、N’-亚双基双丙烯酰胺0.6-0.8、改性多孔葡聚糖1-2、纤维素二醋酸酯0.5-0.7、聚己内酯0.8-1、有机溶剂5-6、脂肪醇聚氧乙烯醚0.7-0.9、适量的浓度1%的醋酸溶液以及适量的水。
2.一种敏感农药用易降解型壳聚糖基包覆膜,其特征在于,包括以下步骤:
(1)取聚乳酸并加入7-9倍的水加热80℃搅拌至均匀,之后缓慢加入N-琥珀酰壳聚糖,升温至80℃加热搅拌完全溶解,之后加入改性多介质孔海藻酸钠,搅拌至均匀后得改性N-琥珀酰壳聚糖溶液备用;
(2)取有机溶剂加热75℃搅拌至均匀,之后缓慢加入过硫酸铵、N、N’-亚双基双丙烯酰胺、纤维素二醋酸酯、聚己内酯、升温至80℃加热搅拌完全溶解,之后加入脂肪醇聚氧乙烯醚,搅拌至均匀后得混合溶液备用;
(3)将改性多孔葡聚糖和丙交酯在高温下180-200℃下共混制得改性葡聚糖交联剂备用;
(4)将改性N-琥珀酰壳聚糖溶液、混合溶液、改性葡聚糖交联剂混合,通过磁力搅拌至均匀,高压低温脱水份含量为总重量的4-6%,之后进行-3~0℃的冷冻2-3h,得胶冻状包覆材料备用;
(5)取胶冻状包覆材料在室温下加入总重量2-3倍的浓度1%的醋酸溶液,浸泡1-2min后即得。